“Dimethylformamide-mediated synthesis of water-soluble platinum nanodendrites for ethanol oxidation electrocatalysis”. Mourdikoudis S, Chirea M, Altantzis T, Pastoriza-Santos I, Perez-Juste J, Silva F, Bals S, Liz-Marzan LM, Nanoscale 5, 4776 (2013). http://doi.org/10.1039/c3nr00924f
Abstract: Herein we describe the synthesis of water-soluble platinum nanodendrites in dimethylformamide (DMF), in the presence of polyethyleneimine (PEI) as a stabilizing agent. The average size of the dendrites is in the range of 20-25 nm while their porosity can be tuned by modifying the concentration of the metal precursor. Electron tomography revealed different crystalline orientations of nanocrystallites in the nanodendrites and allowed a better understanding of their peculiar branching and porosity. The high surface area of the dendrites (up to 22 m(2) g(-1)) was confirmed by BET measurements, while X-ray diffraction confirmed the abundance of high-index facets in the face-centered-cubic crystal structure of Pt. The prepared nanodendrites exhibit excellent performance in the electrocatalytic oxidation of ethanol in alkaline solution. Sensing, selectivity, cycleability and great tolerance toward poisoning were demonstrated by cyclic voltammetry measurements.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 50
DOI: 10.1039/c3nr00924f
|
“Breaking structure sensitivity in CO2 hydrogenation by tuning metal–oxide interfaces in supported cobalt nanoparticles”. Parastaev A, Muravev V, Osta EH, Kimpel TF, Simons JFM, van Hoof AJF, Uslamin E, Zhang L, Struijs JJC, Burueva DB, Pokochueva EV, Kovtunov KV, Koptyug IV, Villar-Garcia IJ, Escudero C, Altantzis T, Liu P, Béché, A, Bals S, Kosinov N, Hensen EJM, Nature Catalysis 5, 1051 (2022). http://doi.org/10.1038/s41929-022-00874-4
Abstract: A high dispersion of the active metal phase of transition metals on oxide supports is important when designing efficient heterogeneous catalysts. Besides nanoparticles, clusters and even single metal atoms can be attractive for a wide range of reactions. However, many industrially relevant catalytic transformations suffer from structure sensitivity, where reducing the size of the metal particles below a certain size substantially lowers catalytic performance. A case in point is the low activity of small cobalt nanoparticles in the hydrogenation of CO and CO2. Here we show how engineering of catalytic sites at the metal–oxide interface in cerium oxide–zirconium dioxide (ceria–zirconia)-supported cobalt can overcome this structure sensitivity. Few-atom cobalt clusters dispersed on 3 nm cobalt(II)-oxide particles stabilized by ceria–zirconia yielded a highly active CO2 methanation catalyst with a specific activity higher than that of larger particles under the same conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 37.8
Times cited: 32
DOI: 10.1038/s41929-022-00874-4
|
“Au@Ag nanoparticles : halides stabilize {100} facets”. Gómez-Graña S, Goris B, Altantzis T, Fernández-López C, Carbó-Argibay E, Guerrero-Martínez A, Almora-Barrios N, López N, Pastoriza-Santos I, Pérez-Juste J, Bals S, Van Tendeloo G, Liz-Marzán LM;, The journal of physical chemistry letters 4, 2209 (2013). http://doi.org/10.1021/jz401269w
Abstract: Seed-mediated growth is the most efficient methodology to control the size and shape of colloidal metal nanoparticles. In this process, the final nanocrystal shape is defined by the crystalline structure of the initial seed as well as by the presence of ligands and other additives that help to stabilize certain crystallographic facets. We analyze here the growth mechanism in aqueous solution of silver shells on presynthesized gold nanoparticles displaying various well-defined crystalline structures and morphologies. A thorough three-dimensional electron microscopy characterization of the morphology and internal structure of the resulting core-shell nanocrystals indicates that {100} facets are preferred for the outer silver shell, regardless of the morphology and crystallinity of the gold cores. These results are in agreement with theoretical analysis based on the relative surface energies of the exposed facets in the presence of halide ions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.353
Times cited: 131
DOI: 10.1021/jz401269w
|
“Vapor Phase Fabrication of Nanoheterostructures Based on ZnO for Photoelectrochemical Water Splitting”. Barreca D, Carraro G, Gasparotto A, Maccato C, Altantzis T, Sada C, Kaunisto K, Ruoko T-P, Bals S, Advanced Materials Interfaces 4, 1700161 (2017). http://doi.org/10.1002/admi.201700161
Abstract: Nanoheterostructures based on metal oxide semiconductors have emerged
as promising materials for the conversion of sunlight into chemical energy.
