Abstract: An epitaxially grown heterostructure consisting of alternating layers of LaMnO3 (8 unit cells) and SrMnO3 (4 unit cells) on a SrTiO3 substrate has been studied by a combination of electron energy-loss spectroscopy (EELS) and high-resolution transmission electron microscopy (HRTEM) on an atomic scale. Excitation edges of all elements are captured with subnanometer spatial accuracy, and parametrized to obtain chemical profiles. The fine-edge structure of O K and Mn L-2,L-3 edges are interpreted as signatures of the local electronic structure and show a spatial modulation of the concentration of holes with O 2p character. The chemical concentration is found to be different for the bottom and top interface of a SrMnO3 layer. HRTEM complements the EELS results and confirms the asymmetry of the interfaces. (C) 2001 American Institute of Physics.

Abstract: The formation of Ni silicides is studied by transmission electron microscopy during in situ heating experiments of 12 nm Ni layers on blanket silicon, or in patterned structures covered with a thin chemical oxide. It is shown that the first phase formed is the NiSi2 which grows epitaxially in pyramidal crystals. The formation of NiSi occurs quite abruptly around 400 degreesC when a monosilicide layer covers the disilicide grains and the silicon in between. The NiSi phase remains stable up to 800 degreesC, at which temperature the layer finally fully transforms to NiSi2. The monosilicide grains show different epitaxial relationships with the Si substrate. Ni2Si is never observed. (C) 2001 American Institute of Physics.

Abstract: Microstructural investigations with transmission electron microscopy were carried out on quenched Ni-Ti alloys with 52 and 54.5 at% Ni. For the Ni52Ti48 specimen long time exposed diffraction patterns of a single grain show besides the expected reflections of the B2-phase, two sets of extra reflections in different zones. The first type of spots is explained by lattice displacement waves, which are regarded as precursors of the martensitic Ni-Ti phases, B 19' and R-phase, respectively. The second set of reflection with more diffuse intensity than the other reflections is related to Ni4Ti3 precipitates in an early state of formation. For the Ni-richer Ni54.5Ti45.5 alloy only Ni4Ti3 precipitates in an early state of formation are found but no precursors of the B 19'- and R-phase.