“Novel MoVSbOx-type catalysts for selective isobutane oxidation”. Paul JS, Groothaert MH, Kirschhock CEA, Lebedev OI, Jacobs PA, Maier WF, Catalysis today
T2 –, 7th European Workshop Meeting on Selective Oxidation, AUG 31-SEP 04, 2003, Innsbruck, AUSTRIA 91-2, 265 (2004). http://doi.org/10.1016/j.cattod.2004.03.041
Abstract: A new sol-gel synthesis procedure is proposed for the preparation of MoVSbOx catalysts for the selective oxidation of isobutane. Physico-chemical characterization of the materials calcined at 400 degreesC, showed essentially amorphous catalysts, with long-range order. Increase of calcination temperature, however, resulted in the formation of small crystalline regions, confirmed through TEM. EPR measurements on the calcined samples pointed to the presence of isolated and magnetically interacting V(IV) species. The reported catalysts proved to be much more selective for partial oxidation compared to a literature reference catalyst. Furthermore, it is shown that this versatile synthesis recipe forms an excellent start for high-throughput and combinatorial studies. (C) 2004 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 12
DOI: 10.1016/j.cattod.2004.03.041
|
“Nitrogen and luminescent nitrogen-vacancy defects in detonation nanodiamond”. Vlasov II, Shenderova O, Turner S, Lebedev OI, Basov AA, Sildos I, Rähn M, Shiryaev AA, Van Tendeloo G, Small 6, 687 (2010). http://doi.org/10.1002/smll.200901587
Abstract: An efficient method to investigate the microstructure and spatial distribution of nitrogen and nitrogen-vacancy (N-V) defects in detonation nanodiamond (DND) with primary particle sizes ranging from approximately 3 to 50 nm is presented. Detailed analysis reveals atomic nitrogen concentrations as high as 3 at% in 50% of diamond primary particles with sizes smaller than 6 nm. A non-uniform distribution of nitrogen within larger primary DND particles is also presented, indicating a preference for location within the defective central part or at twin boundaries. A photoluminescence (PL) spectrum with well-pronounced zero-phonon lines related to the N-V centers is demonstrated for the first time for electron-irradiated and annealed DND particles at continuous laser excitation. Combined Raman and PL analysis of DND crystallites dispersed on a Si substrate leads to the conclusion that the observed N-V luminescence originates from primary particles with sizes exceeding 30 nm. These findings demonstrate that by manipulation of the size/nitrogen content in DND there are prospects for mass production of nanodiamond photoemitters based on bright and stable luminescence from nitrogen-related defects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 84
DOI: 10.1002/smll.200901587
|
“Nickel/carbon composite materials based on expanded graphite”. Afanasov IM, Lebedev OI, Kolozhvary BA, Smirnov AV, Van Tendeloo G, New carbon materials 26, 335 (2011). http://doi.org/10.1016/S1872-5805(11)60085-1
Abstract: Monolithic nickel/carbon (Ni/C) composites were prepared from coal tar pitch-impregnated compressed expanded graphite pre-decorated with NiO particles (EGNiO) by pyrolysis at 550 °C and subsequent steam activation at 800 °C. The microstructural arrangement of the Ni-comprising nanoparticles in the composites was investigated using transmission electron microscopy. The specific surface area and porosity of the composites were analyzed by nitrogen adsorption. The catalytic activity of the composites was compared with the material obtained by the conventional H2 treatment of EGNiO using hydrocracking of 2,2,3-trimethylpentane as a model reaction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1016/S1872-5805(11)60085-1
|
“New nano-architectures of mesoporous silica spheres analyzed by advanced electron microscopy”. Lebedev OI, Turner S, Liu S, Cool P, Van Tendeloo G, Nanoscale 4, 1722 (2012). http://doi.org/10.1039/c2nr11715k
Abstract: Using template-containing silica microspheres as a precursor, novel ordered mesoporous silica nanoparticles with a narrow pore size distribution and high crystallinity have been synthesized by various hydrothermal merging processes. Several architectures like chains, dumbbells, triangles, squares and flowers have been discovered. The linking mechanisms of these interacting silica spheres leading to the formation of ordered nano-structures are studied by HRTEM, HAADF-STEM and electron tomography and a plausible model is presented for several merging processes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 7.367
