“Introduction to a special issue in honour of W. Owen Saxton, David J. Smith and Dirk Van Dyck on the occasion of their 65th birthdays”. Dunin-Borkowski RE, Lichte H, Tillmann K, Van Aert S, Van Tendeloo G, Ultramicroscopy 134, 1 (2013). http://doi.org/10.1016/j.ultramic.2013.07.013
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2013.07.013
|
“Interpretation of electron diffraction from carbon nanotube bundles presenting precise helicity”. Colomer J-F, Henrard L, Launois P, Van Tendeloo G, Lucas AA, Lambin P, Physical review : B : condensed matter and materials physics 70, 075408 (2004). http://doi.org/10.1103/PhysRevB.70.075408
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 19
DOI: 10.1103/PhysRevB.70.075408
|
“Interplay of doping and structural modulation in superconducting Bi2Sr2-xLaxCuO6+\delta thin films”. Li ZZ, Raffy H, Bals S, Van Tendeloo G, Megtert S, Physical review : B : condensed matter and materials physics 71, 174503 (2005). http://doi.org/10.1103/PhysRevB.71.174503
Abstract: We have studied the evolution of the structural modulation in epitaxial, c-axis-oriented, Bi2Sr2-xLaCuO6+delta thin films when varying the La content x and for a given x as a function of oxygen content. A series of thin films with 0 <= x <= 0.8 has been prepared in situ by rf-magnetron sputtering and characterized by R(T) measurements, Rutherford backscattering spectroscopy, transmission electron microscopy, and x-ray diffraction techniques. The oxygen content of each individual film was varied by thermal annealing across the phase diagram. The evolution of the structural modulation has been thoroughly studied by x-ray diffraction in determining the variation of the amplitude of satellite reflections in special two axes 2 theta/theta-theta scans (reciprocal space scans). It is shown that the amplitude of the modulation along the c axis decreases strongly when x increases from 0 to 0.2. It is demonstrated that this variation is essentially governed by La content x and that changing the oxygen content by thermal treatments has a much lower influence, even becoming negligible for x > 0.2. Such study is important to understand the electronical properties of Bi2Sr2-xLaxCuO6+gamma thin films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 11
DOI: 10.1103/PhysRevB.71.174503
|
“Interplay of atomic displacement in the quantum magnet (CuCI)LaNb2O7”. Tsirlin AA, Abakumov AM, Van Tendeloo G, Rosner H, Physical review : B : condensed matter and materials physics 82, 054107 (2010). http://doi.org/10.1103/PhysRevB.82.054107
Abstract: We report on the crystal structure of the quantum magnet CuClLaNb2O7 that was controversially described with respect to its structural organization and magnetic behavior. Using high-resolution synchrotron powder x-ray diffraction, electron diffraction, transmission electron microscopy, and band-structure calculations, we solve the room-temperature structure of this compound -CuClLaNb2O7 and find two high-temperature polymorphs. The -CuClLaNb2O7 phase, stable above 640 K, is tetragonal with asub=3.889 Å, csub =11.738 Å, and the space group P4/mmm. In the -CuClLaNb2O7 structure, the Cu and Cl atoms are randomly displaced from the special positions along the 100 directions. The phase asub2asubcsub, space group Pbmm and the phase 2asub2asubcsub, space group Pbam are stable between 640 K and 500 K and below 500 K, respectively. The structural changes at 500 and 640 K are identified as order-disorder phase transitions. The displacement of the Cl atoms is frozen upon the → transformation while a cooperative tilting of the NbO6 octahedra in the phase further eliminates the disorder of the Cu atoms. The low-temperature -CuClLaNb2O7 structure thus combines the two types of the atomic displacements that interfere due to the bonding between the Cu atoms and the apical oxygens of the NbO6 octahedra. The precise structural information resolves the controversy between the previous computation-based models and provides the long-sought input for understanding CuClLaNb2O7 and related compounds with unusual magnetic properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 13
DOI: 10.1103/PhysRevB.82.054107
|
“Interlayer structure in YBCO-coated conductors prepared by chemical solution deposition”. Molina L, Egoavil R, Turner S, Thersleff T, Verbeeck J, Holzapfel B, Eibl O, Van Tendeloo G, Superconductor science and technology 26, 075016 (2013). http://doi.org/10.1088/0953-2048/26/7/075016
