“Atomic structure of alloys close to phase transitions”. Van Tendeloo G, Schryvers D, Nucleation and growth processes in materials 580, 283 (2000)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Atomic-scale investigation of the heterogeneous precipitation in the E (Al₁₈Mg₃Cr₂) dispersoid of 7075 aluminum alloy”. Ding L, Zhao L, Weng Y, Schryvers D, Liu Q, Idrissi H, Journal Of Alloys And Compounds 851, 156890 (2021). http://doi.org/10.1016/J.JALLCOM.2020.156890
Abstract: The heterogeneous precipitation of the eta (MgZn2) phase on the E (Al18Mg3Cr2) dispersoids of the 7075 aluminum alloy was systematically investigated by atomic resolution high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX). It is found that coarse B particles are heterogeneously precipitated at the E particle interface after water quenching and isothermal aging at 120 degrees C. The incoherent E/Al interface is responsible for the high tendency of heterogeneous precipitation of the B phase. Two different orientation relationships (ORs) between the eta, E and Al matrix are identified: OR1 [2 (11) over bar0](eta)[011](E)//[(1) over bar 12](Al), (01 (1) over bar0)(eta)//(13 (3) over bar)(E)//(201)(Al), OR2 [(1) over bar 12](E)//[0001](eta)//[011](Al), (01 (1) over bar0 )(eta)//(220)(E)//(34 (4) over bar)(Al). The eta phase is preferential to nucleate along the {111}(E) or the {220}(E) planes, depending on its OR. The heterogeneous nucleation of B phase on the E particle could stabilize the E/Al interface by introducing a coherent E/eta interface, which increases the drive force of heterogeneous precipitation. The reorientation of eta phase and mutual diffusion of solute atoms could assist the coherency of the E/eta interface. The present results suggest that increasing the coherency of the E/Al interface is a promising method to suppress the heterogeneous precipitation of the eta phase. (C) 2020 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
DOI: 10.1016/J.JALLCOM.2020.156890
|
|
|
“Atomic-scale viscoplasticity mechanisms revealed in high ductility metallic glass films”. Idrissi H, Ghidelli M, Béché, A, Turner S, Gravier S, Blandin J-J, Raskin J-P, Schryvers D, Pardoen T, Scientific reports 9, 13426 (2019). http://doi.org/10.1038/s41598-019-49910-7
Abstract: The fundamental plasticity mechanisms in thin freestanding Zr65Ni35 metallic glass films are investigated in order to unravel the origin of an outstanding strength/ductility balance. The deformation process is homogenous until fracture with no evidence of catastrophic shear banding. The creep/relaxation behaviour of the films was characterized by on-chip tensile testing, revealing an activation volume in the range 100–200 Å3. Advanced high-resolution transmission electron microscopy imaging and spectroscopy exhibit a very fine glassy nanostructure with well-defined dense Ni-rich clusters embedded in Zr-rich clusters of lower atomic density and a ~2–3 nm characteristic length scale. Nanobeam electron diffraction analysis reveals that the accumulation of plastic deformation at roomtemperature
correlates with monotonously increasing disruption of the local atomic order. These results provide experimental evidences of the dynamics of shear transformation zones activation in metallic glasses. The impact of the nanoscale structural heterogeneities on the mechanical properties including the rate dependent behaviour is discussed, shedding new light on the governing plasticity mechanisms in metallic glasses with initially heterogeneous atomic arrangement.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
DOI: 10.1038/s41598-019-49910-7
|
|
|
“Atomistic structure of Cu-containing \beta", precipitates in an Al-Mg-Si-Cu alloy”. Li K, Béché, A, Song M, Sha G, Lu X, Zhang K, Du Y, Ringer SP, Schryvers D, Scripta materialia 75, 86 (2014). http://doi.org/10.1016/j.scriptamat.2013.11.030
Abstract: The beta '' precipitates in a peak-aged Al-Mg-Si-Cu alloy were measured with an average composition of 28.6Al-38.7Mg-26.5Si-5.17Cu (at.%) using atom probe tomography. High-angle annular dark-field observations revealed that Cu incompletely substitutes for the Mg-1 and Si-3 columns, preferentially for one column in each pair of Si-3. Cu-free Si columns form a parallelogram-shaped network that constitutes the basis of subsequent precipitates in the system, with a = 0.37 nm, b = 0.38 nm, gamma = 113 degrees and c = 0.405 nm. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 22
