Abstract: A two-step process for the formation of sensitivity centers different from earlier described two-step processes was found for sulfur sensitized emulsions. After deposition of sulfur in the first step, it was found that the second step does not consist of rearrangement of sulfur over the surface, but of the supply of silver interstitial ions towards the deposited sulfur clusters. The two processes could be separated by adsorbing and desorbing TAI (4-hydroxy-1, 3,3a, 7-tetraazaindene) at/from the silver halide surface. When 1.5 mmol TAI/mol Ag is added before the sulfur reaction, the silver interstitials are immobilized but sulfur still can be deposited at the same level. By lowering the pH to 2.50 after this sulfur reaction, TAI is desorbed from the surface and the released interstitials then cause a restoration of the properties of a sulfur system without TAI. These effects could be demonstrated via diffuse reflectance spectroscopy (DRS), sensitometry and dielectric loss measurements. We could also confirm the isolation of silver sulfide clusters by TAI from other chemicals in the solution, by adsorption of TAI on the clusters.

Abstract: Eight silicate glasses were prepared by directly fusing and stirring 50-100 g each of basalt, andesite, komatiite, peridotite, rhyolite, and quartz-diorite. These are referred to as MPI-DING glasses and were made for the purpose of providing reference materials for geochemical, in-situ microanalytical work. Results from various analytical techniques indicate that individual glass fragments are well homogenised with respect to major and trace elements at the mu m to mm scale. Heterogeneities due to quench crystallisation of olivine have been observed in small and limited areas of the two komatiitic glasses. In order to obtain concentration values for as many elements as possible, the glasses were analysed by a variety of bulk and microanalytical methods in a number of laboratories. From the analytical data, preliminary reference values for more than sixty elements were calculated. The analytical uncertainties of most elements are estimated to be between 1% and 10%.

Abstract: Multishell tabular grains have a higher speed than pure AgBr tabular grains. Usually the shells differ in size and iodide content, but also the precipitation method for the iodide containing shells has an influence on the iodide incorporation. A TEM investigation was performed to determine the defect structure of multishell AgBr (111) tabular crystals containing a shell with a low iodide concentration and one with a high iodide concentration. The twins that induce tabular growth and stacking fault contrast in the region of the iodide shells have been observed, similar to previously studied AgBr/Ag(Br,I) coreshell crystals. Moreover in some of the crystals dislocations have been observed, sometimes even an entire network. The number of dislocations formed varies for the different methods of iodide addition. Also variations in average thickness between the different iodide addition methods have been observed. A higher number of dislocations and thicker crystals point towards a higher local concentration of iodide. These observations allow deciding which iodide incorporation method is most useful for a preferred dislocation pattern.

Abstract: Multiwall carbon nanotubes are produced by decomposition of acetylene at 600 degreesC on metal catalysts supported on NaY zeolite. The support and the metal are eliminated by dissolving them in aqueous hydrofluoric acid (HF). Two methods were used to eliminate the pyrolitic carbon: oxidation in air at 500 degreesC and oxidation by potassium permanganate in acidic solution at 70 degreesC. The progress and efficacy of the purification methods are verified by TEM. The properties of the purified multiwalled carbon nanotubes are probed using C-13 and Xe-129 NMR spectroscopy under continuous-flow optical-pumping conditions. Xenon is shown to penetrate the interior of the nanotubes. A distribution of inner tube diameters gives rise to chemical shift dispersion. When the temperature is lowered, an increasing fraction of xenon resides inside the nanotubes and is not capable of exchanging with xenon in the interparticle space. In the case of the permanganate-oxidized sample, rapid xenon relaxation is attributed to interaction with residual MnO2 nanoparticles in the interior of the tubes.