Abstract: The use of non-invasive macroscopic imaging techniques is becoming more prevalent in the field of cultural heritage, especially to avoid invasive procedures that damage valuable artworks. For this purpose, an X-ray powder diffraction scanner (MA-XRPD) capable of visualising crystalline compounds in a highly specific manner was recently developed. Many inorganic pigments present in paintings fall into this category of materials. In this study, the 17th century oil painting Girl with a Pearl Earring (c. 1665) by Johannes Vermeer was analysed with a combination of transmission and reflection mode MA-XRPD. By employing this scanner in reflection mode, the relative sensitivity for compounds that are present at the paint surface could be increased, establishing it as a highly relevant technique for investigating the degradation processes that are ongoing at paint surfaces. Many of the original pigments employed by Vermeer could be identified, along with four secondary alteration products: gypsum (CaSO4 center dot 2H(2)O), anglesite (PbSO4), palmierite (K2Pb(SO4)(2)) and weddellite (CaC2O4 center dot 2H(2)O). The formation of gypsum was linked to the presence of chalk in the upper glaze layer while the formation of palmierite and weddellite is driven by the presence of lake pigments (and their substrates). In this manner, MA-XRPD can also be used to pinpoint locations relevant for sampling and synchrotron mu-XRPD analysis, which provides information on the microscopic make-up of the paint. A paint cross-section taken from an area rich in palmierite was analysed with synchrotron mu-XRPD, which confirmed the presence of this secondary compound at the interface of the upper paint layer with the ground layer as well as the presence of anglesite in the ground layer. The capacity of MA-XRPD to identify and chart secondary alteration products in a non-invasive manner has only very recently been demonstrated and makes it a highly relevant technique for the assessment of the chemical condition of works of art.

Abstract: Jackson Pollock's Number 1A, 1948 painting was investigated using in situ scanning macro-x-ray fluorescence mapping (MA-XRF) to help characterize the artist's materials and his creative process. A multivariate curve resolution-alternating least squares (MCR-ALS) approach was used to examine the hyperspectral data and obtain distribution maps and signature spectra for the paints he used. The composition of the paints was elucidated based on the chemical elements identified in the signature spectra and a tentative list of pigments, fillers and other additives is proposed for eleven different paints and for the canvas. The paint distribution maps were used to virtually reconstruct the artist process and document the sequence and manner in which Pollock applied the different paints, using deliberate and specific gestures.

Abstract: Two state-of-the-art methods for non-invasive visualization of subsurface (or overpainted) pictorial layers present in painted works of art are employed to study Le portrait, painted by Belgian artist Rene Magritte in 1935. X-ray radiography, a commonly used method for the nondestructive inspection of paintings, had revealed the presence of an underlying figurative composition, part of an earlier Magritte painting entitled La pose enchantee (1927) which originally depicted two full length nude female figures with exaggerated facial features. On the one hand, macroscopic X-ray fluorescence analysis (MA-XRF), a method capable of providing information on the distribution of the key chemical elements present in many artists' pigments, was employed. The ability of the X-rays to penetrate the upper layer of paint enabled the imaging of the facial features of the female figure and provided information on Magritte's palette for both surface and hidden composition. On the other hand, visible and near infrared hyperspectral imaging spectroscopies in transmission mode were also used, especially in the area of the table cloth in order to look through the upper representation and reveal the pictorial layer(s) below. MA-XRF provided elemental information on the pigment distributions in both the final painting and the prior whereas the transmission mode provided information related to preparatory sketches as well as revealing differences between the paints used in both compositions. These results illustrate very well the manner in which the two imaging methods complement each other, both in the sense of providing different types of information on the nature and presence of paint components/pigments and in the sense of being optimally suited to easily penetrate through different types of overpaint.

Abstract: The combination of several micro-XRF analysis modes is presented for the investigation of an illuminated parchment manuscript. With a commercial instrument, conventional micro-XRF spot analysis (0D) and mapping (2D) are performed, yielding detailed lateral elemental information. Depth resolution becomes accessible by mounting an additional polycapillary lens in front of an SDD detector. Quantitative confocal depth profiles (1D) are presented as well as the full separation of the front and the backside decorations with the help of fast 3D mappings of specific areas. Only through the use of these multidimensional modes can elemental information be assigned both to lateral and depth positions, making the analysis of such heterogeneous samples feasible.

