Abstract: The release of the lattice oxygen due to the thermal degradation of layered lithium transition metal oxides is one of the major safety concerns in Li-ion batteries. The oxygen release is generally attributed to the phase transitions from the layered structure to spinel and rocksalt structures that contain less lattice oxygen. Here, a different degradation pathway in LiCoO2 is found, through oxygen vacancy facilitated cation migration and reduction. This process leaves undercoordinated oxygen that gives rise to oxygen release while the structure integrity of the defect-free region is mostly preserved. This oxygen release mechanism can be called surface degradation due to the kinetic control of the cation migration but has a slow surface to bulk propagation with continuous loss of the surface cation ions. It is also strongly correlated with the high-voltage cycling defects that end up with a significant local oxygen release at low temperatures. This work unveils the thermal vulnerability of high-voltage Li-ion batteries and the critical role of the surface fraction as a general mitigating approach.

Abstract: Conventional CO2 separation in the petrochemical industry via cryogenic distillation or amine-based absorber-stripper units is energy-intensive and environmentally unfriendly. Membrane-based gas separation technology, in contrast, has contributed significantly to the development of energy-efficient systems for processes such as natural gas purification. The implementation of commercial polymeric membranes in gas separation processes is restricted by their permeability-selectivity trade-off and by their insufficient thermal and chemical stability. Herein, we present the fabrication of a Matrimid-based membrane loaded with a breathing metal-organic framework (MOF) (NH2-MIL-53(Al)) which is capable of separating binary CO2/CH4 gas mixtures with high selectivities without sacrificing much of its CO2 permeabilities. NH2-MIL-53(Al) crystals were embedded in a polyimide (PI) matrix, and the mixed-matrix membranes (MMMs) were treated at elevated temperatures (up to 350 degrees C) in air to trigger PI cross-linking and to create PI-MOF bonds at the interface to effectively seal the grain boundary. Most importantly, the MOF transitions from its narrow-pore form to its large-pore form during this treatment, which allows the PI chains to partly penetrate the pores and cross-link with the amino functions at the pore mouth of the NH2-MIL-53(Al) and stabilizes the open-pore form of NH2-MIL-53(Al). This cross-linked MMM, with MOF pore entrances was made more selective by the anchored PI-chains and achieves outstanding CO2/CH4 selectivities. This approach provides significant advancement toward the design of selective MMMs with enhanced thermal and chemical stabilities which could also be applicable for other potential applications, such as separation of hydrocarbons (olefin/paraffin or isomers), pervaporation, and solvent-resistant nanofiltration.

Abstract: Two-dimensional (2D) materials are promising candidates for atomic-scale piezotronics and piezophototronics. Quantum edge states show fascinating fundamental physics such as nontrivial topological behavior and hold promising practical applications for low-power electronic devices. Here, using the tight-binding approach and quantum transport simulations, we investigate the piezotronic effect on the spin polarization of edge states in a zigzag-terminated monolayer MoS2 nanoribbon. We find that the strain-induced piezoelectric potential induces a phase transition of edge states from metal to semiconductor. However, in the presence of exchange field, edge states become semi-metallic with significant spin splitting and polarization that can be tuned by external strain. We show that quantum transport conductance exhibits a 100% spin polarization over a wide range of strain magnitudes. This effect is used in a propose prototype of piezotronic spin transistor. Our results provide a fundamental understanding of the piezotronic effect on edge states in zigzag monolayer MoS2 nanoribbons and are relevant for designing high-performance piezotronic spin devices.

Abstract: We present a quantitative method which allows us to reliably measure dynamic changes in the atomic structure of monatomic crystalline nanomaterials from a time series of atomic resolution annular dark field scanning transmission electron microscopy images. The approach is based on the so-called hidden Markov model and estimates the number of atoms in each atomic column of the nanomaterial in each frame of the time series. We discuss the origin of the improved performance for time series atom-counting as compared to the current state-of-the-art atom-counting procedures, and show that the so-called transition probabilities that describe the probability for an atomic column to lose or gain one or more atoms from frame to frame are particularly important. Using these transition probabilities, we show that the method can also be used to estimate the probability and cross section related to structural changes. Furthermore, we explore the possibilities for applying the method to time series recorded under variable environmental conditions. The method is shown to be promising for a reliable quantitative analysis of dynamic processes such as surface diffusion, adatom dynamics, beam effects, or in situ experiments.