Abstract: The functionality of YBa2Cu3O7−δ (YBCO)-coated conductor technology depends on the reliability and microstructural properties of a given tape or wire architecture. Particularly, the interface to the metal tape is of interest since it determines the adhesion, mechanical stability of the film and thermal contact of the film to the substrate. A trifluoroacetate (TFA)metal organic deposition (MOD) prepared YBCO film deposited on a chemical solution-derived buffer layer architecture based on CeO2/La2Zr2O7 and grown on a flexible Ni5 at.%W substrate with a {100}⟨001⟩ biaxial texture was investigated. The YBCO film had a thickness was 440 nm and a jc of 1.02 MA cm−2 was determined at 77 K and zero external field. We present a sub-nanoscale analysis of a fully processed solution-derived YBCO-coated conductor by aberration-corrected scanning transmission electron microscopy (STEM) combined with electron energy-loss spectroscopy (EELS). For the first time, structural and chemical analysis of the valence has been carried out on the sub-nm scale. Intermixing of Ni, La, Ce, O and Ba takes place at these interfaces and gives rise to nanometer-sized interlayers which are a by-product of the sequential annealing process. Two distinct interfacial regions were analyzed in detail: (i) the YBCO/CeO2/La2Zr2O7 region (10 nm interlayer) and (ii) the La2Zr2O7/Ni5 at.%W substrate interface region (20 nm NiO). This is of particular significance for the functionality of these YBCO-coated conductor architectures grown by chemical solution deposition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 11
DOI: 10.1088/0953-2048/26/7/075016
|
“Interfacial spin glass state and exchange bias in manganite bilayers with competing magnetic orders”. Ding JF, Lebedev OI, Turner S, Tian YF, Hu WJ, Seo JW, Panagopoulos C, Prellier W, Van Tendeloo G, Wu T, Physical review : B : condensed matter and materials physics 87, 054428 (2013). http://doi.org/10.1103/PhysRevB.87.054428
Abstract: The magnetic properties of manganite bilayers composed of G-type antiferromagnetic (AFM) SrMnO3 and double-exchange ferromagnetic (FM) La0.7Sr0.3MnO3 are studied. A spin-glass state is observed as a result of competing magnetic orders and spin frustration at the La0.7Sr0.3MnO3/SrMnO3 interface. The dependence of the irreversible temperature on the cooling magnetic field follows the Almeida-Thouless line. Although an ideal G-type AFM SrMnO3 is featured with a compensated spin configuration, the bilayers exhibit exchange bias below the spin glass freezing temperature, which is much lower than the Néel temperature of SMO, indicating that the exchange bias is strongly correlated with the spin glass state. The results indicate that the spin frustration that originates from the competition between the AFM super-exchange and the FM double-exchange interactions can induce a strong magnetic anisotropy at the La0.7Sr0.3MnO3/SrMnO3 interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 98
DOI: 10.1103/PhysRevB.87.054428
|
“Interfacial gliding-driven lattice oxygen release in layered cathodes”. Sun C, Liao X, Peng H, Zhang C, Van Tendeloo G, Zhao Y, Wu J, Cell reports physical science 3 (2022). http://doi.org/10.1016/J.XCRP.2021.100695
Abstract: The oxygen release of layered cathodes causes many battery failures, but the underlying mechanism in an actual working cathode is still elusive as it involves secondary agglomerates that introduce complicated boundary structures. Here, we report a general structure instability on the mismatch boundaries driven by interfacial gliding-it introduces a shear stress causing a distortion of the metal-oxygen octahedra framework that reduces its kinetic stability. The migration of cations and diffusion of oxygen vacancies continue to degrade the whole particle from the boundary to the interior, followed by the formation of nano-sized cracks on the fast-degrading interfaces. This work reveals a robust chemical and mechanical interplay on the oxygen release inherent to the intergranular boundaries of layered cathodes. It also suggests that radially patterned columnar grains with low-angle planar boundaries would be an efficient approach to mitigate the boundary oxygen release.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.XCRP.2021.100695