Abstract: In cultural heritage science, compositional data is traditionally obtained from works of art through the analysis of samples by means of various bench-top instruments (scanning electron microscope, Raman spectrometer, etc.). Alternatively, the object can be transported to a laboratory where it may be examined, usually by spectroscopic methods working in reflection mode. However, this paper describes how a complementary set of mobile and portable instruments was deployed in situ to gain a comprehensive view on the materials and related ageing compounds of an (almost) unmovable 15th-C polyptych, prior to and in preparation of the extraction of a limited number of samples. In line with the methodological approach discussed, PXRF was first employed as an efficient screening tool. The ensuing elemental data was supplemented by more specific information on both organic as inorganic materials supplied by reflection near- and mid-FTIR spectroscopy and fluorimetry. In completion, a limited number of diffraction patterns were collected with a mobile XRD instrument in order to identify the constituent crystalline phases in pigments, grounding materials and degradation products. In this way, it could be demonstrated how a rich array of colours was obtained by means of a limited palette of pigments: lead white, lead tin yellow, azurite, natural ultramarine, bone black, vermillion, madder lake, and a green copper-organo complex were detected and situated on the panels. Remarkably, next to chalk also gypsum was found in the ground layer(s) of this Western European easel painting. The relatively large surface of the background was covered with gold leaf; the analyses seem to point towards the labour-intensive water gilding technique. The versatility of this combination of analytical techniques was further illustrated by the accurate characterisation of degradation products affecting the readability and conservation of the painting: the overall presence of a calcium oxalate-based film of variable thickness was established. Nevertheless, further analysis of cross-sectioned samples was considered desirable in order to study the stratigraphy, to gain direct access to altered and sub-imposed layers and to allow highly detailed analysis of micrometric degradation products by state-of-the art techniques (i.e. synchrotron radiation).

Abstract: Elemental distribution maps are of great interest in the study of historical paintings, as they allow to investigate the pigment use of the artist, to image changes made in the painting during or after its creation and in some cases to reveal discarded paintings that were later over painted. Yet a method that allows to record such maps of a broad range of elements in a fast, non-destructive and in situ manner is not yet commonly available; a dedicated mobile scanning XRF instrument might fill this gap. In this paper we present three self-built scanning macro-XRF instruments, each based on the experience gained with its precursor. These instruments are compared in terms of sensitivity and limits of detection, which includes a discussion of the use of polycapillary optics and pinhole collimators as beam defining devices. Furthermore, the imaging capabilities of the instruments are demonstrated in three exemplary cases: (parts of) historical paintings from the 15th to the 19th century are examined. These cases illustrate the value of element specific distribution maps in the study of historical paintings and allow in the case of Vincent van Gogh's Patch of Grass a direct comparison between in situ and synchrotron based scanning macro-XRF.

Abstract: Recent studies in which X-ray beams of macroscopic to (sub) microscopic dimensions were used for non-destructive analysis and characterization of pigments, paint micro samples and/or entire paintings by Vincent van Gogh are concisely reviewed. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging as well as with the combined use of X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Microscopic and macroscopic XRF are variants of the method that are well suited to visualize the elemental distribution of key elements, mostly metals, present in paint multi layers, either on the length scale from 1–100 μm inside micro samples taken from paintings or on the 1–100 cm length scale when the (subsurface) distribution of specific pigments in entire paintings is concerned. In the context of the characterization of van Gogh's pigments subject to natural degradation, the use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS and μ-XRD have proven themselves to be very suitable for such studies. Their use is often combined with microscopic Fourier transform infra-red (μ-FTIR) spectroscopy since this method delivers complementary information at more or less the same length scale as the X-ray microprobe techniques. Also in the context of macroscopic imaging of works of art, the complementary use of X-ray based and infra-red based imaging appears very promising; some recent developments are discussed.

