Abstract: Infrared absorption spectra of oxygen precipitates in boron doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function theory of the composite precipitates. The aspect ratio of the platelet precipitates has been determined by transmission electron microscopy measurements. Our analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOgamma precipitates are formed with stoichiometry as in the lightly doped case. In the heavily (>10(18) cm(-3)) boron doped samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3. with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case.

Abstract: In situ HREM irradiation of (110) FZ-Si crystals covered with thin Si3N4 films was carried out in a JEOL-4000EX microscope, operated at 400 keV at room temperature. It is found that clustering of vacancies on (113) planes is realised in a Si layer close to the Si-Si3N4 interface at the initial stage of irradiation. Further aggregation of self-interstitials inside vacancy clusters is considered as an alternative way of point defect recombination in extended shape, to be accomplished with the formation of the extended defects of interstitial type upon interstitial supersaturation.