DOI: 10.1016/j.scriptamat.2013.11.030
|
|
|
“Austenite and martensite microstructures in splat-cooled Ni-Al”. Schryvers D, Holland-Moritz D, Intermetallics 6, 427 (1998). http://doi.org/10.1016/S0966-9795(97)00091-5
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 13
DOI: 10.1016/S0966-9795(97)00091-5
|
|
|
“Bending martensite needles in Ni65Al35 investigated by two-dimensional elasticity and high-resolution transmission electron microscopy”. Boullay P, Schryvers D, Kohn RV, Physical review : B : condensed matter and materials physics 64, 144105 (2001). http://doi.org/10.1103/PhysRevB.64.144105
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 18
DOI: 10.1103/PhysRevB.64.144105
|
|
|
“Cavity nucleation and growth in Cu-Zn-Al irradiated with Cu+ ions at different temperatures”. Zelaya E, Schryvers D, Tolley A, Fitchner PFP, Intermetallics 18, 493 (2010). http://doi.org/10.1016/j.intermet.2009.09.010
Abstract: The effects of high dose ion irradiation in β CuZnAl were investigated between room temperature and 150 °C. Single crystal samples with surface normal close to [001]β were irradiated with 300 keV Cu+ ions. Microstructural changes were characterized using transmission electron microscopy. Irradiation induced cavities located on the surface exposed to the irradiation were observed. The morphology, size and density distribution of these cavities were analyzed as a function of different irradiation conditions. The shape and location of the cavities with respect to the irradiation surface were not affected by irradiation temperature or irradiation dose. Instead, the cavity size distribution showed a bi-modal shape for a dose of 15 dpa, regardless of irradiation temperature. For a dose of 30 dpa the bi-modal distribution was only observed after room temperature irradiation. The diffusion effects of vacancies produced by irradiation are analyzed in shape memory CuZnAl alloys, which main characteristic is the diffusionless martensitic transformation. Particularly, the cavity size distributions were analyzed in terms of nucleation, growth and coalescence.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 1
DOI: 10.1016/j.intermet.2009.09.010
|
|
|
“Characterization of (Ti,Mo,Cr)C nanoprecipitates in an austenitic stainless steel on the atomic scale”. Cautaerts N, Delville R, Stergar E, Schryvers D, Verwerft M, Acta materialia 164, 90 (2019). http://doi.org/10.1016/j.actamat.2018.10.018
Abstract: Nanometer sized (Ti,Mo,Cr)C (MX-type) precipitates that grew in a 24% cold worked Ti-stabilized austenitic stainless steel (grade DIN 1.4970, member of the 15-15Ti austenitic stainless steels) after heat treatment were fully characterized with transmission electron microscopy (TEM), probe corrected high angle annular dark field scanning transmission electron microscopy (HR-HAADF STEM), and atom probe tomography (APT). The precipitates shared the cube-on-cube orientation with the matrix and were facetted on {111} planes, yielding octahedral and elongated octahedral shapes. The misfit dislocations were believed to have Burgers vectors a/6<112> which was verified by geometrical phase analysis (GPA) strain mapping of a matrix-precipitate interface. The dislocations were spaced five to seven atomic
planes apart, on average slightly wider than expected for the lattice parameters of steel and TiC. Quantitative atom probe tomography analysis of the precipitates showed that precipitates were significantly enriched in Mo, Cr and V, and that they were hypostoichiometric with respect to C. These findings were consistent with a reduced lattice parameter. The precipitates were found primarily on Shockley
partial dislocations originating from the original perfect dislocation network. These novel findings could contribute to the understanding of how TiC nanoprecipitates interact with point defects and matrix dislocations. This is essential for the application of these Ti-stabilized steels in high temperature environments or fast spectrum nuclear fission reactors.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 2
DOI: 10.1016/j.actamat.2018.10.018
