“Microstructure and high temperature transport properties of high quality epitaxial SrFeO3-\delta films”. Solís C, Rossell MD, Garcia G, Figueras A, Van Tendeloo G, Santiso J, Solid state ionics 179, 1996 (2008). http://doi.org/10.1016/j.ssi.2008.06.004
Abstract: We report the high temperature electronic transport properties of SrFeO3 − ä epitaxial thin films obtained by pulsed laser deposition on NdGaO3(110) substrates. The films show total conductivity higher than the bulk material and apparent activation energy of about 0.12 eV in O2, lower than reported values for SrFeO3 − ä films. The conductivity dependence with oxygen partial pressure shows a power dependence with an exponent close to + 1/4, in agreement with expected point defect equilibrium. For a given oxygen partial pressure, the temperature coefficient of resistance (TCR) shows a low positive value of about 1.52.5 10− 3 K− 1, which is still suitable for resistive oxygen sensing applications. The transport properties of the films are discussed in view of their particular microstructure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.354
Times cited: 10
DOI: 10.1016/j.ssi.2008.06.004
|
|
|
“Synthesis and characterization of oxygen-deficient oxides BaCo1-xYxO3-y' x = 0.15, 0.25 and 0.33, with the perovskite structure”. Lomakov MV, Istomin SY, Abakumov AM, Van Tendeloo G, Antipov EV, Solid state ionics 179, 1885 (2008). http://doi.org/10.1016/j.ssi.2008.05.004
Abstract: Oxygen-deficient complex cobalt oxides BaCo1 − xYxO3 − y, = 0.15, 0.25 and 0.33, with a cubic perovskite structure have been synthesized in air at 1100 °C using a citrate route. Cation composition of the compounds was confirmed by energy-dispersed X-ray (EDX) microanalysis while oxygen content was determined by iodometric titration. An electron diffraction (ED) study of the x = 0.25 and 0.33 compositions show the presence of a diffuse intensity, indicating possible short-range ordering of the B cations. It was found that the treatment of BaCo0.75Y0.25O2.55 in a humid atmosphere leads to the absorption of water vapour at the first stage. Oxygen permeation studies of the ceramic membranes of BaCo0.75Y0.25O2.55 and BaCo0.67Y0.33O2.55 with variable thickness showed high oxygen fluxes of 0.170.32 µmol/cm2/s at 950 °C.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.354
Times cited: 9
DOI: 10.1016/j.ssi.2008.05.004
|
|
|
“Thickness-dependent transport properties of Sr4Fe6O13 epitaxial thin films”. Pardo JA, Santiso J, Solis C, Garcia G, Figueras A, Rossell MD, Solid state ionics 177, 423 (2006). http://doi.org/10.1016/J.SSI.2005.11.024
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.354
DOI: 10.1016/J.SSI.2005.11.024
|
|