|
“Interface-induced modulation of charge and polarization in thin film Fe3O4”. Tian H, Verbeeck J, Brück S, Paul M, Kufer D, Sing M, Claessen R, Van Tendeloo G, Advanced materials 26, 461 (2014). http://doi.org/10.1002/adma.201303329
Abstract: Charge and polarization modulations in Fe3O4 are controlled by taking advantage of interfacial strain effects. The feasibility of oxidation state control by strain modification is demonstrated and it is shown that this approach offers a stable configuration at room temperature. Direct evidence of how a local strain field changes the atomic coordination and introduces atomic displacements leading to polarization of Fe ions is presented.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 15
DOI: 10.1002/adma.201303329
|
“Interface controlled electronic variations in correlated heterostructures”. Gehrke K, Moshnyaga V, Samwer K, Lebedev OI, Verbeeck J, Kirilenko D, Van Tendeloo G, Physical review : B : condensed matter and materials physics 82, 113101 (2010). http://doi.org/10.1103/PhysRevB.82.113101
Abstract: An interface modification of (LaCa)MnO3-BaTiO3 superlattices was found to massively influence magnetic and magnetotransport properties. Moreover it determines the crystal structure of the manganite layers, changing it from orthorhombic (Pnma) for the conventional superlattice (cSL), to rhombohedral (R3̅ c) for the modified one (mSL). While the cSL shows extremely nonlinear ac transport, the mSL is an electrically homogeneous material. The observations go beyond an oversimplified picture of dead interface layers and evidence the importance of electronic correlations at perovskite interfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 9
DOI: 10.1103/PhysRevB.82.113101
|
“Interface cation migration kinetics induced oxygen release heterogeneity in layered lithium cathodes”. Li C-F, Zhao K, Liao X, Hu Z-Y, Zhang L, Zhao Y, Mu S, Li Y, Li Y, Van Tendeloo G, Sun C, Energy Storage Materials 36, 115 (2021). http://doi.org/10.1016/J.ENSM.2020.12.018
Abstract: The irreversible release of the lattice oxygen in layered cathodes is one of the major degradation mechanisms of lithium ion batteries, which accounts for a number of battery failures including the voltage/capacity fade, loss of cation ions and detachment of the primary particles, etc. Oxygen release is generally attributed to the stepwise thermodynamic controlled phase transitions from the layered to spinel and rock salt phases. Here, we report a strong kinetic effect from the mobility of cation ions, whose migration barrier can be significantly modulated by the phase epitaxy at the degrading interface. It ends up with a clear oxygen release heterogeneity and completely different reaction pathways between the thin and thick areas, as well as the interparticle valence boundaries, both of which widely exist in the mainstream cathode design with the secondary agglomerates. This work unveils the origin of the heterogenous oxygen release in the layered cathodes. It also sheds light on the rational design of cathode materials with enhanced oxygen stability by suppressing the cation migration.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.ENSM.2020.12.018
|
“Insights on growth and nanoscopic investigation of uncommon iron oxide polymorphs”. Carraro G, Maccato C, Bontempi E, Gasparotto A, Lebedev OI, Turner S, Depero LE, Van Tendeloo G, Barreca D, European journal of inorganic chemistry , 5454 (2013). http://doi.org/10.1002/ejic.201300873
Abstract: Si(100)-supported Fe2O3 nanomaterials were developed by a chemical vapor deposition (CVD) approach. The syntheses, which were performed at temperatures between 400 and 550 °C, selectively yielded the scarcely studied β- and ϵ-Fe2O3 polymorphs under O2 or O2 + H2O reaction environments, respectively. Correspondingly, the observed morphology underwent a progressive evolution from interconnected nanopyramids to vertically aligned nanorods. The present study aims to provide novel insights into Fe2O3 nano-organization by a systematic investigation of the system structure/morphology and of their interrelations with growth conditions. In particular, for the first time, the β- and ϵ-Fe2O3 preparation process has been accompanied by a thorough multitechnique investigation, which, beyond X-ray photoelectron spectroscopy (XPS) and field-emission scanning electron