“Photoelectric and electrical responses of several erbium silicide/silicon interfaces”. Muret P, Nguyen TTA, Frangis N, Van Tendeloo G, van Landuyt J, Applied surface science
T2 –, International Symposium on Si Heterostructures –, From Physics to Devices, SEP 11-14, 1995, IRAKLION, GREECE 102, 173 (1996). http://doi.org/10.1016/0169-4332(96)00042-6
Abstract: In this work, photoelectric yield and electrical properties of several types of epitaxial erbium silicide on silicon Schottky diodes are studied, Different preparation conditions are used simultaneously on n- and p-Si(111) substrates for the 200 Angstrom thick silicide films. A last type of sample consists in 1.3 monolayer of epitaxial silicide with root 3 X root 3 superstructure on the Si substrate and covered by silver on the top. Photocurrent measurements are done as a function of photon energy at several temperatures. All these samples show barrier heights near 1 eV on p-type Si, even for the interface comprising only 1.3 monolayer of silicide whereas barrier heights on n-rype Si span the range from 0.28 to 0.67 eV for this last kind of sample, the sum of the barriers always exceeding the silicon band gap, These photoelectric results are confirmed by electrical characterisations, All these results show that the Fermi level is pinned 0.1 eV below the conduction band edge on p-type Si but shifts to various positions lower within the band gap on n-type Si. This fact leads to the hypothesis of a density of -7 interface states close to the charge change in the Si depletion zone from p- to n-type, namely 10(12) eV(-1) cm(-2). Although some inhomogeneities and defects at the interface are detected by electron microscopy for samples annealed at 750 degrees C, Fermi level position seems rather insensitive to the structural details of the interface while the silicide thickness plays a role on n-type Si.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.711
Times cited: 3
DOI: 10.1016/0169-4332(96)00042-6
|
|
|
“Plasmon holographic experiments: theoretical framework”. Verbeeck J, van Dyck D, Lichte H, Potapov P, Schattschneider P, Ultramicroscopy 102, 239 (2005). http://doi.org/10.1016/j.ultramic.2004.10.005
Abstract: A theoretical framework is described to understand the results of plasmon holography experiments leading to insight in the meaning of the experimental results and pointing out directions for future experiments. The framework is based on the formalism of mutual intensity to describe how coherence is transferred through an optical system. For the inelastic interaction with the object, an expression for the volume. plasmon excitations in a free electron gas is used as a model for the behaviour of aluminium. The formalism leads to a clear graphical intuitive tool for under-standing the experiments. It becomes evident that the measured coherence is solely related to the angular distribution of the plasmon scattering in the case of bulk plasmons. After describing the framework, the special case of coherence outside a spherical particle is treated and the seemingly controversial idea of a plasmon with a limited coherence length obtained front experiments is clarified. (C) 2004 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 43
DOI: 10.1016/j.ultramic.2004.10.005
|
|
|
“Quantitative study of particle size distribution in an in-situ grown Al-TiB2 composite by synchrotron X-ray diffraction and electron microscopy”. Tang Y, Chen Z, Borbely A, Ji G, Zhong SY, Schryvers D, Ji V, Wang HW, Materials characterization 102, 131 (2015). http://doi.org/10.1016/j.matchar.2015.03.003
Abstract: Synchrotron X-ray diffraction and transmission electron microscopy (TEM) were applied to quantitatively characterize the average particle size and size distribution of free-standing TiB2 particles and TiB2 particles in an insitu grown Al–TiB2 composite. The detailed evaluations were carried out by X-ray line profile analysis using the restrictedmoment method and multiplewhole profile fitting procedure (MWP). Both numericalmethods indicate that the formed TiB2 particles are well crystallized and free of crystal defects. The average particle size determined from different Bragg reflections by the restricted moment method ranges between 25 and 55 nm, where the smallest particle size is determined using the 110 reflection suggesting the highest lateral-growth velocity of (110) facets. TheMWP method has shown that the in-situ grown TiB2 particles have a very low dislocation density (~1011 m−2) and their size distribution can be described by a log-normal distribution. Good agreement was found between the results obtained from the restricted moment and MWP methods, which was further confirmed by TEM.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 41
