“Influence of stress aging process on variants of nano-N4Ti3precipitates and martensitic transformation temperatures in NiTi shape memory alloy”. Radi A, Khalil-Allafi J, Etminanfar MR, Pourbabak S, Schryvers D, Amin-Ahmadi B, Materials &, design 262, 74 (2018). http://doi.org/10.1016/J.ELECTACTA.2018.01.024
Abstract: In this study, the effect of a stress aging process on the microstructure and martensitic phase transformation of NiTi shape memory alloy has been investigated. NiTi samples were aged at 450 degrees C for 1 h and 5 h under different levels of external tensile stress of 15, 60 and 150 MPa. Transmission electron microscopy (TEM) was used to characterize different variants and morphology of precipitates. The results show that application of all stress levels restricts the formation of precipitates variants in the microstructure after I h stress aging process. However, all variants can be detected by prolonging aging time to 5 h at 15 MPa stress level and the variants formation is again restricted by increasing the stress level. Moreover, the stress aging process resulted in changing the shape of precipitates in comparison with that of the stress-free aged samples. Coffee-bean shaped morphologies were detected for precipitates in all stress levels. According to the Differential Scanning Calorimetry (DSC) results, the martensite start temperature (M-s) on cooling shifts to higher temperatures with increasing the tensile stress during the aging process. This can be related to the change ofaustenite to martensite interface energy due to the different volume fractions and variants of precipitates. (c) 2018 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.364
DOI: 10.1016/J.ELECTACTA.2018.01.024
|
|
“Influence of M23C6 dissolution on the kinetics of ferrite to austenite transformation in Fe-11Cr-0.06C stainless steel”. Miotti Bettanini A, Ding L, Mithieux J-D, Parrens C, Idrissi H, Schryvers D, Delannay L, Pardoen T, Jacques PJ, Materials &, design 162, 362 (2019). http://doi.org/10.1016/j.matdes.2018.12.005
Abstract: The design of high-strength martensitic stainless steels requires an accurate control over the stability of undesired phases, like carbides and ferrite, which can hamper strength and ductility. Here, the ferrite to austenite transformation in Fe-11Cr-0.06C has been studied with a combined experimental-modelling approach. Experimental observations of the austenization process indicate that austenite growth proceeds in multiple steps, each one characterized by a different transformation rate. DICTRA based modelling reveals that the dissolution of the M23C6 Cr-rich carbides leads to Cr partitioning between austenite and parent phases, which controls the rate of transformation through (i) a soft-impingement effect and (ii) consequent stabilization of the ferrite, which remains untransformed inside chromium-enriched-zones even after prolonged austenization stage. Slow heating rate and smaller initial particle sizes allow the design of ferrite-free microstructure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.364
Times cited: 3
DOI: 10.1016/j.matdes.2018.12.005
|
|
“Influence of amorphous phase separation on the crystallization behavior of glass-ceramics in the BaO-TiO2-SiO2 system”. Boulay E, Ragoen C, Idrissi H, Schryvers D, Godet S, Journal of non-crystalline solids 384, 61 (2014). http://doi.org/10.1016/j.jnoncrysol.2013.06.023
Abstract: The possible role of a prior amorphous phase separation on the subsequent crystallization has been the topic of vigorous debates over the last decades and has not yet been clarified, especially regarding the role of the interfaces created by the phase separation. This study proposes to focus on the interplay between a prior amorphous phase separation and the crystallization of fresnoite in the BaO-TiO2-SiO2 system. The crystallization behavior of a non-stoichiometric composition inside the miscibility gap (called APS) is compared with the stoichiometric composition (called FRES) and a non-stoichiometric composition outside the miscibility gap (called NoAPS). The crystallization mechanisms are compared using differential thermal analysis (DTA) by calculating the Avrami parameters and the activation energies as a function of the particle size. The DTA study shows that the two non-stoichiometric compositions exhibit a pronounced surface crystallization behavior whereas FRES undergoes bulk nucleation. This is supported by a multi-scale microstructure characterization. Furthermore, this study demonstrates that the amorphous phase separation and the associated interfaces do not play any significant role in the nucleation step. Moreover, transmission electron microscope (TEM) and local orientation measurements show that the growth of the dendrites is not hindered by the SiO2-rich droplets. The final stage of crystallization of APS is tentatively explained by two composition effects that must be further investigated: the viscosity effect and the formation of a eutectic. (C) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.124
