Abstract: The present paper describes the synthesis, characterization of mixed-valence bismuthates with 3- or 2-dimensional perovskite-like structures and structural criteria that influence superconductivity in these compounds. Single-phase samples of Sr1-xKxBiO3 were prepared for the broad range of K-content: 0.25 less than or equal to x less than or equal to 0.65. For these bismuthates the symmetry of the structure changes from monoclinic to orthorhombic and finally to tetragonal upon increasing the K-content thus resulting in the decrease of the Bi-O distances and reduction of the network distortions. Superconductivity with maximum T-c = 12K exists in the narrow range (x approximate to 0.5 – 0.6) within the stability field of the tetragonal phase (0.33 less than or equal to x less than or equal to 0.65), when the 3-dimensional octahedral framework has close to the ideal perovskite structure arrangement. At the same time compositions with close to optimal Bi-valence (x = 0.33 and 0.43) do not show any sign of superconductivity, probably, due to structural distortions. The layered type (BaK)(3)Bi2O7 and (Ba,K)(2)BiO4 bismuthates belonging to the A(n+1)B(n)O(3n+1) homologous series were investigated Buckling of the (BiO2) layers in the structure of the n = 2 member was revealed The formation of the n=1 bismuthate was found by Electron Microscopy and X-ray powder diffraction studies. Both types of compounds are considered to be possible candidates for new superconducting materials among bismuthates.

Abstract: Twenty-seven glass fragments containing dark coloured grisaille paint layers of different qualities were collected from ten windows of the cathedral St. Michael & St. Gudule in Brussels (Belgium). The windows were made by J.-B. Capronnier (18141891) and cover the period between 1843 and 1878. The samples were cross-sectioned and examined in an electron microscope. Grisaille paint layers are not homogeneous and therefore, it is not meaningful to characterize them in terms of their average composition. Instead, parameters such as granularity, the number of residual gas bubbles per running millimetre of paint, the type of pigments, and the thickness of the paint layer were used to characterize them. The microscopic morphology allows a classification of the grisaille paint layers in four groups, every group associated with a quality level. Moreover, the main causes of the accelerated degradation of some of these paint layers could be explained. The classification made it possible to distinguish two periods in the work of Capronnier: (1) the early period (18431848) is characterized by the presence of either single granular paint layers or of double-layered systems consisting of a granular paint layer on top of a well-melted paint layer. The granular grisaille paint layers tend to pulverize; (2) the later period (18481878) is characterized by the presence of only well-vitrified paint layers. No sign of deterioration was found on the well-vitrified paint layers.

Abstract: Calibration curves with two quasi-linear sections ("double sloping'') were observed for the medium volatile elements, Cr and Cu, with the use of a SIMAA 6000 graphite furnace atomic absorption spectrometer under interrupted internal gas flow conditions. If a standard transversally heated graphite atomizer (THGA) tube was shortened by 0.5 mm at both of its ends, (i.e. the gaps were enlarged between graphite furnace housing and tube ends), a stronger declination of the calibration curves resulted. Elements with fairly high diffusion coefficients (>5.8 cm(2) s(-1)) and with short appearance time of their transients (<0.6 s), such as Cr and Cu, have shown the most characteristic sensitivity drop towards higher concentrations. This anomalous feature could be eliminated in three different ways; (1) by applying end-capped THGA tubes, (2) using mini-flow (50 cm(3) min(-1)) conditions during the atomization stage, and (3) by adding Pd-Mg chemical modifier. For the low volatile Mo and V, the calibration curves had no irregular shape. For Ag, Co, Cr, Cu, Mn and Ni, the mini-flow settings improved the linearity of the calibration curves and extended the upper limit of the linear calibration range by a factor of 1.5-2.0. The irregular characteristic of the analytical curves was interpreted as an increased vapour loss at higher analyte concentrations through the opened ends of the standard THGA tubes. This vapour loss was associated with the significantly diverse expulsion velocities of atoms, caused by the difference in temperature and concentration gradients, when evaporating amounts of analytes with more than one order of magnitude difference.