Abstract: Vincent van Gogh (1853−1890), one of the founding fathers of modern painting, is best known for his vivid colors, his vibrant painting style, and his short but highly productive career. His productivity is even higher than generally realized, as many of his known paintings cover a previous composition. This is thought to be the case in one-third of his early period paintings. Van Gogh would often reuse the canvas of an abandoned painting and paint a new or modified composition on top. These hidden paintings offer a unique and intimate insight into the genesis of his works. Yet, current museum-based imaging tools are unable to properly visualize many of these hidden images. We present the first-time use of synchrotron radiation based X-ray fluorescence mapping, applied to visualize a womans head hidden under the work Patch of Grass by Van Gogh. We recorded decimeter-scale, X-ray fluorescence intensity maps, reflecting the distribution of specific elements in the paint layers. In doing so we succeeded in visualizing the hidden face with unprecedented detail. In particular, the distribution of Hg and Sb in the red and light tones, respectively, enabled an approximate color reconstruction of the flesh tones. This reconstruction proved to be the missing link for the comparison of the hidden face with Van Goghs known paintings. Our approach literally opens up new vistas in the nondestructive study of hidden paint layers, which applies to the oeuvre of Van Gogh in particular and to old master paintings in general.

Abstract: Previous investigations about the darkening of chrome yellow pigments revealed that this form of alteration is attributable to a reduction of the original Cr(VI) to Cr(III), and that the presence of sulfur-containing compounds, most often sulfates, plays a key role during this process. We recently demonstrated that different crystal forms of chrome yellow pigments (PbCrO4 and PbCr1xSxO4) are present in paintings by Vincent van Gogh. In the present work, we show how both the chemical composition and the crystalline structure of lead chromate-based pigments influence their stability. For this purpose, oil model samples made with in-house synthesized powders of PbCrO4 and PbCr1xSxO4 were artificially aged and characterized. We observed a profound darkening only for those paint models made with PbCr1xSxO4, rich in SO42 (x ≥ 0.4), and orthorhombic phases (>30 wt %). Cr and S K-edge micro X-ray absorption near edge structure investigations revealed in an unequivocal manner the formation of up to about 60% of Cr(III)-species in the outer layer of the most altered samples; conversely, independent of the paint models chemical composition, no change in the S-oxidation state was observed. Analyses employing UVvisible diffuse reflectance and Fourier transform infrared spectroscopy were performed on unaged and aged model samples in order to obtain additional information on the physicochemical changes induced by the aging treatment.

Abstract: The darkening of the original yellow areas painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is a phenomenon widely observed on several paintings by Vincent van Gogh, such as the famous different versions of Sunflowers. During our previous investigations on artificially aged model samples of lead chromate, we established for the first time that darkening of chrome yellow is caused by reduction of PbCrO4 to Cr2O3·2H2O (viridian green), likely accompanied by the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide]. In the second part of this work, in order to demonstrate that this reduction phenomenon effectively takes place in real paintings, we study original paint samples from two paintings of V. van Gogh. As with the model samples, in view of the thin superficial alteration layers that are present, high lateral resolution spectroscopic methods that make use of synchrotron radiation (SR), such as microscopic X-ray absorption near edge (μ-XANES) and X-ray fluorescence spectrometry (μ-XRF) were employed. Additionally, μ-Raman and mid-FTIR analyses were carried out to completely characterize the samples. On both paint microsamples, the local presence of reduced Cr was demonstrated by means of μ-XANES point measurements. The presence of Cr(III) was revealed in specific areas, in some cases correlated to the presence of Ba(sulfate) and/or to that of aluminum silicate compounds.