|
|
|
“Characterization of crystal defects and analysis of iodide distribution in mixed tabular silver halide grains by conventional transmission electron microscopy, X-ray diffractometry and back-scattered electron imaging”. Goessens C, Schryvers D, van Landuyt J, Amelinckx S, Geuens I, Gijbels R, Jacob W, Verbeeck A, de Keyzer R, (1991)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
|
|
|
“Characterization of crystal defects in mixed tabular silver halide grains by conventional transmission electron microscopy and X-ray diffractometry”. Goessens C, Schryvers D, van Landuyt J, Amelinckx S, Verbeeck A, de Keyzer R, Journal of crystal growth 110, 930 (1991)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.698
Times cited: 40
|
|
|
“Characterization of IASCC crack tips extracted from neutron-irradiated flux thimble tube specimens in view of a probabilistic fracture model”. Penders AG, Konstantinović, MJ, Van Renterghem W, Bosch R-W, Schryvers D, Somville F, Journal of nuclear materials 571, 154015 (2022). http://doi.org/10.1016/J.JNUCMAT.2022.154015
Abstract: This study reports the properties of irradiation assisted stress corrosion crack tips extracted by means of focused-ion beam from 60 to 80 dpa neutron-irradiated O-ring specimens tested under straining conditions under a pressurized-water reactor environment. Various crack tip morphologies and surrounding deformation features were analyzed as a function of applied stress, surface oxidation state and loading form – constant versus cyclic. All investigated cracks exhibit grain boundary oxidation in front of the crack tip, with the extent of oxidation being proportional to applied stress. These findings clearly demonstrate that, under the subcritical crack propagation regime, the grain boundary oxide grows faster than the crack. On the other hand, crack tips appertaining to specimens with removed oxide layer at the outer surface show comparatively less oxidation at the crack tip, which could indicate towards crack initiation from regions that exemplify lower stress, such as the O-ring inner surface. Cyclic loading is found to have a more pronounced effect on the crack tip microstructure, demonstrating increased deformation twinning and -martensitic transformation, which signifies towards an increased susceptibility to intergranular failure. Still, the extent of crack tip grain boundary oxidation in this case agrees well with expected values for maximum stress applied during cyclic loading. All results are interpreted based on the probabilistic subcritical crack propagation mechanism and provide strong support to a stress-driven internal oxidation model.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1016/J.JNUCMAT.2022.154015
|
|
|
“Characterization of nickel silicides using EELS-based methods”. Verleysen E, Bender H, Richard O, Schryvers D, Vandervorst W, Journal of microscopy 240, 75 (2010). http://doi.org/10.1111/j.1365-2818.2010.03391.x
Abstract: The characterization of Ni-silicides using electron energy loss spectroscopy (EELS) based methods is discussed. A series of Ni-silicide phases is examined: Ni3Si, Ni31Si12, Ni2Si, NiSi and NiSi2. The composition of these phases is determined by quantitative core-loss EELS. A study of the low loss part of the EELS spectrum shows that both the energy and the shape of the plasmon peak are characteristic for each phase. Examination of the Ni-L edge energy loss near edge structure (ELNES) shows that the ratio and the sum of the L2 and L3 white line intensities are also characteristic for each phase. The sum of the white line intensities is used to determine the trend in electron occupation of the 3d states of the phases. The dependence of the plasmon energy on the electron occupation of the 3d states is demonstrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.692
Times cited: 11
DOI: 10.1111/j.1365-2818.2010.03391.x
|
|
|
“Composition gradients surrounding Ni4Ti3 precipitates in a NiTi alloy studied by EELS, EFTEM and EDX”. Yang Z, Schryvers D, International journal of applied electromagnetics and mechanics 23, 17 (2006)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.769
|
|
|
“Compositional characterization of nickel silicides by HAADF-STEM imaging”. Verleysen E, Bender H, Richard O, Schryvers D, Vandervorst W, Journal of materials science 46, 2001 (2011). http://doi.org/10.1007/s10853-010-5191-z