Abstract: In this work, the effect of geometry and orientation of food cans on the heating characteristics of processed liquid foods and the resulting lethality target values as a function of the processing times have been investigated. For this purpose, the governing differential equations have been solved numerically for elliptical and cylindrical cans of varying aspect ratios in different orientations in order to delineate their effect on the heating rate (especially of the slowest heating zone [SHZ]) and lethality values over wide ranges of rheological features including shear thinning (n < 1), Newtonian (n = 1), and shear thickening (n > 1) behaviors. The flow and heat transfer characteristics were analyzed with the help of velocity vectors, isotherm contours, average Nusselt number, SHZ temperature and heat penetration parameters, and lethality target values. Also, comparisons were made in terms of the sterilization time and heat penetration parameters to identify the preferable geometries and orientations of food cans for effective heating of non-Newtonian foodstuffs. Finally, favorable conditions in terms of the shape and orientation of the can and the rheological properties have been delineated which lead to superior heating characteristics. Practical Applications Processed foodstuffs are produced in various forms ranging from that in solid, liquid, or as heterogeneous mixtures. Often such liquid and heterogeneous suspensions products are viscous non-Newtonian in character and their thermal processing (including pasteurization, sterilization, etc.) tends to be much more challenging than that of their Newtonian counterparts like air and water. This work explores heating of non-Newtonian liquid foodstuffs in cans of various shapes, geometries and in different orientations in the free convection regime. The results show that depending upon the rheological properties of the products, some orientations and/or geometries offer potential advantages in terms of shorter processing times and lethality values. This information can be of great potential in customizing the design of containers for different food products as well as of different rheological properties.

Abstract: Lattice strain measurement of nanoscale semiconductor devices is crucial for the semiconductor industry as strain substantially improves the electrical performance of transistors. High resolution scanning transmission electron microscopy (HR-STEM) imaging is an excellent tool that provides spatial resolution at the atomic scale and strain information by applying Geometric Phase Analysis or image fitting procedures. However, HR-STEM images regularly suffer from scanning distortions and sample drift during image acquisition. In this paper, we propose a new scanning strategy that drastically reduces artefacts due to drift and scanning distortion, along with extending the field of view. It consists of the acquisition of a series of independent small subimages containing an atomic resolution image of the local lattice. All subimages are then analysed individually for strain by fitting a nonlinear model to the lattice images. The method allows flexible tuning of spatial resolution and the field of view within the limits of the dynamic range of the scan engine while maintaining atomic resolution sampling within the subimages. The obtained experimental strain maps are quantitatively benchmarked against the Bessel diffraction technique. We demonstrate that the proposed scanning strategy approaches the performance of the diffraction technique while having the advantage that it does not require specialized diffraction cameras.

Abstract: By using density functional theory-based first-principles calculations, we investigate the structural, electronic, optical, and transport properties of pristine single-layer BC6N. Under different external actions and functionalization. Increasing the thickness of the structure results in a decrease of the band gap. Applying a perpendicular electric field decreases the band gap and a semiconductor-to-topological insulator transition is revealed. Uniaxial and biaxial strains of +8% result in a semiconductor-to-metal transition. Nanoribbons of BC6N having zigzag edge with even (odd) values of widths, become metal (semiconductor), while the armchair edge nanoribbons exhibit robust semiconducting behavior. In addition, we systematically investigate the effect of surface adatom and molecule, substitutional impurity and defect engineering on the electronic properties of single-layer BC6N and found transitions from metal to half-metal, to ferromagnetic metal, to dilute magnetic semiconductor, and even to spin-glass semiconductor. Furthermore we found that, topological defects including vacancies and Stone–Wales type, induce magnetism in single-layer BC6N.

Abstract: Grain boundaries between 60 degrees rotated and twinned crystals constitute the dominant type of extended line defects in two-dimensional transition metal dichalcogenides (2D MX2) when grown on a single crystalline template through van der Waals epitaxy. The two most common 60 degrees grain boundaries in MX2 layers, i.e., beta- and gamma-boundaries, introduce distinct distortion and strain into the 2D lattice. They impart a localized tensile or compressive strain on the subsequent layer, respectively, due to van der Waals coupling in bilayer MX2 as determined by combining atomic resolution electron microscopy, geometric phase analysis, and density functional theory. Based on these observations, an alternate route to strain engineering through controlling intrinsic van der Waals forces in homobilayer MX2 is proposed. In contrast to the commonly used external means, this approach enables the localized application of strain to tune the electronic properties of the 2D semiconducting channel in ultra-scaled nanoelectronic applications.

Abstract: Ab initio calculations are performed to investigate the structural, vibrational, electronic, and piezoelectric properties of functionalized single layers of TaS2. We find that single-layer TaS2 is a suitable host material for functionalization via fluorination and hydrogenation. The one-side fluorinated (FTaS2) and hydrogenated (HTaS2) single layers display indirect gap semiconducting behavior in contrast to bare metallic TaS2. On the other hand, it is shown that as both surfaces of TaS2 are saturated anti-symmetrically, the formed Janus structure is a dynamically stable metallic single layer. In addition, it is revealed that out-of-plane piezoelectricity is created in all anti-symmetric structures. Furthermore, the Janus-type single-layer has the highest specific heat capacity to which longitudinal and transverse acoustical phonon modes have contribution at low temperatures. Our findings indicate that single-layer TaS2 is suitable for functionalization via H and F atoms that the formed, anti-symmetric structures display distinctive electronic, vibrational, and piezoelectric properties.