Times cited: 5
DOI: 10.1039/c2nr11715k
|
“New molybdenum oxides Ag4M2Zr(MoO4)6 (M=Mg, Mn, Co, Zn) with a channel-like structure”. Khobrakova ET, Morozov VA, Khasanov SS, Tsyrenova GD, Khaikina EG, Lebedev OI, Van Tendeloo G, Lazoryak BI, Solid state sciences 7, 1397 (2005). http://doi.org/10.1016/j.solidstatesciences.2005.08.010
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 9
DOI: 10.1016/j.solidstatesciences.2005.08.010
|
“New insights in the formation of combined zeolitic/mesoporous materials by using a one-pot templating synthesis”. Vernimmen J, Meynen V, Herregods SJF, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, European journal of inorganic chemistry , 4234 (2011). http://doi.org/10.1002/ejic.201100268
Abstract: Zeolitic growth is often absent or occurs in separate phases when synthetic strategies based on the combination of zeolite templates and mesopore templating agents are applied. In this work, zeolitic growth and mesopore formation have been investigated at different temperatures by applying a one-pot templating approach, based on a TS-1 zeolite synthesis whereby part of the microtemplate (tetrapropylammonium hydroxide, TPAOH) is replaced by a mesotemplate (hexadecyltrimethylammonium bromide, CTMABr). Moreover, the synthesis duration and the molar ratio of the microtemplate/mesotemplate have also been studied. The different syntheses clearly show the inherent competitive mechanism between zeolitic growth and mesopore formation. These insights have led to the conclusion that by following a one-pot templating strategy with standard, nonexotic commercial templates, i.e. CTMABr and TPAOH, it is not possible to develop a true hierarchical mesoporous zeolite, meaning a mesoporous siliceous material with highly crystalline zeolitic walls. The resultant materials are instead combined zeolitic/mesoporous composite structures with, however, highly tuneable and controllable porosity characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.444
Times cited: 7
DOI: 10.1002/ejic.201100268
|
“Negative magnetoresistance in a V3+/V4+ mixed valent vanadate”. Maignan A, Lebedev OI, Van Tendeloo G, Martin C, Hébert S, Applied physics letters 96, 232502 (2010). http://doi.org/10.1063/1.3446892
Abstract: The magnetotransport and magnetic properties of the PbV6O11 vanadate, crystallizing in the P63mc space group, reveal the existence of a negative magnetoresistance related to its ferromagnetic state (TC ∼ 90 K). The maximum effect is observed at 20 K reaching −30% in 9 T. The structural study of this ceramic reveals a V/Pb ratio smaller than expected from the formula. This is explained by the presence of numerous stacking faults observed by high resolution transmission electron microscopy. The existence of these planar defects acting as resistive barriers along the c axis could be responsible for tunneling magnetoresistance.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
DOI: 10.1063/1.3446892
|
“Nanoscale ordering in oxygen deficient quintuple perovskite Sm2-\epsilonBa3+\epsilonFe5O15-\delta : implication for magnetism and oxygen stoichiometry”. Volkova NE, Lebedev OI, Gavrilova LY, Turner S, Gauquelin N, Seikh MM, Caignaert V, Cherepanov VA, Raveau B, Van Tendeloo G, Chemistry of materials 26, 6303 (2014). http://doi.org/10.1021/cm503276p
Abstract: The investigation of the system SmBaFe-O in air has allowed an oxygen deficient perovskite Sm2-epsilon Ba3+epsilon Fe5O15-delta (delta = 0.75, epsilon = 0.125) to be synthesized. In contrast to the XRPD pattern which gives a cubic symmetry (a(p) = 3.934 angstrom), the combined HREM/EELS study shows that this phase is nanoscale ordered with a quintuple tetragonal cell, a(p) X a(p) X 5(ap). The nanodomains exhibit a unique stacking sequence of the A-site cationic layers along the crystallographic c-axis, namely SmBaBa/SmBa/SmBaSm, and are chemically twinned in the three crystallographic directions. The nanoscale ordering of this perovskite explains its peculiar magnetic properties on the basis of antiferromagnetic interactions with spin blockade at the boundary between the nanodomains. The variation of electrical conductivity and oxygen content of this oxide versus temperature suggest potential SOFC applications. They may be related to the particular distribution of oxygen vacancies in the lattice and to the 3d(5)(L) under bar configuration of iron.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/cm503276p