In the present study, ZnO-based nanocomposites have been developed by
a hybrid vapor phase route, consisting in the chemical vapor deposition
of ZnO systems on fluorine-doped tin oxide substrates, followed by the
functionalization with Fe2O3 or WO3 via radio frequency-sputtering. The
target systems are subjected to thermal treatment in air both prior and after
sputtering, and their properties, including structure, chemical composition,
morphology, and optical absorption, are investigated by a variety of characterization
methods. The obtained results evidence the formation of highly
porous ZnO nanocrystal arrays, conformally covered by an ultrathin Fe2O3
or WO3 overlayer. Photocurrent density measurements for solar-triggered
water splitting reveal in both cases a performance improvement with respect
to bare zinc oxide, that is mainly traced back to an enhanced separation of
photogenerated charge carriers thanks to the intimate contact between the
two oxides. This achievement can be regarded as a valuable result in view of
future optimization of similar nanoheterostructured photoanodes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 30
DOI: 10.1002/admi.201700161
|
“Polyhedral iron oxide coreshell nanoparticles in a biodegradable polymeric matrix : preparation, characterization and application in magnetic particle hyperthermia and drug delivery”. Filippousi M, Altantzis T, Stefanou G, Betsiou M, Bikiaris DN, Angelakeris M, Pavlidou E, Zamboulis D, Van Tendeloo G, RSC advances 3, 24367 (2013). http://doi.org/10.1039/c3ra43747g
Abstract: Polyhedral magnetic iron oxide nanocrystals with multiple facets have been embedded in biocompatible and biodegradable polymeric matrices in order to study their structural, magnetic features and alternating-current (AC) magnetic heating efficiency. The encapsulation of iron oxide nanoparticles into a polymer matrix was confirmed by transmission electron microscopy and further corroborated by high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). HAADF-STEM tomography proved that the iron oxide nanocrystals consist of well-defined polyhedral structures with multiple facets. The magnetic features were found to be in good agreement with the structural and morphological features and are maintained even after encapsulation. Furthermore, the magnetic nanoparticles inside these matrices may be considered as good candidates for biomedical applications in hyperthermia treatments because of their high heating capacity exhibited under an alternating magnetic field. The anticancer Taxol drug was encapsulated in these nanoparticles and its physical state and release rate at 37 and 42 °C was studied.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 19
DOI: 10.1039/c3ra43747g
|
“Recent breakthroughs in scanning transmission electron microscopy of small species”. van den Bos KHW, Altantzis T, De Backer A, Van Aert S, Bals S, Advances in Physics: X 3, 1480420 (2018). http://doi.org/10.1080/23746149.2018.1480420
Abstract: Over the last decade, scanning transmission electron microscopy has become one of the most powerful tools to characterise nanomaterials at the atomic scale. Often, the ultimate goal is to retrieve the three-dimensional structure, which is very challenging since small species are typically sensitive to electron irradiation. Nevertheless, measuring individual atomic positions is crucial to understand the relation between the structure and physicochemical properties of these (nano)materials. In this review, we highlight the latest approaches that are available to reveal the 3D atomic structure of small species. Finally, we will provide an outlook and will describe future challenges where the limits of electron microscopy will be pushed even further.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 8
DOI: 10.1080/23746149.2018.1480420
|
“Collective Plasmonic Properties in Few-Layer Gold Nanorod Supercrystals”. Hamon C, Novikov SM, Scarabelli L, Solís DM, Altantzis T, Bals S, Taboada JM, Obelleiro F, Liz-Marzán LM, ACS Photonics 2, 1482 (2015). http://doi.org/10.1021/acsphotonics.5b00369
Abstract: Gold nanorod supercrystals have been widely employed for the detection of relevant bioanalytes with detection limits ranging from nano- to picomolar levels,
