Abstract: The compositional influence of Cr and Y on the microstructure of Mg―Cr―O, and Mg―Y―O films synthesized by reactive magnetron sputtering has been investigated by transmission electron microscopy, X-ray diffraction and molecular dynamics simulations. A decrease in crystallinity is observed in these films as the M (Cr or Y) content is increased. It is found that M forms a solid solution with MgO for metal ratios up to ~ 70% and ~ 50% for Cr and Y respectively. Above ~ 70% Cr metal ratio the Mg―Cr―O films are found to be completely amorphous. The Mg―Y―O films are composed of Mg(Y)O and Y2O3 nano crystallites, up to ~ 50% Y metal ratio. Above this ratio, only Y2O3 nano crystallites are found. The preferential < 111> MgO grain alignment is strongly affected by the increase in M content. For M metal ratios up to ~ 50%, there is a selective promotion of the < 100> MgO grain alignments and a decline in the < 111> grain alignments.

Abstract: The study of materials in cultural heritage artifacts and micro-samples benefits from diagnostic techniques based on intense radiation sources, such as synchrotrons, ion-beam accelerators and lasers. While most of the corresponding techniques are classified as non-destructive, investigation with photons or charged particles entails a number of fundamental processes that may induce changes in materials. These changes depend on irradiation parameters, properties of materials and environmental factors. In some cases, radiation-induced damage may be detected by visual inspection. When it is not, irradiation may still lead to atomic and molecular changes resulting in immediate or delayed alteration and bias of future analyses. Here we review the effects of radiation reported on a variety of cultural heritage materials and describe the usual practice for assessing short-term and long-term effects. This review aims to raise awareness and encourage subsequent research activities to limit radiation side effects.

Abstract: Museum staff usually relies on a proven combination of X-ray radiography (XRR) and infrared reflectography (IRR) to study paintings in a non-destructive manner. In the last decades, however, the research toolbox of heritage scientists has expanded considerably, with a prime example being macro X-ray fluorescence (MA-XRF), producing element-specific images. The goal of this article is to illustrate the added value of augmenting MA-XRF with pulse phase thermography (PPT), a variant of active infrared thermographic imaging (IRT), which is an innovative diagnostic method that is able to reveal variations between or in materials, based on a different response to minor fluctuations in temperature when irradiated with optical radiation. By examining three 16thand 17th-century panel paintings we assess the extent in which combined MA-XRF and PPT contributes to a better understanding of two commonly encountered interventions to panel paintings: (a) Anstuckungen (enlargement of the panel) or (b) substitutions (replacement of part of the panel). Yielding information from different depths of the painting, these two techniques proved highly complementary with IRR and XRR, expanding the understanding of the build-up, genesis, and material history of the paintings. While MA-XRF documented the interventions to the wooden substrate indirectly by revealing variations in painting materials, paint handling and/ or layer sequence between the original part and the extended or replaced planks, PPT proved beneficial for the study of the wooden support itself, by providing a clear image of the wood structure quasi-free of distortion by the superimposed paint or cradling. XRR, on the other hand, revealed other features from the wood structure, not visible with PPT, and allowed looking through the wooden panels, revealing e.g. the dowels used for joining the planks. Additionally, IRR visualised dissimilarities in the underdrawings. In this way, the results indicate that PPT has the potential to become an acknowledged add-on to the expanding set of imaging methods for paintings, especially when used in combination with MA-XRF, IRR and XRR.

Abstract: The measurement of the ratio of stable isotopes of carbon (13C/12C expressed as a δ13C) in the individual components of a sample may be used as a means to identify the origin of these components. This article reviews the approaches and reports on the successes and failures of source identification and apportionment of Polycyclic Aromatic Hydrocarbons (PAHs) with the use of compound-specific isotope analysis (CSIA). One of the conditions for a precise and accurate analysis of isotope ratios with the use of GC-C-IRMS is the need for well separated peaks, with no co-elutions, and reduced unresolved complex mixture (UCM). Additionally, special care needs to be taken for an investigation of possible isotope fractionation effects introduced during the analytical treatment of samples. With the above-mentioned problems in mind, this review discusses in detail and compares current laboratory methodologies, mainly in the extraction and subsequent clean-up techniques used for environmental samples (air particulate matter, soil and sediments). Sampling strategies, the use of isotopic internal standards and the ranges for precision and accuracy are also reported and discussed.

