“Defect healing and enhanced nucleation of carbon nanotubes by low-energy ion bombardment”. Neyts EC, Ostrikov K, Han ZJ, Kumar S, van Duin ACT, Bogaerts A, Physical review letters 110, 065501 (2013). http://doi.org/10.1103/PhysRevLett.110.065501
Abstract: Structural defects inevitably appear during the nucleation event that determines the structure and properties of single-walled carbon nanotubes. By combining ion bombardment experiments with atomistic simulations we reveal that ion bombardment in a suitable energy range allows these defects to be healed resulting in an enhanced nucleation of the carbon nanotube cap. The enhanced growth of the nanotube cap is explained by a nonthermal ion-induced graphene network restructuring mechanism.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 8.462
Times cited: 50
DOI: 10.1103/PhysRevLett.110.065501
|
“Defect structure of ferromagnetic superconducting RuSr2GdCu2O8”. Lebedev OI, Van Tendeloo G, Attfield JP, McLaughlin AC, Physical review : B : condensed matter and materials physics 73 (2006). http://doi.org/10.1103/PhysRevB.73.224524
Abstract: The structure and defect structure of superconducting ferromagnetic bulk RuSr2GdCu2O8 has been investigated using high-resolution transmission electron microscopy and high-resolution scanning transmission microscopy. Two distinct, but closely related structures, due to ordering of rotated RuO6 octahedra and due to Cu substitution in the Ru-O layer, have been revealed. The structure of Ru1-xSr2GdCu2+xO8-delta can be described as a periodic alteration along the c axis of CuO4 planes and RuO6 octahedra. The unit-cell parameters of this phase are root 2a(p) x root 2a(p) x 2c. The possible influence of this phase and defect structure on the sensitivity of the superconductivity and magnetic properties is discussed. Local defects such as 90 S domain boundaries, (130) antiphase boundaries, and the associated dislocations are analyzed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 11
DOI: 10.1103/PhysRevB.73.224524
|
“Defect structure of the low temperature α-cristobalite phase and the cristobalite <->, tridymite transformation in (Si-Ge)O2”. Lemmens H, Czank M, Van Tendeloo G, Amelinckx S, Physics and chemistry of minerals 27, 386 (2000). http://doi.org/10.1007/s002699900082
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.521
Times cited: 5
DOI: 10.1007/s002699900082
|
“Defect structures in CuZr martensite, studies by CTEM and HRTEM”. Seo JW, Schryvers D, Journal de physique: 4 C5, 149 (1997). http://doi.org/10.1051/jp4:1997523
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/jp4:1997523
|
“Defect-directed growth of symmetrically branched metal nanocrystals”. Smith JD, Bladt E, Burkhart JAC, Winckelmans N, Koczkur KM, Ashberry HM, Bals S, Skrabalak SE, Angewandte Chemie-International Edition 59, 943 (2020). http://doi.org/10.1002/ANIE.201913301
Abstract: Branched plasmonic nanocrystals (NCs) have attracted much attention due to electric field enhancements at their tips. Seeded growth provides routes to NCs with defined branching patterns and, in turn, near-field distributions with defined symmetries. Here, a systematic analysis was undertaken in which seeds containing different distributions of planar defects were used to grow branched NCs in order to understand how their distributions direct the branching. Characterization of the products by multimode electron tomography and analysis of the NC morphologies at different overgrowth stages indicate that the branching patterns are directed by the seed defects, with the emergence of branches from the seed faces consistent with minimizing volumetric strain energy at the expense of surface energy. These results contrast with growth of branched NCs from single-crystalline seeds and provide a new platform for the synthesis of symmetrically branched plasmonic NCs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 23
DOI: 10.1002/ANIE.201913301
|
“Defect-induced faceted blue phosphorene nanotubes”. Aierken Y, Leenaerts O, Peeters FM, Physical review : B : condensed matter and materials physics 92, 104104 (2015). http://doi.org/10.1103/PhysRevB.92.104104
