Abstract: Functionalization of photocatalytic metal oxide nanoparticles of TiO 2 , ZnO, WO 3 and CuO with amine‐terminated (oleylamine) and thiol‐terminated (1‐dodecanethiol) alkyl chained ligands was studied under ambient conditions. A high selectivity was observed in the binding specificity of a ligand towards nanoparticles of these different oxides. It was observed that oleylamine binds stably to only TiO 2 and WO 3 , while 1‐dodecanethiol binds stably only to ZnO and CuO. Similarly, polar to non‐polar solvent phase transfer of TiO 2 and WO 3 nanoparticles could be achieved by using oleylamine, but not by 1‐dodecanethiol, while the contrary holds for ZnO and CuO. The surface chemistry of ligand functionalized nanoparticles was probed by ATR‐FTIR spectroscopy, that enabled to elucidate the occupation of the ligands at the active sites. The photo‐stability of the ligands on the nanoparticle surface was determined by the photocatalytic self‐cleaning properties of the material. While TiO 2 and WO 3 degrade the ligands within 24 hours under both UV and visible light, ligands on ZnO and CuO remain unaffected. The gathered insights are also highly relevant from an application point of view. As an example, since the ligand functionalized nanoparticles are hydrophobic in nature, they can thus be self‐assembled at the air‐water interface, for obtaining nanoparticle films with demonstrated photocatalytic as well as anti‐fogging properties.

Abstract: Rh-based structured catalysts for the Catalytic Partial Oxidation of CH4 to syngas were prepared by electrosynthesis of Rh/Mg/Al hydrotalcite-type compounds on FeCrAlloy foams and calcination. The effects of Rh content, total metal concentration, and partial replacement of Mg2+ by Ni2+ in the electrolytic solution on coating thickness, Rh speciation, metallic particle size, and catalytic activity were investigated by SEM/EDS, mu-XRF/XANES and tests under diluted and concentrated reaction conditions. The amount of Rh species, present as Mg (RhxAl1-x)(2)O-4, depended on the thickness of the electrosynthesised layer as well as the Rh particle size and dispersion. Smaller and more dispersed particles were obtained by decreasing the Rh concentration in the electrolytic solution from Rh/Mg/Al=11/70/19 to 5/70/25 and 2/70/28 atomic ratio% (a.r.%) and in thinner rather than thicker layers. Despite the improvement in metallic particles features, the CH4 conversion was negatively affected by the low amount of active sites in the coating, the high metal support interaction and possibly the oxidation of metallic particles and carbon formation. A larger amount of solid containing well dispersed Rh particles was deposited by increasing the total metal concentration from 0.03 M to 0.06 M with the Rh/Mg/Al=5/70/25 a.r.%, and the catalytic performances were enhanced. The partial replacement of Mg2+ by Ni2+ gave rise to a very active bimetallic Rh/Ni catalyst, CH4 conversion and selectivity to syngas were above 90%, however, it slightly deactivated with time-on-stream. (C) 2015 Elsevier B.V. All rights reserved.

Abstract: Historical glass, especially medieval glass, can undergo weathering under the influence of time and environmental conditions. The aim of this investigation was to better understand the processes involved in this natural degradation process by studying artificially altered glass samples prepared for the use of evaluation of conservation methods. Non-durable glass sensors produced by the Fraunhofer Institute (type M1.0) were used as a starting material for artificial alteration. These were immersed in acidic (pH = 0, 2, 4) and neutral solutions (1 h – 8 h). In a second stage the glass samples were immersed in a 0.5 M MnCl2 solution (24 h, 48 h and 72 h), allowing intrusion of Mn from the solution into the gel layer. The samples were characterized at different stages with reflectance FTIR spectroscopy, mu XRF mapping and mu XANES. All measurements were carried out at ESRF, beamline ID21. Reflectance FTIR spectroscopy measurements were performed in the 800 4000 cm(-1) range. Cluster analysis of the resulting maps evidenced the rapid growth of the gel layer in strong acidic conditions. The average spectra for each cluster feature show for the original glass a strong Si-O- stretching band between 900 and 1000 cm(-1), whereas the gel layer could be identified by the increasing Si-O-Si bands around 1100 and 1250 cm(-1). mu XRF maps were recorded at different stages of the experiment at energies around the Mn-K edge (6.539 keV) and with a step size of 2 by 2 m. These confirm the leaching of K+ and Ca+2 from the glass and the intrusion of Mn from the solution. Mn was found throughout the entire gel layer, but with a concentration gradient peaking at the surface. XANES point measurements were recorded at various points where Mn was present. No spatial variation was found, but linear combination fitting of the spectra with various Mn reference compounds indicated that Mn2+Mn23+O4 is the main Mn compound in the gel layer, as was hypothesised by Watkinson et al. The standard corroded glass samples studied here can be used for the evaluation of conservation treatments in follow-up experiments. (C) 2013 The Authors. Published by Elsevier B.V. Selection and peer-review under responsibility of the IA-CS (Italian Association of Conservation Scientists) and University of Antwerp