|
“Nanodiamond photoemitters based on strong narrow-band luminescence from silicon-vacancy defects”. Vlasov II, Barnard AS, Ralchenko VG, Lebedev OI, Kanzyuba MV, Saveliev AV, Konov VI, Goovaerts E, Advanced materials 21, 808 (2009). http://doi.org/10.1002/adma.200802160
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 98
DOI: 10.1002/adma.200802160
|
“Multi-step loading of titania on mesoporous silica: influence of the morphology and the porosity on the catalytic degradation of aqueous pollutants and VOC's”. de Witte K, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Sepúlveda-Escribano A, Rodríguez-Reinoso F, Vansant EF, Cool P, Applied catalysis : B : environmental 84, 125 (2008). http://doi.org/10.1016/j.apcatb.2008.03.015
Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 9.446
Times cited: 24
DOI: 10.1016/j.apcatb.2008.03.015
|
“Mixed (Sr1-xCax)33Bi24Al48O141 fullerenoids: the defect structure analysed by (S)TEM techniques”. Lebedev OI, Bals S, Van Tendeloo G, Snoeck GE, Retoux R, Boudin S, Hervieu M, International journal of materials research 97, 978 (2006). http://doi.org/10.3139/146.101328
Abstract: (Sr1-xCax)(33)Bi-24,partial derivative Al48O141+3 partial derivative/2 fullerenoid solid solutions have been synthesized and the effect of partial substitution of Sr by Ca has been characterized by (scanning) transmission electron microscopy, applying different imaging methods. Most of the defects commonly observed in face centered cubic compounds, have also been observed in (Sr1-xCax)(33)Bi24-partial derivative Al48O141+3 partial derivative/2. Based on purely geometrical and topological models, structural presentations for the coherent twin boundaries and stacking faults have been constructed on the basis of complex spherical “Al84O210” units. The results are compared to defects observed in the crystallite fullerite C-60.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.681
Times cited: 1
DOI: 10.3139/146.101328
|
“Misfit accommodation of epitaxial La1-xAxMnO3 (A=Ca, Sr) thin films”. Lebedev OI, Van Tendeloo G, Amelinckx S, International journal of inorganic materials 3, 1331 (2001). http://doi.org/10.1016/S1466-6049(01)00155-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1016/S1466-6049(01)00155-6
|
“Microstructure of YBa2Cu3O7-\delta Josephson junctions in relation to their properties”. Verbist K, Lebedev OI, Verhoeven MAJ, Winchern R, Rijnders AJHM, Blank DHA, Tafuri F, Bender H, Van Tendeloo G, Superconductor science and technology 11, 13 (1998). http://doi.org/10.1088/0953-2048/11/1/004
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
DOI: 10.1088/0953-2048/11/1/004
|
“Metal to insulator transition in the n-type hollandite vanadate Pb1.6V8O16”. Maignan A, Lebedev OI, Van Tendeloo G, Martin C, Hebert S, Physical review : B : condensed matter and materials physics 82, 035122 (2010). http://doi.org/10.1103/PhysRevB.82.035122
Abstract: The transport and magnetic measurements of polycrystalline Pb1.6V8O16 hollandite reveal a concomitant metal to insulator and antiferromagnetic transition at TMI≈140 K. A clear localization is found below TMI, evidenced by a rapid increase in the absolute value of the negative Seebeck coefficient. The structural study by x-ray and transmission electron microscopy confirms the hollandite structure and shows that no structural transition occurs at TMI, ruling out a possible charge orbital ordering. The negative Seebeck coefficient observed from 50 K up to 900 K, with values reaching S=−38 μV K−1 at 900 K, is explained by the electron doping of ∼1.4e− in the V empty t2g orbitals responsible for the bad metal resistivity (ρ900 K∼2 mΩ cm). As this S value is close to that obtained by considering only the spin and orbital degeneracies, it is expected that |S| for such vanadates will not be sensitive at high temperature to the t2g band filling
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 10
DOI: 10.1103/PhysRevB.82.035122
|
