Abstract: The rational synthesis, comprehensive characterization, and mechanical and micromechanical properties of a calcium phosphate cement are presented. Hydroxyapatite cement biomaterial was synthesized from reactive sub-micrometer-sized dicalcium phosphate dihydrate and tetracalcium phosphate via a dissolution-precipitation reaction using water as the liquid phase. As a result nanostructured, Ca-deficient and carbonated B-type hydroxyapatite is formed. The cement shows good processibility, sets in 22 ± 2 min and entirely transforms to the end product after 6 h of setting reaction, one of the highest conversion rates among previously reported for calcium phosphate cements based on dicalcium and tetracalcium phosphates. The combination of all elucidated physical-chemical traits leads to an essential bioactivity and biocompatibility of the cement, as revealed by in vitro acellular simulated body fluid and cell culture studies. The compressive strength of the produced cement biomaterial was established to be 25 ± 3 MPa. Furthermore, nanoindentation tests were performed directly on the cement to probe its local elasticity and plasticity at sub-micrometer/micrometer level. The measured elastic modulus and hardness were established to be Es = 23 ± 3.5 and H = 0.7 ± 0.2 GPa, respectively. These values are in close agreement with those reported in literature for trabecular and cortical bones, reflecting good elastic and plastic coherence between synthesized cement biomaterial and human bones.

Abstract: Tempering is widely applied to make carbon atoms beneficially rearrange in high strength steel microstructures after quenching; though the nano-scale interaction of carbon atoms with crystallographic defects is hard to experimentally observe. To improve, we investigate the redistribution of carbon atoms along martensite grain boundaries in a quenched and tempered low carbon steel. We observe the tempering-induced microstructural evolution by in-situ heating in a transmission electron microscope (TEM) and by compositional analysis through atom probe tomography (APT). Probe volumes for APT originate from a single martensite packet but in different tempering conditions, which is achieved via a sequential lift-out with in-between tempering treatments. The complementary use of TEM and APT provides crystallographic as well as chemical information on carbon segregation and subsequent carbide precipitation at martensite grain boundaries. The results show that the amount of carbon segregation to martensite grain boundaries is influenced by the boundary type, e.g. low-angle lath or high-angle block boundaries. Also, the growth behavior of cementite precipitates from grain boundary nucleation sites into neighboring martensite grains differs at low- and high-angle grain boundaries. This is due to the crystallographic constraints arising from the semi-coherent orientation relationship between cementite and adjacent martensite. We also show that slower quenching stabilizes thin retained austenite films between martensite grains because of enhanced carbon segregation during cooling. Finally, we demonstrate the effect of carbon redistribution along martensite grain boundaries on the mechanical properties. Here, we compare micro-scale Vickers hardness results from boundary-containing probe volumes to nanoindentation results from pure bulk martensite (boundary-free) probe volumes.

Abstract: The aim of this paper is to gain understanding of the quasi-static, large strain deformation behavior at room-temperature of high-purity alpha-Ti with an initial split-basal texture. Simple shear tests were conducted along different directions in order to quantify the material's anisotropy and hardening evolution for different strain paths such as monotonic, Bauschinger, and cyclic loadings. The stress-strain curves indicate that the material displays strong anisotropy in the flow behavior. In order to capture the link between microstructure evolution (occurrence of twinning, grain size evolution, etc.) and the macroscopic response, a thoroughly detailed multi-scale characterization using scanning electron microscope (SEM) observations and electron backscattered diffraction (EBSD) analysis was also conducted. Specifically, EBSD analyses indicate that the twin activity and grain fragmentation are responsible for the observed difference between the macroscopic hardening rates corresponding to different directions and loading paths. (C) 2011 Elsevier B.V. All rights reserved.