microscopy (FESEM), is carried out by X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDXS), atomic force microscopy (AFM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), scanning TEM electron energy-loss spectroscopy (STEM-EELS), and high-angle annular dark-field STEM (HAADF-STEM). Remarkably, the target materials showed a high structural and compositional homogeneity throughout the whole thickness of the nanodeposit. In particular, spatially resolved EELS chemical maps through the spectrum imaging (SI) technique enabled us to gain important information on the local Fe coordination, which is of crucial importance in determining the system reactivity. The described preparation method is in fact a powerful tool to simultaneously tailor phase composition and morphology of iron(III) oxide nanomaterials, the potential applications of which include photocatalysis, magnetic devices, gas sensors, and anodes for Li-ion batteries.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 18
DOI: 10.1002/ejic.201300873
|
“Insight into the growth of multiple branched MnOOH nanorods”. Li Y, Tan H, Lebedev O, Verbeeck J, Biermans E, Van Tendeloo G, Su B-L, Crystal growth &, design 10, 2969 (2010). http://doi.org/10.1021/cg100009k
Abstract: Multiple branched manganese oxide hydroxide (MnOOH) nanorods prepared by a hydrothermal process were extensively studied by transmission electron microscopy (TEM). A model of the branch formation is proposed together with a study of the interface structure. The sword-like tip plays a crucial role for the nanorods to form different shapes. Importantly, the branching occurs at an angle of around either 57 degrees or 123 degrees. Specifically, a (111) twin plane can only be formed at the interface with a 123 degrees angle. The interfaces formed with a 57 degrees angle usually contain edge dislocations. Electron energy loss spectroscopy (EELS) demonstrates that the whole crystal has a uniform chemical composition. Interestingly, an epitaxial growth of Mn3O4 at the radial surface was also observed under electron beam irradiation; this is because of the rough purification of the products. The proposed mechanism is expected to shed light on the branched/dendrite nanostructure growth and to provide opportunities for further novel nanomaterial structure growth and design.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 41
DOI: 10.1021/cg100009k
|
“Inkjet printing multideposited YBCO on CGO/LMO/MgO/Y2O3/Al2O3/Hastelloy tape for 2G-coated conductors”. Roxana Vlad V, Bartolome E, Vilardell M, Calleja A, Meledin A, Obradors X, Puig T, Ricart S, Van Tendeloo G, Usoskin A, Lee S, Petrykin V, Molodyk A, IEEE transactions on applied superconductivity 28, 6601805 (2018). http://doi.org/10.1109/TASC.2018.2808403
Abstract: We present the preparation of a new architecture of coated conductor by Inkjet printing of low fluorine YBa2Cu3O7-x (YBCO) on top of SuperOx tape: CGO/LMO/IBAD-MgO/Y2O3/Al-2 O-3/Hastelloy. A five-layered multideposited, 475-nm-thick YBCO film was structurally and magnetically characterized. A good texture was achieved using this combination of buffer layers, requiring only a 30-nm-thin ion-beam-assisted deposition (IBAD)-MgO layer. The LF-YBCO CC reaches self-field critical current density values of J(c)(GB) similar to NJ 15.9 MA/cm(2) (5 K), similar to 1.23 MA/cm(2) (77 K) corresponding to an I-c (77 K) = 58.4 A/cm-width. Inkjet printing offers a flexible and cost effective method for YBCO deposition, allowing patterning of structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.288
Times cited: 2
DOI: 10.1109/TASC.2018.2808403
|
“Infrared spectra of type laB diamonds”. Woods GS, Kiflawi I, Luyten W, Van Tendeloo G, Philosophical magazine letters 67, 405 (1993). http://doi.org/10.1080/09500839308240950
