“Characterization and analysis of the adsorption immobilization mechanism of \beta-galactosidase on metal oxide powders”. Satyawali Y, Van Roy S, Roevens A, Meynen V, Mullens S, Jochems P, Doyen W, Cauwenberghs L, Dejonghe W, RSC advances 3, 24054 (2013). http://doi.org/10.1039/C3RA45107K
Abstract: Immobilization of the enzymes plays a vital role in enhancing their applicability in a wide range of applications, thus ensuring the use of sustainable enzymatic processes over the conventional chemical processes on an industrial scale. This study provides the background information for the selection and screening of inorganic metal oxide (MO) powders for their use as fillers in mixed matrix membranes for enzyme immobilization as the future aim. A total of 13 MOs, ranging in size from 0.01 μm to <5 μm, were tested for their performance as a support for enzyme (β-galactosidase) immobilization via adsorption. Alumina appeared to be the best performing MO with the amount and activity of the immobilized enzyme being 64 mg g−1 and up to 288 U g−1, respectively. The amount of immobilized enzyme on alumina (α-Al2O3 C and γ-Al2O3) was >3 times higher than ZrO2 (used as a reference MO in this study). Upon heat treatment at 900 °C, up to 15%, 52% and 42% decline was observed in the amount of immobilized enzyme in case of alumina metal oxides (MOs), ZrO2 and TiO2, respectively. The results suggested that both isoelectric point and surface area of the MO influence the immobilization. The most important observation in this study was that the bonding of the enzyme to the MO surface seems to be mediated by the bonding/interaction of the buffer to the enzyme.
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1039/C3RA45107K
|
“Fluorine doped Fe2O3 nanostructures by a one-pot plasma-assisted strategy”. Carraro G, Gasparotto A, Maccato C, Bontempi E, Lebedev OI, Turner S, Sada C, Depero LE, Van Tendeloo G, Barreca D, RSC advances 3, 23762 (2013). http://doi.org/10.1039/c3ra43775b
Abstract: The present work reports on the synthesis of fluorine doped Fe2O3 nanomaterials by a single-step plasma enhanced-chemical vapor deposition (PE-CVD) strategy. In particular, Fe(hfa)2TMEDA (hfa = 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-tetramethylethylenediamine) was used as molecular source for both Fe and F in Ar/O2 plasmas. The structure, morphology and chemical composition of the synthesized nanosystems were thoroughly analyzed by two-dimensional X-ray diffraction (XRD2), field emission-scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and transmission electron microscopy (TEM). A suitable choice of processing parameters enabled the selective formation of α-Fe2O3 nanomaterials, characterized by an homogeneous F doping, even at 100 °C. Interestingly, a simultaneous control of the system nanoscale organization and fluorine content could be achieved by varying the sole growth temperature. The tailored properties of the resulting materials can be favourably exploited for several technological applications, ranging from photocatalysis, to photoelectrochemical cells and gas sensing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 23
DOI: 10.1039/c3ra43775b
|
“Thermal decomposition synthesis of Al-doped ZnO nanoparticles : an in-depth study”. Damm H, Kelchtermans A, Bertha A, Van den Broeck F, Elen K, Martins JC, Carleer R, D'Haen J, De Dobbelaere C, Hadermann J, Hardy A, Van Bael MK;, RSC advances 3, 23745 (2013). http://doi.org/10.1039/c3ra43328e
Abstract: Al-doped ZnO nanoparticles are synthesized by means of a heating up solution based thermal decomposition method. The synthesis involves a reaction of zinc acetylacetonate hydrate, aluminium acetylacetonate and 1,2-hexadecanediol in the presence of oleic acid and oleyl amine. A proposed reaction mechanism from reagents to monomers is corroborated by analysis of the evolving gases using headspace GC-MS analysis. The Al-doped ZnO nanoparticles synthesized are dynamically stabilized by adsorbed oleate ions, after deprotonation of oleic acid by oleyl amine, as was found by NOESY proton NMR and complementary FTIR spectroscopy. Precession electron diffraction shows a simultaneous increase in lattice parameters with Al concentration. This, together with HAADF-STEM and EDX maps, indicates the incorporation of Al into the ZnO nanoparticles. By the combination of complementary characterization methods during all stages of the synthesis, it is concluded that Al is incorporated into the ZnO wurtzite lattice as a dopant.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 10
DOI: 10.1039/c3ra43328e
|
“Luminescence of oxyfluoride glasses co-doped with Ag nanoclusters and Yb3+ ions”. Tikhomirov VK, Vosch T, Fron E, Rodríguez VD, Velázquez JJ, Kirilenko D, Van Tendeloo G, Hofkens J, Van der Auweraer M, Moshchalkov VV, RSC advances 2, 1496 (2012). http://doi.org/10.1039/c1ra01026c
Abstract: Bulk oxyfluoride glasses co-doped with Ag nanoclusters and Yb3+ ions have been prepared by a melt quenching technique. When excited in the absorption band of the Ag nanoclusters between 300 to 500 nm, these glasses emit a broad band characteristic of the Ag nanoclusters between 400 to 750 nm as well as an emission band between 900 to 1100 nm, originating from Yb3+ ions. The intensity ratio of the Yb3+/Ag emission bands increases with the Ag doping level at a fixed concentration of Yb3+, indicating the presence of energy transfer mechanism from the Ag nanoclusters to the Yb3+ ions. Comparison of time-resolved decay kinetics of the luminescence in the respectively Ag nanocluster-Yb3+ co-doped and single Ag nanocluster doped glasses, hints towards an energy transfer from the red and infrared emitting Ag nanoclusters to the Yb3+ ions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 46
DOI: 10.1039/c1ra01026c
|