Abstract: Modeling results are presented to gain a better insight in the properties of a SiH4/O2/Ar inductively coupled plasma (ICP) and how it interacts with a silicon substrate (wafer), as applied in the microelectronics industry for the fabrication of electronic devices. The SiH4/O2/Ar ICP is used for the filling of microtrenches with isolating material (SiO2), as applied in shallow trench isolation (STI). In this article, a detailed reaction set that describes the plasma chemistry of SiH4/O2/Ar discharges as well as surface processes, such as sputtering, oxidation, and deposition, is presented. Results are presented on the plasma properties during the plasma enhanced chemical vapor deposition process (PECVD) for different gas ratios, as well as on the shape of the filled trenches and the surface compositions of the deposited layers. For the operating conditions under study it is found that the most important species accounting for deposition are SiH2, SiH3O, SiH3 and SiH2O, while SiH+2, SiH+3, O+2 and Ar+ are the dominant species for sputtering of the surface. By diluting the precursor gas (SiH4) in the mixture, the deposition rate versus sputtering rate can be controlled for a desired trench filling process. From the calculation results it is clear that a high deposition rate will result in undesired void formation during the trench filling, while a small deposition rate will result in undesired trench bottom and mask damage by sputtering. By varying the SiH4/O2 ratio, the chemical composition of the deposited layer will be influenced. However, even at the highest SiH4/O2 ratio investigated (i.e., 3.2:1; low oxygen content), the bulk deposited layer consists mainly of SiO2, suggesting that low-volatile silane species deposit first and subsequently become oxidized instead of being oxidized first in the plasma before deposition. Finally, it was found that the top surface of the deposited layer contained less oxygen due to preferential sputtering of O atoms, making the top layer more Si-rich. However, this effect is negligible at a SiH4/O2 ratio of 2:1 or lower.

Abstract: In this article, surface processes occurring during the etching of Si with a Cl2/O2/Ar plasma are investigated by means of experiments and modeling. Cl2-based plasmas are commonly used to etch silicon, while a small fraction of O2 is added to protect the sidewalls from lateral etching during the shallow trench isolation process. When the oxygen fraction exceeds a critical value, the wafer surface process changes from an etching regime to a deposition regime, drastically reducing the etch rate. This effect is commonly referred to as the etch stop phenomenon. To gain better understanding of this mechanism, the oxygen fraction is varied in the gas mixture and special attention is paid to the effects of oxygen and of the redeposition of non-volatile etched species on the overall etch/deposition process. It is found that, when the O2 flow is increased, the etch process changes from successful etching to the formation of a rough surface, and eventually to the actual growth of an oxide layer which completely blocks the etching of the underlying Si. The size of this etch stop island was found to increase as a function of oxygen flow, while its thickness was dependent on the amount of Si etched. This suggests that the growth of the oxide layer mainly depends on the redeposition of non-volatile etch products. The abrupt change in the etch rate as a function of oxygen fraction was not found back in the oxygen content of the plasma, suggesting the competitive nature between oxidation and chlorination at the wafer. Finally, the wafer and reactor wall compositions were investigated by modeling and it was found that the surface rapidly consisted mainly of SiO2 when the O2 flow was increased above about 15 sccm.

Abstract: In the present work, reactive magnetron sputtering in DC mode was used to grow complex oxide thin films, starting from two separate pure metal targets. A series of coatings was produced with a stoichiometry of the film ranging from MgO, over MgxAlyOz to Al2O3. The surface energy, crystallinity, hardness, refractive index, and surface roughness were investigated. A relationship between all properties studied and the Mg content of the samples was found. A critical compositional region for the Mg-Al-O system where all properties exhibit a change was noticed.