DOI: 10.1016/j.matchar.2015.03.003
|
|
|
“Short-range order in phase segregation systems”. De Meulenaere P, Mommaert C, Van Tendeloo G, Solid state communications 102, 687 (1997). http://doi.org/10.1016/S0038-1098(97)00071-9
Abstract: Spin systems on an f.c.c.-lattice which exhibit phase segregation are studied by means of Monte Carlo simulations. Short-range order, both above and below the segregation temperature, is observed. Experimental evidence for short range order in Ti-V is provided by electron diffraction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.554
DOI: 10.1016/S0038-1098(97)00071-9
|
|
|
“Spin effects in electron vortex states”. Van Boxem R, Verbeeck J, Partoens B, Europhysics letters 102, 40010 (2013). http://doi.org/10.1209/0295-5075/102/40010
Abstract: The recent experimental realization of electron vortex beams opens up a wide research domain previously unexplored. The present paper explores the relativistic properties of these electron vortex beams, and quantifies deviations from the scalar wave theory. It is common in electron optics to use the Schrodinger equation neglecting spin. The present paper investigates the role of spin and the total angular momentum J(z) and how it pertains to the vortex states. As an application, we also investigate if it is possible to use holographic reconstruction to create novel total angular momentum eigenstates in a transmission electron microscope. It is demonstrated that relativistic spin coupling effects disappear in the paraxial limit, and spin effects in holographically created electron vortex beams can only be exploited by using specialized magnetic apertures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 1.957
Times cited: 11
DOI: 10.1209/0295-5075/102/40010
|
|
|
“Multiscale investigation of quasi-brittle fracture characteristics in a 9Cr–1Mo ferritic–martensitic steel embrittled by liquid lead–bismuth under low cycle fatigue”. Gong X, Marmy P, Volodin A, Amin-Ahmadi B, Qin L, Schryvers D, Gavrilov S, Stergar E, Verlinden B, Wevers M, Seefeldt M, Corrosion science 102, 137 (2016). http://doi.org/10.1016/j.corsci.2015.10.003
Abstract: Liquid metal embrittlement (LME) induced quasi-brittle fracture characteristics of a 9Cr–1Mo ferritic–martensitic steel (T91) after fatigue cracking in lead–bismuth eutectic (LBE) have been investigated at various length scales. The results show that the LME fracture morphology is primarily characterized by quasi-brittle translath flat regions partially covered by nanodimples, shallow secondary cracks propagating along the martensitic lath boundaries as well as tear ridges covered by micro dimples. These diverse LME fracture features likely indicate a LME mechanism involving multiple physical processes, such as weakening induced interatomic decohesion at the crack tip and plastic shearing induced nano/micro voiding in the plastic zone.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 16
DOI: 10.1016/j.corsci.2015.10.003
|
|
|
“Single femtosecond laser pulse excitation of individual cobalt nanoparticles”. Savchenko TM, Buzzi M, Howald L, Ruta S, Vijayakumar J, Timm M, Bracher D, Saha S, Derlet PM, Béché, A, Verbeeck J, Chantrell RW, Vaz CAF, Nolting F, Kleibert A, Physical Review B 102, 205418 (2020). http://doi.org/10.1103/PhysRevB.102.205418
