Abstract: We present a detailed analysis of the point-defect clustering in strained Si/Si(1-x)Ge(x)/(001)Si structures, including the interaction of the point defects with the strained interfaces and the sample surface during 400 kV electron irradiation at room temperature. Point-defect cluster formation is very sensitive to the type and magnitude of the strain in the Si and Si(1-x)Ge(x) layers. A small compressive strain (-0.3%) in the SiGe alloy causes an aggregation of vacancies in the form of metastable [110]-oriented chains. They are located on {113} planes and further recombine with interstitials. Tensile strain in the Si layer causes an aggregation of interstitial atoms in the forms of additional [110] rows which are inserted on {113} planes with [001]-split configurations. The chainlike configurations are characterized by a large outward lattice relaxation for interstitial rows (0.13 +/-0.01 nm) and a very small inward relaxation for vacancy chains (0.02+/-0.01 nm). A compressive strain higher than -0.5% strongly decreases point-defect generation inside the strained SiGe alloy due to the large positive value of the formation volume of a Frenkel pair. This leads to the suppression of point-defect clustering in a strained SiGe alloy so that SiGe relaxes via a diffusion of vacancies from the Si layer, giving rise to an intermixing at the Si/SiGe interface. In material with a 0.9% misfit a strongly increased flow of vacancies from the Si layer to the SiGe layer and an increased biaxial strain in SiGe bath promote the preferential aggregation of vacancies in the (001) plane, which relaxes to form intrinsic 60 degrees dislocation loops.

Abstract: The reaction of a Ti (8 nm) capped Co film (15 nm) with a Si3N4 layer (150 nm) is studied after rapid thermal annealing at 660 degreesC for 120 s in a N-2 ambient. X-ray photoelectron spectroscopy, transmission electron microscopy, electron energy-loss spectroscopy, and Auger electron spectroscopy are used to study the reaction products. Combining the results of the different analyses yields a layer stack consisting of: TiO2/TiO/unreacted Co/(Ti,Co)(2)N/Co2Si, followed by amorphous Si3N4. The reaction mechanisms are discussed. Conclusions concerning the risk for degradation of nitride spacers in advanced devices are drawn. (C) 2000 American Institute of Physics. [S0003-6951(00)05248-7].

Abstract: The morphology and structure of diamond films, deposited on cubic boron nitride (c-BN) crystals by microwave-plasma-enhanced chemical vapor deposition, is studied by high-resolution scanning electron microscopy and micro-Raman spectroscopy. The c-BN crystals, with sizes of 200 to 350 mu m and grown by a high-temperature/high-pressure technique, were embedded in a copper holder, and used as substrates in deposition runs of 15 min to 5 h. The nucleation centers for diamond appear as well-shaped cuboctahedral crystallites, having diameters of approximately 100 nm. With increasing deposition time the diamond crystallites grew larger, forming islands on the c-BN faces. In some cases, epitaxial growth was observed on the (111) c-BN faces where coalesced particles gave rise to very smooth regions. A number of diamond crystals with peculiar shapes are observed, such as a pseudo five-fold symmetry due to multiple twinning. Moreover, both randomly distributed carbon tubes, about 100 nn in diameter and 1 mu m in length, and spherically shaped features are observed in samples prepared under the typical conditions of diamond deposition, this effect being ascribed to the influence of plasma-sputtered copper contamination. Quite unusual diamond crystals with a deep, pyramidal-shaped hole in the middle grew on the copper substrate between the c-BN crystals. (C) 2000 Elsevier Science S.A. All rights reserved.

Abstract: Despite the general belief that hydrogen-bonded ferro- and antiferroelectrics undergo a pure order/disorder transition at the structural instability, new NMR data and a new theoretical concept yield convincing evidence that a pronounced displacive component is present in these systems, which modifies substantially the temperature dependencies of the tunnel and lattice mode frequencies. The experiments and their interpretation are presented. (C) 1999 Elsevier Science Ltd. All rights reserved.

Abstract: The relationships between incommensurability, charge ordering and magnetotransport properties in Nd0.5Ca0.5Mn1-xCrxO3 manganites have been studied by electron diffraction and lattice imaging versus temperature with 0.02 less than or equal to x less than or equal to 0.07. All compositions show an incommensurate superstructure over the whole temperature domain, despite the fact that they are ferromagnetic and conductive below 140 K, The q-vector (1/2 – delta)a* decreases with increasing temperature for all compositions x. For a given temperature q also decreases with x. Lattice images obtained at low temperature give a clear view of the characteristics of the incommensurate structure. They also provide a better understanding of the charge ordering process. The low-temperature form of the Cr-doped manganites is not a perfectly doubled cell [[2a(p)root 2 x 2a(p) x a(p)root 2]], but defects inducing a tripled cell occur pseudo-periodically. (C) 2000 Elsevier Science B.V. All rights reserved.