Abstract: Glass treated on its surface with silver compounds and an aluminosilicate, such as ochre or clay, at higher temperatures (between 550 and 650 °C) accepts a wide variety of a yellow colour. It is the aim of this study to investigate the parameters of the manufacturing process affecting the final colour of silver stained glass and to correlate them with the final colour and colour intensity. Therefore, defined mixtures of ochre and a silver compound (AgCl, AgNO3, Ag2SO4, Ag3PO4, Ag2O) were prepared and applied on soda-lime glass. The firing process was modified within the range from 563 to 630 °C and glass samples were analysed after treatment with energy dispersive X-ray fluorescence analysis (EDXRF), scanning electron microscopy (SEM/EDX), transmission electron microscopy (TEM), as well as ion beam analysis (IBA) with an external beam. Within the scope of IBA simultaneous measurements using particle-induced X-ray emission (PIXE), particle-induced gamma-ray emission (PIGE), and Rutherford backscattering spectrometry (RBS) were carried out in order to obtain the thickness of the Ag-rich surface layer and the depth distribution of Ag. By means of TEM the microstructure of the silver particles was visualised. XRF results show that the lowest amount of Ag could be detected on glass samples treated with silver stain mixtures containing AgCl and Ag2O. A low kiln temperature (e.g. 563 °C) results in a higher silver concentration at the surface and lower penetration depths. Furthermore, the results obtained with SEM/EDX at cross-sections of the glass samples could be confirmed by PIXE, PIGE, RBS, and TEM.

Abstract: Accuracy and precision of silicon determination in biological matrices (serum, urine, water, beer and spinach) by spectrometric techniques (when necessary after acid destruction) were assessed by means of a collaborative interlaboratory trial. The trial was set up in accordance with ISO 5725-2 (1994). The relative overall repeatability standard deviation was acceptable. It varied between 4% for spinach powder (mean content: 176 mg kg(-1)) and 11% for serum (mean content: 5.33 mg L-1). On the other hand, the relative overall between-laboratory standard deviation was found to vary from a satisfactorily 15% for spinach after destruction (mean content: 3.32 mg L-1) to an unacceptable 107% for spinach powder (mean content: 176 mg kg(-1)). The overall conclusion of the trial was that silicon determination in biological matrices can properly be performed by spectrometric techniques. However, when sample pretreatment (i.e., acid destruction) is needed prior to silicon determination problems still remain.