confirming the promising nature of these structures for biosensing. Even though a relationship between the height of the supercrystal (i.e., the number of stacked nanorod layers)and the enhancement factor has been proposed, no systematic
study has been reported. In order to tackle this problem, we prepared gold nanorod supercrystals with varying numbers of stacked layers and analyzed them extensively by atomic force microscopy, electron microscopy and surface enhanced Raman scattering. The experimental results were compared to numerical
simulations performed on real-size supercrystals composed of thousands of nanorod building blocks. Analysis of the hot spot distribution in the simulated supercrystals showed the presence of standing waves that were distributed at different depths, depending on the number of layers in each supercrystal. On the basis of these theoretical results, we interpreted the experimental
data in terms of analyte penetration into the topmost layer only, which indicates that diffusion to the interior of the supercrystals would be crucial if the complete field enhancement produced by the stacked nanorods is to be exploited. We propose that our conclusions will be of high relevance in the design of next generation plasmonic devices.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.756
Times cited: 70
DOI: 10.1021/acsphotonics.5b00369
|
“Hydrophilic Pt nanoflowers: synthesis, crystallographic analysis and catalytic performance”. Mourdikoudis S, Altantzis T, Liz-Marzan LM, Bals S, Pastoriza-Santos I, Perez-Juste J, CrystEngComm 18, 3422 (2016). http://doi.org/10.1039/C6CE00039H
Abstract: Water-soluble Pt nanoflowers (NFs) were prepared by a diethylene glycol-mediated reduction of Pt acetylacetonate
(Pt(acac)2) in the presence of polyethyleneimine. Advanced electron microscopy analysis showed that NFs consist of
multiple branches with truncated cubic morphology and different crystallographic orientations. We demonstrate that the
nature of the solvent strongly influences the resulting morphology. The catalytic performance of Pt NFs in 4–nitrophenol
reduction was found to be superior to that of other nanoparticle-based catalysts. Additionally, Pt NFs display good
catalytic reusability with no loss of activity after five consecutive cycles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.474
Times cited: 30
DOI: 10.1039/C6CE00039H
|
Altantzis T (2015) Three-dimensional characterization of atomic clusters, nanoparticles and their assemblies by advanced transmission electron microscopy. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
“Depth sectioning combined with atom-counting in HAADF STEM to retrieve the 3D atomic structure”. Alania M, Altantzis T, De Backer A, Lobato I, Bals S, Van Aert S, Ultramicroscopy 177, 36 (2016). http://doi.org/10.1016/j.ultramic.2016.11.002
Abstract: Aberration correction in scanning transmission electron microscopy (STEM) has greatly improved the lateral and depth resolution. When using depth sectioning, a technique during which a series of images is recorded at different defocus values, single impurity atoms can be visualised in three dimensions. In this paper, we investigate new possibilities emerging when combining depth sectioning and precise atom-counting in order to reconstruct nanosized particles in three dimensions. Although the depth resolution does not allow one to precisely locate each atom within an atomic column, it will be shown that the depth location of an atomic column as a whole can be measured precisely. In this manner, the morphology of a nanoparticle can be reconstructed in three dimensions. This will be demonstrated using simulations and experimental data of a gold nanorod.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 13
DOI: 10.1016/j.ultramic.2016.11.002
|
“3D porous nanostructured platinum prepared using atomic layer deposition”. Pulinthanathu Sree S, Dendooven J, Geerts L, Ramachandran RK, Javon E, Ceyssens F, Breynaert E, Kirschhock CEA, Puers R, Altantzis T, Van Tendeloo G, Bals S, Detavernier C, Martens JA, Journal of materials chemistry A : materials for energy and sustainability 5, 19007 (2017). http://doi.org/10.1039/C7TA03257A
Abstract: A robust and easy to handle 3D porous platinum structure was created via replicating the 3D channel system
of an ordered mesoporous silica material using atomic layer deposition (ALD) over micrometer distances.