“Metal and composite nanocluster precipitate formation in silicon dioxide implanted with Sb+ ions”. Ignatova VA, Lebedev OI, Watjen U, van Vaeck L, van Landuyt J, Gijbels R, Adams F, Journal of applied physics 92, 4336 (2002). http://doi.org/10.1063/1.1508425
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.068
Times cited: 5
DOI: 10.1063/1.1508425
|
“Mesoporous material formed by acidic hydrothermal assembly of silicalite-1 precursor nanoparticles in the absence of meso-templates”. Stevens WJJ, Meynen V, Bruijn E, Lebedev OI, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 110, 77 (2008). http://doi.org/10.1016/j.micromeso.2007.09.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 21
DOI: 10.1016/j.micromeso.2007.09.007
|
“Mechanism of preferential orientation in sputter deposited titanium nitride and yttria-stabilized zirconia layers”. Mahieu S, Ghekiere P, de Winter G, Heirwegh S, Depla D, de Gryse R, Lebedev OI, Van Tendeloo G, Journal of crystal growth 279, 100 (2005). http://doi.org/10.1016/j.jcrysgro.2005.02.014
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 41
DOI: 10.1016/j.jcrysgro.2005.02.014
|
“Magnetic and magnetodielectric properties of erbium iron garnet ceramic”. Maignan A, Singh K, Simon C, Lebedev OI, Martin C, Tan H, Verbeeck J, Van Tendeloo G, Journal of applied physics 113, 033905 (2013). http://doi.org/10.1063/1.4776716
Abstract: An Er3Fe5O12 ceramic has been sintered in oxygen atmosphere at 1400 °C for dielectric measurements. Its structural quality at room temperature has been checked by combining transmission electron microscopy and X-ray diffraction. It crystallizes in the cubic space group Ia3d with a = 12.3488(1). The dielectric permittivity ([variantgreekepsilon]′) and losses (tan δ) measurements as a function of temperature reveal the existence of two anomalies, a broad one between 110 K and 80 K, attributed to the Er3+ spin reorientation, and a second sharper feature at about 45 K associated to the appearance of irreversibility on the magnetic susceptibility curves. In contrast to the lack of magnetic field impact on [variantgreekepsilon]′ for the former anomaly, a complex magnetic field effect has been evidenced below 45 K. The isothermal [variantgreekepsilon]′(H) curves show the existence of positive magnetodielectric effect, reaching a maximum of 0.14% at 3 T and 10 K. Its magnitude decreases as H is further increased. Interestingly, for the lowest H values, a linear regime in the [variantgreekepsilon]′(H) curve is observed. From this experimental study, it is concluded that the [variantgreekepsilon]′ anomaly, starting above the compensation temperature Tc (75 K) and driven by the internal magnetic field, is not sensitive to an applied external magnetic field. Thus, below 45 K, it is the magnetic structure which is responsible for the coupling between spin and charge in this iron garnet.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 15
DOI: 10.1063/1.4776716
|
“Low- or high-angle Ar ion-beam etching to create ramp-type Josephson junctions”. Verbist K, Lebedev OI, Van Tendeloo G, Verhoeven MAJ, Rijnders AJHM, Blank DHA, Superconductor science and technology 9, 978 (1996). http://doi.org/10.1088/0953-2048/9/11/009
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.325
Times cited: 10
DOI: 10.1088/0953-2048/9/11/009
|
“LiZnNb4O11.5 : a novel oxygen deficient compound in the Nb-rich part of the Li2O-ZnO-Nb2O5 system”. Morozov VA, Arakcheeva AV, Konovalova VV, Pattison P, Chapuis G, Lebedev OI, Fomichev VV, Van Tendeloo G, Journal of solid state chemistry 183, 408 (2010). http://doi.org/10.1016/j.jssc.2009.12.008
Abstract: A novel lithium zinc niobium oxide LiZnNb(4)O(11.5) (LZNO) has been found in the Nb-rich part of Li(2)O-ZnO-Nb(2)O(5) system. LZNO, with an original alpha-PbO(2) related structure, has been synthesized by the routine ceramic technique and characterized by X-ray diffraction and transmission electron microscopy (TEM). Reflections belonging to the LZNO phase, observed in X-ray powder diffraction (XRPD) and electron diffraction, have been indexed as monoclinic with unit cell parameters a=17.8358(9)angstrom, b=15.2924(7)angstrom, c=5.0363(3)angstrom and gamma=96.607(5)degrees or as alpha-PbO(2)-like with lattice constants a=4.72420(3)angstrom, b=5.72780(3)angstrom, c=5.03320(3)angstrom, gamma=90.048(16)degrees and modulation vector q=0.3a*+1.1b* indicating