Abstract: During the study of a large number of archaeological glass fragments, manganese-rich inclusions in leached layers were observed in a limited number of cases. This phenomenon occurs only in black-coloured leached layers. Since the formation mechanism of such manganese-rich inclusions is still unclear, a combination of several analytical techniques was used in order to investigate this phenomenon and, more specifically, to obtain more information on (a) the composition and morphology of the inclusions, (b) the chemical state of Mn and (c) the 3D morphology of the inclusions. A mechanism that might explain the formation of these inclusions is proposed.

Abstract: The speed and effectiveness of a conservation treatment used for stained glass windows have been investigated. Dark-coloured Mn-rich stains can be found in the alteration layer of ancient glass artefacts and cause the surface to turn brown/black: this phenomenon is known as Mn-browning or Mn-staining. While in glass manganese is present in the +II or +III oxidation states, in the Mn-rich bodies, manganese is in a higher oxidation state (+IV). In restoration practice, mildly reducing solutions are employed to eliminate the dark colour and restore the clear appearance of the glass. In this paper the effectiveness and side effects of the use of hydroxylamine hydrochloride for this purpose are assessed. Archaeological fragments of stained glass windows, dated to the 14th century and originating from Sidney Sussex College, Cambridge (UK), were examined by means of synchrotron radiation (SR) based microscopic X-ray Absorption Near-Edge Spectroscopy (μ-XANES) and microscopic X-Ray Fluorescence (μ-XRF) and with high resolution computed absorption tomography (μ-CT) before, during and after the treatment. The monitoring of the glass fragments during the treatment allows us to better understand the manner in which the process unfolds and its kinetics. The results obtained reveal that the hydroxylamine hydrochloride treatment is effective, but also that it has a number of unwanted side effects. These findings are useful for optimizing the time and other modalities of the Mn-reducing treatment as well as minimizing its unwanted results.

Abstract: Glass treated on its surface with silver compounds and an aluminosilicate, such as ochre or clay, at higher temperatures (between 550 and 650 °C) accepts a wide variety of a yellow colour. It is the aim of this study to investigate the parameters of the manufacturing process affecting the final colour of silver stained glass and to correlate them with the final colour and colour intensity. Therefore, defined mixtures of ochre and a silver compound (AgCl, AgNO3, Ag2SO4, Ag3PO4, Ag2O) were prepared and applied on soda-lime glass. The firing process was modified within the range from 563 to 630 °C and glass samples were analysed after treatment with energy dispersive X-ray fluorescence analysis (EDXRF), scanning electron microscopy (SEM/EDX), transmission electron microscopy (TEM), as well as ion beam analysis (IBA) with an external beam. Within the scope of IBA simultaneous measurements using particle-induced X-ray emission (PIXE), particle-induced gamma-ray emission (PIGE), and Rutherford backscattering spectrometry (RBS) were carried out in order to obtain the thickness of the Ag-rich surface layer and the depth distribution of Ag. By means of TEM the microstructure of the silver particles was visualised. XRF results show that the lowest amount of Ag could be detected on glass samples treated with silver stain mixtures containing AgCl and Ag2O. A low kiln temperature (e.g. 563 °C) results in a higher silver concentration at the surface and lower penetration depths. Furthermore, the results obtained with SEM/EDX at cross-sections of the glass samples could be confirmed by PIXE, PIGE, RBS, and TEM.

Abstract: Chemical transformations in paintings often induce discolorations, disturbing the appearance of the image. For an appropriate conservation of such valuable and irreplaceable heritage objects, it is important to have a good know-how on the degradation processes of the (historical) materials: which pigments have been discolored, what are the responsible processes, and which (environmental) conditions have the highest impact on the pigment degradation and should be mitigated. Pigment degradation is already widely studied, either by analyzing historical samples or by accelerated weathering experiments on dummies. However, in historic samples several processes may have taken place, increasing the complexity of the current state, while aging experiments are time-consuming due to the often extended aging period. An alternative method is proposed for a fast monitoring of degradation processes of semiconductor pigments, using an electrochemical setup mimicking the real environment and allowing the identification of harmful environmental parameters for each pigment. Examples are given for the pigments cadmium yellow (CdS) and vermilion (α-HgS).