After ALD of Pt in the silica material, the host template was digested using hydrogen fluoride (HF). A fully
connected ordered Pt nanostructure was obtained with morphology and sizes corresponding to that of
the pores of the host matrix, as revealed with high-resolution scanning transmission electron
microscopy and electron tomography. The Pt nanostructure consisted of hexagonal Pt rods originating
from the straight mesopores (11 nm) of the host structure and linking features resulting from Pt
replication of the interconnecting mesopore segments (2–4 nm) present in the silica host structure.
Electron tomography of partial replicas, made by incomplete infilling of Zeotile-4 material with Pt,
provided insight in the connectivity and formation mechanism of the Pt nanostructure by ALD. The Pt
replica was evaluated for its potential use as electrocatalyst for the hydrogen evolution reaction, one of
the half-reactions of water electrolysis, and as microelectrode for biomedical sensing. The Pt replica
showed high activity for the hydrogen evolution reaction and electrochemical characterization revealed
a large impedance improvement in comparison with reference Pt electrodes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 9
DOI: 10.1039/C7TA03257A
|
“Multimode Electron Tomography as a Tool to Characterize the Internal Structure and Morphology of Gold Nanoparticles”. Winckelmans N, Altantzis T, Grzelczak M, Sánchez-Iglesias A, Liz-Marzán LM, Bals S, The journal of physical chemistry: C : nanomaterials and interfaces 122, 13522 (2018). http://doi.org/10.1021/acs.jpcc.7b12379
Abstract: Three dimensional (3D) characterization of structural defects in nanoparticles by transmission electron microscopy is far from straightforward. We propose the use of a dose-efficient approach, so-called multimode tomography, during which tilt series of low and high angle annular dark field scanning transmission electron microscopy projection images are acquired simultaneously. In this manner, not only reliable information can be obtained concerning the shape of the nanoparticles, but also the twin planes can be clearly visualized in 3D. As an example, we demonstrate the application of this approach to identify the position of the seeds with respect to the twinning planes in anisotropic gold nanoparticles synthesized using a seed mediated growth approach.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 23
DOI: 10.1021/acs.jpcc.7b12379
|
“Do Binary Supracrystals Enhance the Crystal Stability?”.Yang Z, Altantzis T, Bals S, Tendeloo GV, Pileni M-P, The journal of physical chemistry: C : nanomaterials and interfaces 122, 13515 (2018). http://doi.org/10.1021/acs.jpcc.7b12373
Abstract: We study the oxygen thermal stability of two binary
systems. The larger particles are magnetic amorphous Co (7.2 nm) or
Fe3O4 (7.5 nm) nanocrystals, whereas the smaller ones (3.7 nm) are
Au nanocrystals. The nanocrystal ordering as well as the choice of the
magnetic nanoparticles very much influence the stability of the binary
system. A perfect crystalline structure is obtained with the Fe3O4/Au
binary supracrystals. For the Co/Au binary system, oxidation of Co
results in the chemical transformation from Co to CoO, where the size
of the amorphous Co nanoparticles increases from 7.2 to 9.8 nm in
diameter. During the volume expansion of the Co nanoparticles, Au
nanoparticles within the binary assemblies coalesce and are at the
origin of the instability of the binary nanoparticle supracrystals. On the
other hand, for the Fe3O4/Au binary system, the oxidation of Fe3O4 to
γ-Fe2O3 does not lead to a size change of the nanoparticles, which
maintains the stability of the binary nanoparticle supracrystals. A similar behavior is observed for an AlB2-type Co−Ag binary
