“Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses”. Penders A, Konstantinovic MJ, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology , 1 (2020). http://doi.org/10.1080/1478422X.2020.1785651
Abstract: Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.8
Times cited: 1
DOI: 10.1080/1478422X.2020.1785651
|
|
|
“Microstructural investigation of IASCC crack tips extracted from thimble tube O-ring specimens”. Penders AG, Konstantinovic MJ, Yang T, Bosch R-w, Schryvers D, Somville F, Journal of nuclear materials 565, 153727 (2022). http://doi.org/10.1016/J.JNUCMAT.2022.153727
Abstract: The microstructural features of intergranular irradiation-assisted stress corrosion crack tips from a redeemed neutron-irradiated flux thimble tube (60 dpa) have been investigated using focused-ion beam analysis and (scanning) transmission electron microscopy. The current work presents a close examination of the deformation field and oxide assembly associated with intergranular cracking, in addition to the analysis of radiation-induced segregation at leading grain boundaries. Evidence of stress induced martensitic transformation extending from the crack tips is presented. Intergranular crack arrest is demonstrated on the account of the external tensile stress orientation, and as a consequence of MnS inclusion particles segregating close to the fractured grain boundary. Exclusive observations of grain boundary oxidation prior to the cracking are presented, which is in full-agreement with the internal oxidation model.(c) 2022 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1016/J.JNUCMAT.2022.153727
|
|
|
“TEM investigation of SCC crack tips in high Si stainless steel tapered specimens”. Penders A, Konstantinovic MJ, Van Renterghem W, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology (2021). http://doi.org/10.1080/1478422X.2021.1961665
Abstract: The stress corrosion cracking (SCC) mechanism is investigated in high Si duplex stainless steel in a simulated PWR environment based on TEM analysis of FIB-extracted SCC crack tips. The microstructural investigation in the near vicinity of SCC crack tips illustrates a strain-rate dependence in SCC mechanisms. Detailed analysis of the crack tip morphology, that includes crack tip oxidation and surrounding deformation field, indicates the existence of an interplay between corrosion- and deformation-driven failure as a function of the strain rate. Slow strain-rate crack tips exhibit a narrow cleavage failure which can be linked to the film-induced failure mechanism, while rounded shaped crack tips for faster strain rates could be related to the strain-induced failure. As a result, two nominal strain-rate-dependent failure regimes dominated either by corrosion or deformation-driven cracking mechanisms can be distinguished.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 0.879
DOI: 10.1080/1478422X.2021.1961665
|
|