Abstract: Twenty-seven glass fragments containing dark coloured grisaille paint layers of different qualities were collected from ten windows of the cathedral St. Michael & St. Gudule in Brussels (Belgium). The windows were made by J.-B. Capronnier (18141891) and cover the period between 1843 and 1878. The samples were cross-sectioned and examined in an electron microscope. Grisaille paint layers are not homogeneous and therefore, it is not meaningful to characterize them in terms of their average composition. Instead, parameters such as granularity, the number of residual gas bubbles per running millimetre of paint, the type of pigments, and the thickness of the paint layer were used to characterize them. The microscopic morphology allows a classification of the grisaille paint layers in four groups, every group associated with a quality level. Moreover, the main causes of the accelerated degradation of some of these paint layers could be explained. The classification made it possible to distinguish two periods in the work of Capronnier: (1) the early period (18431848) is characterized by the presence of either single granular paint layers or of double-layered systems consisting of a granular paint layer on top of a well-melted paint layer. The granular grisaille paint layers tend to pulverize; (2) the later period (18481878) is characterized by the presence of only well-vitrified paint layers. No sign of deterioration was found on the well-vitrified paint layers.

Abstract: Stained glass windows incorporating dark blue and purple enamel paint layers are in some cases subject to severe degradation while others from the same period survived the ravages of time. A series of dark blue, greenblue and purple enamel glass paints from the same region (Northwestern Europe) and from the same period (16early 20th centuries) has been studied by means of a combination of microscopic X-ray fluorescence analysis, electron probe micro analysis and transmission electron microscopy with the aim of better understanding the causes of the degradation. The chemical composition of the enamels diverges from the average chemical composition of window glass. Some of the compositions appear to be unstable, for example those with a high concentration of K2O and a low content of CaO and PbO. In other cases, the deterioration of the paint layers was caused by the less than optimal vitrification of the enamel during the firing process. Recipes and chemical compositions indicate that glassmakers of the 1617th century had full control over the color of the enamel glass paints they made. They mainly used three types of coloring agents, based on Co (dark blue), Mn (purple) and Cu (light-blue or greenblue) as coloring elements. Bluepurple enamel paints were obtained by mixing two different coloring agents. The coloring agent for redpurple enamel, introduced during the 19th century, was colloidal gold embedded in grains of lead glass.

Abstract: The chemical composition, as determined by electron probe X-ray microanalysis of a series of ca. 100 archaeological glass fragments, excavated at the Raversijde site (Belgium) is discussed. In the 15th-16th century, Raversijde was a flourishing fishermen town located on the shore of the North Sea, close to the city of Ostend. As a consequence of several battles that were fought in its vicinity, the site was abandoned in the 16th century and was not occupied since then. It is one of the rare archaeological sites in Europe that contains a significant amount of information on the daily life inside a small but affluent medieval community. A comparison of the chemical composition of fragments of vessels and window glass encountered in Raversijde to those found in urban centres in Belgium and to literature date on German and French archaeological finds shows that glass made with wood ash dominates. Usually, it concerns artifacts with a predominantly utilitarian use. A few objects made with sodic (i.e., Na-rich) glass were also encountered, likely to have been imported from Venice during the 15th century or in later periods from an urban centre such as Antwerp, where Facon-de-Venice glass manufacturing activities were established near the start of the 16th century. (C) 2004 Elsevier B.V. All rights reserved.