Abstract: It is shown that the infrared absorption spectra of pure type IaB diamonds, namely those that on cursory examination show only a B one-phonon component and neither A nor D, and the complete absence of a B' localized-mode platelet absorption peak, may be divided into two subgroups. The defect content of specimens of one of these subgroups has been studied before and comprises slip dislocations and voidites in random homogeneous distributions unconnected with the transformation of platelets to dislocation loops. Electron microscopy of a specimen of the other subgroup, which may be recognized by the presence of weak additional one-phonon absorption near 1100 cm-1, shows a population of dislocation loops resulting from the complete transformation of a former platelet population, plus accompanying voidites. It is suggested that the extra absorption is caused by the dislocation loops. Observation of the way in which loops and voidites are distributed suggests that voidite production and platelet transformation may not, after all, be interlinked phenomena, but parallel independent processes both promoted by the same unknown conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.087
Times cited: 5
DOI: 10.1080/09500839308240950
|
“Influence of the synthesis parameters of TiO2-SBA-15 materials on the adsorption and photodegradation of rhodamine-6G”. de Witte K, Busuioc AM, Meynen V, Mertens M, Bilba N, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 110, 100 (2008). http://doi.org/10.1016/j.micromeso.2007.09.035
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 54
DOI: 10.1016/j.micromeso.2007.09.035
|
“Influence of the structure on the properties of NaxEuy(MoO4)z red phosphors”. Morozov VA, Lazoryak BI, Shmurak SZ, Kiselev AP, Lebedev OI, Gauquelin N, Verbeeck J, Hadermann J, Van Tendeloo G, Chemistry of materials 26, 3238 (2014). http://doi.org/10.1021/cm500966g
Abstract: Scheelite related compounds (A',A '')(n)[(B',B '')O-4](m) with B', B '' = W and/or Mo are promising new materials for red phosphors in pc-WLEDs (phosphor-converted white-light-emitting-diode) and solid-state lasers. Cation substitution in CaMoO4 of Ca2+ by the combination of Na+ and Eu3+, with the creation of A cation vacancies, has been investigated as a factor for controlling the scheelite-type structure and the luminescent properties. Na5Eu(MoO4)(4) and NaxEu(2-x)/33+square(2-x)/3MoO4 (0.138 <= x <= 0.5) phases with a scheelite-type structure were synthesized by the solid state method; their structural characteristics were investigated using transmission electron microscopy. Contrary to powder synchrotron X-ray diffraction before, the study by electron diffraction and high resolution transmission electron microscopy in this paper revealed that Na0.286Eu0.571MoO4 has a (3 + 2)D incommensurately modulated structure and that (3 + 2)D incommensurately modulated domains are present in Na0.200Eu0.600MoO4. It also confirmed the (3 + 1)D incommensurately modulated character of Na(0.138)Eu(0.621)Mo04. The luminescent properties of all phases under near-ultraviolet (n-UV) light have been investigated. The excitation spectra of these phosphors show the strongest absorption at about 395 nm, which matches well with the commercially available n-UV-emitting GaN-based LED chip. The emission spectra indicate an intense red emission due to the D-5(0) -> F-7(2) transition of Eu3+, with local minima in the intensity at Na0.286Eu0.571MoO4 and Na0.200Eu0.600MoO4 for similar to 613 nm and similar to 616 nm bands. The phosphor Na5Eu(MoO4)(4) shows the brightest red light emission among the phosphors in the Na2MoO4-Eu2/3MoO4 system and the maximum luminescence intensity of Na5Eu(MoO4)(4) (lambda(ex) = 395 nm) in the D-5(0) -> F-7(2) transition region is close to that of the commercially used red phosphor YVO4:Eu3+ (lambda(ex) = 326 nm). Electron energy loss spectroscopy measurements revealed the influence of the structure and Na/Eu cation distribution on the number and positions of bands in the UV-optical-infrared regions of the EELS spectrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 53
DOI: 10.1021/cm500966g
|
“Influence of the morphology on the magneto-transport properties of laser-ablated ultrathin La0.7Ba0.3MnO3 films”. Das A, Gordon I, Wagner P, Cannaerts M, Moshchalkov VV, Bruynseraede Y, Schuddinck W, Van Tendeloo G, Borghs G, Journal of applied physics 90, 1429 (2001). http://doi.org/10.1063/1.1380217
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 2
DOI: 10.1063/1.1380217
|
“Influence of the microstructure on the high-temperature transport properties of GdBaCo2O5.5+\delta epitaxial films”. Burriel M, Casa-Cabanas M, Zapata J, Tan H, Verbeeck J, Solis C, Roqueta J, Skinner SJ, Kilner JA, Van Tendeloo G, Santiso J, Chemistry of materials 22, 5512 (2010). http://doi.org/10.1021/cm101423z
