“3D strain fields surrounding Ni4Ti3: direct measurement and correlation with the R-phase”. Tirry W, Schryvers D, , 02032 (2009). http://doi.org/10.1051/esomat/200902032
Abstract: Strain fields introduced by coherent Ni4Ti3 precipitates in austenitic Ni-Ti are believed to be a possible origin of why the R-phase transformation is introduced as an extra step before transforming to the B19'. The presence of this strain field was already confirmed in the past by conventional transmission electron microscopy (TEM) techniques and measured quantitatively by high resolution TEM (HRTEM). This time the geometrical phase method is applied on HRTEM micrographs to measure the full 3D strain tensor of the strain fields. Since each atomic resolution micrograph only results in a 2D measurement of the strain, observations in two different zone orientations are combined to retrieve the 3 x 3 strain tensor. In this work observations in a [1-1 1](B2) and [1 0-1](B2) zone orientation are used and this in case of precipitates with a diameter of around 50nm. In a next step the measured strain tensor is compared to the calculated eigenstrain of the R-phase in reference to the B2 matrix. This comparison shows that the introduced strain is very similar to the eigenstrain of one R-phase variant. Since for both structures, Ni4Ti3 and R-phase, four orientation variants are possible, each variant of the R-phase is thus able to accommodate the strain field of one of the Ni4Ti3 variants.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
DOI: 10.1051/esomat/200902032
|
|
|
“Linking a completely three-dimensional nanostrain to a structural transformation eigenstrain”. Tirry W, Schryvers D, Nature materials 8, 752 (2009). http://doi.org/10.1038/NMAT2488
Abstract: NiTi is one of the most popular shape-memory alloys, a phenomenon resulting from a martensitic transformation. Commercial NiTi-based alloys are often thermally treated to contain Ni4Ti3 precipitates. The presence of these precipitates can introduce an extra transformation step related to the so-called R-phase. It is believed that the strain field surrounding the precipitates, caused by the matrixprecipitate lattice mismatch, lies at the origin of this intermediate transformation step. Atomic-resolution transmission electron microscopy in combination with geometrical phase analysis is used to measure the elastic strain field surrounding these precipitates. By combining measurements from two different crystallographic directions, the three-dimensional strain matrix is determined from two-dimensional measurements. Comparison of the measured strain matrix to the eigenstrain of the R-phase shows that both are very similar and that the introduction of the R-phase might indeed compensate the elastic strain introduced by the precipitate.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
Times cited: 53
DOI: 10.1038/NMAT2488
|
|
|
“In situ transmission electron microscopy of stress-induced martensite with focus on martensite twinning”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 420 (2008). http://doi.org/10.1016/j.msea.2006.12.214
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 22
DOI: 10.1016/j.msea.2006.12.214
|
|
|
“Quantitative determination of strain fields around Ni4Ti3 precipitates in NiTi”. Tirry W, Schryvers D, Acta materialia 53, 1041 (2005). http://doi.org/10.1016/j.actamat.2004.10.049
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 97
DOI: 10.1016/j.actamat.2004.10.049
|
|
|
“High resolution TEM study of Ni4Ti3 precipitates in austenitic Ni51Ti49”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 157 (2004). http://doi.org/10.1016/j.msea.2003.10.336
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 19
DOI: 10.1016/j.msea.2003.10.336
|
|