“Microstructure of adiabatic shear bands in Ti6Al4V”. Peirs J, Tirry W, Amin-Ahmadi B, Coghe F, Verleysen P, Rabet L, Schryvers D, Degrieck J, Materials characterization 75, 79 (2013). http://doi.org/10.1016/j.matchar.2012.10.009
Abstract: Microstructural deformation mechanisms in adiabatic shear bands in Ti6Al4V are studied using traditional TEM and selected area diffraction, and more advanced microstructural characterisation techniques such as energy dispersive X-ray spectroscopy, high angle annular dark field STEM and conical dark field TEM. The shear bands under investigation are induced in Ti6Al4V samples by high strain rate compression of cylindrical and hat-shaped specimens in a split Hopkinson pressure bar setup. Samples from experiments interrupted at different levels of deformation are used to study the evolution of the microstructure in and nearby the shear bands. From the early stages of adiabatic shear band formation, TEM revealed strongly elongated equiaxed grains in the shear band. These band-like grains become narrower towards the centre of the band and start to fraction even further along their elongated direction to finally result in a nano-crystalline region in the core. In fully developed shear bands, twins and a needle-like martensite morphology are observed near the shear band.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 56
DOI: 10.1016/j.matchar.2012.10.009
|
“Twinning in pure Ti subjected to monotonic simple shear deformation”. Tirry W, Bouvier S, Benmhenni N, Hammami W, Habraken AM, Coghe F, Schryvers D, Rabet L, Materials characterization 72, 24 (2012). http://doi.org/10.1016/j.matchar.2012.07.001
Abstract: The aim of this paper is to provide a thorough study on the occurrence and importance of deformation twinning in simple shear deformed pure α-Ti. A statistically relevant inspection of the morphology of the deformation twins in relation to the applied strain/deformation is performed. The investigated microstructural aspects are the twin volume fraction, the twin thickness distribution and the resolved shear stress distribution on the twin plane. All these aspects are examined as a function of the twin types and two initial textures. Monotonic simple shear experiments are carried out for three different loading directions with respect to a direction linked to the initial crystallographic texture. EBSD and TEM observations reveal the presence of View the MathML source and View the MathML source twins. The statistical analysis reveals that View the MathML source and View the MathML source twins have a similar average thickness around 1.9 nm, but the View the MathML source twins show a far larger spread on their thickness and can grow to almost the size of the original parent grain. Correlation of the twin fractions with the RSS analysis shows that RSS is an acceptable method explaining the difference in twin fractions for different textures and orientations. A detailed analysis shows that View the MathML source twins occur in average with a smaller volume fraction but with a higher RSS, indicating they are more difficult to nucleate or grow compared to View the MathML source twinning. In general a higher RSS value on the twin plane is not connected to a higher twin thickness; only in the case of View the MathML source twins the highest RSS values show clearly thicker twins.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 25
DOI: 10.1016/j.matchar.2012.07.001
|
“Tailoring the Ti-C nanoprecipitate population and microstructure of titanium stabilized austenitic steels”. Cautaerts N, Delville R, Stergar E, Schryvers D, Verwerft M, Journal of nuclear materials 507, 177 (2018). http://doi.org/10.1016/J.JNUCMAT.2018.04.041
Abstract: The present work reports on the microstructural evolution of a new heat of 24% cold worked austenitic DIN 1.4970 (15-15Ti) nuclear cladding steel subjected to ageing heat treatments of varying duration between 500 and 800 degrees C (by steps of 100 degrees C). The primary aim was studying the finely dispersed Ti-C nanoprecipitate population, which are thought to be beneficial for creep and swelling resistance during service. Their size distribution and number density were estimated through dark field imaging and bright field Moire imaging techniques in the transmission electron microscope. Nanoprecipitates formed at and above 600 degrees C, which is a lower temperature than previously reported. The observed nucleation, growth and coarsening behavior of the nanoprecipitates were consistent with simple diffusion arguments. The formation of nanoprecipitates coincided with significant dissociation of dislocations as evidenced by weak beam dark field imaging. Possible mechanisms, including Silcock's stacking fault growth model and Suzuki segregation, are discussed. Recrystallization observed after extended ageing at 800 degrees C caused the redissolution of nanoprecipitates. Large primary Ti(C,N) and (Ti,Mo)C precipitates that occur in the as-received material, and M23C6 precipitates that nucleate on grain boundaries at low temperatures were also characterized by a selective dissolution procedure involving filtration, X-ray diffraction and quantitative Rietveld refinement. The partitioning of key elements between the different phases was derived by combining these findings and was consistent with thermodynamic considerations and the processing history of the steel. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.048