Abstract: Epitaxial thin films of GdBaCo2O5.5+δ (GBCO) grown by pulsed laser deposition have been studied as a function of deposition conditions. The variation in film structure, domain orientation, and microstructure upon deviations in the cation composition have been correlated with the charge transport properties of the films. The epitaxial GBCO films mainly consist of single- and double-perovskite regions that are oriented in different directions depending on the deposition temperature. Additionally, cobalt depletion induces the formation of a high density of stacking defects in the films, consisting of supplementary GdO planes along the c-axis of the material. The presence of such defects progressively reduces the electrical conductivity. The films closer to the stoichiometric composition have shown p-type electronic conductivity at high pO2 with values as high as 800 S/cm at 330 °C in 1 atm O2, and with a pO2 power dependence with an exponent as low as 1/25, consistent with the behavior reported for bulk GBCO. These values place GBCO thin films as a very promising material to be applied as cathodes in intermediate temperature solid oxide fuel cells.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 17
DOI: 10.1021/cm101423z
|
“Influence of the Ar/O2 ratio on the growth and biaxial alignment of yttria stabilized zirconia layers during reactive unbalanced magnetron sputtering”. Mahieu S, Ghekiere P, de Winter G, Depla D, de Gryse R, Lebedev OI, Van Tendeloo G, Thin solid films : an international journal on the science and technology of thin and thick films 484, 18 (2005). http://doi.org/10.1016/j.tsf.2005.01.021
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 23
DOI: 10.1016/j.tsf.2005.01.021
|
“Influence of substrate tilt angle on the incorporation of BaHfO3 in thick YBa2Cu3O7-&delta, films”. Sieger M, Pahlke P, Ottolinger R, Stafford BH, Lao M, Meledin A, Bauer M, Eisterer M, Van Tendeloo G, Schultz L, Nielsch K, Hühne R, IEEE transactions on applied superconductivity 27, 1 (2016). http://doi.org/10.1109/Tasc.2016.2631587
Abstract: High critical current densities can be realized in high-temperature superconductors such as YBa2Cu3O7-δ (YBCO) by controlling density, shape, size and direction of a secondary phase. Whereas the dependence on the growth rate and deposition temperature has been widely studied as key parameters for nano-engineering the pinning landscape, the vicinal tilt of the substrate surface might have an additional influence. Therefore, we deposited 6 mol% BaHfO3 (BHO) doped YBCO on SrTiO3 (STO) substrates with vicinal angles α between 0° and 40° to identify the influence of the tilt on the growth mode of BHO. An undisturbed epitaxial growth of the superconductor as well as an epitaxial integration of the BHO phase in the YBCO matrix is observed for all vicinal angles investigated. The critical temperature is constant up to α = 20°, whereas the self-field critical current density at 77 K starts to decrease above 10°. A detailed structural analysis of the film cross sections showed that the growth mode of BHO changes already for a vicinal tilt of 2° from a pure c-axis oriented growth to a layered structure with BHO aligned parallel to the YBCO ab-plane. We identified a strong influence of such a microstructure on the current flow in BHO doped YBCO films on STO substrates as well as on MgO based coated conductors prepared by inclined substrate deposition
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.1109/Tasc.2016.2631587
|
“Influence of strain, specimen orientation and background estimation on composition evaluation of InAs/GaAs by TEM”. Rossi EHM, Van Tendeloo G, Rosenauer A, Philosophical magazine 87, 4461 (2007). http://doi.org/10.1080/14786430701551905
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
Times cited: 1
DOI: 10.1080/14786430701551905
|
“Influence of oxygen content on the charge-ordering process in La0.5Ca0.5MnO3”. Schuddinck W, Van Tendeloo G, Martin C, Hervieu M, Raveau B, Journal of alloys and compounds 333, 13 (2002). http://doi.org/10.1016/S0925-8388(01)01691-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 9
DOI: 10.1016/S0925-8388(01)01691-7
|
“Influence of oxygen content on the charge-ordering process in La0.5Ca0.5MnO3”. Schuddinck W, Van Tendeloo G, Martin C, Hervieu M, Raveau B s.l., page 199 (2000).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