Abstract: In this report, the possibility of Pt catalytic activity for the dissociation of hydrogen molecules and subsequent hydrogen adsorption on sucrose templated carbon at ambient temperature has been studied. In order to investigate Pt catalytic effect for hydrogen storage solely, 6.8 wt.% Pt-doped (Pt/TC) and pure templated carbon (TC) possessing almost identical specific surface area (SSA) and pore volume (Vp) have been successfully synthesized. Since both Pt/TC and TC shares for their textural properties (e.g. SSA and Vp), any difference of hydrogen adsorption characteristic and storage capacity can be ascribed to the presence of Pt nanoparticles. Both samples are characterized by various techniques such as powder Xray diffraction, ICP-OES, Raman spectroscopy, transmission electron microscopy, cryogenic thermal desorption spectroscopy, low-pressure high-resolution hydrogen and nitrogen BET and high-pressure hydrogen adsorption isotherms in a Sieverts' apparatus. By applying hydrogen and deuterium isotope mixture, cryogenic thermal desorption spectroscopy point to a Pt catalytic activity for the dissociation of hydrogen molecules. Furthermore, the hydrogen adsorption isotherms at RT indicate an enhancement of the initial hydrogen adsorption kinetics in Pt-doped system. However, the hydrogen storage capacity of Pt/TC exhibits a negligible enhancement with a strong hysteresis, suggesting no connection between the spillover effect and a feasible hydrogen storage enhancement. (C) 2013 Elsevier Inc. All rights reserved.

Abstract: The effect of thermal treatment and mechanical stress on the structural and photocatalytic properties of eight different (synthetic and commercial) photocatalysts has been thoroughly investigated. Different mesoporous Ti-based materials were prepared via surfactant based synthesis routes (e.g. Pluronic 123, CTMABr = Cetyltrimethylammonium bromide) or via template-free synthesis routes (e.g. trititanate nanotubes). Also, the stabilizing effect of the NaOH/NH4OH post-treatment on the templated mesoporous materials and their photocatalytic activity was investigated. Furthermore, the thermal and mechanical properties of commercially available titanium dioxides such as P25 Evonik® and Millenium PC500® were studied. The various photocatalysts were analyzed with N2-sorption, X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) to obtain information concerning the specific surface area, pore volume, crystal structure, morphology, phase transitions, etc. In general, results show that the NaOH post-treatment leads to an increased control of the crystallization process during calcination resulting in a higher thermal stability, but at the same time diminishes the photocatalytic activity. Mesoporous materials in which pre-synthesized nanoparticles are used as titania source have the best mechanical stability whereas the mechanical stability of the nanotubes is the most limited. At increased temperatures and pressures, the tested commercial titanium dioxides lose their superior photocatalytic activity caused by a decreased accessibility of the active sites. The observed changes in adsorption capacities and photocatalytic activities cannot be assigned to one single phenomenon. In this respect, it shows the need to define a general/standard method to compare different photocatalysts. Furthermore, it is shown that the photocatalytic properties do not necessarily deteriorate under thermal stress, but can be improved due to crystallization, even though the initial material is (partially) destroyed. It is shown that the usefulness of a specific type of photocatalyst strongly depends on the application and the temperature/pressure to which it needs to resist.

Abstract: A new cyclosilicate hydrate with composition (C6H14N)4·[Si8O16(OH)4]·12H2O was crystallized and the structure determined by single-crystal X-ray diffraction. The structure, described by the tetragonal space group I41/a, with unit cell dimensions of a = 39.2150(2) Å and c = 14.1553(2) Å, contains columns of hydrogen-bonded cubic octamer silicate anions. The space between silicate columns holds hydrogen-bonded water and protonated hexamethyleneimine molecules compensating the negative charge of the silicate. The crystal water can be removed resulting in a rearrangement of the columns into orthorhombic symmetry. Removal of the organic moiety causes amorphisation. Flash evacuation results in a new microporous material with pore volumes typical of a zeolite.

Abstract: Post-synthesis hydrothermal treatments have been used to improve the quality of MCM-41 materials. In our latest work, merging of surfactant-containing silica microspheres during the hydrothermal treatments was observed. Mechanistic insights and the different stages that are involved in the merging process can be summarized as follows. First, the surfaces of the starting microspheres open up due to the dissolution of silica. Then the dissolved silica species provide mass source for the formation of particle necks connecting two neighboring microspheres. Gradually, surfaces of the starting microspheres are flattened to meet the needs of further growth of the necks. Finally, some chain-like highly-ordered mesoporous structures up to several micrometers are formed. The observed merging of the surfactant-containing microspheres is a re-assembling process, which is under the control of electrostatic force between the dissolved silica species and the surfactant cations. The occluded surfactant cations in the precursor spheres play important roles in the merging process.