system: The crystalline structure is maintained, whereas in disordered assemblies, coalescence of Ag nanocrystals is observed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 5
DOI: 10.1021/acs.jpcc.7b12373
|
“Controlled Growth of Supported ZnO Inverted Nanopyramids with Downward Pointing Tips”. Barreca D, Carraro G, Maccato C, Altantzis T, Kaunisto K, Gasparotto A, Crystal growth &, design , acs.cgd.8b00198 (2018). http://doi.org/10.1021/acs.cgd.8b00198
Abstract: High purity porous ZnO nanopyramids with controllable properties are grown on their tips on
Si(100) substrates by means of a catalyst-free vapor phase deposition route in a wet oxygen
reaction environment. The system degree of preferential [001] orientation, as well as
nanopyramid size, geometrical shape and density distribution, can be finely tuned by varying the
growth temperature between 300 and 400°C, whereas higher temperatures lead to more compact
systems with a three-dimensional (3D) morphology. A growth mechanism of the obtained ZnO
nanostructures based on a self-catalytic vapor-solid (VS) mode is proposed, in order to explain
the evolution of nanostructure morphologies as a function of the adopted process conditions. The
results obtained by a thorough chemico-physical characterization enable to get an improved
control over the properties of ZnO nanopyramids grown by this technique. Taken together, they
are of noticeable importance not only for fundamental research on ZnO nanomaterials with
controlled nano-organization, but also to tailor ZnO functionalities in view of various potential
applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 6
DOI: 10.1021/acs.cgd.8b00198
|
“Controlled Surface Modification of ZnO Nanostructures with Amorphous TiO2for Photoelectrochemical Water Splitting”. Gasparotto A, Maccato C, Sada C, Carraro G, Kondarides DI, Bebelis S, Petala A, La Porta A, Altantzis T, Barreca D, Advanced Sustainable Systems , 1900046 (2019). http://doi.org/10.1002/adsu.201900046
Abstract: The utilization of solar radiation to trigger photoelectrochemical (PEC) water splitting has gained interest for sustainable energy production. In this study, attention is focused on the development of ZnO–TiO2 nanocomposite photoanodes. The target systems are obtained by growing porous arrays of highly crystalline, elongated ZnO nanostructures on indium tin oxide (ITO) by chemical vapor deposition. Subsequently, the obtained nanodeposits are functionalized with TiO2 via radio frequency-sputtering for different process durations, and subjected to final annealing in air. Characterization results demonstrate the successful formation of high purity composite systems in which the surface of ZnO nanostructures is decorated by ultra-small amounts of amorphous titania, whose content can be conveniently tailored as a function of deposition time. Photocurrent density measurements in sunlight triggered water splitting highlight a remarkable performance enhancement with respect to single-phase zinc and titanium oxides, with up to a threefold photocurrent increase compared to bare ZnO. These results, mainly traced back to the formation of ZnO/TiO2 heterojunctions yielding an improved photocarrier separation, show that the target nanocomposites are attractive photoanodes for efficient PEC water splitting.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
DOI: 10.1002/adsu.201900046
|
“Chemical and Structural Configuration of Pt Doped Metal Oxide Thin Films Prepared by Atomic Layer Deposition”. Ramachandran RK, Filez M, Solano E, Poelman H, Minjauw MM, Van Daele M, Feng J-Y, La Porta A, Altantzis T, Fonda E, Coati A, Garreau Y, Bals S, Marin GB, Detavernier C, Dendooven J, Chemistry of materials 31, 9673 (2019). http://doi.org/10.1021/acs.chemmater.9b03066