Times cited: 1
DOI: 10.1016/J.JNUCMAT.2018.04.041
|
“Influence of amorphous phase separation on the crystallization behavior of glass-ceramics in the BaO-TiO2-SiO2 system”. Boulay E, Ragoen C, Idrissi H, Schryvers D, Godet S, Journal of non-crystalline solids 384, 61 (2014). http://doi.org/10.1016/j.jnoncrysol.2013.06.023
Abstract: The possible role of a prior amorphous phase separation on the subsequent crystallization has been the topic of vigorous debates over the last decades and has not yet been clarified, especially regarding the role of the interfaces created by the phase separation. This study proposes to focus on the interplay between a prior amorphous phase separation and the crystallization of fresnoite in the BaO-TiO2-SiO2 system. The crystallization behavior of a non-stoichiometric composition inside the miscibility gap (called APS) is compared with the stoichiometric composition (called FRES) and a non-stoichiometric composition outside the miscibility gap (called NoAPS). The crystallization mechanisms are compared using differential thermal analysis (DTA) by calculating the Avrami parameters and the activation energies as a function of the particle size. The DTA study shows that the two non-stoichiometric compositions exhibit a pronounced surface crystallization behavior whereas FRES undergoes bulk nucleation. This is supported by a multi-scale microstructure characterization. Furthermore, this study demonstrates that the amorphous phase separation and the associated interfaces do not play any significant role in the nucleation step. Moreover, transmission electron microscope (TEM) and local orientation measurements show that the growth of the dendrites is not hindered by the SiO2-rich droplets. The final stage of crystallization of APS is tentatively explained by two composition effects that must be further investigated: the viscosity effect and the formation of a eutectic. (C) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.124
Times cited: 10
DOI: 10.1016/j.jnoncrysol.2013.06.023
|
“Microstructural dependence on middle eigenvalue in Ti-Ni-Au”. Shi H, Delville R, Srivastava V, James RD, Schryvers D, Journal of alloys and compounds 582, 703 (2013). http://doi.org/10.1016/j.jallcom.2013.08.132
Abstract: The microstructure of various compounds of the Ti-Ni-Au alloy system is investigated by transmission electron microscopy in relation with changing lattice parameters improving the compatibility conditions between austenite and martensite expressed by the lambda(2) = 1 equation based on the Geometrically NonLinear Theory of Martensite (GNLTM). Although local differences in microstructure are observed, when increasing the gold content compound twins are replaced by Type I twins, while twinned lamellar structures are replaced by untwinned plates and self-accommodating structures when lambda(2) = 1 is approached, all confirming the predictions of the GNLTM. (c) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 8
DOI: 10.1016/j.jallcom.2013.08.132
|
“Microstructure and precipitates in annealed Co38Ni33Al29 ferromagnetic shape memory alloy”. Lu JB, Shi H, Sedlakova-Ignacova S, Espinoza R, Kopeček J, Sittner P, Bártová, B, Schryvers D, Journal of alloys and compounds 572, 5 (2013). http://doi.org/10.1016/j.jallcom.2013.03.228
Abstract: Transmission electron microscopy was performed to investigate the microstructure and precipitates in the annealed Co38Ni33Al29 ferromagnetic shape memory alloy. Apart from the dendritic secondary phase in the austenite matrix, micron-sized (up to 100 μm) fcc-based precipitates with partial γ′ L12 ordering and containing none, one or three {1 1 1}p parallel twin planes were found. The orientation relationship between the precipitates and matrix was found to be KurdjumovSachs. STEMEDX analysis indicates that twinned and non-twinned precipitates are Co-rich and Al- and Ni-deficient with respect to the matrix and with a lower Co/Al ratio for the latter. The 3D morphologies of precipitates were reconstructed with focused ion beam/scanning electron microscope dual-beam slice-and-view imaging, showing that the single {1 1 1}p plane twinned precipitates have a plate-like shape while the non-twinned precipitates are lath-like and often bent.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 10
DOI: 10.1016/j.jallcom.2013.03.228
