Abstract: The spontaneous chemical alteration of artists' pigment materials may be caused by several degradation processes. Some of these are well known while others are still in need of more detailed investigation and documentation. These changes often become apparent as color modifications, either caused by a change in the oxidation state in the original material or the formation of degradation products or salts, via simple or more complex, multistep reactions. Arsenic-based pigments such as orpiment (As2S3) or realgar (alpha-As4S4) are prone to such alterations and are often described as easily oxidizing upon exposure to light. Macroscopic X-ray powder diffraction (MA-XRPD) imaging on a sub area of a still life painting by the 17th century Dutch painter Martinus Nellius was employed in combination with microscopic (mu-) XRPD imaging of a paint cross section taken in the area imaged by MA-XRPD. In this way, the in situ formation of secondary metal arsenate and sulfate species and their migration through the paint layer stack they originate from could be visualized. In the areas originally painted with orpiment, it could be shown that several secondary minerals such as schultenite (PbHAsO4), mimetite (Pb-5(AsO4)(3)Cl), palmierite (K2Pb(SO4)(2)) and syngenite (K2Ca(SO4)(2)center dot H2O) have formed. Closer inspection of the cross-sectioned paint layer stack with mu-XRPD illustrates that the arsenate minerals schultenite and mimetite have precipitated at the interface between the orpiment layer and the layer below that is rich in lead white, i.e. close to the depth of formation of the arsenate ions. The sulfate palmierite has mostly precipitated at the surface and upper layers of the painting.

Abstract: Over the past years a number of studies have described the instability of the pigment cadmium yellow (CdS). In a previous paper we have shown how cadmium sulfide on paintings by James Ensor oxidizes to CdSO4 center dot H2O. The degradation process gives rise to the fading of the bright yellow color and the formation of disfiguring white crystals that are present on the paint surface in approximately 50 mu m sized globular agglomerations. Here, we study cadmium yellow in the painting “Flowers in a blue vase” by Vincent van Gogh. This painting differs from the Ensor case in the fact that (a) a varnish was superimposed onto the degraded paint surface and (b) the CdS paint area is entirely covered with an opaque crust. The latter obscures the yellow color completely and thus presents a seemingly more advanced state of degradation. Analysis of a cross-sectioned and a crushed sample by combining scanning microscopic X-ray diffraction (mu-XRD), microscopic X-ray absorption near-edge spectroscopy (mu-XANES), microscopic X-ray fluorescence (mu-XRF) based chemical state mapping and scanning microscopic Fourier transform infrared (mu-FT-IR) spectrometry allowed unravelling the complex alteration pathway. Although no crystalline CdSO4 compounds were identified on the Van Gogh paint samples, we conclude that the observed degradation was initially caused by oxidation of the original CdS pigment, similar as for the previous Ensor case. However, due to the presence of an overlying varnish containing lead-based driers and oxalate ions, secondary reactions took place. In particular, it appears that upon the photoinduced oxidation of its sulfidic counterion, the Cd2+ ions reprecipitated at the paint/varnish interface after having formed a complex with oxalate ions that themselves are considered to be degradation products of the resin and/or oil in the varnish. The SO42- anions, for their part, found a suitable reaction partner in Pb2+ ions stemming from a dissolved lead-based siccative that was added to the varnish to promote its drying. The resulting opaque anglesite compound in the varnish, in combination with the underlying CdC2O4 layer at the paint/varnish interface, account for the orange-gray crust that is disfiguring the painting on a macroscopic level. In this way, the results presented in this paper demonstrate how, through a judicious combined use of several microanalytical methods with speciation capabilities, many new insights can be obtained from two minute, but highly complex and heterogeneous paint samples.

Abstract: A set of ca. 500 window glass fragments originating from different historical sites in Belgium and covering the period 12(th)- 18(th) century was analyzed by rneans of electron probe microanalysis. Most samples are archaeological finds deriving from non-figurative windows in secular buildings. However. the analyzed set also contains glass sampled from still existing non-figurative windows in secular buildings and stained-glass windows in religious buildings. A sudden compositional change at the end of the 14(th) century can be noticed among the series of glass compositions that were obtained. These changes could be related to the use of different glassmaker recipes and to the introduction of new raw materials for glass making. (c) 2007 Elsevier B.V All rights reserved.

Abstract: Focused narrow-band beam of the synchrotron radiation was used for in-depth analysis of historic and modern paint layers. The fluorescent radiation induced by 21 keV impact radiation was detected by a Si(Li) detector equipped with a polycapillary X-ray lens in con-focal geometry. Scanning of the sample was performed by a motorized xyz stage. Space resolution of 30 ìm was achieved. The procedure of evaluation of concentrations was based on the independent parameter method and included absorption of radiation in the outer layers and secondary fluorescence enhancement induced by hard X-rays of the same and neighboring layers.