Abstract: Ion chromatographic (IC) methods have been compared in order to achieve an optimal separation of fluoride, acetate and formate under various elution conditions on two formerly introduced analytical columns (i and ii) and a novel one (iii): (i) an IonPac AS14 (250 mm × 4 mm I.D.), (ii) Allsep A-2 (150 mm × 4.6 mm I.D.), and (iii) an IC SI-50 4E (250 mm (length) × 4 mm (internal diameter – I.D.)). The IC conditions for the separation of the anions concerned were optimized on the IC SI-50 4E column. A near baseline separation of these anions was attained on the IonPac AS14, whereas the peaks of fluoride and acetate could not be resolved on the Allsep A-2. A baseline separation for the three anions was achieved on the IC SI-50 4E column, when applying an eluent mixture of 3.2 mmol/L Na2CO3 and 1.0 mmol/L NaHCO3 with a flow rate of 1.0 mL/min. The highest precision of 1.7, 3.0 and 2.8% and the best limits of detection (LODs) of 0.014, 0.22 and 0.17 mg/L for fluoride, acetate and formate, respectively, were obtained with the IC SI-50 4E column. Hence, this column was applied for the determination of the acetic and formic acid contents of air samples taken by means of passive gaseous sampling at the Metropolitan Museum of Art in New York, USA. Atmospheric concentrations of acetic and formic acid up to 1050 and 450 μg/m3, respectively, were found in non-aerated showcases of the museum. In galleries and outdoors, rather low levels of acetic and formic acid were detected with average concentrations of 50 and 10 μg/m3, respectively. The LOD data of acetate and formate on the IC SI-50 4E column correspond to around 0.5 μg/m3 for both acetic and formic acid in air samples.

Abstract: For the isocratic ion chromatography (IC) separation of low-molecular-mass organic acids and inorganic anions three different anion-exchange columns were studied: IonPac AS14 (9 ìm particle size), Allsep A-2 (7 ìm particle size), and IC SI-50 4E (5 ìm particle size). A complete baseline separation for all analyzed anions (i.e., F−, acetate, formate, Cl−, NO2−, Br−, NO3−, HPO42− and SO42−) in one analytical cycle of shorter than 17 min was achieved on the IC SI-50 4E column, using an eluent mixture of 3.2 mM Na2CO3 and 1.0 mM NaHCO3 with a flow rate of 1.0 mL min−1. On the IonPac AS14 column, it was possible to separate acetate from inorganic anions in one run (i.e., less than 9 min), but not formate, under the following conditions: 3.5 mM Na2CO3 plus 1.0 mM NaHCO3 with a flow rate of 1.2 mL min−1. Therefore, it was necessary to adapt a second run with a 2.0 mM Na2B4O7 solution as an eluent under a flow rate of 0.8 mL min−1 for the separation of organic ions, which considerably enlarged the analysis time. For the Allsep A-2 column, using an eluent mixture of 1.2 mM Na2CO3 plus 1.5 mM NaHCO3 with a flow rate of 1.6 mL min−1, it was possible to separate almost all anions in one run within 25 min, except the fluoride-acetate critical pair. A Certified Multianion Standard Solution PRIMUS for IC was used for the validation of the analytical methods. The lowest RSDs (less than 1%) and the best LODs (0.02, 0.2, 0.16, 0.11, 0.06, 0.05, 0.04, 0.14 and 0.09 mg L−1 for F−, Ac−, For−, Cl−, NO2−, Br−, NO3−, HPO42− and SO42−, respectively) were achieved using the IC SI-50 4E column. This column was applied for the separation of concerned ions in environmental precipitation samples such as snow, hail and rainwater.