Abstract: Laser-induced manipulation of magnetism at the nanoscale is a rapidly growing research topic with potential for applications in spintronics. In this work, we address the role of the scattering cross section, thermal effects, and laser fluence on the magnetic, structural, and chemical stability of individual magnetic nanoparticles excited by single femtosecond laser pulses. We find that the energy transfer from the fs laser pulse to the nanoparticles is limited by the Rayleigh scattering cross section, which in combination with the light absorption of the supporting substrate and protective layers determines the increase in the nanoparticle temperature. We investigate individual Co nanoparticles (8 to 20 nm in size) as a prototypical model system, using x-ray photoemission electron microscopy and scanning electron microscopy upon excitation with single femtosecond laser pulses of varying intensity and polarization. In agreement with calculations, we find no deterministic or stochastic reversal of the magnetization in the nanoparticles up to intensities where ultrafast demagnetization or all-optical switching is typically reported in thin films. Instead, at higher fluences, the laser pulse excitation leads to photo-chemical reactions of the nanoparticles with the protective layer, which results in an irreversible change in the magnetic properties. Based on our findings, we discuss the conditions required for achieving laser-induced switching in isolated nanomagnets.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.7
Times cited: 1
DOI: 10.1103/PhysRevB.102.205418
|
|
|
“Band flattening in buckled monolayer graphene”. Milovanović, SP, Andelkovic M, Covaci L, Peeters FM, Physical Review B 102, 245427 (2020). http://doi.org/10.1103/PHYSREVB.102.245427
Abstract: The strain fields of periodically buckled graphene induce a periodic pseudomagnetic field (PMF) that modifies the electronic band structure. From the geometry, amplitude, and period of the periodic pseudomagnetic field, we determine the necessary conditions to access the regime of correlated phases by examining the band flattening. As compared to twisted bilayer graphene the proposed system has the advantages that (1) only a single layer of graphene is needed, (2) one is not limited to hexagonal superlattices, and (3) narrower flat bandwidth and larger separation between flat bands can be induced. We, therefore, propose that periodically strained graphene single layers can become a platform for the exploration of exotic many-body phases.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.7
Times cited: 11
DOI: 10.1103/PHYSREVB.102.245427
|
|
|
“Bond length variation in Ga1-xInxAs crystals from the Tersoff potential”. Titantah JT, Lamoen D, Schowalter M, Rosenauer A, Journal of applied physics 101, 123508 (2007). http://doi.org/10.1063/1.2748338
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 19
DOI: 10.1063/1.2748338
|
|
|
“Convergent beam electron-diffraction investigation of lattice mismatch and static disorder in GaAs/GaAs1-xNx intercalated GaAs/GaAs1-xNx:H heterostructures”. Frabboni S, Grillo V, Gazzadi GC, Balboni R, Trotta R, Polimeni A, Capizzi M, Martelli F, Rubini S, Guzzinati G, Glas F;, Applied physics letters 101, 111912 (2012). http://doi.org/10.1063/1.4752464
Abstract: Hydrogen incorporation in diluted nitride semiconductors dramatically modifies the electronic and structural properties of the crystal through the creation of nitrogen-hydrogen complexes. We report a convergent beam electron-diffraction characterization of diluted nitride semiconductor-heterostructures patterned at a sub-micron scale and selectively exposed to hydrogen. We present a method to determine separately perpendicular mismatch and static disorder in pristine and hydrogenated heterostructures. The roles of chemical composition and strain on static disorder have been separately assessed. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4752464]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 1
DOI: 10.1063/1.4752464
|
|
|
“Direct visualization of boron dopant distribution and coordination in individual chemical vapor deposition nanocrystalline B-doped diamond grains”. Lu Y-G, Turner S, Verbeeck J, Janssens SD, Wagner P, Haenen K, Van Tendeloo G, Applied physics letters 101, 041907 (2012). http://doi.org/10.1063/1.4738885
Abstract: The boron dopant distribution in individual heavily boron-doped nanocrystalline diamond film grains, with sizes ranging from 100 to 350nm in diameter, has been studied using a combination of high resolution annular dark field scanning transmission electron microscopy and spatially resolved electron energy-loss spectroscopy. Using these tools, the boron distribution and local boron coordination have been determined. Quantification results reveal embedding of B dopants in the diamond lattice, and a preferential enrichment of boron at defective areas and twin boundaries. Coordination mapping reveals a distinct difference in coordination of the B dopants in “pristine” diamond areas and in defective regions. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4738885]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 59