Abstract: The properties of a new class of phosphorene nanotubes (PNT) are investigated by performing first-principles calculations. We demonstrate that it is advantageous to use blue phosphorene in order to make small nanotubes and propose a way to create low-energy PNTs by the inclusion of defect lines. Five different types of defect lines are investigated and incorporated in various combinations. The resulting defect-induced faceted PNTs have negligible bending stresses which leads to a reduction in the formation energy with respect to round PNTs. Our armchair faceted PNTs have similar formation energies than the recently proposed multiphase faceted PNTs, but they have a larger variety of possible structures. Our zigzag faceted PNTs have lower formation energies than round tubes and multiphase faceted nanotubes. The electronic properties of the defect-induced faceted PNTs are determined by the defect lines which control the band gap and the shape of the electronic states at the band edges. These band gaps increase with the radius of the nanotubes and converge to those of isolated defect lines.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 24
DOI: 10.1103/PhysRevB.92.104104
|
“Defect-limited thermal conductivity in MoS₂”. Polanco CA, Pandey T, Berlijn T, Lindsay L, Physical review materials 4, 014004 (2020). http://doi.org/10.1103/PHYSREVMATERIALS.4.014004
Abstract: The wide measured range of thermal conductivities (k) for monolayer MoS2 and the corresponding incongruent calculated values in the literature all suggest that extrinsic defect thermal resistance is significant and varied in synthesized samples of this material. Here we present defect-mediated thermal transport calculations of MoS2 using interatomic forces derived from density functional theory combined with Green's function methods to describe phonon-point-defect interactions and a Peierls-Boltzmann formalism for transport. Conductivity calculations for bulk and monolayer MoS2 using different density functional formalisms are compared. Nonperturbative first-principles methods are used to describe defect-mediated spectral functions, scattering rates, and phonon k, particularly from sulfur vacancies (VS), and in the context of the plethora of measured and calculated literature values. We find that k of monolayer MoS2 is sensitive to phonon-VS scattering in the range of experimentally observed densities, and that first-principles k calculations using these densities can explain the range of measured values found in the literature. Furthermore, measured k values for bulk MoS2 are more consistent because VS defects are not as prevalent.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.4
DOI: 10.1103/PHYSREVMATERIALS.4.014004
|
“Defect-modulated transistors and gas-enhanced photodetectors on ReS2 nanosheets”. Yang S, Kang J, Yue Q, Coey JMD, Jiang C, Advanced Materials Interfaces 3, 1500707 (2016). http://doi.org/10.1002/admi.201500707
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 4.279
Times cited: 22
DOI: 10.1002/admi.201500707
|
“Defected graphene nanoribbons under axial compression”. Neek-Amal M, Peeters FM, Applied physics letters 97, 153118 (2010). http://doi.org/10.1063/1.3496467
Abstract: The buckling of defected rectangular graphene nanoribbons when subjected to axial stress with supported boundary conditions is investigated using atomistic simulations. The buckling strain and mechanical stiffness of monolayer graphene decrease with the percentage of randomly distributed vacancies. The elasticity to plasticity transition in the stress-strain curve, at low percentage of vacancies, are found to be almost equal to the buckling strain thresholds and they decrease with increasing percentage of vacancies.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.411
Times cited: 43
DOI: 10.1063/1.3496467
|
“Defective biphenylene as high-efficiency hydrogen evolution catalysts”. Luo Y, He Y, Ding Y, Zuo L, Zhong C, Ma Y, Sun M, Inorganic chemistry 63, 1136 (2023). http://doi.org/10.1021/ACS.INORGCHEM.3C03503
