Abstract: The microstructure of (Bi,Pb)2Sr2Ca2Cu3Ox (Bi-2223) tapes has been investigated by means of transmission electron microscopy (TEM) and high-resolution TEM. The emphasis has been placed on: (1) an examination of the grain morphology and size, (2) grain and colony boundary angles, which are formed during the tape processing, (3) a study of the grain boundaries on an atomic scale, including intergrowth investigations. Tapes with different process parameters have been compared with respect to the microstructure. A fully processed tape has on the average 50% thicker Bi-2223 grains than a tape after the first annealing. The angles of c-axis tilt grain boundaries are on average 14° and 26° for the fully processed tape and the tape after the first annealing, respectively. The intergrowth content (15%) and distribution are similar in these two tapes.

Abstract: The formation of Ni silicides is studied by transmission electron microscopy during in situ heating experiments of 12 nm Ni layers on blanket silicon, or in patterned structures covered with a thin chemical oxide. It is shown that the first phase formed is the NiSi2 which grows epitaxially in pyramidal crystals. The formation of NiSi occurs quite abruptly around 400 degreesC when a monosilicide layer covers the disilicide grains and the silicon in between. The NiSi phase remains stable up to 800 degreesC, at which temperature the layer finally fully transforms to NiSi2. The monosilicide grains show different epitaxial relationships with the Si substrate. Ni2Si is never observed. (C) 2001 American Institute of Physics.

Abstract: Using pulsed laser deposition ultra-thin DyBa2Cu3O7-x films were deposited on a single terminated (0 0 1) SrTiOr(3) substrate. The initial growth was studied by high-resolution electron microscopy. Two different types of interface arrangements occur and were determined as: bulk-SrO-TiO2-BaO-CuO-BaO-CuO2-Dy-CuO2-BaO bulk and bulk-SrO-TiO2-BaO-CuO2-Dy-CuO2-BaO-CuO-BaO-bulk This variable growth sequence causes structural shifts, resulting in antiphase boundaries with displacement vector R = [0 0 1/3]. as well as local chemical variations. (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: Results of dielectric and resonance frequency (f(r)) measurements below room temperature are presented for Pb(ZrxTi1-x)O-3, x = 0.515 and 0.520. It is shown that the temperature coefficient of f(r) changes sign from negative to positive around 210 and 265 K for x = 0.520 and 200 and 260 K for x = 0.515. Anomalies in the real part of the dielectric constant (epsilon') are observed around the same temperatures at which the temperature coefficient of f(r) changes sign because of the electrostrictive coupling between the elastic and dielectric responses. Low-temperature powder x-ray-diffraction (XRD) data, however, reveal only one transition from the tetragonal to monoclinic phase similar to that reported by Noheda et al. [Phys. Rev. B, 61, 8687 (2000)]. Electron-diffraction data, on the other hand, reveal yet another structural transition at lower temperatures corresponding to the second anomaly in the epsilon' vs T and f(r) vs T curves. This second transition is shown to be a cell-doubling transition not observed by Noheda et al. in their XRD studies. The observation of superlattice reflections raises doubts about the correctness of the Cm space group proposed by Noheda et al. for the monoclinic phase of Pb(ZrxTi(1-x))O-3 below the second transition temperature.