Times cited: 10
DOI: 10.1016/j.jnoncrysol.2013.06.023
|
|
“In-situ TEM study of the Ni5Al3 to B2 + L12 decomposition in Ni65Al35”. Schryvers D, Ma Y, Materials letters 23, 105 (1995). http://doi.org/10.1016/0167-577X(95)00030-5
Abstract: Homogenised and quenched Ni65Al35 samples were heated and studied in situ in a CM20 electron microscope up to 900 degrees C. The Ni5Al3 phase first forming around 550 degrees C in the quenched L1(0) microtwinned martensite starts to decompose around 800 degrees C yielding B2 precipitates in a twinned L1(2) matrix. The latter twinning is a remainder of the microtwinning in the original room temperature martensite. Also the crystallographic relations between precipitates and matrix can be traced back to the original formation of twinned martensite plates within the austenite. Some aspects of the dynamics of the process are discussed on the basis of snap shots and video recordings.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.489
Times cited: 5
DOI: 10.1016/0167-577X(95)00030-5
|
|
“In-Situ TEM Stress Induced Martensitic Transformation in Ni50.8Ti49.2 Microwires”. Pourbabak S, Orekhov A, Samaee V, Verlinden B, Van Humbeeck J, Schryvers D, Shape memory and superelasticity 5, 154 (2019). http://doi.org/10.1007/s40830-019-00217-6
Abstract: In-situ transmission electron microscopy tensile straining is used to study the stress induced martensitic transformation in Ni50.8Ti49.2. Two microwire samples with different heat treatment are investigated from which one single crystal and three polycrystalline TEM specimens, the latter with micro- and nano-size grains, have been produced. The measured Young’s modulus for all TEM specimens is around 70 GPa, considerably higher than the averaged 55 GPa of the original microwire sample. The height of the superelastic stress plateau shows an inverse relationship with the specimen thickness for the polycrystalline specimens. Martensite starts nucleating within the elastic region of the stress–strain curve and on the edges of the specimens while also grain boundaries act as nucleation sites in the polycrystalline specimens. When a martensite plate reaches a grain boundary in the polycrystalline specimen, it initiates the transformation in the neighboring grain at the other side of the grain boundary. In later stages martensite plates coalesce at higher loads in the stress plateau. In highly strained specimens, residual martensite remains after release.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1007/s40830-019-00217-6
|
|
“In-situ HREM observation of electron-irradation-induced martensitic transformation in a Ni63Al37 alloy”. Muto S, Schryvers D, Journal of alloys and compounds 199, 1 (1993)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.999
Times cited: 8
|
|
“In situ transmission electron microscopy of stress-induced martensite with focus on martensite twinning”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 420 (2008). http://doi.org/10.1016/j.msea.2006.12.214
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 22
DOI: 10.1016/j.msea.2006.12.214
|
|
“In Situ Quantitative Tensile Testing of Antigorite in a Transmission Electron Microscope”. Idrissi H, Samaee V, Lumbeeck G, Werf T, Pardoen T, Schryvers D, Cordier P, Journal Of Geophysical Research-Solid Earth 125 (2020). http://doi.org/10.1029/2019JB018383
Abstract: The determination of the mechanical properties of serpentinites is essential toward the understanding of the mechanics of faulting and subduction. Here we present the first in situ tensile tests on antigorite in a transmission electron microscope. A push‐to‐pull deformation device is used to perform quantitative tensile tests, during which force and displacement are measured, while the evolving microstructure is imaged with the microscope. The experiments have been performed at room temperature on 2 × 1 × 0.2 μm3 beams prepared by focused ion beam. The specimens are not single crystals despite their small sizes. Orientation mapping indicated that several grains were well oriented for plastic slip. However, no dislocation activity has been observed even though the engineering tensile stress went up to 700 MPa. We show also that antigorite does not exhibit a purely elastic‐brittle behavior since, despite the presence of defects, the specimens accumulate permanent deformation and did not fail within the elastic regime. Instead, we observe that strain localizes at grain boundaries. All observations concur to show that under these experimental conditions, grain boundary sliding is the dominant deformation mechanism. This study sheds a new light on the mechanical properties of antigorite and calls for further studies on the structure and properties of grain boundaries in antigorite and more generally in phyllosilicates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.9
DOI: 10.1029/2019JB018383
|
|
