Abstract: An in situ study of more than 100 ballast tanks of merchant marine vessels looks to the corrosion process in these tanks from another perspective. The developed corrosion model shows major similarities with earlier studies based on laboratory experiments. The field work exposes the influence of ship construction parameters such as land of construction, coating type and the presence of sacrificial anodes on the corrosion process in the ballast tanks. Possible alternatives for vessels constructed with ordinary grade A steel and coated according to IMO PSPC standards are presented, even though further research is required to come to final conclusions.

Abstract: A study was undertaken to determine causes and effects of corrosion processes in ballast tanks. Part 1 of this article (October 2009 MP) described the data collection. Part 2 describes the development of a corrosion index (CI) derived from the general International Association of Classification Societies corrosion assessment methods. The CI can be used in situ to assess ballast tank corrosion. An average timeline for-corrosion of tanks is presented.

Abstract: The engineering, construction, performance and running costs of a catalytic flue gas cleaning component in the low dust area of a municipal waste incinerator is discussed. For this purpose, the case study of a Flemish incineration plant is presented, covering the history, the design procedure of the catalyst, relevant process data and the financial aspects. A reliable PCDD/F-destruction by means of oxidation by the catalyst to typical values of 0.001 ng TEQ/N m3 has been demonstrated. At the same time, NOx- and CO-emissions are reduced by 90% and 20% to about 50 mg/N m3 and below 10 mg/N m3, respectively.

Abstract: Oxygen-permeable perovskites with mixed ionic-electronic conducting properties can play an important role in the separation of oxygen from air which is needed in the oxy-fuel and pre-combustion technologies for the removal and capture of CO2. In this work, gastight, macrovoid-free Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) capillaries were successfully shaped by a phase-inversion spinning technique, followed by calcination and sintering. It was found that both the rheology of the ceramic suspension and the composition of bore liquid and coagulation bath are key factors for making macrovoid-free green capillaries. Gastight BSCF capillaries were obtained by sintering for 5 h at 1100 °C. The sintered BSCF capillaries contained a significant amount of BaSO4 due to a reaction with the polysulfone binder during calcination. The oxygen permeation flux through the BSCF capillaries was measured and compared to literature data on BSCF disk and hollow fiber membranes measured in similar conditions.

Abstract: Analysis of oxygen permeation fluxes through Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) capillary membranes, fabricated via a phase-inversion spinning technique using polysulfone as binder, showed a significant limiting role of the surface-oxygen exchange kinetics. Within the studied temperature and oxygen partial pressure ranges, the activation of core and shell sides of the BSCF capillary with praseodymium oxide (PrOx) resulted in an increase in permeation rate of about 300%. At 11231223 K the activated BSCF membranes demonstrate almost 3-times lower activation energies for the overall oxygen transport (not, vert, similar35 kJ/mol) than the non-activated capillaries, indicating that the mechanism of oxygen transport through the activated capillaries becomes significantly controlled by bulk diffusion limitations, allowing further improvement of the overall performance by decreasing the wall thickness. XRD, EDS and EPMA studies revealed the formation of (Pr,Ba,Sr)(Co,Fe)O3−δ perovskite-type oxides on the surface of the PrOx-modified membranes, which may be responsible for the drastic increase in oxygen exchange rate. At T > 1123 K both non-activated and activated Ba0.5Sr0.5Co0.8Fe0.2O3−δ membranes demonstrate stable performance with time, while at 1073 K only a small initial decrease in permeation was observed.

Abstract: In this paper, the reaction mechanism of the photocatalytic oxidation of ethylene is elucidated by means of an in-house developed FTIR in situ reactor. This reactor allowed us to look at the catalytic surface at the moment the reactions actually occur. This new approach gave some exciting new insights in how ethylene is photocatalytically oxidised. It was found that there is a change in dipole moment of the ethylene molecule when it is brought in the neighbourhood of the catalyst. From this finding, a hypothesis was formulated on how the CC-bond from ethylene will break. It was found that the aforementioned interaction between the catalyst and the molecule, allows the excited electrons from the UV irradiated catalyst to occupy the lowest unoccupied molecular orbital (LUMO) of the ethylene molecule through a process known as backdonation. Following this hypothesis, it was found that the degradation occurs through the formation of two intermediates: formaldehyde and formic acid, for which formaldehyde is bound in two different ways (coordinatively and as bidentate). Finally CO2 and H2O are found as end products, resulting in the complete mineralisation of the pollutant.

Abstract: In this study, a new fouling sensor was validated under different conditions of hydraulic (HRT) and sludge retention time (SRT). The MBR-VFM (membrane bioreactor-VITO Fouling Measurement) allows the simultaneous determination of the physically reversible and irreversible fouling potential of a mixed liquor during a single crossflow filtration test. In accordance with the on-line filtration behavior, the measured reversible and irreversible fouling propensities differed significantly between MBRs operated at different combinations of HRT-SRT. Moreover, a significant negative correlation was found between the on-line permeability and the reversible and irreversible fouling propensity measured by the MBR-VFM. This corresponded to observations made on membrane recovery after physical or chemical cleaning actions. Higher reversible and irreversible fouling were observed at lower HRT, presumably as a consequence of increased concentrations of foulants present. The effect of SRT was much smaller and restricted to the reversible fouling component. Possible explanations for the increased fouling at prolonged SRT are the higher sludge and colloid concentration and the smaller floc size. It can be concluded that the MBR-VFM is a useful tool to monitor fluctuations in a mixed liquors (ir)reversible fouling potential and can contribute to a deeper understanding of the occurring fouling phenomena.

Abstract: In the field of photocatalytic air purification, the immobilisation of catalyst particles on support surfaces without loss of photon efficiency is an important challenge. Therefore, an immobilisation method involving a one-step suspension coating of pre-synthesised photocatalysts on glass beads was applied. The various benefits are exemplified in the gas phase photodegradation of ethylene. Coating of glass beads is easy, fast, cheap and offers a more efficient alternative to bulk catalyst pellets. Furthermore, this coating procedure allows to use porous, pre-synthesised catalysts to their full potential, as the surface area and morphology of the initial powder is barely altered after coating, in strong contrast to pelletising. With this technique it became possible to study the gas phase photocatalytic activity of commercial titanium dioxide, trititanate nanotubes and mixed phase anatase/trititanate nanotubes in a packed bed reactor towards the degradation of ethylene without changing the catalyst properties. Coating of glass beads with the photocatalyst revealed the superior activity of the as-prepared nanotubes, compared to TiO2 Aerolyst® 7710 in gaseous phase.