Abstract: This study deals with the process of zeolite formation in an agricultural soil artificially polluted by high amounts of Cu (15 mg of Cu/g of soil dry weight) and treated with fused coal fly ash at 30 and 60 degrees C and how this process affects the mobility and availability of the metal. As a consequence of the treatment, the amount of dissolved Cu, and thus its mobility, was strongly reduced, and the percentage of the metal stabilized in the solid phase increased over time, reaching values of 30% at 30 degrees C and 40% at 60 degrees C. The physicochemical phenomena responsible for Cu stabilization in the solid phase have been evaluated by EDTA sequential extractions and synchrotron radiation based X-ray microanalytical techniques. These techniques were used for the visualization of the spatial distribution and the speciation of Cu in and/or on the neo-formed zeolite particles. In particular, micro XRF (X-ray fluorescence) tomography showed direct evidence that Cu can be entrapped as clusters inside the porous zeolitic structures while,mu-XANES (X-ray absorption near edge structure) spectroscopy determinations revealed Cu to be present mainly as Cu(II) hydroxide and Cu(II) oxide. The reported results could be useful as a basic knowledge for planning new technologies for the on site physicochemical stabilization of heavy metals in heavily polluted soils.

Abstract: A combined Raman and electrochemical study of natural orpiment (As2S3), an arsenic sulfide pigment, was used to assess the quick formation of oxidized species such as arsenic oxide (As2O3) upon exposing the pigment to 405 nm or 532 nm monochromatic light while simultaneously recording the Raman spectra of the exposed sample. During this process, a distortion of the main band at 355 cm−1, associated with the stretching of the AsS3/2 pyramids of natural orpiment, was observed as well as an increased intensity of the 359 cm−1 band, corresponding to covalent AsAs bonds in natural orpiment. The distortion was accompanied by an overall decrease of the global Raman signal for natural orpiment, which could be explained by a loss in the crystal structure. The same phenomena were recorded in reference natural orpiment model paint samples stored for a long time together with verdigris (Cu(OH)2·(CH3COO)2·5H2O) and minium (Pb3O4) paints, the latter two appearing darkened on their sides closest to the orpiment sample as well as in several historical samples containing natural orpiment mixed with various blue pigments. By SEM-EDX and XRPD analysis, respectively on loose material and cast thin-sections of model paint samples, the darkening was identified as dark sulfide species such as chalcocite (Cu2S) and galena (PbS), suggesting the release of volatile sulfide or related species by the natural orpiment paint. XANES analyses of paint samples presenting AsAs bond increase indicated the presence of sulfur species most likely identified as organosulfur compounds formed upon the AsAs bond formation and explained the darkening of the Cu- and Pb-based pigments. To the best of our knowledge, this article reports for the first time the light-induced formation of AsAs bonds in natural orpiment used as an artists' pigment and objectively demonstrates the incompatibility between orpiment and (arsenic) sulfide-sensitive pigments.

Abstract: In this work we attempt to elucidate the chronological and geographical origin of deeply coloured and black glass dating between 100 bc and ad 300 on the basis of their major and trace element compositions. Samples from the western and eastern parts of the Roman Empire were analysed. Analytical data were obtained by means of a scanning electron microscope – energy-dispersive system (SEM-EDS, 63 samples analysed) and laser ablation – inductively coupled plasma – mass spectrometry (LA-ICP-MS, 41 samples analysed). Among the glass fragments analysed, dark brown, dark purple and dark green hues could be distinguished. Only among the dark green fragments could a clear compositional distinction be observed between fragments dated to the periods before and after ad 150. In the early samples (first century bc to first century ad), iron, responsible for the green hue, was introduced by using impure sand containing relatively high amounts of Ti. In contrast, a Ti-poor source of iron was employed, containing Sb, Co and Pb in trace quantities, in order to obtain the dark green colour in the later glass samples. The analytical results obtained by combining SEM-EDS and LA-ICP-MS are therefore consistent with a differentiation of glassmaking recipes, detectable in glass composition, occurring in the period around ad 150.

