Abstract: In order to find out whether the existing laser systems can be employed to remove superimposed layers of paint on secco wall paintings in a selective way, laser tests were carried out on three types of prepared samples simulating three stratigraphies that are frequently encountered in practice. OM, EPMA, colorimetry, mu Raman, and FT-IR were used to evaluate the results. It was found that Q-switched Nd:YAG lasers emitting at 1,064 nm could be employed to remove unwanted layers of oil paint and limewash, but the treatment of large areas requires implementation of a computer-controlled X-Y-Z station in order to control the parameters. However, the applicability of this technique will remain limited as ablation at the established optimum parameters implied a discoloration of the pigments cinnabar, yellow ochre, and burnt sienna. Moreover, it was observed that no ablation took place when the limewash thickness exceeds 25 mu m. Unwanted layers of acrylic could be removed in an efficient way with an excimer laser emitting at 193 nm.

Abstract: Recent studies in which X-ray beams of macroscopic to (sub) microscopic dimensions were used for non-destructive analysis and characterization of pigments, paint micro samples and/or entire paintings by Vincent van Gogh are concisely reviewed. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging as well as with the combined use of X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Microscopic and macroscopic XRF are variants of the method that are well suited to visualize the elemental distribution of key elements, mostly metals, present in paint multi layers, either on the length scale from 1–100 μm inside micro samples taken from paintings or on the 1–100 cm length scale when the (subsurface) distribution of specific pigments in entire paintings is concerned. In the context of the characterization of van Gogh's pigments subject to natural degradation, the use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS and μ-XRD have proven themselves to be very suitable for such studies. Their use is often combined with microscopic Fourier transform infra-red (μ-FTIR) spectroscopy since this method delivers complementary information at more or less the same length scale as the X-ray microprobe techniques. Also in the context of macroscopic imaging of works of art, the complementary use of X-ray based and infra-red based imaging appears very promising; some recent developments are discussed.

Abstract: During the conservation treatment of Memling’s Christ with Singing and Music-making Angels, three panel paintings that are among the most monumental works in early Netherlandish art, the conservators came across insoluble surface layers containing calcium oxalates. A very thin and irregular layer of this type, hardly visible to the naked eye, was spread across the surface of all three panels. A much thicker layer forming an opaque and highly disfiguring crust that obscured the composition (Figs. 15.1 and 15.7) was locally present on areas of dark copper-containing paint, where multiple layers of old discolored coatings and accretions remained in place before the most recent cleaning. This article describes the application of a wide range of analytical techniques in order to fully understand the stratigraphy and composition of the crusts on the Memling paintings. FTIR spectroscopy in transmission and reflection mode, micro-ATR-FTIR imaging and macro-rFTIR scanning, SEM-EDX, mobile XRD, and SR-μXRD showed that the crusts contained two related Ca-based oxalate salts, whewellite and weddellite, and were separated from the original paint surface by varnish, indicating that they did not originate from degradation of the original paint but from a combination of microbial action and a thick accumulation of dirt. Supported by the results from these different analytical techniques, which when used together proved to be very effective in providing complementary information that addressed this specific conservation problem, and aided by the presence of the intermediate varnish layer(s), the conservators were able to remove most of the crusts with spectacular results.