a commensurately modulated alpha-PbO(2) related structure. The monoclinic cell is a supercell related to the latter. Using synchrotron powder diffraction data, the structure has been solved and refined as a commensurate modulation (superspace group P112(1)/n(alpha beta 0)00) as well as a supercell (space group P2(1)/b). The superspace description allows us to consider the LZNO structure as a member of the proposed alpha-PbO(2)-Z (3 + 1)D structure type, which unifies both incommensurately and commensurately modulated structures. HRTEM reveals several types of defects in LZNO and structural models for these defects are proposed. Two new phases in Li(2)O-ZnO-Nb(2)O(5) system are predicted on the basis of this detailed HRTEM analysis. (C) 2009 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 9
DOI: 10.1016/j.jssc.2009.12.008
|
“Ion beam synthesis of Te and Bi nanoclusters in silicon: the effect of post-implantation high frequency electromagnetic field”. Kalitzova M, Peeva A, Ignatova V, Lebedev OI, Zollo G, Vitali G, Nuclear instruments and methods in physics research: B: beam interactions with materials and atoms 242, 209 (2006). http://doi.org/10.1016/j.nimb.2005.08.017
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.109
Times cited: 1
DOI: 10.1016/j.nimb.2005.08.017
|
“Interfacial spin glass state and exchange bias in manganite bilayers with competing magnetic orders”. Ding JF, Lebedev OI, Turner S, Tian YF, Hu WJ, Seo JW, Panagopoulos C, Prellier W, Van Tendeloo G, Wu T, Physical review : B : condensed matter and materials physics 87, 054428 (2013). http://doi.org/10.1103/PhysRevB.87.054428
Abstract: The magnetic properties of manganite bilayers composed of G-type antiferromagnetic (AFM) SrMnO3 and double-exchange ferromagnetic (FM) La0.7Sr0.3MnO3 are studied. A spin-glass state is observed as a result of competing magnetic orders and spin frustration at the La0.7Sr0.3MnO3/SrMnO3 interface. The dependence of the irreversible temperature on the cooling magnetic field follows the Almeida-Thouless line. Although an ideal G-type AFM SrMnO3 is featured with a compensated spin configuration, the bilayers exhibit exchange bias below the spin glass freezing temperature, which is much lower than the Néel temperature of SMO, indicating that the exchange bias is strongly correlated with the spin glass state. The results indicate that the spin frustration that originates from the competition between the AFM super-exchange and the FM double-exchange interactions can induce a strong magnetic anisotropy at the La0.7Sr0.3MnO3/SrMnO3 interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 98
DOI: 10.1103/PhysRevB.87.054428
|
“Interface controlled electronic variations in correlated heterostructures”. Gehrke K, Moshnyaga V, Samwer K, Lebedev OI, Verbeeck J, Kirilenko D, Van Tendeloo G, Physical review : B : condensed matter and materials physics 82, 113101 (2010). http://doi.org/10.1103/PhysRevB.82.113101
Abstract: An interface modification of (LaCa)MnO3-BaTiO3 superlattices was found to massively influence magnetic and magnetotransport properties. Moreover it determines the crystal structure of the manganite layers, changing it from orthorhombic (Pnma) for the conventional superlattice (cSL), to rhombohedral (R3̅ c) for the modified one (mSL). While the cSL shows extremely nonlinear ac transport, the mSL is an electrically homogeneous material. The observations go beyond an oversimplified picture of dead interface layers and evidence the importance of electronic correlations at perovskite interfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 9
DOI: 10.1103/PhysRevB.82.113101
|
“Insights on growth and nanoscopic investigation of uncommon iron oxide polymorphs”. Carraro G, Maccato C, Bontempi E, Gasparotto A, Lebedev OI, Turner S, Depero LE, Van Tendeloo G, Barreca D, European journal of inorganic chemistry , 5454 (2013). http://doi.org/10.1002/ejic.201300873