“Influence of finite size effects on exchange anisotropy in oxidized Co nanocluster assembled films”. Dobrynin AN, Ievlev DN, Hendrich C, Temst K, Lievens P, Hörmann U, Verbeeck J, Van Tendeloo G, Vantomme A, Physical review : B : condensed matter and materials physics 73, 245416 (2006). http://doi.org/10.1103/PhysRevB.73.245416
Abstract: We compare the magnetic properties of Co cluster assembled films with different degrees of oxidation. Clusters with grain size (2.3 +/- 0.7) nm are produced in a laser vaporization cluster source and soft-landed in ultrahigh vacuum conditions, forming highly porous nanogranular films. After exposure to air for different periods of time, the Co clusters oxidize and the sample may be considered as a thin antiferromagnetic Co oxide matrix containing ferromagnetic Co clusters. Magnetization measurements were performed in a temperature range from 300 down to 5 K, at applied magnetic fields up to 30 kOe. The exchange bias value at 5 K for the strongly oxidized sample is 4.8 kOe against the value of 0.75 kOe for the less oxidized sample. The mean values of the thicknesses of the Co oxide layers are estimated to be 0.6 and 0.3 nm for the more and less oxidized sample, respectively. We propose a method of measuring the exchange bias inducing temperature, i.e., the temperature at which exchange anisotropy is established. We determined the mean inducing temperatures for both samples, which are 55 and 25 K, respectively, for the more and less oxidized samples. Both temperatures are well below the bulk CoO Neel temperature of 292 K. A low value of the inducing temperature of the Co oxide layer is a consequence of its subnanometer thickness, while a large exchange bias value is a consequence of different dimensionality of Co clusters and Co oxide matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 17
DOI: 10.1103/PhysRevB.73.245416
|
“Influence of defect distribution on the reducibility of CeO2-x nanoparticles”. Spadaro MC, Luches P, Bertoni G, Grillo V, Turner S, Van Tendeloo G, Valeri S, D'Addato S, Nanotechnology 27, 425705 (2016). http://doi.org/10.1088/0957-4484/27/42/425705
Abstract: Ceria nanoparticles (NPs) are fundamental in heterogeneous catalysis because of their ability to store or release oxygen depending on the ambient conditions. Their oxygen storage capacity is strictly related to the exposed planes, crystallinity, density and distribution of defects. In this work a study of ceria NPs produced with a ligand-free, physical synthesis method is presented. The NP films were grown by a magnetron sputtering based gas aggregation source and studied by high resolution- and scanning-transmission electron microscopy and x-ray photoelectron spectroscopy. In particular, the influence of the oxidation procedure on the NP reducibility has been investigated. The different reducibility has been correlated to the exposed planes, crystallinity and density and distribution of structural defects. The results obtained in this work represent a basis to obtain cerium oxide NP with desired oxygen transport properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 11
DOI: 10.1088/0957-4484/27/42/425705
|
“Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates”. Pahlke P, Sieger M, Ottolinger R, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Haenisch J, Holzapfel B, Schultz L, Nielsch K, Huehne R, Superconductor science and technology 31, 044007 (2018). http://doi.org/10.1088/1361-6668/AAAFBE
Abstract: Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I-c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 mu m using pulsed laser deposition with a growth rate of about 1.2 nm s(-1). Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O-6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 mu m, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J(c) of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I-c increases up to a thickness of 5 mu m. A comparison between films with a thickness of 1.3 mu m revealed that the anisotropy of the critical current density J(c)(theta) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B vertical bar vertical bar c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J(c) values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 9
DOI: 10.1088/1361-6668/AAAFBE
|