Abstract: This chapter lays out a conservation timeline, from past to future, for the Amsterdam version of Van Gogh's Sunflowers. It starts by considering the restoration history of the painting in order to assess its current physical state, and looks ahead to formulate an appropriate strategy for future conservation treatment and display. Due attention is paid to the two recorded episodes of restoration performed in 1927 and 1961 by the Dutch restorer, Jan Cornelis Traas. Based on physical and chemical investigation of Sunflowers we attempt to reconstruct what these former treatments (which are barely documented) entailed and consider the repercussions for the present condition of the painting. The former interventions by Traas also serve as a benchmark to reflect on current choices made, highlighting the extent to which ideas and methodologies have continued to evolve over the past century as conservation has moved further away from being a singularly craft-based activity to become an established historical and scientific discipline underpinned by ethical guidelines. Jan Cornelis Traas (1898–1984) As mentioned, the two main recorded interventions to the Amsterdam Sunflowers may be associated with the Dutch restorer, Jan Cornelis Traas, who treated the picture in 1927, close to the start of his career, and again in 1961, shortly before he retired. Traas was the first restorer to be appointed at the Mauritshuis in The Hague where he worked from 1931 to 1962 and treated hundreds of paintings, including iconic masterpieces such as Girl with a Pearl Earring by Johannes Vermeer. Yet despite the magnitude and importance of his restoration oeuvre, J.C. Traas (as he is usually referred to in surviving documents), has remained somewhat obscure. He is shown here in the only known surviving photograph of him at work, shortly before he retired (fig. 7.1). Unlike his illustrious contemporaries, A. Martin de Wild (1899–1969) and Helmut Ruhemann (1891–1973), for example, Traas did not publish anything, he appears to have kept no records of his work and no personal archive is known. However, the study of some newly discovered historical documents, combined with physical examination of Sunflowers and a large number of other works he treated, allows us to recover an idea of his working practices and approaches viewed within the context of his day.

Abstract: On several paintings by artists of the end of the 19th century and the beginning of the 20th Century a darkening of the original yellow areas, painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is observed. The most famous of these are the various Sunflowers paintings Vincent van Gogh made during his career. In the first part of this work, we attempt to elucidate the degradation process of chrome yellow by studying artificially aged model samples. In view of the very thin (1−3 μm) alteration layers that are formed, high lateral resolution spectroscopic methods such as microscopic X-ray absorption near edge (μ-XANES), X-ray fluorescence spectrometry (μ-XRF), and electron energy loss spectrometry (EELS) were employed. Some of these use synchrotron radiation (SR). Additionally, microscopic SR X-ray diffraction (SR μ-XRD), μ-Raman, and mid-FTIR spectroscopy were employed to completely characterize the samples. The formation of Cr(III) compounds at the surface of the chrome yellow paint layers is particularly observed in one aged model sample taken from a historic paint tube (ca. 1914). About two-thirds of the chromium that is present at the surface has reduced from the hexavalent to the trivalent state. The EELS and μ-XANES spectra are consistent with the presence of Cr2O3·2H2O (viridian). Moreover, as demonstrated by μ-XANES, the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide], is likely.

Abstract: Recent studies are concisely reviewed, in which X-ray beams of (sub)micrometre to millimetre dimensions have been used for non-destructive analysis and characterization of pigments, minute paint samples, and/or entire paintings from the seventeenth to the early twentieth century painters. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging, as well as with the combined use of X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Microscopic XRF is a variant of the method that is well suited to visualize the elemental distribution of key elements, mostly metals, present in paint multi-layers, on the length scale from 1 to 100 μm inside micro-samples taken from paintings. In the context of the characterization of artists pigments subjected to natural degradation, the use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS and μ-XRD have proven themselves to be very suitable for such studies. Their use is often combined with microscopic Fourier transform infra-red spectroscopy and/or Raman microscopy since these methods deliver complementary information of high molecular specificity at more or less the same length scale as the X-ray microprobe techniques. Since microscopic investigation of a relatively limited number of minute paint samples, taken from a given work of art, may not yield representative information about the entire artefact, several methods for macroscopic, non-invasive imaging have recently been developed. Those based on XRF scanning and full-field hyperspectral imaging appear very promising; some recent published results are discussed.