Abstract: Pt doped semiconducting metal oxides and Pt metal clusters embedded in an oxide matrix are of interest for applications such as catalysis and gas sensing, energy storage and memory devices. Accurate tuning of the dopant level is crucial for adjusting the properties of these materials. Here, a novel atomic layer deposition (ALD) based method for doping Pt into In2O3 in specific, and metals in metal oxides in general, is demonstrated. This approach combines alternating exposures of Pt and In2O3 ALD processes in a single ‘supercycle’, followed by supercycle repetition leading to multilayered nanocomposites. The atomic level control of ALD and its conformal nature make the method suitable for accurate dopant control even on high surface area supports. Oxidation state, local structural environment and crystalline phase of the embedded Pt dopants were obtained by means of X-ray characterization methods and high angle annular dark-field scanning transmission electron microscopy (HAADF-STEM). In addition, this approach allows characterization of the nucleation stages of metal ALD processes, by stacking those states multiple times in an oxide matrix. Regardless of experimental conditions, a few Pt ALD cycles leads to the formation of oxidized Pt species due to their highly dispersed nature, as proven by X-ray absorption spectroscopy (XAS). Grazing-incidence small-angle X-ray scattering (GISAXS) and highresolution scanning transmission electron microscopy, combined with energy dispersive X-ray spectroscopy (HR-STEM/EDXS) show that Pt is evenly distributed in the In2O3 metal oxide matrix without the formation of clusters. For a larger number of Pt ALD
cycles, typ. > 10, the oxidation state gradually evolves towards fully metallic, and metallic Pt clusters are obtained within the In2O3 metal oxide matrix. This work reveals how tuning of the ALD supercycle approach for Pt doping allows controlled engineering of the Pt compositional and structural configuration within a metal oxide matrix.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/acs.chemmater.9b03066
|
“Binary icosahedral clusters of hard spheres in spherical confinement”. Wang D, Dasgupta T, van der Wee EB, Zanaga D, Altantzis T, Wu Y, Coli GM, Murray CB, Bals S, Dijkstra M, van Blaaderen A, Nature Physics , 1 (2020). http://doi.org/10.1038/S41567-020-1003-9
Abstract: The influence of geometry on the local and global packing of particles is important to many fundamental and applied research themes, such as the structure and stability of liquids, crystals and glasses. Here we show by experiments and simulations that a binary mixture of hard-sphere-like nanoparticles crystallizing into a MgZn(2)Laves phase in bulk spontaneously forms icosahedral clusters in slowly drying droplets. Using advanced electron tomography, we are able to obtain the real-space coordinates of all the spheres in the icosahedral clusters of up to about 10,000 particles. The local structure of 70-80% of the particles became similar to that of the MgCu(2)Laves phase. These observations are important for photonic applications. In addition, we observed in simulations that the icosahedral clusters nucleated away from the spherical boundary, which is distinctly different from that of the single species clusters. Our findings open the way for particle-level studies of nucleation and growth of icosahedral clusters, and of binary crystallization. The authors investigate out-of-equilibrium crystallization of a binary mixture of sphere-like nanoparticles in small droplets. They observe the spontaneous formation of an icosahedral structure with stable MgCu(2)phases, which are promising for photonic applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 19.6
Times cited: 38
DOI: 10.1038/S41567-020-1003-9
|