Abstract: The darkening of lead chromate yellow pigments, caused by a reduction of the chromate ions to Cr(III) compounds, is known to affect the appearance of several paintings by Vincent van Gogh. In previous papers of this series, we demonstrated that the darkening is activated by light and depends on the chemical composition and crystalline structure of the pigments. In this work, the results of Part 2 are extended and complemented with a new study aimed at deepening the knowledge of the nature and distribution of Cr and S species at the interface between the chrome yellow paint and the nonoriginal coating layer. For this purpose, three microsamples from two varnished paintings by Van Gogh and a waxed low relief by Gauguin (all originally uncoated) have been examined. Because nonoriginal coatings are often present in artwork by Van Gogh and contemporaries, the understanding of whether or not their application has influenced the morphological and/or physicochemical properties of the chrome yellow paint underneath is relevant in view of the conservation of these masterpieces. In all the samples studied, microscopic X-ray fluorescence (mu-XRF) and X-ray absorption near edge structure (mu-XANES) investigations showed that Cr(III)-based alteration products are present in the form of grains inside the coating (generally enriched of S species) and also homogeneously widespread at the paint surface. The distribution of Cr(III) species may be explained by the mechanical friction caused by the coating application by brush that picked up and redistributed the superficial Cr compounds, likely already present in the reduced state as result of the photodegradation process. The analysis of the XANES profiles allowed us to obtain new insights into the nature of the Cr(III) alteration products, that were identified as sulfate-, oxide-, organo-metal-, and chloride-based compounds. Building upon the knowledge acquired through the examination of original paint samples and from the investigation of aged model paints in the last Part 4 paper, in this study we aim to characterize a possible relation between the chemical composition of the coating and the chrome yellow degradation pathways by studying photochemically aged model samples covered with a dammar varnish contaminated with sulfide and sulfate salts. Cr speciation results did not show any evidence of the active role of the varnish and added S species on the reduction process of chrome yellows.

Abstract: An important part of the European cultural heritage is composed of hand-written documents. Many of these documents were drawn up with iron-gall ink. This type of ink present a serious conservation problem, as it slowly oxidizes ('burns') the paper it is written on, thereby gradually disintegrating the historic document. Acid hydrolysis of the cellulose and/or the oxidation of organic compounds promoted by radical intermediates that are formed due to the presence of Fe2+ ions are considered to be the cause of the disintegration. mu-XANES measurements were performed with a lateral resolution of 30-50 mum in order to determine the local Fe2+/Fe3+ ratio in 19th C. documents from the Austrian National Archives and fragments of 16th C documents from the Polish National Library. In the 19th C documents, no significant amount of Fe2+ was detected. On the other hand, in the 16th C fragments, significant amounts of Fe2+ and appreciable differences in distribution of Fe2+ and Fe3+ within individual letters/ink stains were observed. (C) 2003 Elsevier B.V. All rights reserved.

Abstract: Colors in many paintings of great art historical value have changed over time, due to the combined effects of natural ageing, accumulated surface grime, and materials added during later conservation treatments. The physical restoration of the colors in such paintings is not possible. This article describes one part of work done to digitally restore the colors of Van Gogh's painting Field with Irises near Arles, dating from May 1888. We have used multispectral reflectance data to estimate absorption K and backscattering S parameters of Kubelka-Munk 2-constant theory. This was done for all 13 pigments known to have been used by Van Gogh in this painting, and based on this the concentration maps for each of these pigments were calculated. We validated the calculated concentration maps in several ways. For some pigments, we were able to predict spots on the painting where the pigment is expected to occur in unmixed form based on visual examination. For several other pigments, the concentration maps could be shown to agree with XRF data. Finally, for some other pigments the concentration maps were supported by additional evidence from microscopic examinations, remarks in Van Gogh's letters and from early color reproductions. For the 1.7 million pixels for which multispectral data is available, the average color difference between the calculated and measured spectral reflectance curves is CIEDE2000 = 1.05. This further confirms that the Kubelka-Munk calculations are well suited to describe the variety of spectral reflectance on the painting.

Abstract: Samples of cretaceous limestone have been treated with three application methods (poultice, immersion and brushing) using different concentrations of ammonium oxalate solution (AmOx) and varying treatment time in order to test the efficiency of surface and in-depth formation of a protective layer of calcium oxalate (CaOx). Synchrotron-based microanalytical techniques (SR-mu XRD with 12.5 mu mx7.5 mu m (HxV) probe size, SR-mu FTIR with 10 mu mx10 mu m and 8 mu mx20 mu m probe sizes) and laboratory mu FTIR, XRD and SEM have been employed for analysis of the treated samples. Synchrotron-based techniques showed variations in the CaOx distribution along the surface on a micrometer scale. All treatments resulted in the development of a CaOx layer with a maximum thickness of approximately 40 mu m. Application by the brushing method with 10 1-min applications with 5-min breaks during one hour showed a development of the calcium oxalate layer equivalent to the poultice treatment taking 10 h. This treatment could be preferred for large marble or limestone surfaces where poultice usage is economically not feasible.