“Controllable nitrogen doping in as deposited TiO2 film and its effect on post deposition annealing”. Deng S, Verbruggen SW, Lenaerts S, Martens JA, Van den Berghe S, Devloo-Casier K, Devulder W, Dendoover J, Deduytsche D, Detavernier C, Journal of vacuum science and technology: A: vacuum surfaces and films 32, 01a123 (2014). http://doi.org/10.1116/1.4847976
Abstract: In order to narrow the band gap of TiO2, nitrogen doping by combining thermal atomic layer deposition (TALD) of TiO2 and plasma enhanced atomic layer deposition (PEALD) of TiN has been implemented. By altering the ratio between TALD TiO2 and PEALD TiN, the as synthesized TiOxNy films showed different band gaps (from 1.91 eV to 3.14 eV). In situ x-ray diffraction characterization showed that the crystallization behavior of these films changed after nitrogen doping. After annealing in helium, nitrogen doped TiO2 films crystallized into rutile phase while for the samples annealed in air a preferential growth of the anatase TiO2 along (001) orientation was observed. Photocatalytic tests of the degradation of stearic acid were done to evaluate the effect of N doping on the photocatalytic activity.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 1.374
Times cited: 10
DOI: 10.1116/1.4847976
|
|
|
“Determination of fluorine in uranium oxyfluoride particles as an indicator of particle age”. Kips R, Pidduck AJ, Houlton MR, Leenaers A, Mace JD, Marie O, Pointurier F, Stefaniak EA, Taylor PDP, van den Berghe S, van Espen P, Van Grieken R, Wellum R, Spectrochimica acta: part B : atomic spectroscopy 64, 199 (2009). http://doi.org/10.1016/J.SAB.2008.12.001
Abstract: As swipe samples from enrichment activities typically contain uranium particles with a detectable amount of fluorine, the question was raised whether the analysis of fluorine in particles could complement the information on the uranium isotope ratios. For this, uranium oxyfluoride particles were prepared from the controlled hydrolysis of uranium hexafluoride (UF6). The relative amount of fluorine was characterized by scanning electron microscopy combined with energy-dispersive X-ray spectrometry (SEM-EDX), as well as ion-microprobe secondary ion mass spectrometry (IM-SIMS). Of particular interest was the assessment of the reduction of the amount of fluorine over time, and after exposure to UV-light and high temperatures. Micro-Raman spectrometry (MRS) was applied to look for differences in molecular structure between these various sample types. Both SEM-EDX and IM-SIMS showed a general reduction of the fluorine-to-uranium ratio after 12 years of storage. The exposure to UV-light and high temperatures was found to have accelerated the loss of fluorine. A distinct peak at 865 cm− 1 Raman shift was detected for the majority of particles analyzed by MRS. For the particles that were heat-treated, the Raman spectra were similar to the spectrum of U3O8. Although often large variations were observed between particles from the same sample, the three particle measurement techniques (IM-SIMS, SEM-EDX and MRS) showed some consistent trends. They therefore appear promising in terms of the ability to place bounds on particle age, as well as shedding light on the complex processes involved in UO2F2 particle ageing.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Chemometrics (Mitac 3)
DOI: 10.1016/J.SAB.2008.12.001
|
|
|
“Local structure and oxidation state of uranium in some ternary oxides: X-ray absorption analysis”. Soldatov AV, Lamoen D, Konstantinović, MJ, van den Berghe S, Scheinost AC, Verwerft M, Journal Of Solid State Chemistry 180, 54 (2007). http://doi.org/10.1016/j.jssc.2006.08.038
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 2.299
Times cited: 60
DOI: 10.1016/j.jssc.2006.08.038
|
|