“Understanding and Controlling the Crystallization Process in Reconfigurable Plasmonic Superlattices”. Bagiński M, Pedrazo-Tardajos A, Altantzis T, Tupikowska M, Vetter A, Tomczyk E, Suryadharma RNS, Pawlak M, Andruszkiewicz A, Górecka E, Pociecha D, Rockstuhl C, Bals S, Lewandowski W, Acs Nano , acsnano.0c09746 (2021). http://doi.org/10.1021/acsnano.0c09746
Abstract: The crystallization of nanomaterials is a primary source of solid-state, photonic structures. Thus, a detailed understanding of this process is of paramount importance for the successful application of photonic nanomaterials in emerging optoelectronic technologies. While colloidal crystallization has been thoroughly studied, for example, with advanced in situ electron microscopy methods, the noncolloidal crystallization (freezing) of nanoparticles (NPs) remains so far unexplored. To fill this gap, in this work, we present proof-of principle experiments decoding a crystallization of reconfigurable assemblies of NPs at a solid state. The chosen material corresponds to an excellent testing bed, as it enables both in situ and ex situ investigation using X-ray diffraction (XRD), transmission electron microscopy (TEM), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), atomic force microscopy (AFM), and optical spectroscopy in visible and ultraviolet range (UV−vis) techniques. In particular, ensemble measurements with small-angle XRD highlighted the dependence of the correlation length in the NPs assemblies on the number of heating/cooling cycles and the rate of cooling. Ex situ TEM imaging further supported these results by revealing a dependence of domain size and structure on the sample preparation route and by showing we can control the domain size over 2 orders of magnitude. The application of HAADF-STEM tomography, combined with in situ thermal control, provided three-dimensional single-particle level information on the positional order evolution within assemblies. This combination of real and reciprocal space provides insightful information on the anisotropic, reversibly reconfigurable assemblies of NPs. TEM measurements also highlighted the importance of interfaces in the polydomain structure of nanoparticle solids, allowing us to understand experimentally observed differences in UV−vis extinction spectra of the differently prepared crystallites. Overall, the obtained results show that the combination of in situ heating HAADF-STEM tomography with XRD and ex situ TEM techniques is a powerful approach to study nanoparticle freezing processes and to reveal the crucial impact of disorder in the solid-state aggregates of NPs on their plasmonic properties.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 13.942
Times cited: 10
DOI: 10.1021/acsnano.0c09746
|
“3D Atomic‐Scale Dynamics of Laser‐Light‐Induced Restructuring of Nanoparticles Unraveled by Electron Tomography”. Albrecht W, Arslan Irmak E, Altantzis T, Pedrazo‐Tardajos A, Skorikov A, Deng T‐S, van der Hoeven JES, van Blaaderen A, Van Aert S, Bals S, Advanced Materials , 2100972 (2021). http://doi.org/10.1002/adma.202100972
Abstract: Understanding light–matter interactions in nanomaterials is crucial for
optoelectronic, photonic, and plasmonic applications. Specifically, metal
nanoparticles (NPs) strongly interact with light and can undergo shape
transformations, fragmentation and ablation upon (pulsed) laser excitation.
Despite being vital for technological applications, experimental insight into
the underlying atomistic processes is still lacking due to the complexity of
such measurements. Herein, atomic resolution electron tomography is performed
on the same mesoporous-silica-coated gold nanorod, before and after
femtosecond laser irradiation, to assess the missing information. Combined
with molecular dynamics (MD) simulations based on the experimentally
determined 3D atomic-scale morphology, the complex atomistic rearrangements,
causing shape deformations and defect generation, are unraveled.