DOI: 10.1063/1.4738885
|
|
|
“Model based quantification of EELS spectra”. Verbeeck J, Van Aert S, Ultramicroscopy 101, 207 (2004). http://doi.org/10.1016/j.ultramic.2004.06.004
Abstract: Recent advances in model based quantification of electron energy loss spectra (EELS) are reported. The maximum likelihood method for the estimation of physical parameters describing an EELS spectrum, the validation of the model used in this estimation procedure, and the computation of the attainable precision, that is, the theoretical lower bound on the variance of these estimates, are discussed. Experimental examples on An and GaAs samples show the power of the maximum likelihood method and show that the theoretical prediction of the attainable precision can be closely approached even for spectra with overlapping edges where conventional EELS quantification fails. To provide end-users with a low threshold alternative to conventional quantification, a user friendly program was developed which is freely available under a GNU public license. (C) 2004 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 147
DOI: 10.1016/j.ultramic.2004.06.004
|
|
|
“Observation of Co/CoO nanoparticles below the critical size for exchange bias”. Dobrynin AN, Temst K, Lievens P, Margueritat J, Gonzalo J, Afonso CN, Piscopiello E, Van Tendeloo G, Journal of applied physics 101, 113913 (2007). http://doi.org/10.1063/1.2736303
Abstract: We compare the magnetic properties of pure and oxidized Co nanoparticles embedded in an amorphous Al2O3 matrix. Nanoparticles with diameters of 2 or 3 nm were prepared by alternate pulsed laser deposition in high vacuum conditions, and some of them were exposed to O-2 after production and before being embedded. The nanoparticles are organized in layers, the effective edge-to-edge in-depth separation being 5 or 10 nm. The lower saturation magnetizations per Co atom for the samples containing oxidized nanoparticles provide evidence for the formation of antiferromagnetic CoO shells in the nanoparticles. None of the samples with Co/CoO nanoparticles show exchange bias, while vertical hysteresis loop shifts and enhanced coercivities (as compared to samples with pure Co nanoparticles) are observed. This constitutes evidence for the nanoparticles size being in all cases smaller than the critical size for exchange bias. The difference in coercivity versus temperature dependences for the samples with pure and oxidized Co nanoparticles shows that the exchange anisotropy in Co/CoO nanoparticles appears at temperatures lower than 50 K. (c) 2007 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 27
DOI: 10.1063/1.2736303
|
|
|
“On the superconducting phase boundary for a mesoscopic square loop”. Fomin VM, Misko VR, Devreese JT, Moshchalkov VV, Solid State Communications 101, 303 (1997)
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.554
Times cited: 39
|
|
|
“Site-specific mapping of transition metal oxygen coordination in complex oxides”. Turner S, Egoavil R, Batuk M, Abakumov AA, Hadermann J, Verbeeck J, Van Tendeloo G, Applied physics letters 101, 241910 (2012). http://doi.org/10.1063/1.4770512
Abstract: We demonstrate site-specific mapping of the oxygen coordination number for transition metals in complex oxides using atomically resolved electron energy-loss spectroscopy in an aberration-corrected scanning transmission electron microscope. Pb2Sr2Bi2Fe6O16 contains iron with a constant Fe3+ valency in both octahedral and tetragonal pyramidal coordination and is selected to demonstrate the principle of site-specific coordination mapping. Analysis of the site-specific Fe-L2,3 data reveals distinct variations in the fine structure that are attributed to Fe in a six-fold (octahedron) or five-fold (distorted tetragonal pyramid) oxygen coordination. Using these variations, atomic resolution coordination maps are generated that are in excellent agreement with simulations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 12
