Abstract: Infrared absorption spectra of composite precipitates are analysed with a modified Day-Thorpe algorithm, assuming a precipitated phase consisting of a mixture of two components with known optical properties. Additional constraints are introduced when solving the model equations by using a priori knowledge making the algorithm more reliable. It is shown that this novel approach allows determining both morphology and composition of precipitates. The method is applied to characterise oxide precipitates in boron-doped silicon. The results indicate that for the resistivity range above 60 mOmegacm, the precipitated phase is most probably SiO1.17+/-0.14, while for resistivities below 20 mOmega cm, precipitates consist of a SiO2/B2O3 composite with a large volume fraction of B(2)0(3) (up to 40% for 8 mOmegacm material). (C) 2003 Elsevier B.V. All rights reserved.

Abstract: Time-of-flight static secondary ion mass spectrometry (TOF-S-SIMS) was used to characterize thin layers of oxy- and thiocarbocyanine dyes on Ag and Si. Apart from adduct ions a variety of structural fragment ions were detected for which a fragmentation pattern is proposed. Peak assignments were confirmed by comparing spectra of dyes with very similar structures. All secondary ions were assigned with a mass accuracy better than 50 ppm. The intensity of molecular ions as well as fragment ions has been studied as a function of the type of organic dye, the substrate, the layer thickness and the type of primary ion. A large yield difference of two orders of magnitude was observed between the precursor ions of cationic carbocyanine dyes and the protonated molecules of the anionic dyes. Fragment ions, on the other hand, yielded similar intensities for both types of dye. As the dye layers deposited on an Ag substrate yielded higher secondary ion intensities than those deposited on a Si substrate, the Ag metal clearly acts as a promoting agent for secondary ion formation. The effect was more pronounced for precursor signals than for fragment ions. The promoting effect decreased as the deposited layer thickness of the organic dye layer was increased. Copyright (C) 2003 John Wiley Sons, Ltd.

Abstract: It is known that the neutral image tone of a developed photographic film becomes brownish when the thickness of the original silver halide tabular crystals is reduced. We investigate by electron microscopy to what extent the silver filament structure has changed and how it induces the shift in image tone. Therefore, two samples of AgBr {111} tabular crystals with average thicknesses of 160 nm and 90 nm respectively, are compared. It is shown that the dimensions and defect structure of the filaments are comparable, but that the 90 nm crystals result in a more widely spaced structure, which explains the shift in image tone on a qualitative level. The influence of the addition of an image toner, i.e., phenylmercaptotetrazole, on the filament structure is also investigated. An even more open filament structure of longer, but smaller filaments was observed.

Abstract: The influence of the amount of catalyst and the reaction time on the quantity and quality of catalytically grown single wall carbon nanotubes (SWNT) was investigated. The aim was to optimize some of the SWNT growth parameters using TEM and HRTEM. The thickness of catalyst layer influences the synthesis of the nanotube because the gas composition can differ between top and bottom. Microscopic investigation of the grown SWNT samples showed that the thicker the catalyst layer the lower relative nanotube content, so the deeper parts of the catalyst layer are less effective: The optimum time for the reaction was found to be 10 minutes. This may be understood assuming that nanotube growth needs an initial incubation time while the activity of the catalyst decreases steadily until the nariotube growth stops.