|
“Morphological characterization and distribution of autocatalytic-grown Ni4Ti3 precipitates in a Ni-Ti single crystal”. Cao S, Ke CB, Zhang XP, Schryvers D, Journal of alloys and compounds 577, 215 (2013). http://doi.org/10.1016/j.jallcom.2012.02.013
Abstract: The 3D size, morphology and distribution of autocatalytic-grown Ni4Ti3 precipitates in a Ni51Ti49 single crystal were characterized via a FIB/SEM Slice-and-View procedure and phase-field simulation. Important parameters on size and shape of the precipitates were measured. The pair distribution function and the minimum distance between two precipitates from different variants were calculated to describe the 3D distribution of the autocatalytic-grown Ni4Ti3 precipitates in single crystal Ni-Ti, with a comparison to the polycrystalline Ni50.8Ti49.2 alloy. Phase-field simulation was conducted to study the nucleation behavior of precipitates in the single crystal Ni-Ti. (C) 2012 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 5
DOI: 10.1016/j.jallcom.2012.02.013
|
“Recent EM investigations on nano-and micro-defect structures in SMAs”. Schryvers D, Cao S, Pourbabak, Shi H, Lu, Journal of alloys and compounds 577, S705 (2013). http://doi.org/10.1016/j.jallcom.2011.10.112
Abstract: The present contribution reviews some recent electron microscopy investigations on different shape memory systems in which a variety of nano- and micro-defect structures play an essential role in the functional behaviour of the material. (NiTi3)-Ti-4 precipitates in Ni-Ti are a well-known example for which the focus is now on the 3D configurations, in Ni-Ti-Nb Nb-rich nanoprecipitates are thought to have a large impact on the hysteresis, in Co-Ni-Al an Al-enriched zone nearby the y'-precipitates yields a small sandwiched austenite while some first signs of quasidynamical lattice deformation in non-frozen Ni-Ti strain glass are measured by Cs-aberration-corrected transmission electron microscopy. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 7
DOI: 10.1016/j.jallcom.2011.10.112
|
“Unexpected ordering behaviour of Pt3Al intermetallic precipitates”. Douglas A, Neethling JH, Santamarta R, Schryvers D, Cornish LA, Journal of alloys and compounds 432, 96 (2007). http://doi.org/10.1016/j.jallcom.2006.05.106
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 18
DOI: 10.1016/j.jallcom.2006.05.106
|
“Transmission electron microscopy study of combined precipitation of Ti2Ni(Pd) and Ti2Pd(Ni) in a Ti50Ni30Pd20 alloy”. Delville R, Schryvers D, Intermetallics 18, 2353 (2010). http://doi.org/10.1016/j.intermet.2010.08.006
Abstract: We report a new mode of precipitation in a B19 martensitic Ti50Ni30Pd20 shape memory alloy consisting of a central Ti2Ni(Pd) precipitate surrounded by an austenite area containing Ti2Pd(Ni) precipitates. The morphology and crystallography of the precipitation area is investigated using conventional and high resolution electron microscopy. In particular, the orientation relationship and the coherency strain between the Ti2Pd(Ni) precipitate and the surrounding retained B2 matrix are discussed. A study of local composition in relation with a ternary phase diagram using X-ray energy dispersive spectroscopy with a nanoprobe gives evidences of the formation mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 9
DOI: 10.1016/j.intermet.2010.08.006
|
“Cavity nucleation and growth in Cu-Zn-Al irradiated with Cu+ ions at different temperatures”. Zelaya E, Schryvers D, Tolley A, Fitchner PFP, Intermetallics 18, 493 (2010). http://doi.org/10.1016/j.intermet.2009.09.010
Abstract: The effects of high dose ion irradiation in β CuZnAl were investigated between room temperature and 150 °C. Single crystal samples with surface normal close to [001]β were irradiated with 300 keV Cu+ ions. Microstructural changes were characterized using transmission electron microscopy. Irradiation induced cavities located on the surface exposed to the irradiation were observed. The morphology, size and density distribution of these cavities were analyzed as a function of different irradiation conditions. The shape and location of the cavities with respect to the irradiation surface were not affected by irradiation temperature or irradiation dose. Instead, the cavity size distribution showed a bi-modal shape for a dose of 15 dpa, regardless of irradiation temperature. For a dose of 30 dpa the bi-modal distribution was only observed after room temperature irradiation. The diffusion effects of vacancies produced by irradiation are analyzed in shape memory CuZnAl alloys, which main characteristic is the diffusionless martensitic transformation. Particularly, the cavity size distributions were analyzed in terms of nucleation, growth and coalescence.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 1
DOI: 10.1016/j.intermet.2009.09.010
|
