“Pd-zeolites as heterogeneous catalysts in heck chemistry”. Dams M, Drijkoningen L, Pauwels B, Van Tendeloo G, de Vos DE, Jacobs PA, Journal of catalysis 209, 225 (2002). http://doi.org/10.1006/jcat.2002.3630
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 157
DOI: 10.1006/jcat.2002.3630
|
“Synthesis and catalytic activity of Ti-MCM-41 nanoparticles with highly active titanium sites”. Lin K, Pescarmona PP, Vandepitte H, Liang D, Van Tendeloo G, Jacobs PA, Journal of catalysis 254, 64 (2008). http://doi.org/10.1016/j.jcat.2007.11.017
Abstract: Ti-MCM-41 nanoparticles 80-160 nm in diameter (Ti-MCM-41 NP) were successfully prepared by a dilute solution route in sodium hydroxide medium at ambient temperature. Ti-MCM-41 NP were characterized by X-ray diffraction, nitrogen adsorption/desorption isotherms, SEM, TEM. FT-IR, and UV-vis spectroscopy. The characterization results showed the existence of highly ordered hexagonal mesoporous structure and tetrahedral Ti species in Ti-MCM-41 NP. In the epoxidation of cyclohexene with aqueous H2O2, Ti-MCM-41 NP displayed higher conversion and initial reaction rate than a Ti-MCM-41 sample with normal particle size (Ti-MCM-41 LP). Diffusion of the reactants was accelerated and the accessibility to the catalytic Ti species was enhanced in the shorter channels in Ti-MCM-41 NP samples. Ti-MCM-41 NP showed much higher selectivity for cyclohexene oxide compared with Ti-MCM-41 LP, suggesting reduced hydrolysis of cyclohexene oxide with water in the former case. The increased selectivity for cyclohexene oxide can be attributed to the lower concentration of residual surface silanols in Ti-MCM-41 NP and the shorter residence time of epoxide in the shorter mesoporous channels. Ti-MCM-41 NP also appears to be a suitable catalyst in the epoxidation of a bulky substrate, like cholesterol, with tert-butyl hydroperoxide. (c) 2007 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 52
DOI: 10.1016/j.jcat.2007.11.017
|
“Direct room-temperature synthesis of methyl-functionalized Ti-MCM-41 nanoparticles and their catalytic performance in epoxidation”. Lin K, Pescarmona PP, Houthoofd K, Liang D, Van Tendeloo G, Jacobs PA, Journal of catalysis 263, 75 (2009). http://doi.org/10.1016/j.jcat.2009.01.013
Abstract: Methyl-functionalized Ti-MCM-41 nanoparticles with a size of 80 to 160 nm (Me-Ti-MCM-41 NP) were directly prepared via a dilute solution route by the co-condensation of tetraethoxysilane and methylalkoxysilanes in sodium hydroxide medium at room temperature. The characterization results showed the existence of ordered hexagonal mesoporous structure and tetrahedral Ti species in the nanoparticles. In the epoxidation of cyclohexene with tert-butyl hydroperoxide and aqueous H2O2, Me-Ti-MCM-41 NP samples displayed higher turnover frequencies (TOFs) for cyclohexene and initial reaction rates compared to Ti-MCM-41 and methyl-functionalized Ti-MCM-41 with normal particle size and to non-functionalized Ti-MCM-41 nanoparticles. Simultaneously, a higher selectivity for cyclohexene epoxide was observed in the case of aqueous H2O2, suggesting that the hydrolysis of cyclohexene epoxide with water is reduced on Me-Ti-MCM-41 NP samples. The improved catalytic behavior of Me-Ti-MCM-41 NP is discussed both in terms of the nanosize and methylation of the surface of the catalyst particles. The regeneration of Me-Ti-MCM-41 NP with tert-butyl hydroperoxide solution was evaluated via washing and calcination approaches.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 89
DOI: 10.1016/j.jcat.2009.01.013
|
“Selectivity in sorption and hydrogenation of methyl oleate and elaidate on MFI zeolites”. Philippaerts A, Paulussen S, Turner S, Lebedev OI, Van Tendeloo G, Poelman H, Bulut M, de Clippel F, Smeets P, Sels B, Jacobs P, Journal of catalysis 270, 172 (2010). http://doi.org/10.1016/j.jcat.2009.12.022
Abstract: Different zeolites were tested for selective removal of methyl elaidate (trans isomer) from an equimolar mixture with methyl oleate (cis isomer). Sorption experiments of the geometric isomers show that only ZSM-5 samples with reduced Al content in the framework are able to discriminate among the bent cis and the linear trans fatty acid methyl esters. Hydrogenation experiments of equimolar methyl oleate and elaidate mixtures at low temperature (65 °C) and high hydrogen pressure (6.0 MPa), using Pt catalysts, confirm this result. Only with a Pt/NaZSM-5 catalyst outspoken selectivity for the hydrogenation of the trans isomer is obtained. In order to prepare a selective Pt/ZSM-5 catalyst, the influence of Pt addition (impregnation, ion-exchange and competitive ion-exchange) and Pt activation (different calcination and reduction temperatures) on the Pt-distribution and Pt particle size was investigated using SEM, bright-field and HR TEM, EDX, electron tomography, CO-chemisorption, XPS, XRD, and UVvis measurements. The best result in terms of hydrogenation activity and selectivity is obtained with a Pt/ZSM-5 catalyst, which is prepared via competitive ion-exchange, followed by slow calcination up to 350 °C under high O2 flow and a reduction up to 500 °C under H2. This preparation method leads to a Pt/ZSM-5 catalyst with the best Pt distribution and the smallest Pt clusters occluded in the zeolite structure. Finally, the influence of zeolite crystal size, morphology, and elemental composition of ZSM-5 on hydrogenation activity and selectivity was investigated in detail.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 24
DOI: 10.1016/j.jcat.2009.12.022
|
“Heterogeneous conjugation of vegetable oil with alkaline treated highly dispersed Ru/USY catalysts”. Van Aelst J, Philippaerts A, Turner S, Van Tendeloo G, Jacobs P, Sels B, Applied catalysis : A : general 526, 172 (2016). http://doi.org/10.1016/J.APCATA.2016.08.026
Abstract: Heterogeneous metal catalysts enable the direct conjugation of linoleic acid tails in vegetable oil to their conjugated linoleic acid (CIA) isomers. CIA-enriched oils are useful as renewable feedstock for the chemical industry and as nutraceutical. Up to now, a solvent-free process for conjugated oils without significant formation of undesired hydrogenation products was not existing. This work shows the design of Ru/USY catalysts able to directly conjugate highly unsaturated vegetable oils such as safflower oil in absence of solvent and hydrogen. Key is fast molecular transport of the bulky reagent and reactive product triglycerides in the zeolite crystal. A two-step zeolite post-synthetic treatment (with NH4OH and acetate salt) was applied to create the necessary mesoporosity. More open zeolite structures allow for a faster conjugation reaction, while securing a fast removal of the reactive conjugated triglycerides, otherwise rapidly deactivating through fouling and pore blockage by polymers. The best Ru/USY catalyst in this contribution is capable of producing exceptionally high yields of conjugated oils, containing up to almost 30 wt% conjugated fatty acid tails in safflower oil, at an initial production rate of 328 g(CLA) mL(-1) h(-1) per gram metal catalyst. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 1
DOI: 10.1016/J.APCATA.2016.08.026
|