Abstract: A methodology for the quantitative compositional characterization of nickel silicides by high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) imaging is presented. HAADF-STEM images of a set of nickel silicide reference samples Ni3Si, Ni31Si12, Ni2Si, NiSi and NiSi2 are taken at identical experimental conditions. The correlation between sample thickness and HAADF-STEM intensity is discussed. In order to quantify the relationship between the experimental Z-contrast intensities and the composition of the analysed layers, the ratio of the HAADF-STEM intensity to the sample thickness or to the intensity of the silicon substrate is determined for each nickel silicide reference sample. Diffraction contrast is still detected on the HAADF-STEM images, even though the detector is set at the largest possible detection angle. The influence on the quantification results of intensity fluctuations caused by diffraction contrast and channelling is examined. The methodology is applied to FUSI gate devices and to horizontal TFET devices with different nickel silicides formed on source, gate and drain. It is shown that, if the elements which are present are known, this methodology allows a fast quantitative 2-dimensional compositional analysis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 1
DOI: 10.1007/s10853-010-5191-z
|
|
|
“Conventional and HREM study of structural defects in nanostructured silver halides”. Schryvers D, Goessens C, van Renterghem W, van Landuyt J, de Keyzer R, , 1 (1998)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses”. Penders A, Konstantinovic MJ, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology , 1 (2020). http://doi.org/10.1080/1478422X.2020.1785651
Abstract: Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.8
Times cited: 1
DOI: 10.1080/1478422X.2020.1785651
|
|
|
“Critical assessments and thermodynamic modeling of BaO-SiO2 and SiO2-TiO2 systems and their extensions into liquid immiscibility in the BaO-SiO2-TiO2 system”. Boulay E, Nakano J, Turner S, Idrissi H, Schryvers D, Godet S, Calphad computer coupling of phase diagrams and thermochemistry 47, 68 (2014). http://doi.org/10.1016/j.calphad.2014.06.004
Abstract: This study discusses rational reproduction of liquid immiscibility in the BaO-SiO2-TiO2 system. While a ternary assessment requires sub-binary descriptions in the same thermodynamic model, the related sub-binary systems BaO-SiO2, BaO-TiO2 and SiO2-TiO2 liquid and solid phases have been evaluated using different thermodynamic models in the literature. In this study, BaO-SiO2 and SiO2-TiO2 were assessed using the Ionic Two Sublattice model (I2SL) based on experimental data from the literature. BaO-TiO2 was already assessed using this model. Binary descriptions developed were then used for the assessment of liquid immiscibility in the BaO-SiO2-TiO2 system. Ternary interaction parameters were found necessary for rational reproduction of the new ternary experimental data gathered in the present work. The model parameters for each system were evaluated using a CAPLHAD approach. A set of parameters is proposed. They show good agreement between the calculated and experimental equilibrium liquidus, liquid immiscibility and thermochemical properties in the BaO-SiO2-TiO2 system. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.6
Times cited: 9
DOI: 10.1016/j.calphad.2014.06.004
|
|
|
“Cross-section transmission electron microscopy characterization of the near-surface structure of medical Nitinol superelastic tubing”. Potapov PL, Tirry W, Schryvers D, Sivel VGM, Wu M-Y, Aslanidis D, Zandbergen H, Journal of materials science: materials in medicine 18, 483 (2007). http://doi.org/10.1007/s10856-007-2008-y
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.325
Times cited: 14
DOI: 10.1007/s10856-007-2008-y
|
|
|
“Datasets for the analysis of dislocations at grain boundaries and during vein formation in cyclically deformed Ni micropillars”. Sandfeld S, Samaee V, Idrissi H, Groten J, Pardoen T, Schwaiger R, Schryvers D, Data in Brief 27, 104724 (2019). http://doi.org/10.1016/J.DIB.2019.104724