Abstract: Electrocatalysts play a pivotal role in advancing the application of water splitting for hydrogen production. This research unveils the potential of defective biphenylenes as high-efficiency catalysts for the hydrogen evolution reaction. Using first-principles simulations, we systematically investigated the structure, stability, and catalytic performance of defective biphenylenes. Our findings unveil that defect engineering significantly enhances the electrocatalytic activity for hydrogen evolution. Specifically, biphenylene with a double-vacancy defect exhibits an outstanding Gibbs free energy of -0.08 eV, surpassing that of Pt, accompanied by a remarkable exchange current density of -3.08 A cm(-2), also surpassing that of Pt. Furthermore, we find the preference for the Volmer-Heyrovsky mechanism in the hydrogen evolution reaction, with a low energy barrier of 0.80 eV. This research provides a promising avenue for developing novel metal-free electrocatalysts for water splitting with earth-abundant carbon elements, making a significant step toward sustainable hydrogen production.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 4.6
DOI: 10.1021/ACS.INORGCHEM.3C03503
|
“Defects and growth mechanisms of AgCl(100) tabular crystals”. van Renterghem W, Goessens C, Schryvers D, van Landuyt J, Verrept P, Bollen D, van Roost C, de Keyzer R, Journal of crystal growth 187, 410 (1998). http://doi.org/10.1016/S0022-0248(98)00004-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 8
DOI: 10.1016/S0022-0248(98)00004-9
|
“Defects and phase transformation in monclinic natural hollandite: BaxMn8O16”. Nistor LC, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 109, 152 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 13
|
“Defects and phase transition in monoclinic natural hollandite : BaxMn8O16”. Nistor LC, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 109, 152 (1994). http://doi.org/10.1006/jssc.1994.1085
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 13
DOI: 10.1006/jssc.1994.1085
|
“Defects in amorphous semiconductors : the case of amorphous indium gallium zinc oxide”. de de Meux AJ, Pourtois G, Genoe J, Heremans P, Physical review applied 9, 054039 (2018). http://doi.org/10.1103/PHYSREVAPPLIED.9.054039
Abstract: Based on a rational classification of defects in amorphous materials, we propose a simplified model to describe intrinsic defects and hydrogen impurities in amorphous indium gallium zinc oxide (a-IGZO). The proposed approach consists of organizing defects into two categories: point defects, generating structural anomalies such as metal-metal or oxygen-oxygen bonds, and defects emerging from changes in the material stoichiometry, such as vacancies and interstitial atoms. Based on first-principles simulations, it is argued that the defects originating from the second group always act as perfect donors or perfect acceptors. This classification simplifies and rationalizes the nature of defects in amorphous phases. In a-IGZO, the most important point defects are metal-metal bonds (or small metal clusters) and peroxides (O-O single bonds). Electrons are captured by metal-metal bonds and released by the formation of peroxides. The presence of hydrogen can lead to two additional types of defects: metal-hydrogen defects, acting as acceptors, and oxygen-hydrogen defects, acting as donors. The impact of these defects is linked to different instabilities observed in a-IGZO. Specifically, the diffusion of hydrogen and oxygen is connected to positive-and negative-bias stresses, while negative-bias illumination stress originates from the formation of peroxides.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.808
Times cited: 7
DOI: 10.1103/PHYSREVAPPLIED.9.054039
|
“Defects in high-dose oxygen implanted silicon : a TEM study”. Deveirman A, van Landuyt J, Vanhellemont J, Maes HE, Yallup K, Vacuum: the international journal and abstracting service for vacuum science and technology
T2 –, 1ST SIOMX WORKSHOP ( SEPARATION BY IMPLANTATION OF OXYGEN ) ( SWI-88 ), NOV 07-08, 1988, UNIV SURREY, GUILDFORD, ENGLAND 42, 367 (1991). http://doi.org/10.1016/0042-207X(91)90055-N
Abstract: Results are discussed of a transmission electron microscopy study of high-dose oxygen implanted silicon. In addition to the general high temperature (> 1200-degrees-C) annealing treatments also annealings at 'low' temperatures (1000-1100-degrees-C) were performed in order to slow down the precipitate and defect reactions. The observed dissolution of the oxide precipitates during prolonged high temperature annealing is explained by critical radius considerations. Threading dislocations are the remaining lattice defects in the silicon overlayer and cannot be removed by further annealing. Low temperature annealing results in the formation and subsequent unfaulting of extrinsic stacking fault loops below the buried oxide layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.858
Times cited: 4
