Abstract: Mesoporous titanium dioxide is a material finding its use in a wide range of applications. For many of these, it is important to achieve a high degree of crystallinity in the material. It is generally accepted that the use of the soft templating approach to synthesize mesoporous titania, results in a compromise between crystallinity and specific surface area due to thermal instability of the used templates. In this paper, we explore how the use of microwave irradiation can influence the crystallinity, specific surface area, and the electronic properties of mesoporous titania. Therefore, we combined microwave radiation with an evaporation-induced self-assembly (EISA) synthesis. We show that additional microwave treatment at carefully chosen synthesis steps can enhance the crystallinity with 20 % without causing significant loss of surface area (>360 m2/g). Surface photovoltage measurements were used to investigate the electronic properties. The photocatalytic activity of the samples was evaluated in aqueous media by following the degradation of an industrial dye, methylene blue, and the herbicide isoproturon under UV irradiation and in gaseous media looking at the degradation of acetaldehyde, a common indoor pollutant under UVA irradiation. In all cases, the microwave treatment results in more active materials.

Abstract: The present work reports on the application and the evaluation of a multitude of crosslinking approaches including high-energy irradiation, redox-initiating systems and conventional carbodiimide-coupling chemistry for frozen and/or freeze-dried porous gelatin scaffolds. The latter is particularly relevant for a plethora of biomedical applications such as tissue engineering supports, wound dressings, adhesive and absorbent pads for surgery, etc. Moreover, the results obtained for gelatin can be considered a proof-of-concept to be extrapolated to other polymer systems containing double bonds and/or amines and carboxylic acids to also realize scaffold crosslinking in dry or frozen state. The results showed that high-energy irradiation at -5 A degrees C enabled sufficient segmental mobility to induce chemical crosslinking after performing a cryogenic treatment of methacrylamide-modified gelatin scaffolds. Alternatively, although several redox-initiating systems were unable to chemically crosslink functionalized gelatin, the combination of ammonium persulphate and TEMED resulted in the formation of scaffolds with a reasonable gel fraction. Interestingly, carbodiimide-coupling was found suitable to crosslink freeze-dried gelatin matrices.

Abstract: The use of temperature-time series measured in streambed sediments as input to coupled water flow and heat transport models has become standard when quantifying vertical groundwater-surface water exchange fluxes. We develop a novel methodology, called LPML, to estimate the parameters for 1-D water flow and heat transport by combining a local polynomial (LP) signal processing technique with a maximum likelihood (ML) estimator. The LP method is used to estimate the frequency response functions (FRFs) and their uncertainties between the streambed top and several locations within the streambed from measured temperature-time series data. Additionally, we obtain the analytical expression of the FRFs assuming a pure sinusoidal input. The estimated and analytical FRFs are used in an ML estimator to deduce vertical groundwater-surface water exchange flux and its uncertainty as well as information regarding model quality. The LPML method is tested and verified with the heat transport models STRIVE and VFLUX. We demonstrate that the LPML method can correctly reproduce a priori known fluxes and thermal conductivities and also show that the LPML method can estimate averaged and time-variable fluxes from periodic and nonperiodic temperature records. The LPML method allows for a fast computation of exchange fluxes as well as model and parameter uncertainties from many temperature sensors. Moreover, it can utilize a broad frequency spectrum beyond the diel signal commonly used for flux calculations.

Abstract: Human urine contains a high concentration of nitrogen and is therefore an interesting source for nutrient recovery. Ureolysis is a key requirement in many processes aiming at nitrogen recovery from urine. Although ureolytic activity is widespread in terrestrial and aquatic environments, very little is known about the urease activity and regulation in specific bacteria other than human pathogens. Given the relatively high salt concentration of urine, marine bacteria would be particularly well suited for biotechnological applications involving nitrogen recovery from urine, and therefore, in this study, we investigated ureolytic activity and its regulation in marine vibrios. Thirteen out of 14 strains showed ureolytic activity. The urease activity was induced by urea, since complete and very rapid hydrolysis, up to 4 g L-1 of urea, was observed in synthetic human urine when the bacteria were pretreated with 10 g L-1 urea, whereas slow hydrolysis occurred when they were pretreated with 1 g L-1 urea (14-35% hydrolysis after 2 days). There was no correlation between biofilm formation and "motility on one hand, and ureolysis on the other hand, and biofilm and motility inhibitors did not affect ureolysis. Together, our data demonstrate for the first time the potential of marine vibrios as fast urea hydrolyzers for biotechnological applications aiming at nutrient recovery from human urine.

Abstract: Factors affecting the structure and orientation of the crystallographic shear (CS) planes in anion-deficient perovskites are investigated using the (Pb1−zSrz)1−xFe1+xO3−y perovskites as a model system. The orientation of the CS planes in the system varies unevenly with z. A comparison of the structures with different CS planes revels that the orientation of the CS planes is governed mainly by the stereochemical activity of the lone-electron-pair cations inside the perovskite blocks.

Abstract: The low-temperature transport properties are studied for electrons confined in delta-doped semiconductor structures with two sheets in parallel. The subband quantum mobility and transport mobility are calculated numerically for the Si delta-doped GaAs systems. The effect of coupling of the two delta layers on the electron transport is investigated. Our calculations are in good agreement with experimental results.

Abstract: The nuclear and magnetic structure of a novel oxychloride Pb4BiFe4O11Cl has been studied over the temperature range 1.5700 K using a combination of transmission electron microscopy and synchrotron and neutron powder diffraction [space group P4/mbm, a = 5.5311(1) Å, c = 19.586(1) Å, T = 300 K]. Pb4BiFe4O11Cl is built of truncated (Pb,Bi)3Fe4O11 quadruple perovskite blocks separated by CsCl-type (Pb,Bi)2Cl slabs. The perovskite blocks consist of two layers of FeO6 octahedra located between two layers of FeO5 tetragonal pyramids. The FeO6 octahedra rotate about the c axis, resulting in a √2ap × √2ap × c superstructure. Below TN = 595(17) K, Pb4BiFe4O11Cl adopts a G-type antiferromagnetic structure with the iron magnetic moments confined to the ab plane. The ordered magnetic moments at 1.5 K are 3.93(3) and 3.62(4) μB on the octahedral and square-pyramidal iron sites, respectively. Pb4BiFe4O11Cl can be considered a member of the perovskite-based An+1BnO3n1Cl homologous series (A = Pb/Bi; B = Fe) with n = 4. The formation of a subsequent member of the series with n = 5 is also demonstrated.

Abstract: We have developed a microscopic theory which describes the orientational dynamics of C-70 molecules and its coupling to lattice displacements in the face-centered-cubic phase of C-70 fullerite. The single-molecule orientational density distribution in the disordered phase is calculated. The ferroelastic transition to the rhombohedral phase is investigated. The discontinuity of the orientational order parameter at the phase transition is calculated. It is found that the transition leads to a stretching of the primitive unit cell along a [111] cubic direction. A softening of the elastic constant c(44) at the transition is predicted.

Abstract: Getting the picture: The investigation of 100 year old chrome yellow paint by transmission electron microscopy and spectroscopy has led to the identification of four types of coreshell particles. This nanoscale investigation has allowed a mechanism to be proposed for the darkening of some bright yellow colors in Van Gogh's paintings (e.g. in Falling leaves (Les Alyscamps), 1888).