Abstract: Si(100)-supported Fe2O3 nanomaterials were developed by a chemical vapor deposition (CVD) approach. The syntheses, which were performed at temperatures between 400 and 550 °C, selectively yielded the scarcely studied β- and ϵ-Fe2O3 polymorphs under O2 or O2 + H2O reaction environments, respectively. Correspondingly, the observed morphology underwent a progressive evolution from interconnected nanopyramids to vertically aligned nanorods. The present study aims to provide novel insights into Fe2O3 nano-organization by a systematic investigation of the system structure/morphology and of their interrelations with growth conditions. In particular, for the first time, the β- and ϵ-Fe2O3 preparation process has been accompanied by a thorough multitechnique investigation, which, beyond X-ray photoelectron spectroscopy (XPS) and field-emission scanning electron microscopy (FESEM), is carried out by X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDXS), atomic force microscopy (AFM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), scanning TEM electron energy-loss spectroscopy (STEM-EELS), and high-angle annular dark-field STEM (HAADF-STEM). Remarkably, the target materials showed a high structural and compositional homogeneity throughout the whole thickness of the nanodeposit. In particular, spatially resolved EELS chemical maps through the spectrum imaging (SI) technique enabled us to gain important information on the local Fe coordination, which is of crucial importance in determining the system reactivity. The described preparation method is in fact a powerful tool to simultaneously tailor phase composition and morphology of iron(III) oxide nanomaterials, the potential applications of which include photocatalysis, magnetic devices, gas sensors, and anodes for Li-ion batteries.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 18
DOI: 10.1002/ejic.201300873
|
“Influence of the structure on the properties of NaxEuy(MoO4)z red phosphors”. Morozov VA, Lazoryak BI, Shmurak SZ, Kiselev AP, Lebedev OI, Gauquelin N, Verbeeck J, Hadermann J, Van Tendeloo G, Chemistry of materials 26, 3238 (2014). http://doi.org/10.1021/cm500966g
Abstract: Scheelite related compounds (A',A '')(n)[(B',B '')O-4](m) with B', B '' = W and/or Mo are promising new materials for red phosphors in pc-WLEDs (phosphor-converted white-light-emitting-diode) and solid-state lasers. Cation substitution in CaMoO4 of Ca2+ by the combination of Na+ and Eu3+, with the creation of A cation vacancies, has been investigated as a factor for controlling the scheelite-type structure and the luminescent properties. Na5Eu(MoO4)(4) and NaxEu(2-x)/33+square(2-x)/3MoO4 (0.138 <= x <= 0.5) phases with a scheelite-type structure were synthesized by the solid state method; their structural characteristics were investigated using transmission electron microscopy. Contrary to powder synchrotron X-ray diffraction before, the study by electron diffraction and high resolution transmission electron microscopy in this paper revealed that Na0.286Eu0.571MoO4 has a (3 + 2)D incommensurately modulated structure and that (3 + 2)D incommensurately modulated domains are present in Na0.200Eu0.600MoO4. It also confirmed the (3 + 1)D incommensurately modulated character of Na(0.138)Eu(0.621)Mo04. The luminescent properties of all phases under near-ultraviolet (n-UV) light have been investigated. The excitation spectra of these phosphors show the strongest absorption at about 395 nm, which matches well with the commercially available n-UV-emitting GaN-based LED chip. The emission spectra indicate an intense red emission due to the D-5(0) -> F-7(2) transition of Eu3+, with local minima in the intensity at Na0.286Eu0.571MoO4 and Na0.200Eu0.600MoO4 for similar to 613 nm and similar to 616 nm bands. The phosphor Na5Eu(MoO4)(4) shows the brightest red light emission among the phosphors in the Na2MoO4-Eu2/3MoO4 system and the maximum luminescence intensity of Na5Eu(MoO4)(4) (lambda(ex) = 395 nm) in the D-5(0) -> F-7(2) transition region is close to that of the commercially used red phosphor YVO4:Eu3+ (lambda(ex) = 326 nm). Electron energy loss spectroscopy measurements revealed the influence of the structure and Na/Eu cation distribution on the number and positions of bands in the UV-optical-infrared regions of the EELS spectrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 53
DOI: 10.1021/cm500966g
|
“Influence of the Ar/O2 ratio on the growth and biaxial alignment of yttria stabilized zirconia layers during reactive unbalanced magnetron sputtering”. Mahieu S, Ghekiere P, de Winter G, Depla D, de Gryse R, Lebedev OI, Van Tendeloo G, Thin solid films : an international journal on the science and technology of thin and thick films 484, 18 (2005). http://doi.org/10.1016/j.tsf.2005.01.021