Abstract: This paper reports on how the application of macro X-ray fluorescence (MA-XRF) imaging, in combination with the re-examination of existing paint cross-sections, has led to the discovery of a new pigment in Rembrandt's palette: artificial orpiment. In the NWO Science4Arts 'ReVisRembrandt' project, novel chemical imaging techniques are being developed and applied to the study of Rembrandt's late paintings in order to help resolve outstanding questions and to gain a better understanding of his late enigmatic painting technique. One of the selected case studies is the Portrait of a Couple as Isaac and Rebecca, known as 'The Jewish Bride', dated c. 1665 and on view in the Rijksmuseum. During the re-installation of the Rijksmuseum in 2013, the picture was scanned using the Bruker M6 Jetstream MAXRF scanner. The resulting elemental distribution maps made it possible to distinguish many features in the painting, such as bone black remains of the original hat (P, Ca maps), and the now discolored smalt-rich background (Co, Ni, As, K maps). The arsenic (As) map also revealed areas of high-intensity in Isaac's sleeve and Rebecca's dress where it could be established that it was not related with the pigment smalt that also contains arsenic. This pointed to the presence of a yellow or orange arsenic-containing pigment, such as realgar or orpiment that is not associated with the artist's palette. Subsequent examination of existing paint cross-sections from these locations taken by Karin Groen in the 1990s identified isolated, almost perfectly round particles of arsenic sulfide. The round shape corresponds with published findings on a purified form of artificial orpiment glass obtained by dry processing, a sublimation reaction. In bright field, the particles characteristically exhibit a dark cross in the middle caused by internal light reflections. The results of additional non-invasive techniques (portable XRD and portable Raman) are discussed, as well as the implications of this finding and how it fits with Rembrandt's late experimental painting technique.

Abstract: On several paintings of James Ensor (1860−1949), a gradual fading of originally bright yellow areas, painted with the pigment cadmium yellow (CdS), is observed. Additionally, in some areas exposed to light, the formation of small white-colored globules on top of the original paint surface is observed. In this paper the chemical transformation leading to the color change and to the formation of the globules is elucidated. Microscopic X-ray absorption near-edge spectroscopy (ì-XANES) experiments show that sulfur, originally present in sulfidic form (S2−), is oxidized during the transformation to the sulfate form (S6+). Upon formation (at or immediately below the surface), the highly soluble cadmium sulfate is assumed to be transported to the surface in solution and reprecipitates there, forming the whitish globules. The presence of cadmium sulfate (CdSO4·2H2O) and ammonium cadmium sulfate [(NH4)2Cd(SO4)2] at the surface is confirmed by microscopic X-ray diffraction measurements, where the latter salt is suspected to result from a secondary reaction of cadmium sulfate with ammonia. Measurements performed on cross sections reveal that the oxidation front has penetrated into the yellow paint down to ca. 1−2 ìm. The morphology and elemental distribution of the paint and degradation product were examined by means of scanning electron microscopy equipped with an energy-dispersive spectrometer (SEM-EDS) and synchrotron radiation based micro-X-ray fluorescence spectrometry (SR ì-XRF). In addition, ultraviolet-induced visible fluorescence photography (UIVFP) revealed itself to be a straightforward technique for documenting the occurrence of this specific kind of degradation on a macroscale by painting conservators.

Abstract: The discoloration rate of chrome yellow (CY), a class of synthetic inorganic pigments (PbCr1-xSxO4) frequently used by Van Gogh and his contemporaries, strongly depends on its sulfate content and on its crystalline structure (either monoclinic or orthorhombic). Macroscopic X-Ray powder diffraction imaging of selected areas on Van Gogh's Sunflowers (Van Gogh Museum, Amsterdam) revealed the presence of two subtypes of CY: the light-fast monoclinic PbCrO4 (LF-CY) and the light-sensitive monoclinic PbCr1-xSxO4 (x approximate to 0.5; LS-CY). The latter was encountered in large parts of the painting (e.g., in the pale-yellow background and the bright-yellow petals, but also in the green stems and flower hearts), thus indicating their higher risk for past or future darkening. Overall, it is present in more than 50% of the CY regions. Preferred orientation of LS-CY allows observation of a significant ordering of the elongated crystallites along the direction of Van Gogh's brush strokes.

