Abstract: Results of dielectric and resonance frequency (f(r)) measurements below room temperature are presented for Pb(ZrxTi1-x)O-3, x = 0.515 and 0.520. It is shown that the temperature coefficient of f(r) changes sign from negative to positive around 210 and 265 K for x = 0.520 and 200 and 260 K for x = 0.515. Anomalies in the real part of the dielectric constant (epsilon') are observed around the same temperatures at which the temperature coefficient of f(r) changes sign because of the electrostrictive coupling between the elastic and dielectric responses. Low-temperature powder x-ray-diffraction (XRD) data, however, reveal only one transition from the tetragonal to monoclinic phase similar to that reported by Noheda et al. [Phys. Rev. B, 61, 8687 (2000)]. Electron-diffraction data, on the other hand, reveal yet another structural transition at lower temperatures corresponding to the second anomaly in the epsilon' vs T and f(r) vs T curves. This second transition is shown to be a cell-doubling transition not observed by Noheda et al. in their XRD studies. The observation of superlattice reflections raises doubts about the correctness of the Cm space group proposed by Noheda et al. for the monoclinic phase of Pb(ZrxTi(1-x))O-3 below the second transition temperature.

Abstract: An epitaxially grown heterostructure consisting of alternating layers of LaMnO3 (8 unit cells) and SrMnO3 (4 unit cells) on a SrTiO3 substrate has been studied by a combination of electron energy-loss spectroscopy (EELS) and high-resolution transmission electron microscopy (HRTEM) on an atomic scale. Excitation edges of all elements are captured with subnanometer spatial accuracy, and parametrized to obtain chemical profiles. The fine-edge structure of O K and Mn L-2,L-3 edges are interpreted as signatures of the local electronic structure and show a spatial modulation of the concentration of holes with O 2p character. The chemical concentration is found to be different for the bottom and top interface of a SrMnO3 layer. HRTEM complements the EELS results and confirms the asymmetry of the interfaces. (C) 2001 American Institute of Physics.

Abstract: The double phosphate Ca9In(PO4)(7) was obtained by solid-state reaction and was studied by room and high-temperature Xray powder diffraction, electron diffraction, high-resolution electron microscopy, second-harmonic generation (SHG) technique, differential scanning calorimetry, dielectric and conductivity measurements. The beta-Ca9In(PO4)(7) room-temperature phase is related to the mineral whitlockite and is similar to beta-Ca-3(PO4)(2). It has space group R (3) over barc, with unit cell parameters: a = 10.4008(1) Angstrom, c = 37.272(1) Angstrom, Z = 6. The structure was refined by the Rietveld method (R-wp = 4.69, R-I = 1.81). A reversible first-order beta <----> beta' phase transition of the ferroelectric type with T-c = 902 K is revealed by SHG, differential scanning calorimetry and dielectric measurements. The centrosymmetric beta'-Ca9In(PO4)(7) (973 K) has space group R (3) over barc, a = 10.4611(2) Angstrom, c = 37.874 (1) Angstrom (R-wp = 4.27, R-I = 4.11). Compared to the low-temperature beta-Ca9In(PO4)(7) structure, beta'-Ca9In(PO4)(7) can be described as an orientational disordering of the P1O(4) tetrahedra together with a calcium disordering on the M3 site. (C) 2002 Elsevier Science (USA).

Abstract: The microstructure of BaTiO3 thin films, epitaxially deposited on (001) MgO by pulsed laser ablation, has been investigated by transmission electron microscopy. The films are always c-axis-orientated, but dislocations, {111} stacking faults, and antiphase boundaries are frequently observed. Conventional TEM and high-resolution microscopy allow one to deduce the Burgers vectors of dislocations as b(1) = <100> or b(2) = <110>, both being perfect dislocations. Most extrinsic stacking faults are ending at 1/3<112> or 1/3<111> partial dislocations; the displacement vector of the antiphase boundaries is 1/2<101>. Studying the interfacial structure by means of zone images taken along [100] and [110] shows that the misfit is mainly released by dislocations with Burgers vectors of 1/2<110> and 1/2<101>.