Abstract: The dataset together with the corresponding Python scripts and Jupyter notebooks presented in this article are supplementary data for the work presented in Samaee et al., 2019 [1]. The data itself consists of two parts: the simulation data that was used in [1] to analyze the effect of a particular grain boundary on curved dislocations and the precession electron diffraction (PED) strain maps together with post-processed data for analyzing details of the observed dislocation vein structures. Additionally, the complete stress tensor components, which are not shown in [1], have also been included. The data sets are accompanied by Python code explaining the file formats and showing how to post-process the data. (c) 2019 The Author(s). Published by Elsevier Inc. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.DIB.2019.104724
|
|
|
“Deciphering the interactions between single arm dislocation sources and coherent twin boundary in nickel bi-crystal”. Samaee V, Dupraz M, Pardoen T, VAn Swygenhoven H, Schryvers D, Idrissi H, Nature Communications 12, 962 (2021). http://doi.org/10.1038/S41467-021-21296-Z
Abstract: The introduction of a well-controlled population of coherent twin boundaries (CTBs) is an attractive route to improve the strength ductility product in face centered cubic (FCC) metals. However, the elementary mechanisms controlling the interaction between single arm dislocation sources (SASs), often present in nanotwinned FCC metals, and CTB are still not well understood. Here, quantitative in-situ transmission electron microscopy (TEM) observations of these mechanisms under tensile loading are performed on submicron Ni bi-crystal. We report that the absorption of curved screw dislocations at the CTB leads to the formation of constriction nodes connecting pairs of twinning dislocations at the CTB plane in agreement with large scale 3D atomistic simulations. The coordinated motion of the twinning dislocation pairs due to the presence of the nodes leads to a unique CTB sliding mechanism, which plays an important role in initiating the fracture process at a CTB ledge. TEM observations of the interactions between non-screw dislocations and the CTB highlight the importance of the synergy between the repulsive force of the CTB and the back stress from SASs when the interactions occur in small volumes. Interactions of dislocations with coherent twin boundaries contribute to strength and ductility in metals, but investigating the interaction mechanisms is challenging. Here the authors unravel these mechanisms through quantitative in-situ transmission electron microscopy observations in nickel bi-crystal samples under tensile loading.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
DOI: 10.1038/S41467-021-21296-Z
|
|
|
“Decomposition of a metastable bcc phase in rapidly solidified Ni-9 at.% Zr and Ni-8 at.%X alloys”. Chandrasekaran M, Ghosh G, Schryvers D, de Graef M, Delaey L, Van Tendeloo G, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 75, 677 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
|
|
|
“Decomposition phenomena in Ni-Mn-Ti austenite”. Schryvers D, Seo JW, Richard O, Vermeulen W, Potapov P s.l., page 887 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Dedicated TEM on domain boundaries from phase transformations and crystal growth”. Schryvers D, Van Aert S, Delville R, Idrissi H, Turner S, Salje EKH, Phase transitions 86, 15 (2013). http://doi.org/10.1080/01411594.2012.694435
Abstract: Investigating domain boundaries and their effects on the behaviour of materials automatically implies the need for detailed knowledge on the structural aspects of the atomic configurations at these interfaces. Not only in view of nearest neighbour interactions but also at a larger scale, often surpassing the unit cell, the boundaries can contain structural elements that do not exist in the bulk. In the present contribution, a number of special boundaries resulting from phase transformations or crystal growth and those recently investigated by advanced transmission electron microscopy techniques in different systems will be reviewed. These include macrotwins between microtwinned martensite plates in NiAl, austenite-single variant martensite habit planes in low hysteresis NiTiPd, nanotwins in non-textured nanostructured Pd and ferroelastic domain boundaries in CaTiO3. In all discussed cases these boundaries play an essential role in the properties of the respective materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.06