Abstract: Over the past years a number of studies have described the instability of the pigment cadmium yellow (CdS). In a previous paper we have shown how cadmium sulfide on paintings by James Ensor oxidizes to CdSO4 center dot H2O. The degradation process gives rise to the fading of the bright yellow color and the formation of disfiguring white crystals that are present on the paint surface in approximately 50 mu m sized globular agglomerations. Here, we study cadmium yellow in the painting “Flowers in a blue vase” by Vincent van Gogh. This painting differs from the Ensor case in the fact that (a) a varnish was superimposed onto the degraded paint surface and (b) the CdS paint area is entirely covered with an opaque crust. The latter obscures the yellow color completely and thus presents a seemingly more advanced state of degradation. Analysis of a cross-sectioned and a crushed sample by combining scanning microscopic X-ray diffraction (mu-XRD), microscopic X-ray absorption near-edge spectroscopy (mu-XANES), microscopic X-ray fluorescence (mu-XRF) based chemical state mapping and scanning microscopic Fourier transform infrared (mu-FT-IR) spectrometry allowed unravelling the complex alteration pathway. Although no crystalline CdSO4 compounds were identified on the Van Gogh paint samples, we conclude that the observed degradation was initially caused by oxidation of the original CdS pigment, similar as for the previous Ensor case. However, due to the presence of an overlying varnish containing lead-based driers and oxalate ions, secondary reactions took place. In particular, it appears that upon the photoinduced oxidation of its sulfidic counterion, the Cd2+ ions reprecipitated at the paint/varnish interface after having formed a complex with oxalate ions that themselves are considered to be degradation products of the resin and/or oil in the varnish. The SO42- anions, for their part, found a suitable reaction partner in Pb2+ ions stemming from a dissolved lead-based siccative that was added to the varnish to promote its drying. The resulting opaque anglesite compound in the varnish, in combination with the underlying CdC2O4 layer at the paint/varnish interface, account for the orange-gray crust that is disfiguring the painting on a macroscopic level. In this way, the results presented in this paper demonstrate how, through a judicious combined use of several microanalytical methods with speciation capabilities, many new insights can be obtained from two minute, but highly complex and heterogeneous paint samples.

Abstract: The darkening of lead chromate yellow pigments, caused by a reduction of the chromate ions to Cr(III) compounds, is known to affect the appearance of several paintings by Vincent van Gogh. In previous papers of this series, we demonstrated that the darkening is activated by light and depends on the chemical composition and crystalline structure of the pigments. In this work, the results of Part 2 are extended and complemented with a new study aimed at deepening the knowledge of the nature and distribution of Cr and S species at the interface between the chrome yellow paint and the nonoriginal coating layer. For this purpose, three microsamples from two varnished paintings by Van Gogh and a waxed low relief by Gauguin (all originally uncoated) have been examined. Because nonoriginal coatings are often present in artwork by Van Gogh and contemporaries, the understanding of whether or not their application has influenced the morphological and/or physicochemical properties of the chrome yellow paint underneath is relevant in view of the conservation of these masterpieces. In all the samples studied, microscopic X-ray fluorescence (mu-XRF) and X-ray absorption near edge structure (mu-XANES) investigations showed that Cr(III)-based alteration products are present in the form of grains inside the coating (generally enriched of S species) and also homogeneously widespread at the paint surface. The distribution of Cr(III) species may be explained by the mechanical friction caused by the coating application by brush that picked up and redistributed the superficial Cr compounds, likely already present in the reduced state as result of the photodegradation process. The analysis of the XANES profiles allowed us to obtain new insights into the nature of the Cr(III) alteration products, that were identified as sulfate-, oxide-, organo-metal-, and chloride-based compounds. Building upon the knowledge acquired through the examination of original paint samples and from the investigation of aged model paints in the last Part 4 paper, in this study we aim to characterize a possible relation between the chemical composition of the coating and the chrome yellow degradation pathways by studying photochemically aged model samples covered with a dammar varnish contaminated with sulfide and sulfate salts. Cr speciation results did not show any evidence of the active role of the varnish and added S species on the reduction process of chrome yellows.