“In situ HREM study of electron irradiation effects in AgCl microcrystals”. Goessens C, Schryvers D, de Keyzer R, van Landuyt J Eurem 92, Granada, page 646 (1992).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
|
“In situ HREM study of electron irradiation effects in AgCl microcrystals”. Goessens C, Schryvers D, van Landuyt J, de Keyzer R, Ultramicroscopy 40, 151 (1992). http://doi.org/10.1016/0304-3991(92)90056-P
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.436
Times cited: 10
DOI: 10.1016/0304-3991(92)90056-P
|
|
“In situ high resolution electron microscopy observation of electron-irradiation-induced martensitic transformation in a Ni63Al37 alloy”. Muto S, Schryvers D, Journal of alloys and compounds 199, 1 (1993). http://doi.org/10.1016/0925-8388(93)90422-J
Abstract: An electron-irradiation-induced transformation from cubic beta2 austenite to monoclinic 7M martensite was observed in situ under high resolution electron microscopy conditions in a thin foil of Ni63Al37 beta2 phase (B2, CsCl structure), with the start temperature of the martensitic transformation below but very close to room temperature. The structure of the martensite is consistent with thermoelastic or stress-induced martensite at this composition, including the existence of multiple stacking faults. The transformation is described by a gradual increase in the shear and shuffle amplitudes already existing in the precursor domains. Possible origins of the transformation are discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.999
Times cited: 8
DOI: 10.1016/0925-8388(93)90422-J
|
|
“Importance of twinning in static and dynamic compression of a Ti-6Al-4V titanium alloy with an equiaxed microstructure”. Coghe F, Tirry W, Rabet L, Schryvers D, Van Houtte P, Materials science and engineering: part A: structural materials: properties, microstructure and processing 537, 1 (2012). http://doi.org/10.1016/j.msea.2011.12.047
Abstract: Whereas deformation twinning is known to be an important deformation mechanism for hexagonal materials like magnesium and pure titanium, so far almost no literature exists on the twinning behaviour of the Ti-6Al-4V alloy. In this work it was shown that the activation of twinning as a deformation mechanism could have a pronounced effect on the mechanical behaviour of the Ti-6Al-4V alloy. This effect is even more pronounced under dynamic loading conditions. Transmission electron microscopy showed that only the {1 0 1 2}{1 0 1 1} tensile twin system was activated under certain loading conditions. Light-optical microscopy and electron backscatter diffraction data were afterwards used to experimentally determine the twin fractions. The importance of twinning for the texture evolution was also studied. It was shown that even small twin fractions can lead to distinct texture features, especially due to the discrete reorientation of the c-axes. The experimental results were compared to simulated results that were obtained with a viscoplastic self-consistent crystal plasticity code, after experimental validation that twinning can be reliably modelled as a unidirectional slip system. Although good agreement was obtained for the experimental and simulated stress-strain curves, the simulated results concerning twinning correlated well only on a qualitative basis as the simulated twin fractions were systematically higher than the experimental fractions. This seems to strengthen the hypothesis made by other research groups that complete grains might reorient by twinning. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 35
DOI: 10.1016/j.msea.2011.12.047
|
|
“HRTEM study of austenite and martensite in splat-cooled and nanoscale thin film Ni-Al”. Schryvers D, Yandouzi M, Holland-Moritz D, Toth L, Journal de physique: 4 C5, 203 (1997). http://doi.org/10.1051/jp4:1997532
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1051/jp4:1997532
|
|
“HREM investigation of martensite precursor effects and stacking sequences in Ni-Mn-Ti alloys”. Schryvers D, Lahjouji DE, Slootmaekers B, Potapov PL, Scripta metallurgica et materialia 35, 1235 (1996). http://doi.org/10.1016/1359-6462(96)00271-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.224
Times cited: 2
DOI: 10.1016/1359-6462(96)00271-0
|
|
“HREM imaging analysis in the study of pretransition and nucleation phenomena in alloys (Invited)”. Schryvers D, Van Tendeloo G, van Landuyt J, Le Tanner, , 659 (1994)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
“HREM imaging analysis in the study of pretransition and nucleation phenomena in alloys”. Schryvers D, Van Tendeloo G, van Landuyt J, Tanner LE, Icem 13, 659 (1994)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
“HREM and ED study of the displacive transformation of the Ni2Al phase in a Ni65Al35 alloy and associated with the martensitic transformation”. Muto S, Schryvers D, Merk N, Tanner LE, Acta metallurgica et materialia 41, 2377 (1993)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 31
|
|
“Homogeneous flow and size dependent mechanical behavior in highly ductile Zr 65 Ni 35 metallic glass films”. Ghidelli M, Idrissi H, Gravier S, Blandin J-J, Raskin J-P, Schryvers D, Pardoen T, Acta materialia 131, 246 (2017). http://doi.org/10.1016/j.actamat.2017.03.072