Abstract: The 21st century revival of large-scale water resources development projects makes it important to keep assessing their impacts – preferably from an interdisciplinary perspective – in order to not repeat past mistakes and explore whether they could improve livelihood conditions for rural communities. In this study, costs and benefits of the World Bank-funded Ribb Irrigation and Drainage Project (RIDP) were investigated using a unique systems approach. The impact for farmers with different initial farming systems (rainfed – residual moisture – irrigated) was studied using field observations, document analyses, remote sensing, agronomic data and semi-structured interviews (n = 165). Data on project-induced changes to land and water availability, cropping patterns, farming systems and farm-level economics were collected. The results show that dam and dyke construction has reduced flooding, which has resulted in declining rice productivity ( – 42%) and concomitant shifts to lower value cropping systems. Results also reveal that the land redistribution has caused widespread livelihood deterioration as households had to give up 25% of their farmland and the communal grazing land was fully converted into farmland. Due to top-down implementation, nontransparent communication, delayed construction and lagging financial compensation, social resistance has appeared in the command area, impeding the construction works. In addition to these problems, if no rapid change to higher value crops can be realized, 20.5% of the farmers (those who already irrigate) will experience a loss of livelihood, 64.1% of the farmers (those with rainfed and residual moisture cultivation) will be on the verge of livelihood deterioration and only 13.5% of the farmers (those with solely rainfed cultivation) will enjoy RIDP-induced improved livelihoods. The fate of this project stresses the importance of investigating initial farming systems, exploring worthy project alternatives, improving participation, communication and benefit-sharing and strengthening the institutional capacity of implementing authorities.

Abstract: The formation of metal oxalates in paintings has recently gained a great deal of interest within the field of heritage science as several types of oxalate compounds have been identified in oil paintings. The present work investigates the formation of metal oxalates in linseed oil in the presence of the artists' pigments zinc white, calcite, lead white, zinc yellow, chrome yellow, cadmium yellow, cobalt violet, and verdigris. The oil paint films were artificially photo-aged by exposure to UVA light at low and high relative humidity, and afterwards analysed by attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR). The results showed that, compared to the other pigments investigated, zinc white is especially prone to metal oxalate formation and that high humidity is a crucial factor in this process. Consequently, the reactivity and photo-aging of ZnO in various oil binding media was investigated further under simulated solar radiation and at high relative humidity levels. ATR-FTIR showed that zinc oxalate is formed in all oil binding media while X-ray powder diffraction (PXRD) revealed it was mainly present in an amorphous state. To examine whether atmospheric CO2(g) has any influence on the formation of zinc oxalate, experiments with isotopically enriched (CO2(g))-C-13 were performed. Based on ATR-FTIR measurements, neither (ZnC2O4)-C-13 nor (ZnCO3)-C-13 were formed which suggests that the carbon source for the oxalate formation is most likely the paint itself (and its oil component) and not the surrounding atmosphere.

Abstract: We investigate the ground-state and dynamical properties of nonuniform two-dimensional (2D) clusters of long-range interacting particles. We demonstrate that, when the confining external potential is designed to produce an approximate 1/ r 2 density profile, the particles crystallize into highly ordered structures featuring spiral crystalline lines. Despite the strong inhomogeneity of the observed configurations, most of them are characterized by small density of topological defects, typical of conformal crystals, and the net topological charge induced by the simply-connected geometry of the system is concentrated near the cluster center. These crystals are shown to be robust with respect to thermal fluctuations up to a certain threshold temperature, above which the net charge is progressively redistributed from the center to the rest of the system and the topological order is lost. The crystals are also resilient to the shear stress produced by a small nonuniform azimuthal force field, rotating as a rigid body (RB). For larger forces, topological defects proliferate and the RB rotation gives place to plastic flow.

Abstract: MXenes are an emerging class of two-dimensional materials, which in their thinnest limit consist of a monolayer of carbon or nitrogen (X) sandwiched between two transition metal (M) layers. We have systematically searched for superconductivity among MXenes for a range of transition metal elements, based on a full first-principles characterization in combination with the Eliashberg formalism. Thus, we identified six superconducting MXenes: three carbides (Mo2C, W2C and Sc2C) and three nitrides (Mo2N, W2N and Ta2N). The highest critical temperature of similar to 16 K is found in Mo2N, for which a successful synthesis method has been established [Urbankowskiet al.,Nanoscale, 2017,9, 17722-17730]. Moreover, W2N presents a novel case of competing superconducting and charge density wave phases.

Abstract: The fine balance between dipole-field energy and anion drift force defines the switching mechanism during polarization reversal: for the first time we show that only Pbcm mechanism obeys the ferroelectric switching physics, whereas P4(2)/nmc (or any other) mechanism does not. However, with lower energy barrier, it represents an important antiferroelectric mechanism. Constraints relaxation can lead to 90 degrees polarization rotation (domain deactivation). Intrinsically, the Si/VO-doping can switch faster than undoped HfO2 or HfZrOx. Theoretical Arrhenius model / intrinsic material switching (DFT) overestimates the switching speed extracted from experiments.