Abstract: The morphology and structure of diamond films, deposited on cubic boron nitride (c-BN) crystals by microwave-plasma-enhanced chemical vapor deposition, is studied by high-resolution scanning electron microscopy and micro-Raman spectroscopy. The c-BN crystals, with sizes of 200 to 350 mu m and grown by a high-temperature/high-pressure technique, were embedded in a copper holder, and used as substrates in deposition runs of 15 min to 5 h. The nucleation centers for diamond appear as well-shaped cuboctahedral crystallites, having diameters of approximately 100 nm. With increasing deposition time the diamond crystallites grew larger, forming islands on the c-BN faces. In some cases, epitaxial growth was observed on the (111) c-BN faces where coalesced particles gave rise to very smooth regions. A number of diamond crystals with peculiar shapes are observed, such as a pseudo five-fold symmetry due to multiple twinning. Moreover, both randomly distributed carbon tubes, about 100 nn in diameter and 1 mu m in length, and spherically shaped features are observed in samples prepared under the typical conditions of diamond deposition, this effect being ascribed to the influence of plasma-sputtered copper contamination. Quite unusual diamond crystals with a deep, pyramidal-shaped hole in the middle grew on the copper substrate between the c-BN crystals. (C) 2000 Elsevier Science S.A. All rights reserved.

Abstract: Nano-scale ordering may be revealed in transmission electron microscopy (TEM) by at least three techniques that will be presented in this work: selected area electron diffraction, conventional TEM and high-resolution TEM. Digital image processing is used to extract additional information from the high-resolution micrographs. The described methods are illustrated in a microstructural and compositional study of a 90%Pb(Mg1/3Nb2/3)O-3-10%PbTiO2 ceramic sample. High-resolution images reveal the presence of ordered compositional nano-domains, observable in two specific crystallographic orientations. Antiphase boundaries lying in the (111) planes separate them, while (100) and (111) facets separate the ordered domains from the disordered matrix.

Abstract: The results of an in situ transmission electron microscopy study of the formation of Co-silicides on patterned (001) Si substrates are discussed. It is shown that the results of the in situ heating experiments agreed very well with the data based on standard rapid thermal annealing experiments. Fast heating rates resulted in better definition of the silicide lines. Also, better lines were obtained for samples that received already a low-temperature ex situ anneal. A Ti cap layer gave rise to a higher degree of epitaxy in the CoSi2 silicide.

Abstract: Laser induced phase transition from b.c.c.(alpha) to f.c.c.(gamma) iron thin films is studied by high resolution TEM. The iron film has been covered on both sides with carbon layers to protect it against oxidation. Single pulse, tau FWHM = 20ns KrF (lambda = 248nm) excimer laser irradiation was performed in air with the film on the substrate. The laser pulse acts like a heat pulse followed by a rapid quenching revealing sequential aspects of the phase transition process. The presence of a fine mixture of the alpha + gamma phases between the alpha and gamma regions of the film has been interpreted as an incomplet transformation. The results are explained by assuming that the transformation took place via a phonon drag mechanism.

Abstract: Multifrequency electron paramagnetic resonance (EPR) and high resolution transmission electron microscopy (HRTEM) investigations were performed on small (2 nm) cubic ZnS nanocrystals (quantum dotsQDs) doped with 0.2% mol Mn2+, self-assembled into a mesoporous structure. The EPR data analysis shows that the substitutional Mn2+ ions are localized at Zn2+ sites subjected to a local axial lattice distortion, resulting in the observed zero-field-splitting parameter |D|=41×10−4 cm−1. The local distortion is attributed to the presence in the second shell of ligands of a stacking fault or twin, which alters the normal stacking sequence of the cubic structure. The HRTEM results confirm the presence of such extended planar defects in a large percentage of the investigated QDs, which makes possible the proposed substitutional Mn2+ impurity ions localization model. Based on these results it is suggested that the high doping levels of Mn2+ ions observed in cubic ZnS and possible in other II-VI semiconductor QDs prepared at low temperatures can be explained by the assistance of the extended lattice defects in the impurities incorporation.