Abstract: Motivated by recent studies demonstrating a high strength – high ductility potential of nano-scale metallic glass samples, the mechanical response of freestanding Zr65Ni35 film with sub-micron thickness has been investigated by combining advanced on-chip tensile testing and electron microscopy. Large deformation up to 15% is found for specimen thicknesses below 500 nm with variations depending on specimen size and frame compliance. The deformation is homogenous until fracture, with no evidence of shear banding. The yield stress is doubled when decreasing the specimen cross-section, reaching ~3 GPa for small cross-sections. The fracture strain variation is related to both the stability of the test device and to the specimen size. The study concludes on clear disconnect between the mechanisms controlling the onset of plasticity and the fracture process.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 42
DOI: 10.1016/j.actamat.2017.03.072
|
|
“High-resolution visualization techniques : structural aspects”. Schryvers D, Van Aert S Springer, Berlin, page 135 (2012).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
|
“High-quality sample preparation by low kV FIB thinning for analytical TEM measurements”. Bals S, Tirry W, Geurts R, Yang Z, Schryvers D, Microscopy and microanalysis 13, 80 (2007). http://doi.org/10.1017/S1431927607070018
Abstract: Focused ion beam specimen preparation has been used for NiTi samples and SrTiO(3)/SrRuO(3) multilayers with prevention of surface amorphization and Ga implantation by a 2-kV cleaning procedure. Transmission electron microscopy techniques show that the samples are of high quality with a controlled thickness over large scales. Furthermore, preferential thinning effects in multicompounds are avoided, which is important when analytical transmission electron microscopy measurements need to be interpreted in a quantitative manner. The results are compared to similar measurements acquired for samples obtained using conventional preparation techniques such as electropolishing for alloys and ion milling for oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 82
DOI: 10.1017/S1431927607070018
|
|
“High strength-ductility of thin nanocrystalline palladium films with nanoscale twins : on-chip testing and grain aggregate model”. Colla M-S, Wang B, Idrissi H, Schryvers D, Raskin J-P, Pardoen T, Acta materialia 60, 1795 (2012). http://doi.org/10.1016/j.actamat.2011.11.054
Abstract: The mechanical behaviour of thin nanocrystalline palladium films with an ∼30 nm in plane grain size has been characterized on chip under uniaxial tension. The films exhibit a large strain hardening capacity and a significant increase in the strength with decreasing thickness. Transmission electron microscopy has revealed the presence of a moderate density of growth nanotwins interacting with dislocations. A semi-analytical grain aggregate model is proposed to investigate the impact of different contributions to the flow behaviour, involving the effect of twins, of grain size and of the presence of a thin surface layer. This model provides guidelines to optimizing the strength/ductility ratio of the films.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 38
DOI: 10.1016/j.actamat.2011.11.054
|
|
“High resolution transmission electron microscopy study of nanoscale Ni-rich Ni-Al films evaporated onto NaCl and KCl”. Yandouzi M, Toth L, Schryvers D, Nanostructured materials 10, 99 (1998). http://doi.org/10.1016/S0965-9773(98)00025-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1016/S0965-9773(98)00025-7
|
|
“High resolution transmission electron microscopy characterization of fcc ->, 9R transformation in nanocrystalline palladium films due to hydriding”. Amin-Ahmadi B, Idrissi H, Delmelle R, Pardoen T, Proost J, Schryvers D, Applied physics letters 102, 071911 (2013). http://doi.org/10.1063/1.4793512
Abstract: Sputtered nanocrystalline palladium thin films with nanoscale growth twins have been subjected to hydriding cycles. The evolution of the twin boundaries has been investigated using high resolution transmission electron microscopy. Surprisingly, the Sigma 3{112} incoherent twin boundaries dissociate after hydriding into two phase boundaries bounding a 9R phase. This phase which corresponds to single stacking faults located every three {111} planes in the fcc Pd structure was not expected because of the high stacking fault energy of Pd. This observation is connected to the influence of the Hydrogen on the stacking fault energy of palladium and the high compressive stresses building up during hydriding. (C) 2013 American Institute of Physics. [http://dx.doi.org/10.1063/1.4793512]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 14
DOI: 10.1063/1.4793512
|
|
“High resolution TEM study of Ni4Ti3 precipitates in austenitic Ni51Ti49”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 157 (2004). http://doi.org/10.1016/j.msea.2003.10.336