DOI: 10.1063/1.4770512
|
|
|
“Structural variants of Ca0.85CuO2(Ca5+xCu6O12)”. Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Greaves C, Journal of solid state chemistry 101, 92 (1992). http://doi.org/10.1016/0022-4596(92)90205-A
Abstract: The structure of Ca0.85CuO2 was reexamined by means of electron diffraction and electron microscopy using the newly developed method of selective imaging in intergrowth structures in which the two substructures are based on different sublattices. The results of previous work are confirmed. Moreover, it is shown that two stacking variants and their twin related structures occur in the calcium substructure. The copper-oxygen substructure occurs in one variant only; it is often modulated by the various calcium arrangements, leading to phase disorder in its modulation pattern. It is shown that the ribbons of CuO4 clusters are presumably tilted with respect to the (010) plane.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 10
DOI: 10.1016/0022-4596(92)90205-A
|
|
|
“Enhancement of second harmonic generation signal in thermally poled glass ceramic with NaNbO3 nanocrystals”. Malakho A, Fargin E, Lahaye M, Lazoryak B, Morozov V, Van Tendeloo G, Rodriguez V, Adamietz F, Journal of applied physics 100, 063103 (2006). http://doi.org/10.1063/1.2259816
Abstract: Glass ceramic composites were prepared by bulk crystallization of NaNbO3 in sodium niobium borate glasses. A homogeneous bulk crystallization of the NaNbO3 phase takes place during heat treatments that produces visible-near infrared transparent materials with similar to 30 nm NaNbO3 nanocrystallites. Upon thermal poling, a strong Na+ depleted nonlinear optical thin layer is observed at the anode side that should induce a large internal static electric field. In addition, the chi((2)) response of the poled glass ceramic composites increases from 0.2 up to 1.9 pm/V with the rate of crystallization. Two mechanisms may be considered: a pure structural chi((2)) process connected with the occurrence of a spontaneous ferroelectric polarization or an increase of the chi((3)) response of the nanocrystallites that enhances the electric field induced second harmonic generation process. (c) 2006 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 13
DOI: 10.1063/1.2259816
|
|
|
“Magnetic and electronic properties of the interface between half metallic Fe3O4 and semiconducting ZnO”. Brück S, Paul M, Tian H, Müller A, Kufer D, Praetorius C, Fauth K, Audehm P, Goering E, Verbeeck J, Van Tendeloo G, Sing M, Claessen R;, Applied physics letters 100, 081603 (2012). http://doi.org/10.1063/1.3687731
Abstract: We have investigated the magnetic depth profile of an epitaxial Fe3O4 thin film grown directly on a semiconducting ZnO substrate by soft x-ray resonant magnetic reflectometry (XRMR) and electron energy loss spectroscopy (EELS). Consistent chemical profiles at the interface between ZnO and Fe3O4 are found from both methods. Valence selective EELS and XRMR reveal independently that the first monolayer of Fe at the interface between ZnO and Fe3O4 contains only Fe3+ ions. Besides this narrow 2.5 Å interface layer, Fe3O4 shows magnetic bulk properties throughout the whole film making highly efficient spin injection in this system feasible.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 12
DOI: 10.1063/1.3687731
|
|
|
“Optimizing Er/Yb ratio and content in Er-Yb co-doped glass-ceramics for enhancement of the up- and down-conversion luminescence”. Tikhomirov VK, Rodríguez VD, Méndez-Ramos J, del- Castillo J, Kirilenko D, Van Tendeloo G, Moshchalkov VV, Solar energy materials and solar cells 100, 209 (2012). http://doi.org/10.1016/j.solmat.2012.01.019
Abstract: Er3+Yb3+ co-doped transparent glass-ceramics with varying Er/Yb content and ratio have been prepared. High quantum yields for up- and down-conversion luminescence by energy transfer from Yb3+ to Er3+ and from Er3+ to Yb3+, respectively, have been detected and optimized with respect to the Er/Yb content and ratio, and proposed in particular for up- and down-conversion of solar spectrum for enhancement of the efficiency of solar cells. The rise and decay kinetics for the population of the excited levels of Er3+ and Yb3+ have been studied and fit. Based on these experimental data, the mechanisms for the energy transfers have been suggested with emphasis on the optimized Er/Yb content and ratio for enhancement of the efficiency of the Er3+↔Yb3+ energy transfers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.784