“Grain growth and precipitation in an annealed cold-rolled Ni50.2Ti49.8 alloy”. Srivastava AK, Schryvers D, van Humbeeck J, Intermetallics 15, 1538 (2007). http://doi.org/10.1016/j.intermet.2007.06.003
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 37
DOI: 10.1016/j.intermet.2007.06.003
|
“Twinned b.c.c. sherical particles in a partially crystallised Ti50Ni25Cu25 melt-spun ribbon”. Santamarta R, Schryvers D, Intermetallics 12, 341 (2004). http://doi.org/10.1016/j.intermet.2003.12.002
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 14
DOI: 10.1016/j.intermet.2003.12.002
|
“Advanced TEM investigation of the plasticity mechanisms in nanocrystalline freestanding palladium films with nanoscale twins”. Wang B, Idrissi H, Galceran M, Colla MS, Turner S, Hui S, Raskin JP, Pardoen T, Godet S, Schryvers D, International journal of plasticity 37, 140 (2012). http://doi.org/10.1016/j.ijplas.2012.04.003
Abstract: Nanocrystalline palladium thin films deposited by electron-beam evaporation and deformed by on-chip tensile testing reveal a surprisingly large strain hardening capacity when considering the small similar to 25 nm grain size. The as-grown films contain several coherent single and multifold twin boundaries. The coherency of the twin boundaries considerably decreases with deformation due to dislocation/twin boundary interactions. These reactions are described based on a detailed analysis of the number and the type of dislocations located at the twin boundaries using high-resolution TEM, including aberration corrected microscopy. Sessile Frank dislocations were observed at the twin/matrix interfaces, explaining the loss of the TB coherency due to the Burgers vector pointing out of the twinning plane. Grain boundary mediated processes were excluded as a mechanism dominating the plastic deformation based on the investigation of the grain size distribution as well as the crystallographic texture using Automated Crystallographic Orientation Indexation TEM. Other factors influencing the plastic deformation such as impurities and the presence of a native passivation oxide layer at the surface of the films were investigated using analytical TEM. The twin boundaries observed in the present work partly explain the high strain hardening capacity by providing both increasing resistance to dislocation motion with deformation and a source for dislocation multiplication. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.702
Times cited: 44
DOI: 10.1016/j.ijplas.2012.04.003
|
“Transmission electron microscopy investigation of dislocation slip during superelastic cycling of NiTi wires”. Delville R, Malard B, Pilch J, Sittner P, Schryvers D, International journal of plasticity 27, 282 (2011). http://doi.org/10.1016/j.ijplas.2010.05.005
Abstract: Superelastic deformation of thin NiTi wires containing various nanograined microstructures was investigated by tensile cyclic loading with in situ evaluation of electric resistivity. Defects created by the superelastic cycling in these wires were analyzed by transmission electron microscopy. The role of dislocation slip in superelastic deformation is discussed. NiTi wires having finest microstructures (grain diameter <100 nm) are highly resistant against dislocation slip, while those with fully recrystallized microstructure and grain size exceeding 200 nm are prone to dislocation slip. The density of the observed dislocation defects increases significantly with increasing grain size. The upper plateau stress of the superelastic stressstrain curves is largely grain size independent from 10 up to 1000 nm. It is hence claimed that the HallPetch relationship fails for the stress-induced martensitic transformation in this grain size range. It is proposed that dislocation slip taking place during superelastic cycling is responsible for the accumulated irreversible strains, cyclic instability and degradation of functional properties. No residual martensite phase was found in the microstructures of superelastically cycled wires by TEM and results of the in situ electric resistance measurements during straining also indirectly suggest that none or very little martensite phase remains in the studied cycled superelastic wires after unloading. The accumulation of dislocation defects, however, does not prevent the superelasticity. It only affects the shape of the stressstrain response, makes it unstable upon cycling and changes the deformation mode from localized to homogeneous. The activity of dislocation slip during superelastic deformation of NiTi increases with increasing test temperature and ultimately destroys the superelasticity as the plateau stress approaches the yield stress for slip. Deformation twins in the austenite phase ({1 1 4} compound twins) were frequently found in cycled wires having largest grain size. It is proposed that they formed in the highly deformed B19′ martensite phase during forward loading and are retained in austenite after unloading. Such twinning would represent an additional deformation mechanism of NiTi yielding residual irrecoverable strains.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.702