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 19
DOI: 10.1016/j.msea.2003.10.336
|
|
“Heterogeneous interfacial chemical nature and bonds in a W-coated diamond/Al composite”. Ji G, Tan Z, Lu Y, Schryvers D, Li Z, Zhang D, Materials characterization 112, 129 (2016). http://doi.org/10.1016/j.matchar.2015.12.013
Abstract: Heterogeneous Al/Al4C3/Al2O3/diamond{111}, Al/nanolayered Al4C3/diamond{111} and Al12W particle/Al4C3/Al2O3/diamond{111} multi-interfaces have been developed at the nanoscale in a W-coated diamond/Al composite produced by vacuum hot pressing. The formation of nanoscale Al4C3 crystals is strongly associated with local O enrichment and can be further promoted by Al12W interfacial particles. The latter effectively contributes to enhance interfacial chemical bonding reducing interfacial thermal resistance and, in turn, enhancing thermal conductivity.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 7
DOI: 10.1016/j.matchar.2015.12.013
|
|
“Hepatocellular transport and gastrointestinal absorption of lanthanum in chronic renal failure”. Bervoets ARJ, Behets GJ, Schryvers D, Roels F, Yang Z, Verberckmoes SC, Damment SJP, Dauwe S, Mubiana VK, Blust R, de Broe ME, d' Haese PC, Kidney international 75, 389 (2009). http://doi.org/10.1038/ki.2008.571
Abstract: Lanthanum carbonate is a new phosphate binder that is poorly absorbed from the gastrointestinal tract and eliminated largely by the liver. After oral treatment, we and others had noticed 23 fold higher lanthanum levels in the livers of rats with chronic renal failure compared to rats with normal renal function. Here we studied the kinetics and tissue distribution, absorption, and subcellular localization of lanthanum in the liver using transmission electron microscopy, electron energy loss spectrometry, and X-ray fluoresence. We found that in the liver lanthanum was located in lysosomes and in the biliary canal but not in any other cellular organelles. This suggests that lanthanum is transported and eliminated by the liver via a transcellular, endosomal-lysosomal-biliary canicular transport route. Feeding rats with chronic renal failure orally with lanthanum resulted in a doubling of the liver levels compared to rats with normal renal function, but the serum levels were similar in both animal groups. These levels plateaued after 6 weeks at a concentration below 3 g/g in both groups. When lanthanum was administered intravenously, thereby bypassing the gastrointestinal tract-portal vein pathway, no difference in liver levels was found between rats with and without renal failure. This suggests that there is an increased gastrointestinal permeability or absorption of oral lanthanum in uremia. Lanthanum levels in the brain and heart fluctuated near its detection limit with long-term treatment (20 weeks) having no effect on organ weight, liver enzyme activities, or liver histology. We suggest that the kinetics of lanthanum in the liver are consistent with a transcellular transport pathway, with higher levels in the liver of uremic rats due to higher intestinal absorption.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Pathophysiology
Impact Factor: 8.395
Times cited: 29
DOI: 10.1038/ki.2008.571
|
|
“Grain growth and precipitation in an annealed cold-rolled Ni50.2Ti49.8 alloy”. Srivastava AK, Schryvers D, van Humbeeck J, Intermetallics 15, 1538 (2007). http://doi.org/10.1016/j.intermet.2007.06.003
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 37
DOI: 10.1016/j.intermet.2007.06.003
|
|
“GP-zones in Al-Zn-Mg alloys and their role in artificial aging”. Berg LK, Gjønnes J, Hansen V, Li XZ, Knutson-Wedel M, Waterloo G, Schryvers D, Wallenberg LR, Acta materialia 49, 3443 (2001). http://doi.org/10.1016/S1359-6454(01)00251-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 261
DOI: 10.1016/S1359-6454(01)00251-8
|
|
“Functional twin boundaries”. Van Aert S, Turner S, Delville R, Schryvers D, Van Tendeloo G, Ding X, Salje EKH, Phase transitions 86, 1052 (2013). http://doi.org/10.1080/01411594.2012.748909
Abstract: Functional interfaces are at the core of research in the emerging field of domain boundary engineering where polar, conducting, chiral, and other interfaces and twin boundaries have been discovered. Ferroelectricity was found in twin walls of paraelectric CaTiO3. We show that the effect of functional interfaces can be optimized if the number of twin boundaries is increased in densely twinned materials. Such materials can be produced by shear in the ferroelastic phase rather than by rapid quench from the paraelastic phase.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.06
Times cited: 5
DOI: 10.1080/01411594.2012.748909
|
|
“From the lattice measurements of the austenite and the martensite cells to the macroscopic mechanical behavior of shape memory alloys”. Lexcellent C, Vivet A, Bouvet C, Blanc P, Satto C, Schryvers D, Journal de physique: 4 11, 317 (2001)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|