DOI: 10.1080/01411594.2012.694435
|
|
|
“Defect induced thickness growth in silver chloride (111) tabular crystals: a TEM study”. Van Renterghem W, Schryvers D, van Landuyt J, Bollen D, Van Roost C, De Keyzer RB, , 38 (2000)
Abstract: Defects in AgG tabular crystals with {111} surfaces are characterised by transmission electron microscopy (TEM) and their influence on the growth process is discussed. In the tabular crystals, twins parallel to the tabular face as well as dislocations along different directions are observed. The twins induce the tabular growth, while the dislocations do not influence the morphology. In 10 to 30% of the crystals that have been characterised, thickness growth is observed and it is shown that in all cases twins on other planes than the tabular ones are present. Two configurations occur more frequently and are analysed in detail. For the first group, twins parallel to the tabular face as well as a microtwin along a non-parallel {111} plane and ending inside the crystal are present. In the crystals of the second group only one extra non-parallel twin occurs giving rise to a bicrystal built up by a tetrahedral shaped part and a flat triangular or trapezoidal part. More complex twin configurations give rise to various, less characteristic morphologies.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
|
|
|
“Defect related growth of tabular AgCl(100) crystals: a TEM study”. van Renterghem W, Schryvers D, van Landuyt J, van Roost C, , 389 (1998)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Defect structures in CuZr martensite, studies by CTEM and HRTEM”. Seo JW, Schryvers D, Journal de physique: 4 C5, 149 (1997). http://doi.org/10.1051/jp4:1997523
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/jp4:1997523
|
|
|
“Defects and growth mechanisms of AgCl(100) tabular crystals”. van Renterghem W, Goessens C, Schryvers D, van Landuyt J, Verrept P, Bollen D, van Roost C, de Keyzer R, Journal of crystal growth 187, 410 (1998). http://doi.org/10.1016/S0022-0248(98)00004-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 8
DOI: 10.1016/S0022-0248(98)00004-9
|
|
|
“Defects in AgCl and AgBr(100) tabular crystals studied by TEM”. van Renterghem W, Goessens C, Schryvers D, van Landuyt J, Verrept P, Bollen D, van Roost C, de Keyzer R, , 6 (1998)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Demonstration of lanthanum in liver cells by energy-dispersive X-ray spectroscopy, electron energy loss spectroscopy and high-resolution transmission electron microscopy”. Yang Z, Schryvers D, Roels F, d' Haese PC, de Broe ME, Journal of microscopy 223, 133 (2006). http://doi.org/10.1111/j.1365-2818.2006.01601.x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Pathophysiology
Impact Factor: 1.692
Times cited: 29
DOI: 10.1111/j.1365-2818.2006.01601.x
|
|
|
“Determination of the atomic width of an APB in ordered CoPt using quantified HAADF-STEM”. Akamine H, Van den Bos KHW, Gauquelin N, Farjami S, Van Aert S, Schryvers D, Nishida M, Journal of alloys and compounds 644, 570 (2015). http://doi.org/10.1016/j.jallcom.2015.04.205
Abstract: Anti-phase boundaries (APBs) in an ordered CoPt alloy are planar defects which disturb the ordered structure in their vicinity and decrease the magnetic properties. However, it has not yet been clarified to what extend the APBs disturb the ordering. In this study, high-resolution HAADF-STEM images are statistically analysed based on the image intensities estimated by the statistical parameter estimation theory. In the procedure, averaging intensities, fitting the intensity profiles to specific functions, and assessment based on a statistical test are performed. As a result, the APBs in the stable CoPt are found to be characterised by two atomic planes, and a contrast transition range as well as the centre of an inclined APB is determined. These results show that the APBs are quite sharp and therefore may have no notable effect on the net magnetic properties due to their small volume fraction. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 12
DOI: 10.1016/j.jallcom.2015.04.205
|
|