DOI: 10.1016/0042-207X(91)90055-N
|
“Defect‐Directed Growth of Symmetrically Branched Metal Nanocrystals”. Smith JD, Bladt E, Burkhart JAC, Winckelmans N, Koczkur KM, Ashberry HM, Bals S, Skrabalak SE, Angewandte Chemie (International ed. Print) 132, 953 (2020). http://doi.org/10.1002/ange.201913301
Abstract: Branched plasmonic nanocrystals (NCs) have attracted much attention due to electric field enhancements at their tips. Seeded growth provides routes to NCs with defined branching patterns and, in turn, near‐field distributions with defined symmetries. Here, a systematic analysis was undertaken in which seeds containing different distributions of planar defects were used to grow branched NCs in order to understand how their distributions direct the branching. Characterization of the products by multimode electron tomography and analysis of the NC morphologies at different overgrowth stages indicate that the branching patterns are directed by the seed defects, with the emergence of branches from the seed faces consistent with minimizing volumetric strain energy at the expense of surface energy. These results contrast with growth of branched NCs from single‐crystalline seeds and provide a new platform for the synthesis of symmetrically branched plasmonic NCs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1002/ange.201913301
|
“Deflection of ferromagnetic and antiferromagnetic skyrmions at heterochiral interfaces”. Menezes RM, Mulkers J, de Souza Silva CC, Milošević, MV, Physical review B 99, 104409 (2019). http://doi.org/10.1103/PHYSREVB.99.104409
Abstract: Devising magnetic nanostructures with spatially heterogeneous Dzyaloshinskii-Moriya interaction (DMI) is a promising pathway toward advanced confinement and control of magnetic skyrmions in potential devices. Here we discuss theoretically how a skyrmion interacts with a heterochiral interface using micromagnetic simulations and analytic arguments. We show that a heterochiral interface deflects the trajectory of ferromagnetic (FM) skyrmions, and that the extent of such deflection is tuned by the applied spin-polarized current and the difference in DMI across the interface. Further, we show that this deflection is characteristic of the FM skyrmion, and it is completely absent in the antiferromagnetic (AFM) case. In turn, we reveal that the AFM skyrmion achieves much higher velocities than its FM counterpart, yet experiences far stronger confinement in nanoengineered heterochiral tracks, which reinforces AFM skyrmions as a favorable choice for skyrmion-based devices.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 19
DOI: 10.1103/PHYSREVB.99.104409
|
“Deformation-induced austenite grain rotation and transformation in TRIP-assisted steel”. Tirumalasetty GK, van Huis MA, Kwakernaak C, Sietsma J, Sloof WG, Zandbergen HW, Acta materialia 60, 1311 (2012). http://doi.org/10.1016/j.actamat.2011.11.026
Abstract: Uniaxial straining experiments were performed on a rolled and annealed Si-alloyed TRIP (transformation-induced plasticity) steel sheet in order to assess the role of its microstructure on the mechanical stability of austenite grains with respect to martensitic transformation. The transformation behavior of individual metastable austenite grains was studied both at the surface and inside the bulk of the material using electron back-scattered diffraction (EBSD) and X-ray diffraction (XRD) by deforming the samples to different strain levels up to about 20%. A comparison of the XRD and EBSD results revealed that the retained austenite grains at the surface have a stronger tendency to transform than the austenite grains in the bulk of the material. The deformation-induced changes of individual austenite grains before and after straining were monitored with EBSD. Three different types of austenite grains can be distinguished that have different transformation behaviors: austenite grains at the grain boundaries between ferrite grains, twinned austenite grains, and embedded austenite grains that are completely surrounded by a single ferrite grain. It was found that twinned austenite grains and the austenite grains present at the grain boundaries between larger ferrite grains typically transform first, i.e. are less stable, in contrast to austenite grains that are completely embedded in a larger ferrite grain. In the latter case, straining leads to rotations of the harder austenite grain within the softer ferrite matrix before the austenite transforms into martensite. The analysis suggests that austenite grain rotation behavior is also a significant factor contributing to enhancement of the ductility. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 80