Times cited: 157
DOI: 10.1016/j.ijplas.2010.05.005
|
“Influence of stress aging process on variants of nano-N4Ti3precipitates and martensitic transformation temperatures in NiTi shape memory alloy”. Radi A, Khalil-Allafi J, Etminanfar MR, Pourbabak S, Schryvers D, Amin-Ahmadi B, Materials &, design 262, 74 (2018). http://doi.org/10.1016/J.ELECTACTA.2018.01.024
Abstract: In this study, the effect of a stress aging process on the microstructure and martensitic phase transformation of NiTi shape memory alloy has been investigated. NiTi samples were aged at 450 degrees C for 1 h and 5 h under different levels of external tensile stress of 15, 60 and 150 MPa. Transmission electron microscopy (TEM) was used to characterize different variants and morphology of precipitates. The results show that application of all stress levels restricts the formation of precipitates variants in the microstructure after I h stress aging process. However, all variants can be detected by prolonging aging time to 5 h at 15 MPa stress level and the variants formation is again restricted by increasing the stress level. Moreover, the stress aging process resulted in changing the shape of precipitates in comparison with that of the stress-free aged samples. Coffee-bean shaped morphologies were detected for precipitates in all stress levels. According to the Differential Scanning Calorimetry (DSC) results, the martensite start temperature (M-s) on cooling shifts to higher temperatures with increasing the tensile stress during the aging process. This can be related to the change ofaustenite to martensite interface energy due to the different volume fractions and variants of precipitates. (c) 2018 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.364
DOI: 10.1016/J.ELECTACTA.2018.01.024
|
“TEM and Raman characterisation of diamond micro- and nanostructures in carbon spherules from upper soils”. Yang ZQ, Verbeeck J, Schryvers D, Tarcea N, Popp J, Rösler W, Diamond and related materials 17, 937 (2008). http://doi.org/10.1016/j.diamond.2008.01.104
Abstract: Carbonaceous spherules of millimeter size diameter and found in the upper soils throughout Europe are investigated by TEM, including SAED, HRTEM and EELS, and Raman spectroscopy. The spherules consist primarily of carbon and have an open cell-like internal structure. Most of the carbon appears in an amorphous state, but different morphologies of nano- and microdiamond particles have also been discovered including flake shapes. The latter observation, together with the original findings of some of these spherules in crater-like structures in the landscape and including severely deformed rocks with some spherules being embedded in the fused crust of excavated rocks, points towards unique conditions of origin for these spherules and particles, possibly of exogenic origin. (C) 2008 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 26
DOI: 10.1016/j.diamond.2008.01.104
|
“Stress-assisted crystallisation in anodic titania”. Vanhumbeeck J-F, Tian H, Schryvers D, Proost J, Corrosion science 53, 1269 (2011). http://doi.org/10.1016/j.corsci.2010.12.020
Abstract: The relationship between the microstructural and internal stress evolution during Ti anodising is discussed. Samples anodised galvanostatically to 12 V and 40 V, corresponding to different stages of the internal stress evolution, were examined by in-plane and cross-section transmission electron microscopy. Electron diffraction patterns have been complemented with stoichiometry data obtained from energy loss near edge structure spectra. The sample anodised to 40 V was observed to consist of two regions, with a crystallised inner region adjacent to the metal/oxide interface. Crystallisation of this region is associated with the presence of large compressive internal stresses which build up during anodising up to 12 V.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.245
Times cited: 11
DOI: 10.1016/j.corsci.2010.12.020
|
“Critical assessments and thermodynamic modeling of BaO-SiO2 and SiO2-TiO2 systems and their extensions into liquid immiscibility in the BaO-SiO2-TiO2 system”. Boulay E, Nakano J, Turner S, Idrissi H, Schryvers D, Godet S, Calphad computer coupling of phase diagrams and thermochemistry 47, 68 (2014). http://doi.org/10.1016/j.calphad.2014.06.004