Abstract: One of the most striking but unexplained phenomena in the natural degradation of glass is the transformation of an almost colorless, transparent and homogeneous glass into a colored, opaque and heterogeneous degradation layer. In many cases, the degradation layer consists of numerous lamellae with a thickness between 0.1 and 10 pm. However, both internal structure and formation proess of laminated degradation layers remain unclear. In this paper, a model is proposed where we assume that transformed (degraded) glass consists of a random packing of nano-sized silica particles while the lamellae are the result of different packing densities. The model is able to connect the texture of numerous lamellae observed by several types of microscopic techniques with the structure at molecular level determined by means of chemical analysis. In addition, the model is able to explain numerous properties such as the parameters responsible for the contrast between lamellae. This contrast can be caused by differences in color, density, elemental composition, or surface roughness. (C) 2016 Elsevier B.V. All rights reserved.

Abstract: Porous limestone and mortar are able to absorb large quantities of water. This phenomenon will accelerate the deterioration of the material. In such cases, the material might be treated with a hydrophobic product, which creates a superficial layer that hampers the penetration of water. In order to decide if such a treatment should be applied or not, the water absorbing behaviour of the material should be measured. With the same measuring technique the efficiency of the hydrophobic barrier can be evaluated. Moreover, it allows the monitoring of such barriers as a function of time. At the same time, the water absorption of porous stone material is an indication of the degree of deterioration and its sensitivity to future deterioration. Up to now, two different measuring techniques exist, but one can only be used in laboratory and the other, which can be operated in laboratory as well as in situ, is not always reliable for in situ analyses. This article proposes an alternative method: the contact sponge method. This recently developed method was tested on non-treated porous stone materials in a laboratory environment in order to evaluate its performance in comparison with the two existing methods.

Abstract: Four x-ray techniques: computed radiography, emission radiography, energy-resolved radiography and imaging x-ray fluorescence were compared using four mock-up panel paintings. The paintings have different stratigraphy and pigments and are representative for different historical periods. One of the paintings has a hidden underlying painting. The type of pigments used mainly influences the information obtained by both the emission and absorption measurements; high-Z white pigment and high-Z color pigments giving the best contrast. Each of the techniques revealed interesting aspects of the paintings, but none of them could reveal the hidden painting to a satisfactory level. Due to the statistical quality of the spectral data, x-ray fluorescence gives elemental images with high contrast. The radiographic images are better to reveal the internal structure. Imaging x-ray fluorescence and energy-resolved radiography measurements can be done simultaneously, and the combination has the highest potential for the study of complex multilayer paintings. Copyright (c) 2015 John Wiley & Sons, Ltd.

Abstract: In this study, the results of analysing of a series of 16th-19th century painted enamel objects of the Limoges School currently in collections in three Dutch and Flemish museums by means of portable and micro x-ray fluorescence analysis (PXRF and µ-XRF) and electron probe micro analysis (EPMA) are presented. The aim of the investigation was the authentication of specific pieces. Therefore, the glass compositions as well as the (glass) colouring agents used by the Limoges' artists were studied as a function of the age of the objects. Due to the evolution of these properties, it is possible to approximately date these objects based on their chemical composition. The complete émail peint collection of the Museum Boijmans-Van Beuningen (Rotterdam, The Netherlands), consisting of 20 émail peint plaques, was analysed with µ-XRF. Quantitative information was obtained by EPMA analysis of 15 enamel fragments of objects from museum and private collections in the Low Countries. PXRF analyses were performed on the painted enamel collection of the Antwerp Vleeshuis Museum (13 objects) and the Mayer van den Bergh Museum (4 objects) and on a set of 18 plaques that were donated to the Boijmans-Van Beuningen Museum by a private collector. The results obtained by means of EPMA, µ-XRF and PXRF proved to be useful in the discrimination of 16th century painted enamel objects from those of the19th century. From a total of 70 objects examined, 2 objects (OM964A and OM993) featured a chemical signature that deviated from the published literature composition and pigment use consistent with its presumed period of manufacture.