Abstract: This chapter lays out a conservation timeline, from past to future, for the Amsterdam version of Van Gogh's Sunflowers. It starts by considering the restoration history of the painting in order to assess its current physical state, and looks ahead to formulate an appropriate strategy for future conservation treatment and display. Due attention is paid to the two recorded episodes of restoration performed in 1927 and 1961 by the Dutch restorer, Jan Cornelis Traas. Based on physical and chemical investigation of Sunflowers we attempt to reconstruct what these former treatments (which are barely documented) entailed and consider the repercussions for the present condition of the painting. The former interventions by Traas also serve as a benchmark to reflect on current choices made, highlighting the extent to which ideas and methodologies have continued to evolve over the past century as conservation has moved further away from being a singularly craft-based activity to become an established historical and scientific discipline underpinned by ethical guidelines. Jan Cornelis Traas (1898–1984) As mentioned, the two main recorded interventions to the Amsterdam Sunflowers may be associated with the Dutch restorer, Jan Cornelis Traas, who treated the picture in 1927, close to the start of his career, and again in 1961, shortly before he retired. Traas was the first restorer to be appointed at the Mauritshuis in The Hague where he worked from 1931 to 1962 and treated hundreds of paintings, including iconic masterpieces such as Girl with a Pearl Earring by Johannes Vermeer. Yet despite the magnitude and importance of his restoration oeuvre, J.C. Traas (as he is usually referred to in surviving documents), has remained somewhat obscure. He is shown here in the only known surviving photograph of him at work, shortly before he retired (fig. 7.1). Unlike his illustrious contemporaries, A. Martin de Wild (1899–1969) and Helmut Ruhemann (1891–1973), for example, Traas did not publish anything, he appears to have kept no records of his work and no personal archive is known. However, the study of some newly discovered historical documents, combined with physical examination of Sunflowers and a large number of other works he treated, allows us to recover an idea of his working practices and approaches viewed within the context of his day.

Abstract: This chapter explains the materials and techniques employed in the Amsterdam Sunflowers, enabling a comparison with the London version described in chapter 3. Building upon the 2016 article published in the National Gallery Technical Bulletin, it incorporates the latest findings gained by computer-assisted methods used to characterize the canvas support, as well as in-situ campaigns of non-invasive investigation together with further analysis of microscopic paint samples. The chapter sequence follows the steps in Van Gogh's working practice. Starting with the canvas, automated analysis of the weave enables the provenance of the canvas to be traced back to a particular roll of linen ordered by Van Gogh. Combining technical evidence with knowledge of historical manufacturing techniques further allows us to reconstruct the way in which Van Gogh divided his canvas roll into pieces used for Sunflowers and other paintings. We go on to consider how, with the original painting at hand, he used charcoal to transfer the motif of the London Sunflowers onto his blank canvas. Despite careful planning of the composition, an adjustment was required late in the working process, when Van Gogh added a painted wooden strip to extend the background above the flower at the top edge of the canvas. The artist's process of working up the composition in paint is described, paying special attention to his use of colour. The pigments and pigment mixtures used in the Amsterdam Sunflowers have been comprehensively mapped and are compared with the London picture, with discussion of some similarities and differences that account for the distinctive colour scheme of each painting. This understanding of colour application in the Amsterdam Sunflowers lays the foundation for subsequent chapters that will go on to consider the impact of light-induced colour changes that have taken place over time, and the related need to define appropriate lighting guidelines for the future safe preservation of this painting and others made with similar materials (chapters 5 and 7).

Abstract: Museum staff usually relies on a proven combination of X-ray radiography (XRR) and infrared reflectography (IRR) to study paintings in a non-destructive manner. In the last decades, however, the research toolbox of heritage scientists has expanded considerably, with a prime example being macro X-ray fluorescence (MA-XRF), producing element-specific images. The goal of this article is to illustrate the added value of augmenting MA-XRF with pulse phase thermography (PPT), a variant of active infrared thermographic imaging (IRT), which is an innovative diagnostic method that is able to reveal variations between or in materials, based on a different response to minor fluctuations in temperature when irradiated with optical radiation. By examining three 16thand 17th-century panel paintings we assess the extent in which combined MA-XRF and PPT contributes to a better understanding of two commonly encountered interventions to panel paintings: (a) Anstuckungen (enlargement of the panel) or (b) substitutions (replacement of part of the panel). Yielding information from different depths of the painting, these two techniques proved highly complementary with IRR and XRR, expanding the understanding of the build-up, genesis, and material history of the paintings. While MA-XRF documented the interventions to the wooden substrate indirectly by revealing variations in painting materials, paint handling and/ or layer sequence between the original part and the extended or replaced planks, PPT proved beneficial for the study of the wooden support itself, by providing a clear image of the wood structure quasi-free of distortion by the superimposed paint or cradling. XRR, on the other hand, revealed other features from the wood structure, not visible with PPT, and allowed looking through the wooden panels, revealing e.g. the dowels used for joining the planks. Additionally, IRR visualised dissimilarities in the underdrawings. In this way, the results indicate that PPT has the potential to become an acknowledged add-on to the expanding set of imaging methods for paintings, especially when used in combination with MA-XRF, IRR and XRR.