Abstract: Micro-and nanoscopic X-ray techniques were used to investigate the relationship between uranium (U) tissue distributions and adverse effects to the digestive tract of aquatic model organism Daphnia magna following uranium nanoparticle (UNP) exposure. X-ray absorption computed tomography measure-ments of intact daphnids exposed to sublethal concentrations of UNPs or a U reference solution (URef) showed adverse morphological changes to the midgut and the hepatic ceca. Histological analyses of exposed organisms revealed a high proportion of abnormal and irregularly shaped intestinal epithelial cells. Disruption of the hepatic ceca and midgut epithelial tissues implied digestive functions and intestinal barriers were compro-mised. Synchrotron-based micro X-ray fluorescence (XRF) elemental mapping identified U co-localized with morphological changes, with substantial accumulation of U in the lumen as well as in the epithelial tissues. Utilizing high-resolution nano-XRF, 400-1000 nm sized U particulates could be identified throughout the midgut and within hepatic ceca cells, coinciding with tissue damages. The results highlight disruption of intestinal function as an important mode of action of acute U toxicity in D. magna and that midgut epithelial cells as well as the hepatic ceca are key target organs.

Abstract: The illicit consumption of heroin is an increasing concern in our society. For this reason, rapid analytical methods to seize heroin samples in the field are of paramount importance to hinder drug trafficking, and thus prevent the availability of heroin in the drug market. The present work reports on the enriched electrochemical fingerprint of heroin, allowing its selective detection in street samples, based on the use of electrochemical pretreated screen printed electrodes (p-SPE). The voltammetric identification is built on two oxidation peaks of both heroin and its degradation product 6-monoacetylmorphine (6-MAM), generated in alkaline conditions. Interestingly, an anodic pretreatment of the screen printed electrodes (SPE) shifts the peak potential of paracetamol (the most encountered cutting agent in heroin seizures), allowing the detection of 6-MAM peak, overlapping with the paracetamol signal in the case of untreated SPE. Subsequently, the characterization of the p-SPE with scanning electron microscopy, cyclic voltammetry, electrochemical impedance spectroscopy, Raman and Fourier transform infrared (FTIR) spectroscopy is provided to demonstrate local changes on the surface of the electrode. From an analytical perspective, p-SPE provide higher sensitivity (0.019 μA μM-1), excellent reproducibility (6-MAM, RSD = 2.85%, and heroin RSD = 0.91%, n = 5) and lower limits of detection (LOD) (5.2 μM) in comparison to untreated SPE. The proposed protocol which integrates a tailor-made script is interrogated against common cutting agents, and finally, validated with the screening of 14 street samples, also analyzed by standard methods. Besides, a comparison with portable spectroscopic techniques on the confiscated samples shows the better performance of the electrochemical strategy. Overall, this sensing approach offers promising results for the rapid on-site profiling of suspicious heroin samples, also in the presence of paracetamol.

Abstract: Orpiment and realgar, both arsenic sulfide pigments respectively used for their vivid yellow and red-orange hues, are two of many artists' pigments that appear not to be stable upon light exposure, quickly degrading to arsenic trioxide and arsenate. This often results in whitening or transparency in the painted surfaces. While conventional techniques such as microscopic Raman (mu-RS) and microscopic Fourier transform infrared (mu-FTIR) spectroscopies can allow a quick and relatively easy identification of the orpiment, realgar, artificial arsenic sulfide glass and, to some extent, arsenic oxide, the identification and visualization of distributions of the degradation products – and especially arsenate compounds – in the paint micro-samples is generally more challenging. This challenge is due to the rather unfavorable limit of detection and low spectral resolution of such conventional spectroscopic techniques. This restricts the conclusions that can be drawn regarding the conservation state of valuable works of art. In this paper, we present how synchrotron radiation (SR) based techniques can overcome this challenge while working on painting cross-sections taken from a 17th-century painting by the Flemish artist Daniel Seghers (oil on canvas, Statens Museum for Kunst, Denmark) and an 18th-century French Chinoiserie (private collection, France). SR micro-X-ray fluorescence (m-XRF) mapping analysis performed on a visually degraded orpiment-containing paint stratigraphy reveals that arsenic is distributed throughout the entire cross-section, while X-ray absorption near edge structure (mu-XANES) demonstrated that the arsenic is present in both arsenite (As-III) and arsenate (As-V) forms. The latter compound(s), despite being barely identifiable by means of FTIR, were not only located at the surface of large and partially altered grains of arsenic sulfide but also spread throughout the entire paint stratigraphy. Their presence and distribution are attributed either to the complete degradation of smaller arsenic sulfide grains or to migration of the arsenates within the paint layer away from their original location of formation. The combination of mu-XRF and mu-XANES was very useful for the characterization of the advanced degradation state of the arsenic-containing pigments in paint systems; this type of information could not be obtained by means of conventional spectroscopic methods of microanalysis.