Times cited: 66
DOI: 10.1016/j.solmat.2012.01.019
|
|
|
“Sharpening the shape distribution of gold nanoparticles by laser irradiation”. Resta V, Siegel J, Bonse J, Gonzalo J, Afonso CN, Piscopiello E, Van Tenedeloo G;, Journal of applied physics 100, Doi: 10.1063/1.2358822 (2006). http://doi.org/10.1063/1.2358822
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 36
DOI: 10.1063/1.2358822
|
|
|
“Chemical stability of YBiO3 buffer layers for implementation in YBa2Cu3O7-&delta, coated conductors”. Pollefeyt G, Meledin A, Pop C, Ricart S, Hühne R, Van Tendeloo G, Van Driessche I, Acta materialia 100, 224 (2015). http://doi.org/10.1016/j.actamat.2015.08.023
Abstract: In this work, the chemical and microstructural stability of YBiO3 buffer layers during the growth of YBa2Cu3O7-δ (YBCO) was studied. The superconducting YBCO films were deposited via both Pulsed Laser Deposition as well as Chemical Solution Deposition. Although excellent superconducting properties are obtained in both cases, self-field critical current densities of 3.6 and 1.2 MA/cm2 respectively, chemical instability of the YBiO3 buffer layer is observed. An elaborate transmission electron microscopy study showed that in the case of vacuum deposited YBCO, the YBiO3 becomes unstable and Bi2O3 sublimates out of the architecture. Due to this structural instability, an intermediate Y2O3 layer is obtained which maintains it microstructural orientation relation with the substrate and acts as growth template for YBCO. For chemical solution deposited YBCO, reaction of YBCO with the YBiO3 buffer layer is observed, leading to large grains of YBa2BiO6 which are pushed towards the surface of the films and strongly reduce the superconducting properties. Upon using high growth temperatures for the superconducting layer, these secondary phases decompose, which subsequently leads to Bi2O3 sublimation and a textured YBCO film which directly nucleated onto the LaAlO3 single crystal substrate. Hence, this electron microscopy study indicates that bismuth-based buffer layers systems are not suitable for implementation in coated conductors.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
DOI: 10.1016/j.actamat.2015.08.023
|
|
|
“Three-dimensional fabrication and characterisation of core-shell nano-columns using electron beam patterning of Ge-doped SiO2”. Gontard LC, Jinschek JR, Ou H, Verbeeck J, Dunin-Borkowski RE, Applied physics letters 100, 263113 (2012). http://doi.org/10.1063/1.4731765
Abstract: A focused electron beam in a scanning transmission electron microscope (STEM) is used to create arrays of core-shell structures in a specimen of amorphous SiO2 doped with Ge. The same electron microscope is then used to measure the changes that occurred in the specimen in three dimensions using electron tomography. The results show that transformations in insulators that have been subjected to intense irradiation using charged particles can be studied directly in three dimensions. The fabricated structures include core-shell nano-columns, sputtered regions, voids, and clusters. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4731765]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 11
DOI: 10.1063/1.4731765
|
|
|
“Survival of the Dirac points in rippled graphene”. Covaci L, Berciu M, Physical Review Letters 100, 256405 (2008). http://doi.org/10.1103/PhysRevLett.100.256405
Abstract: We study the effects of the rippling of a graphene sheet on quasiparticle dispersion. This is achieved using a generalization to the honeycomb lattice of the momentum average approximation, which is accurate for all coupling strengths and at all energies. We show that even though the position of the Dirac points may move and the Fermi speed can be renormalized significantly, quasiparticles with very long lifetimes survive near the Dirac points even for very strong couplings.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 8.462
Times cited: 15
DOI: 10.1103/PhysRevLett.100.256405
|
|
|