Abstract: Almost seventy years after artists such as Frank Stella (1936), Andy Warhol (1928-1987), James Rosenquist (1933-2017), Herb Aach (1923-1985) and Richard Bowman (1918-2001) started to incorporate Daylight Fluorescent Pigments (DFPs) in their artworks, the extent of the conservation problems that are associated with these pigments has increased progressively. Since their first appearance on the market, their composition has constantly been improved in terms of permanency. However, conservation practices on the artworks that are used in, are complicated by the fact that the composition of DFPs is proprietary and the information provided by the manufactures is limited. To be able to propose adequate conservation strategies for artworks containing DFPs, a thorough understanding of the DFPs composition must be acquired. In contrast with previous research that concentrated on identification of the coloring dye, this paper focuses on the characterization of the resin, used as the carrier for the dye. The proposed approach, involving ATR-FTIR, SPME-GC-MS and XRF analysis, provided additional insights on the organic and inorganic components of the resin. Using this approach, we investigated historical DFPs and new formulations, as well as different series from the main manufacturing companies (DayGlo, Swada, Radiant Color and Kremer) in order to obtain a full characterization of DFPs used by the artists along the years. First, the initial PCA-assisted ATR-FTIR spectroscopy allowed for an efficient classification of the main monomers in the resin polymer. Next, a further distinction was made by mass spectrometry and XRF which were optimized to allow a more specific classification of the resin and for detection of additives. In this paper we show the potential of SPME-GC-MS, never applied for the characterization of artistic materials, at present undervalued for heritage science purposes. We anticipate that this information will be highly relevant in the future stability studies and for defining (preventive) conservation strategies of fluorescent artworks.

Abstract: The painting Saul and David, considered to date from c. 1652 and previously attributed to Rembrandt van Rijn and/or his studio, is a complex work of art that has been recently subjected to intensive investigation and conservation treatment. The goal of the research was to give insight into the painting's physical construction and condition in preparation for conservation treatment. It was also anticipated that analysis would shed light on authenticity questions and Rembrandt's role in the creation of the painting. The painting depicts the Old Testament figures of King Saul and David. At left is Saul, seated, holding a spear and wiping a tear from his eye with a curtain. David kneels before him at the right playing his harp. In the past, the large sections with the life-size figures were cut apart and later reassembled. A third piece of canvas was added to replace a missing piece of canvas above the head of David. As part of the investigation into the authenticity of the curtain area, a number of paint micro samples were examined with LM and SEM-EDX. Given that the earth, smalt and lake pigments used in the painting could not be imaged with traditional imaging techniques, the entire painting was also examined with state of the art non-destructive imaging techniques. Special attention was devoted to the presence of cobalt-containing materials, specifically the blue glass pigment smalt considered characteristic for the late Rembrandt. A combination of quantitative electron microprobe analysis and macroscopic X-ray fluorescence scanning revealed that three types of cobalt-containing materials are present in the painting. The first type is a cobalt drier that was found in the overpaint used to cover up the canvas inset and the joins that were added in the 19th century. The other two Co-containing materials are part of the original paint used by Rembrandt and comprise two varieties of smalt, a K-rich glass pigment that derives its gray-blue color by doping with Co-ions. Smalt paint with a higher Ni content (NiO:CoO ratio of around 1:4) was used to depict the blue stripes in Saul's colorful turban, while smalt with a lower Ni content was employed (NiO:CoO ratio of around 1:5) for the broad expanses of Saul's garments. The presence of two types of smalt not only supports the recent re-attribution of the painting to Rembrandt, but also that the picture was painted in two phases. Saul's dark red garment is painted in a rough, “loose” manner and the now discolored smalt-rich layer was found to have been partially removed during a past restoration treatment/s. In contrast, the blue-green smalt in the turban is much better preserved and provides a colorful accent. While the use of different types of smalt in a Rembrandt painting has been previously identified using quantitative EDX analysis of paint cross-sections, to the best of our knowledge this is the first time such a distinction has been observed in a 17th-century painting using non-destructive imaging techniques. In addition to the XRF-based non-invasive elemental mapping, hyperspectral imaging in the visual to near-infrared (VNIR) region was also carried out. (C) 2016 Elsevier B.V. All rights reserved.