Abstract: In situ irradiation experiments in a high resolution electron microscope JEOL-4000EX at room temperature resulted in discovery of the isolated and combined clustering of vacancies and self-interstitial atoms on {111}- and {113}-habit planes both leading to an extended defect formation in Si crystals. The type of the defect is strongly affected by the type of supersaturation of point defects depending on the crystal thickness during electron irradiation. Because of the existence of energy barriers against recombination of interstitials with the extended aggregates of vacancies, a large family of intermediate defect configurations (IDCs) is formed on {113}- and {111}-habit planes at a low temperature under interstitial supersaturation in addition to the well-known {133}-defects of interstitial type. The formation of metastable IDCs inside vacancy aggregates prevents a way of recombination of defects in extended shape.

Abstract: In situ HREM irradiation of (110) FZ-Si crystals covered with thin Si3N4 films was carried out in a JEOL-4000EX microscope, operated at 400 keV at room temperature. It is found that clustering of vacancies on (113) planes is realised in a Si layer close to the Si-Si3N4 interface at the initial stage of irradiation. Further aggregation of self-interstitials inside vacancy clusters is considered as an alternative way of point defect recombination in extended shape, to be accomplished with the formation of the extended defects of interstitial type upon interstitial supersaturation.

Abstract: Materials with low dielectric constant ("low-k'') in combination with Cu metallization are replacing the oxide based dielectrics with Al metallization in future generations of micro-electronic devices. In this work, a carbon doped oxide low-k dielectric material is studied after different kinds of etch/strip steps in single damascene Cu. filled line structures. Interline capacitance measurements indicate a dependence of the dielectric constant on the strip conditions. EFTEM is used to study the composition of the dielectric material and the modification of the low-k material at the sidewall of the etched structures for the various treatment conditions.

Abstract: The structure of Fe/GaN/Fe ferromagnetic electrodes is studied by high resolution transmission electron microscopy. The layers grow epitaxially on the GaAs substrate with the top Fe layer 90degrees rotated compared to the bottom one. The interfaces are quite rough. There is an indication of the possible occurrence of Fe3GaAs formation on the GaAs interface.

Abstract: Four aq. solns. contg. natural peat components and the water from Odra river were treated with 3 anion-exchange resins (2.5 to 15 cm(3) of resin per 1 dm(3) of the sample) for 5-60 min to remove the org. matter. The process efficiency was detd. by UV absorbance (254 nm) and colour intensity measurements. The treatment resulted in discoloration of the solns. A resin with weak alky, was the most efficient. The degree of removal increased with increasing the resin dose and contact time. The presence of inorg. anions in the soins. contributed to a decrease of process effectivity.