Abstract: A copper(II) hexafluoroacetylacetonate (1,1,1,5,5,5-hexafluoro-2,4-pentanedionate, hfa) adduct with N,N,N¡ä,N¡ä-tetramethylethylenediamine (TMEDA) [Cu(hfa)2¡¤TMEDA] is used for the first time as precursor for the chemical vapor deposition (CVD) of copper oxide nanosystems. The syntheses are carried out under both O2 and O2+H2O reaction atmospheres on Si(100) substrates, at temperatures ranging between 250 and 550 ¡ãC. Subsequently, the interrelations between the preparative conditions and the system composition, nanostructure, and morphology are elucidated by means of complementary analytical techniques [Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron and X-ray excited auger electron spectroscopies (XPS and XE-AES), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM)]. The obtained data revealed a gradual transformation from Cu2O, to Cu2O + CuO, to CuO nanosystems upon increasing the deposition temperature from 250 to 550 ¡ãC under both growth atmospheres. Such a phenomenon was accompanied by a progressive morphological evolution from continuous films to 1D hyperbranched nanostructures. Water vapor introduction in the deposition environment enabled to lower the deposition temperature and resulted in a higher aggregate interconnection, attributed to a higher density of nucleation centers.

Abstract: The synthesis of materials with well-controlled composition and structure improves our understanding of their intrinsic electrical transport properties. Recent developments in atomically controlled growth have been shown to be crucial in enabling the study of new physical phenomena in epitaxial oxide heterostructures. Nevertheless, these phenomena can be influenced by the presence of defects that act as extrinsic sources of both doping and impurity scattering. Control over the nature and density of such defects is therefore necessary to fully understand the intrinsic materials properties and exploit them in future device technologies. Here, it is shown that incorporation of a strontium copper oxide nano-layer strongly reduces the impurity scattering at conducting interfaces in oxide LaAlO3SrTiO3(001) heterostructures, opening the door to high carrier mobility materials. It is proposed that this remote cuprate layer facilitates enhanced suppression of oxygen defects by reducing the kinetic barrier for oxygen exchange in the hetero-interfacial film system. This design concept of controlled defect engineering can be of significant importance in applications in which enhanced oxygen surface exchange plays a crucial role.

Abstract: Uniaxial straining experiments were performed on a rolled and annealed Si-alloyed TRIP (transformation-induced plasticity) steel sheet in order to assess the role of its microstructure on the mechanical stability of austenite grains with respect to martensitic transformation. The transformation behavior of individual metastable austenite grains was studied both at the surface and inside the bulk of the material using electron back-scattered diffraction (EBSD) and X-ray diffraction (XRD) by deforming the samples to different strain levels up to about 20%. A comparison of the XRD and EBSD results revealed that the retained austenite grains at the surface have a stronger tendency to transform than the austenite grains in the bulk of the material. The deformation-induced changes of individual austenite grains before and after straining were monitored with EBSD. Three different types of austenite grains can be distinguished that have different transformation behaviors: austenite grains at the grain boundaries between ferrite grains, twinned austenite grains, and embedded austenite grains that are completely surrounded by a single ferrite grain. It was found that twinned austenite grains and the austenite grains present at the grain boundaries between larger ferrite grains typically transform first, i.e. are less stable, in contrast to austenite grains that are completely embedded in a larger ferrite grain. In the latter case, straining leads to rotations of the harder austenite grain within the softer ferrite matrix before the austenite transforms into martensite. The analysis suggests that austenite grain rotation behavior is also a significant factor contributing to enhancement of the ductility. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.