Abstract: Infrared absorption spectra of polyhedral and platelet oxygen precipitates in silicon are analyzed using a modified Day-Thorpe approach [J. Phys.: Condens. Matter 11, 2551 (1999)]. The aspect ratio of the precipitates is determined by transmission electron microscopy analysis. The reduced spectral function and the stoichiometry of the precipitate are extracted from the absorption spectra and the amount of precipitated interstitial oxygen. The experimental absorption spectra can be divided in a set with a Frohlich frequency of around 1100 cm(-1) and in a set with a Frohlich frequency between 1110 and 1120 cm(-1). It is shown that the shift in the Frohlich frequency is not due to a differing stoichiometry, but to the detailed structure of the reduced spectral function. Inverse modeling of the spectra suggests that the oxide precipitates consist of substoichiometric SiOgamma with gamma=1.17+/-0.14. (C) 2002 American Institute of Physics.

Abstract: The formation of Ni silicides is studied by transmission electron microscopy during in situ heating experiments of 12 nm Ni layers on blanket silicon, or in patterned structures covered with a thin chemical oxide. It is shown that the first phase formed is the NiSi2 which grows epitaxially in pyramidal crystals. The formation of NiSi occurs quite abruptly around 400 degreesC when a monosilicide layer covers the disilicide grains and the silicon in between. The NiSi phase remains stable up to 800 degreesC, at which temperature the layer finally fully transforms to NiSi2. The monosilicide grains show different epitaxial relationships with the Si substrate. Ni2Si is never observed. (C) 2001 American Institute of Physics.

Abstract: Two CoSi2/Si1-xGex/Si(100) heterostructures, with different Ge content, made by molecular beam epitaxy are characterized by high resolution electron microscopy. In general, the interface between the CoSi2 thin film and the Si1-xGex layer is of a high structural quality and the strained Si1-xGex layer exhibits few defects. For both samples, different interface structures are present, although the dominant interfacial configuration is similar to the unreconstructed interface present at the CoSi2/Si(100) interface. Only occasionally (2x1) reconstructed interface regions are found which are just a few nanometers in length. Phenomena such as Ge segregation and the introduction of defects are also observed in the Si1-xGex layer. We attribute the minimal presence of the reconstructed interface to both the (2x8):Si1-xGex(100) surface reconstruction and the Ge segregation that takes place. (C) 1999 American Institute of Physics. [S0021-8979(99)02104-0].