These rearrangements are simultaneously driven by surface diffusion, facet
restructuring, and strain formation, and are influenced by subtleties in the
atomic distribution at the surface.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 19.791
Times cited: 8
DOI: 10.1002/adma.202100972
|
“Interface Pattern Engineering in Core‐Shell Upconverting Nanocrystals: Shedding Light on Critical Parameters and Consequences for the Photoluminescence Properties”. Hudry D, De Backer A, Popescu R, Busko D, Howard IA, Bals S, Zhang Y, Pedrazo‐Tardajos A, Van Aert S, Gerthsen D, Altantzis T, Richards BS, Small , 2104441 (2021). http://doi.org/10.1002/smll.202104441
Abstract: Advances in controlling energy migration pathways in core-shell lanthanide (Ln)-based hetero-nanocrystals (HNCs) have relied heavily on assumptions about how optically active centers are distributed within individual HNCs. In this article, it is demonstrated that different types of interface patterns can be formed depending on shell growth conditions. Such interface patterns are not only identified but also characterized with spatial resolution ranging from the nanometer- to the atomic-scale. In the most favorable cases, atomic-scale resolved maps of individual particles are obtained. It is also demonstrated that, for the same type of core-shell architecture, the interface pattern can be engineered with thicknesses of just 1 nm up to several tens of nanometers. Total alloying between the core and shell domains is also possible when using ultra-small particles as seeds. Finally, with different types of interface patterns (same architecture and chemical composition of the core and shell domains) it is possible to modify the output color (yellow, red, and green-yellow) or change (improvement or degradation) the absolute upconversion quantum yield. The results presented in this article introduce an important paradigm shift and pave the way toward the emergence of a new generation of core-shell Ln-based HNCs with better control over their atomic-scale organization.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 8.643
Times cited: 17
DOI: 10.1002/smll.202104441
|
“Monitoring oxygen production on mass-selected iridium–tantalum oxide electrocatalysts”. Zheng Y-R, Vernieres J, Wang Z, Zhang K, Hochfilzer D, Krempl K, Liao T-W, Presel F, Altantzis T, Fatermans J, Scott SB, Secher NM, Moon C, Liu P, Bals S, Van Aert S, Cao A, Anand M, Nørskov JK, Kibsgaard J, Chorkendorff I, Nature Energy (2021). http://doi.org/10.1038/s41560-021-00948-w
Abstract: Development of low-cost and high-performance oxygen evolution reaction catalysts is key to implementing polymer electrolyte membrane water electrolyzers for hydrogen production. Iridium-based oxides are the state-of-the-art acidic oxygen evolution reactio catalysts but still suffer from inadequate activity and stability, and iridium's scarcity motivates the discovery of catalysts with lower iridium loadings. Here we report a mass-selected iridium-tantalum oxide catalyst prepared by a magnetron-based cluster source with considerably reduced noble-metal loadings beyond a commercial IrO2 catalyst. A sensitive electrochemistry/mass-spectrometry instrument coupled with isotope labelling was employed to investigate the oxygen production rate under dynamic operating conditions to account for the occurrence of side reactions and quantify the number of surface active sites. Iridium-tantalum oxide nanoparticles smaller than 2 nm exhibit a mass activity of 1.2 ± 0.5 kA “g” _“Ir” ^“-1” and a turnover frequency of 2.3 ± 0.9 s-1 at 320 mV overpotential, which are two and four times higher than those of mass-selected IrO2, respectively. Density functional theory calculations reveal that special iridium coordinations and the lowered aqueous decomposition free energy might be responsible for the enhanced performance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Times cited: 95
DOI: 10.1038/s41560-021-00948-w
|
“Atomic-scale detection of individual lead clusters confined in Linde Type A zeolites”. Fatermans J, Romolini G, Altantzis T, Hofkens J, Roeffaers MBJ, Bals S, Van Aert S, Nanoscale (2022). http://doi.org/10.1039/D2NR01819E
Abstract: Structural analysis of metal clusters confined in nanoporous materials is typically performed by X-ray-driven techniques. Although X-ray analysis has proved its strength in the characterization of metal clusters, it provides averaged structural information. Therefore, we here present an alternative workflow for bringing the characterization of confined metal clusters towards the local scale. This workflow is based on the combination of aberration-corrected transmission electron microscopy (TEM), TEM image simulations, and powder X-ray diffraction (XRD) with advanced statistical techniques. In this manner, we were able to characterize the clustering of Pb atoms in Linde Type A (LTA) zeolites with Pb loadings as low as 5 wt%. Moreover, individual Pb clusters could be directly detected. The proposed methodology thus enables a local-scale characterization of confined metal clusters in zeolites. This is important for further elucidation of the connection between the structure and the physicochemical properties of such systems.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 6.7
Times cited: 2
DOI: 10.1039/D2NR01819E
|