Abstract: This study discusses rational reproduction of liquid immiscibility in the BaO-SiO2-TiO2 system. While a ternary assessment requires sub-binary descriptions in the same thermodynamic model, the related sub-binary systems BaO-SiO2, BaO-TiO2 and SiO2-TiO2 liquid and solid phases have been evaluated using different thermodynamic models in the literature. In this study, BaO-SiO2 and SiO2-TiO2 were assessed using the Ionic Two Sublattice model (I2SL) based on experimental data from the literature. BaO-TiO2 was already assessed using this model. Binary descriptions developed were then used for the assessment of liquid immiscibility in the BaO-SiO2-TiO2 system. Ternary interaction parameters were found necessary for rational reproduction of the new ternary experimental data gathered in the present work. The model parameters for each system were evaluated using a CAPLHAD approach. A set of parameters is proposed. They show good agreement between the calculated and experimental equilibrium liquidus, liquid immiscibility and thermochemical properties in the BaO-SiO2-TiO2 system. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.6
Times cited: 9
DOI: 10.1016/j.calphad.2014.06.004
|
“The influence of surface oxides on the distribution and release of nickel from Nitinol wires”. Shabalovskaya SA, Tian H, Anderegg JW, Schryvers DU, Carroll WU, van Humbeeck J, Biomaterials 30, 468 (2009). http://doi.org/10.1016/j.biomaterials.2008.10.014
Abstract: The patterns of Ni release from Nitinol vary depending on the type of material (NiTi alloys with low or no processing versus commercial wires or sheets). A thick TiO2 layer generated on the wire surface during processing is often considered as a reliable barrier against Ni release. The present study of Nitinol wires with surface oxides resulting from production was conducted to identify the sources of Ni release and its distribution in the surface sublayers. The chemistry and topography of the surfaces of Nitinol wires drawn using different techniques were studied with XPS and SEM. The distribution of Ni into surface depth and the surface oxide thickness were evaluated using Auger spectroscopy, TEM with FIB and ELNES. Ni release was estimated using either ICPA or AAS. Potentiodynamic potential polarization of selected wires was performed in as-received state with no strain and in treated strained samples. Wire samples in the as-received state showed low breakdown potentials (200 mV); the improved corrosion resistance of these wires after treatment was not affected by strain. It is shown how processing techniques affect surface topography, chemistry and also Ni release. Nitinol wires with the thickest surface oxide TiO2 (up to 720 nm) showed the highest Ni release, attributed to the presence of particles of essentially pure Ni whose number and size increased while approaching the interface between the surface and the bulk. The biological implications of high and lasting Ni release are also discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.402
Times cited: 102
DOI: 10.1016/j.biomaterials.2008.10.014
|
“Evolution of the phase stability of NiAl under low energy ball milling”. Zelaya E, Esquivel MR, Schryvers D, Advanced powder technology 24, 1063 (2013). http://doi.org/10.1016/j.apt.2013.03.008
Abstract: Low energy mechanical alloying of Ni35 at.%Al and Ni40 at.%Al material was performed and the resulting structures were investigated by XRD and TEM. The final intermetallics observed consist of two phases, NiAl(B2) and Ni3Al while 7R and 3R martensite was observed in post-annealed samples. Different integrated milling times were associated to the intermetallic consolidation and initial blend dissociation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.659
Times cited: 10
DOI: 10.1016/j.apt.2013.03.008
|
“Stability of Ni in nitinol oxide surfaces”. Tian H, Schryvers D, Liu D, Jiang Q, van Humbeeck J, Acta biomaterialia 7, 892 (2011). http://doi.org/10.1016/j.actbio.2010.09.009
Abstract: The stability of Ni in titanium oxide surface layers on nitinol wires known to release certain amounts of Ni was investigated by first principles density functional theory and transmission electron microscopy. The oxides were identified as a combination of TiO and TiO2 depending on the thickness of the layer. The calculations indicate that free Ni atoms can exist in TiO at ambient temperature while Ni particles form in TiO2, which was confirmed by the transmission electron microscopy observations. The results are discussed with respect to surface stability and Ni release due to free Ni atoms and Ni particles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 39
DOI: 10.1016/j.actbio.2010.09.009
|
“Effect of nanoprecipitates on the transformation behavior and functional properties of a Ti50.8 at.% Ni alloy with micron-sized grains”. Wang X, Kustov S, Li K, Schryvers D, Verlinden B, Van Humbeeck J, Acta materialia 82, 224 (2015). http://doi.org/10.1016/j.actamat.2014.09.018