“Strain mapping for the silicon-on-insulator generation of semiconductor devices by high-angle annular dark field scanning electron transmission microscopy”. Cooper D, Le Royer C, Béché, A, Rouvière J-L, Applied Physics Letters 100, 233121 (2012). http://doi.org/10.1063/1.4723572
Abstract: The strain in pMOS p-type metal-oxide-semiconductor devicesgrown on silicon-on-insulator substrates has been measured by using the geometrical phase analysis of high angle annular dark field scanning electron microscopy. We show that by using the latest generations of electron microscopes, the strain can now be quantitatively measured with a large field of view, a spatial resolution as low as 1 nm with a sensitivity as good as 0.15%. This technique is extremely flexible, provides both structural and strain information, and can be applied to all types of nanoscale materials both quickly and easily.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
DOI: 10.1063/1.4723572
|
|
|
“Atomic scale electron vortices for nanoresearch”. Verbeeck J, Schattschneider P, Lazar S, Stöger-Pollach M, Löffler S, Steiger-Thirsfeld A, Van Tendeloo G, Applied physics letters 99, 203109 (2011). http://doi.org/10.1063/1.3662012
Abstract: Electron vortex beams were only recently discovered and their potential as a probe for magnetism in materials was shown. Here we demonstrate a method to produce electron vortex beams with a diameter of less than 1.2 Å. This unique way to prepare free electrons to a state resembling atomic orbitals is fascinating from a fundamental physics point of view and opens the road for magnetic mapping with atomic resolution in an electron microscope.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 90
DOI: 10.1063/1.3662012
|
|
|
“Deposition of vanadium silicalite-1 nanoparticles on SBA-15 materials: structural and transport characteristics of SBA-VS-15”. Meynen V, Cool P, Vansant EF, Kortunov P, Grinberg F, Kärger J, Mertens M, Lebedev OI, Van Tendeloo G, Microporous and mesoporous materials 99, 14 (2007). http://doi.org/10.1016/j.micromeso.2006.08.029
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 23
DOI: 10.1016/j.micromeso.2006.08.029
|
|
|
“Measuring the absolute position of EELS ionisation edges in a TEM”. Potapov PL, Schryvers D, Ultramicroscopy 99, 73 (2004). http://doi.org/10.1016/S0304-3991(03)00185-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 29
DOI: 10.1016/S0304-3991(03)00185-2
|
|
|
“New Andreev-type states in superconducting nanowires”. Shanenko AA, Croitoru MD, Mints RG, Peeters FM, Physical review letters 99, 067007 (2007). http://doi.org/10.1103/PhysRevLett.99.067007
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 30
DOI: 10.1103/PhysRevLett.99.067007
|
|
|
“Resistive switching at manganite/manganite interfaces”. Kalkert C, Krisponeit J-O, Esseling M, Lebedev OI, Moshnyaga V, Damaschke B, Van Tendeloo G, Samwer K, Applied physics letters 99, 132512 (2011). http://doi.org/10.1063/1.3643425
Abstract: We report bipolar resistive switching between the interfaces of manganite nanocolumns. La0.7Sr0.3MnO3 films were prepared on Al2O3 substrates, where the films grow in nanocolumns from the substrate to the surface. Conductive atomic force microscopy directly detects that the resistive switching is located at the boundaries of the grains. Furthermore, mesoscopic transport measurements reveal a tunnel magnetoresistance. In combination with the resistive switching, this leads to a total of four different resistive states.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 10
DOI: 10.1063/1.3643425
|
|
|
“Quantitative strain mapping of InAs/InP quantum dots with 1 nm spatial resolution using dark field electron holography”. Cooper D, Rouvière J-L, Béché, A, Kadkhodazadeh S, Semenova ES, Dunin-Borkowsk R, Applied physics letters 99, 261911 (2011). http://doi.org/10.1063/1.3672194
Abstract: The optical properties of semiconductor quantum dots are greatly influenced by their strain state. Dark field electron holography has been used to measure the strain in InAsquantum dotsgrown in InP with a spatial resolution of 1 nm. A strain value of 5.4% ± 0.1% has been determined which is consistent with both measurements made by geometrical phase analysis of high angle annular dark field scanning transmission electron microscopy images and with simulations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 26
DOI: 10.1063/1.3672194
|
|