Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.

Abstract: The spectral properties of a classical two-dimensional (2D) cluster of charged particles which are confined by a quadratic potential are calculated. Using the method of Newton optimization we obtain the ground state and the metastable states. For a given configuration the eigenvectors and eigenfrequencies for the normal modes are obtained using the Householder diagonalization technique for the dynamical matrix whose elements are the second derivative of the potential energy. For small clusters the lowest excitation corresponds to an intershell rotation. Magic numbers are associated to clusters which are most stable against intershell rotation. For large clusters the lowest excitation is a vortex/anti-vortex pair.

Abstract: The occurrence and origin of diffuse intensity contours in electron micrographs of AgBr crystals are investigated. The observations are interpreted in terms of a model, which attributes diffuse scattering to the presence of predominant atom or vacancy clusters of a particular polyhedral type. It is shown that irrespective of the crystal morphology, interstitial Ag ions order in AgBr material in clusters of finite size along 001 type planes. A different geometry of the diffuse intensity locus observed for triangular and hexagonal tabular grains is explained in terms of the different twin plane morphology of these grains.

Abstract: Magnetoreflectivity measurements of the 1s and 2s exciton energies in a CdTe/Cd1-xMnxTe superlattice have been made in magnetic fields up to 45 T, showing the resonant polaron coupling of electrons to LO phonons. Strong reflectivity features are seen for both the 1s and 2s excitons, which show a strong field-dependent spin splitting due to the dilute magnetic barriers. At B-z=0, the 2s exciton feature is observed lying 18 meV above the Is state, and is shifted upward in energy by the magnetic fields. No resonant behavior occurs when the 2s state passes through the LO-phonon energy of 21 meV, but at higher fields of around 20 T, the resonances for both spin states (sigma(+/-)) of the 2s exciton broaden and show a strong anticrossing behavior. These experiments are shown to be in excellent agreement with a theoretical treatment which includes the resonant polaron coupling of the electrons alone. Both experiment and theory demonstrate an extremely strong resonant splitting of the 2s exciton states of approximately 11 meV, which is over 50% of the LO-phonon energy. The dominance of single-particle polaron coupling is attributed to the relative sizes of the polaron (35 Angstrom A) and the exciton (50 Angstrom A) radius.

Abstract: A new superconducting mercury oxycarbonate, Pb0.7Hg0.3Sr4Cu2CO3O7, has been synthesized. This tetragonal phase (a = 3.824 angstrom, c= 16.468 angstrom) consists of an intergrowth of two nonsuperconducting compounds, Sr2CuO2CO3 and Pb0.7Hg0.3Sr2CuO5. It exhibits after optimization a critical temperature of 70 K, with a sharp transition and a superconducting volume fraction of 50%. Its behavior can be compared to that of thallium oxycarbonates previously isolated. This study is completed by a reinvestigation of the 1212 cuprate of the system Hg-Pb-Sr-Ca-Nd-Cu. A superconducting phase with the 1212 structure, similar to that previously obtained but with a significantly different composition, Pb0.7Hg0.3Sr2+xCa0.7Nd0.3-xCu2O7, has been obtained, with a T(c onset) of 100 K. The behavior of the latter is compared with other lead-based 1212 cuprates.