Abstract: In order to take advantage of both grain refinement and precipitation hardening effects, nanoscaled Ni4Ti3 precipitates are introduced in a Ti50.8 at.% Ni alloy with micron-sized grains (average grain size of 1.7 μm). Calorimetry, electrical resistance studies and thermomechanical tests were employed to study the transformation behavior and functional properties in relation to the obtained microstructure. A significant suppression of martensite transformation by the obtained microstructure is observed. The thermomechanical tests show that the advantageous properties of both grain refinement and precipitation hardening are combined in the developed materials, resulting in superior shape memory characteristics and stability of pseudoelasticity. It is concluded that introducing nanoscaled Ni4Ti3 precipitates into small grains is a new approach to improve the functional properties of NiTi shape memory alloys.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 51
DOI: 10.1016/j.actamat.2014.09.018
|
“Site occupation of Nb atoms in ternary Ni-Ti-Nb shape memory alloys”. Shi H, Frenzel J, Martinez GT, Van Rompaey S, Bakulin A, Kulkova A, Van Aert S, Schryvers D, Acta materialia 74, 85 (2014). http://doi.org/10.1016/j.actamat.2014.03.062
Abstract: Nb occupancy in the austenite B2-NiTi matrix and Ti2Ni phase in NiTiNb shape memory alloys was investigated by aberration-corrected scanning transmission electron microscopy and precession electron diffraction. In both cases, Nb atoms were found to prefer to occupy the Ti rather than Ni sites. A projector augmented wave method within density functional theory was used to calculate the atomic and electronic structures of the austenitic B2-NiTi matrix phase and the Ti2Ni precipitates both with and without addition of Nb. The obtained formation energies and analysis of structural and electronic characteristics explain the preference for Ti sites for Nb over Ni sites.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 21
DOI: 10.1016/j.actamat.2014.03.062
|
“High strength-ductility of thin nanocrystalline palladium films with nanoscale twins : on-chip testing and grain aggregate model”. Colla M-S, Wang B, Idrissi H, Schryvers D, Raskin J-P, Pardoen T, Acta materialia 60, 1795 (2012). http://doi.org/10.1016/j.actamat.2011.11.054
Abstract: The mechanical behaviour of thin nanocrystalline palladium films with an ∼30 nm in plane grain size has been characterized on chip under uniaxial tension. The films exhibit a large strain hardening capacity and a significant increase in the strength with decreasing thickness. Transmission electron microscopy has revealed the presence of a moderate density of growth nanotwins interacting with dislocations. A semi-analytical grain aggregate model is proposed to investigate the impact of different contributions to the flow behaviour, involving the effect of twins, of grain size and of the presence of a thin surface layer. This model provides guidelines to optimizing the strength/ductility ratio of the films.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 38
DOI: 10.1016/j.actamat.2011.11.054
|
“A weak compatibility condition for precipitation with application to the microstructure of PbTe-Sb2Te3 thermoelectrics”. Chen X, Cao S, Ikeda T, Srivastava V, Snyder GJ, Schryvers D, James RD, Acta materialia 59, 6124 (2011). http://doi.org/10.1016/j.actamat.2011.06.025
Abstract: We propose a weak condition of compatibility between phases applicable to cases exhibiting full or partial coherence and Widmanstätten microstructure. The condition is applied to the study of Sb2Te3 precipitates in a PbTe matrix in a thermoelectric alloy. The weak condition of compatibility predicts elongated precipitates lying on a cone determined by a transformation stretch tensor. Comparison of this cone with the long directions of precipitates determined by a slice-and-view method of scanning electron microscopy combined with focused ion beam sectioning shows good agreement between theory and experiment. A further study of the morphology of precipitates by the Eshelby method suggests that interfacial energy also plays a role and gives an approximate value of interfacial energy per unit area of 250 dyn cm−1.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 8
DOI: 10.1016/j.actamat.2011.06.025
|
“Quantitative three-dimensional analysis of Ni4Ti3 precipitate morphology and distribution in polycrystalline Ni-Ti”. Cao S, Nishida M, Schryvers D, Acta materialia 59, 1780 (2011). http://doi.org/10.1016/j.actamat.2010.11.044
Abstract: The three-dimensional size, morphology and distribution of Ni4Ti3 precipitates in a Ni50.8Ti49.2 polycrystalline shape memory alloy with a heterogeneous microstructure have been investigated using a focused ion beam/scanning electron microscopy slice-and-view procedure. The mean volume, central plane diameter, thickness, aspect ratio and sphericity of the precipitates in the grain interior as well as near to the grain boundary were measured and/or calculated. The morphology of the precipitates was quantified by determining the equivalent ellipsoids with the same moments of inertia and classified according to the Zingg scheme. Also, the pair distribution functions describing the three-dimensional distributions were obtained from the coordinates of the precipitate mass centres. Based on this new data it is suggested that the existence of the heterogeneous microstructure could be due to a very small concentration gradient in the grains of the homogenized material and that the resulting multistage martensitic transformation originates in strain effects related to the size of the precipitates and scale differences of the available B2 matrix in between the precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 34