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 23
DOI: 10.1016/j.tsf.2005.01.021
|
“Inducing superconductivity and structural transformations by fluorination of reduced YBCO”. Shpanchenko RV, Rozova MG, Abakumov AM, Ardashnikova EI, Kovba ML, Putilin SN, Antipov EV, Lebedev OI, Van Tendeloo G, Physica: C : superconductivity 280, 272 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 35
|
“In-situ HREM irradiation study of point defect clustering in strained GexSi1-x/(001)Si heterostructure”. Fedina L, Lebedev OI, Van Tendeloo G, van Landuyt J, Conference series of the Institute of Physics 157, 55 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
|
“In situ HREM irradiation study of point-defect clustering in MBE-grown strained Si1-xGex/(001)Si structures”. Fedina L, Lebedev OI, Van Tendeloo G, van Landuyt J, Mironov OA, Parker EHC, Physical review : B : condensed matter and materials physics 61, 10336 (2000). http://doi.org/10.1103/PhysRevB.61.10336
Abstract: We present a detailed analysis of the point-defect clustering in strained Si/Si(1-x)Ge(x)/(001)Si structures, including the interaction of the point defects with the strained interfaces and the sample surface during 400 kV electron irradiation at room temperature. Point-defect cluster formation is very sensitive to the type and magnitude of the strain in the Si and Si(1-x)Ge(x) layers. A small compressive strain (-0.3%) in the SiGe alloy causes an aggregation of vacancies in the form of metastable [110]-oriented chains. They are located on {113} planes and further recombine with interstitials. Tensile strain in the Si layer causes an aggregation of interstitial atoms in the forms of additional [110] rows which are inserted on {113} planes with [001]-split configurations. The chainlike configurations are characterized by a large outward lattice relaxation for interstitial rows (0.13 +/-0.01 nm) and a very small inward relaxation for vacancy chains (0.02+/-0.01 nm). A compressive strain higher than -0.5% strongly decreases point-defect generation inside the strained SiGe alloy due to the large positive value of the formation volume of a Frenkel pair. This leads to the suppression of point-defect clustering in a strained SiGe alloy so that SiGe relaxes via a diffusion of vacancies from the Si layer, giving rise to an intermixing at the Si/SiGe interface. In material with a 0.9% misfit a strongly increased flow of vacancies from the Si layer to the SiGe layer and an increased biaxial strain in SiGe bath promote the preferential aggregation of vacancies in the (001) plane, which relaxes to form intrinsic 60 degrees dislocation loops.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 27
DOI: 10.1103/PhysRevB.61.10336
|
“Immersion calorimetry as a tool to evaluate the catalytic performance of titanosilicate materials in the epoxidation of cyclohexene”. Vernimmen J, Guidotti M, Silvestre-Albero J, Jardim EO, Mertens M, Lebedev OI, Van Tendeloo G, Psaro R, Rodríguez-Reinoso F, Meynen V, Cool P, Langmuir: the ACS journal of surfaces and colloids 27, 3618 (2011). http://doi.org/10.1021/la104808v
Abstract: Different types of titanosilicates are synthesized, structurally characterized, and subsequently catalytically tested in the liquid-phase epoxidation of cyclohexene. The performance of three types of combined zeolitic/mesoporous materials is compared with that of widely studied Ti-grafted-MCM-41 molecular sieve and the TS-1 microporous titanosilicate. The catalytic test results are correlated with the structural characteristics of the different catalysts. Moreover, for the first time, immersion calorimetry with the same substrate molecule as in the catalytic test reaction is applied as an extra means to interpret the catalytic results. A good correlation between catalytic performance and immersion calorimetry results is found. This work points out that the combination of catalytic testing and immersion calorimetry can lead to important insights into the influence of the materials structural characteristics on catalysis. Moreover, the potential of using immersion calorimetry as a screening tool for catalysts in epoxidation reactions is shown.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.833
Times cited: 19
DOI: 10.1021/la104808v
|