Abstract: Cubic as well as hexagonal single crystals of C70 have been grown and investigated by electron diffraction, electron microscopy and X-ray diffraction. Several phase transitions have been detected and crystallographic models are proposed. Hexagonal crystals, stable at room temperature with c/a = 1.63 will undergo two transitions, upon cooling. First the c/a ratio will increase to 1.82 owing to c-axis allignment of the molecules; at a lower temperature the molecules will orientationally order, resulting in a monoclinic structure.

Abstract: YBCO-based materials containing SO4-tetrahedra centered on the Cu(1)-sites of the CuO-chain plane have been examined by means of electron diffraction and high resolution electron microscopy. An incommensurate modulation is observed and attributed to the ordering of b-oriented SO4-rich chains in the Cu(1)-S-O-layer, described in terms of an SO4-concentration wave.

Abstract: In Bi2Sr2Ca0.6Y0.4Cu2Oy single crystals we have identified the intergrowth of two phases; a normal Bi2Sr2CaCu2Oy type phase with a 4.6b modulation period and a secondary,phase with a 9.4b modulation period. Both the two phases have orthorhombic basic structures with similar lattice parameters but different symmetries, i.e. Bbmb for the normal phase and Ccca for the secondary phase. The c-parameters of these two phases are found to vary independently upon changing the nominal Y content. The modulation characteristics of the secondary phase implies a close structural relation between the two phases. Both phases are discussed from a structural and a compositional point of view.

Abstract: http://dx.doi.org/doi:10.1103/PhysRevLett.69.1065

Abstract: Single crystals with two different morphologies, black and brown, of C60 with about 12% C70 have been studied by synchrotron X-ray diffraction. Integrated intensities from 8 reflections show that the charge distribution of the C60 cluster is shell-like giving rise to an oscillatory behaviour in the diffracted intensities. From the intensities, the distance between diametrically opposite carbon atoms has been determined to be (7.24 +/- 0.22) angstrom. The thickness of the charge distribution of the shell can be estimated as 3.06 angstrom and the cavity within a C60 cluster to have a diameter of about 4.18 angstrom. The finite longitudinal width of the diffraction peaks from black crystals indicates a lack of long-range crystalline order. The rocking curves are about 7-degrees broad and depict an unusually smooth behaviour. This may be indicative of a glassy or hexatic phase. High-resolution electron microscopy allows small crystallites with a relatively well-defined orientation relationship to be identified. In contrast, brown crystals have long-range order.

Abstract: Oxygen ordering has been investigated in superconducting ABa2Cu3O7-delta ceramic materials with A = Er, Nd, Sm and Yb, as well as in samples of this type with the rate earth A partially substituted by Pr. The critical temperature T(c) was determined as a function of the oxygen deficiency-delta of the compound and the corresponding microstructures were investigated by electron diffraction and electron microscopy. A distinct relationship exists between the width of the 60 K plateau and the ortho II ordering. Our results show that the ortho II ordered phase is the superconducting phase with a characteristic T(c) of 60 K.

Abstract: The structure of Ca0.85CuO2 was reexamined by means of electron diffraction and electron microscopy using the newly developed method of selective imaging in intergrowth structures in which the two substructures are based on different sublattices. The results of previous work are confirmed. Moreover, it is shown that two stacking variants and their twin related structures occur in the calcium substructure. The copper-oxygen substructure occurs in one variant only; it is often modulated by the various calcium arrangements, leading to phase disorder in its modulation pattern. It is shown that the ribbons of CuO4 clusters are presumably tilted with respect to the (010) plane.