“Influence of 4H-SiC substrate miscut on the epitaxy and microstructure of AlGaN/GaN heterostructures”. Gkanatsiou A, Lioutas CB, Frangis N, Polychroniadis EK, Prystawko P, Leszczynski M, Altantzis T, Van Tendeloo G, Materials science in semiconductor processing 91, 159 (2019). http://doi.org/10.1016/j.mssp.2018.11.008
Abstract: AlGaN/GaN heterostructures were grown on “on-axis” and 2° off (0001) 4H-SiC substrates by metalorganic vapor phase epitaxy (MOVPE). Structural characterization was performed by transmission electron microscopy. The dislocation density, being greater in the on-axis case, is gradually reduced in the GaN layer and is forming
dislocation loops in the lower region. Steps aligned along [11̅00] in the off-axis case give rise to simultaneous defect formation. In the on-axis case, an almost zero density of steps is observed, with the main origin of defects probably being the orientation mismatch at the grain boundaries between the small not fully coalesced AlN grains. V-shaped formations are observed in the AlN nucleation layer, but are more frequent in the off-axis case, probably enhanced by the presence of steps. These V-shaped formations are completely overgrown by the GaN layer, during the subsequent deposition, presenting AlGaN areas in the walls of the defect, indicating an interdiffusion between the layers. Finally, at the AlGaN/GaN heterostructure surface in the on-axis case, V-shapes are observed, with the AlN spacer and AlGaN (21% Al) thickness on relaxed GaN exceeding the critical thickness for relaxation. On the other hand, no relaxation in the form of V-shape creation is observed in the off-axis case, probably due to the smaller AlGaN thickness (less than 21% Al). The AlN spacer layer, grown in between the heterostructure, presents a uniform thickness and clear interfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.359
Times cited: 1
DOI: 10.1016/j.mssp.2018.11.008
|
“Inferred phase relations in part of the system Au-Ag-Te: an integrated analytical study of gold ore from the Golden Mile, Kalgoorlie, Australia”. Bindi L, Rossell MD, Van Tendeloo G, Spry PG, Cipriani C, Mineralogy and petrology 83, 283 (2005). http://doi.org/10.1007/s00710-004-0065-1
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.236
Times cited: 15
DOI: 10.1007/s00710-004-0065-1
|
“Inducing superconductivity and structural transformations by fluorination of reduced YBCO”. Shpanchenko RV, Rozova MG, Abakumov AM, Ardashnikova EI, Kovba ML, Putilin SN, Antipov EV, Lebedev OI, Van Tendeloo G, Physica: C : superconductivity 280, 272 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 35
|
“Incorporation of pure fullerene into organoclays : towards C60-pillared clay structures”. Tsoufis T, Georgakilas V, Ke X, Van Tendeloo G, Rudolf P, Gournis D, Chemistry: a European journal 19, 7937 (2013). http://doi.org/10.1002/chem.201300164
Abstract: In this work, we demonstrate the successful incorporation of pure fullerene from solution into two-dimensional layered aluminosilicate minerals. Pure fullerenes are insoluble in water and neutral in terms of charge, hence they cannot be introduced into the clay galleries by ion exchange or intercalation from water solution. To overcome this bottleneck, we organically modified the clay with quaternary amines by using well-established reactions in clay science in order to expand the interlayer space and render the galleries organophilic. During the reaction with the fullerene solution, the organic solvent could enter into the clay galleries, thus transferring along the fullerene molecules. Furthermore, we demonstrate that the surfactant molecules, can be selectively removed by either simple ion-exchange reaction (e.g., interaction with Al(NO3)3 solution to replace the surfactant molecules with Al3+ ions) or thermal treatment (heating at 350 °C) to obtain novel fullerene-pillared clay structures exhibiting enhanced surface area. The synthesized hybrid materials were characterized in detail by a combination of experimental techniques including powder X-ray diffraction, transmission electron microscopy, X-ray photoemission, and UV/Vis spectroscopy as well as thermal analysis and nitrogen adsorptiondesorption measurements. The reported fullerene-pillared clay structures constitute a new hybrid system with very promising potential for the use in areas such as gas storage and/or gas separation due to their high surface area.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 3
DOI: 10.1002/chem.201300164
|