Abstract: In order to obtain full information coverage on melt inclusions in Martian meteorites (subgroup nakhlites) complementary micro-analytical techniques were used, i.e. focused ion beam, transmission electron microscopy and laser ablation. Using focused ion beam several lamellae for transmission electron microscopy were prepared and secondary electron images of cross-sections could be acquired. Laser ablation-inductively coupled plasma mass spectrometry analyses were performed on selected inclusions to obtain mass-oriented bulk composition of inclusions at depth. The differences in composition between melt inclusions in olivine and augite crystals would suggest a xenocrystic origin for olivine. Furthermore, electron diffraction patterns clearly indicated that the SiO2-rich phase in inclusions from augite in meteorites from Northwest Africa site is re-crystallized, whereas it is still vitreous in the inclusions from Nakhla sampling site. Therefore, different post-entrapment evolutions were active for the two nakhlite meteorite sets, the Nakhla and the NWA817 set. Melt inclusions in Nakhla olivine presented alteration veins, which were presumably produced before their landing on Earth. If this is the case, this would indicate a alteration stage already on Mars with all the consequence in terms of climate history. Melt inclusions in Nakhla augite resulted unaffected by any alteration or modification following the entrapment, and therefore represent the best candidate to indicate the pristine magma composition. (c) 2005 Elsevier B.V. All rights reserved.

Abstract: The mechanism allowing the transition from a two-dimensional strained layer of CdSe on ZnSe to self-assembled islands induced by the use of amorphous selenium is still not fully understood. For a better understanding, atomic force microscopy and transmission electron microscopy studies were performed on CdSe films with a thickness close to that for quantum dot formation. Below this thickness, the sample surface results in undulations along the [110] crystal direction, while few quantum dots are situated in the wave valleys. Plan view transmission electron microscopy studies reveal a strong anisotropy of the islands and show that the Se desorption conditions are crucial. (C) 2006 Elsevier B.V. All rights reserved.

Abstract: In this work, the carbon (C) and silicon (Si) doping and codoping effects on beta-arsenene (As) monolayer structural, electronic, and magnetic properties have been comprehensively investigated using first-principles calculations. The studied two-dimensional (2D) materials exhibit good stability. Pristine beta-As single layer is an indirect gap semiconductor with a band gap of 1.867(2.441) eV as determined by PBE(HSE06) functional. Due to the difference in atomic size and electronic interactions, C and Si substitution induces a significant local structural distortion. Depending upon dopant concentration and doping sites, feature-rich electronic properties including non-magnetic semiconductor, magnetic semiconductor and half-metallicity may be obtained, which result from p-p interactions. High spin-polarization at the Fermi level vicinity and significant magnetism suggest As:1C, As:2C, As:1Si, As:2Si, and As:CSi systems as prospective spintronic 2D materials. While, the C-C, Si-Si, and C-Si dimer doping decreases electronic band gap, making the layer more suitable for applications in optoelectronic devices. Results presented herein may suggest an efficient approach to create novel multi-functional 2D materials from beta-As monolayer.

Abstract: We report the high temperature electronic transport properties of SrFeO3 − ä epitaxial thin films obtained by pulsed laser deposition on NdGaO3(110) substrates. The films show total conductivity higher than the bulk material and apparent activation energy of about 0.12 eV in O2, lower than reported values for SrFeO3 − ä films. The conductivity dependence with oxygen partial pressure shows a power dependence with an exponent close to + 1/4, in agreement with expected point defect equilibrium. For a given oxygen partial pressure, the temperature coefficient of resistance (TCR) shows a low positive value of about 1.52.5 10− 3 K− 1, which is still suitable for resistive oxygen sensing applications. The transport properties of the films are discussed in view of their particular microstructure.