DOI: 10.1016/j.actamat.2010.11.044
|
“Microstructure changes during non-conventional heat treatment of thin NiTi wires by pulsed electric current studied by transmission electron microscopy”. Delville R, Malard B, Pilch J, Schryvers D, Acta materialia 58, 4503 (2010). http://doi.org/10.1016/j.actamat.2010.04.046
Abstract: Transmission electron microscopy, electrical resistivity measurements and mechanical testing were employed to investigate the evolution of microstructure and functional superelastic properties of 0.1 mm diameter as-drawn NiTi wires subjected to a non-conventional heat treatment by controlled electric pulse currents. This method enables a better control of the recovery and recrystallization processes taking place during the heat treatment and accordingly a better control on the final microstructure. Using a stepwise approach of millisecond pulse annealing, it is shown how the microstructure evolves from a severely deformed state with no functional properties to an optimal nanograined microstructure (2050 nm) that is partially recovered through polygonization and partially recrystallized and that has the best functional properties. Such a microstructure is highly resistant against dislocation slip upon cycling, while microstructures annealed for longer times and showing mostly recrystallized grains were prone to dislocation slip, particularly as the grain size exceeds 200 nm.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 110
DOI: 10.1016/j.actamat.2010.04.046
|
“On the mechanism of twin formation in FeMnC TWIP steels”. Idrissi H, Renard K, Ryelandt L, Schryvers D, Jacques PJ, Acta materialia 58, 2464 (2010). http://doi.org/10.1016/j.actamat.2009.12.032
Abstract: Although it is well known that FeMnC TWIP steels exhibit high work-hardening rates, the elementary twinning mechanisms controlling the plastic deformation of these steels have still not been characterized. The aim of the present study is to analyse the extended defects related to the twinning occurrence using transmission electron microscopy. Based on these observations, the very early stage of twin nucleation can be attributed to the pole mechanism with deviation proposed by Cohen and Weertman or to the model of Miura, Takamura and Narita, while the twin growth is controlled by the pole mechanism proposed by Venables. High densities of sessile Frank dislocations are observed within the twins at the early stage of deformation, which can affect the growth and the stability of the twins, but also the strength of these twins and their interactions with the gliding dislocations present in the matrix. This experimental evidence is discussed and compared to recent results in order to relate the defects analysis to the macroscopic behaviour of this category of material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 244
DOI: 10.1016/j.actamat.2009.12.032
|
“Microstructure of precipitates and magnetic domain structure in an annealed Co38Ni33Al29 shape memory alloy”. Bartova B, Wiese N, Schryvers D, Chapman JN, Ignacova S, Acta materialia 56, 4470 (2008). http://doi.org/10.1016/j.actamat.2008.05.006
Abstract: The microstructure of a Co38Ni33Al29 ferromagnetic shape memory alloy was determined by conventional transmission electron microscopy (TEM), electron diffraction studies together with advanced microscopy techniques and in situ Lorentz microscopy. Rod-like precipitates, 1060 nm long, of hexagonal close-packed -Co were confirmed to be present by high-resolution TEM. The orientation relationship between the precipitates and B2 matrix is described by the Burgers orientation relationship. The crystal structure of the martensite obtained after cooling is tetragonal L10 with a (111) twinning plane. The magnetic domain structure was determined during an in situ cooling experiment using the Fresnel mode of Lorentz microscopy. While transformation proceeds from B2 austenite to L10 martensite, new domains are nucleated, leading to a decrease in domain width, with the magnetization lying predominantly along a single direction. It was possible to completely describe the relationship between magnetic domains and crystallographic directions in the austenite phase though complications existed for the martensite phase.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 23
DOI: 10.1016/j.actamat.2008.05.006
|