DOI: 10.1016/j.actamat.2011.11.026
|
“Degradation of galvanised iron roofing material in Tanzania by atmospheric corrosion”. Potgieter-Vermaak SS, Mmari A, Van Grieken R, McCrindle RI, Potgieter JH, Corrosion engineering science and technology 46, 642 (2011). http://doi.org/10.1179/147842210X12695149033972
Abstract: Galvanised iron is popular in many applications, particular as a roofing material. However, just like other materials, especially metallic ones, it is prone to degradation by corrosion. In this particular study, the degradation of galvanised roof sheets was investigated at a coastal, urban and rural site in Tanzania, Africa. Samples were exposed to various outdoor environments over a period of 3 years. In addition, some accelerated laboratory investigations were conducted in different simulated air pollution environments in an artificial corrosion chamber constructed for this purpose to supplement the outdoor exposure tests. It was found that the combination of the tropical climate and increasing air pollution due to industrial development in the capital Dar-es-Salaam resulted in substantial atmospheric corrosion of the roof sheets, which eventually leads to failure and the necessity for replacement. The rural site had the lowest degree of atmospheric corrosion as expected. A combination of different corrosion products was identified as a result of the atmospheric corrosion by Raman and EDX analyses. The information gained from this investigation could be utilised to construct more durable structures requiring less frequent replacement and maintenance in future.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1179/147842210X12695149033972
|
“Degradation potential of airborne particulate matter at the Alhambra monument : a Raman spectroscopic and electron probe X-ray microanalysis study”. Potgieter-Vermaak S, Horemans B, Anaf W, Cardell C, Van Grieken R, Journal of Raman spectroscopy 43, 1570 (2012). http://doi.org/10.1002/JRS.4052
Abstract: It is well known that airborne particulate matter (APM) has an impact on our cultural heritage. A limited number of articles have been published on the sequential application of elemental and molecular techniques to estimate the degradation potential of APM in environments of cultural heritage importance, and most of these were concerned with indoor environments. The Alhambra monument (Granada, Spain) represents one of the grandest and finest examples of Islamic art and architecture from the Middle Ages. As part of an air quality investigation, two sets of APM were collected at the Hall of the Ambassadors and characterised to determine its potential degradation profile. These were analysed by means of micro-Raman spectroscopy (MRS) and electron probe microanalysis with X-ray detection (EPXMA). The Raman data indicated the presence of various mixed salts of acidic and/or hygroscopic nature, such as sodium and ammonium nitrates and sulfates, especially in the finer fraction. Automated EPXMA estimated this fraction to be as high as 50%. Apart from the potential chemical attack, the soiling due to carbonaceous matter deposition is a real concern. Soot was identified by MRS and EPXMA in all size fractions, reaching values of up to 55%, and was often intertwined with soluble inorganic salts. Ongoing degradation of the pigments is implicated by the presence of brightly coloured particles. MRS and molar abundance ternary diagrams elicited the chemical structure of individual APM so that the degradation potential could be established.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1002/JRS.4052
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of spectromicroscopic methods : 3 : synthesis, characterization, and detection of different crystal forms of the chrome yellow pigment”. Monico L, Janssens K, Miliani C, Brunetti BG, Vagnini M, Vanmeert F, Falkenberg G, Abakumov A, Lu Y, Tian H, Verbeeck J, Radepont M, Cotte M, Hendriks E, Geldof M, van der Loeff L, Salvant J, Menu M;, Analytical chemistry 85, 860 (2013). http://doi.org/10.1021/ac302158b
Abstract: The painter, Vincent van Gogh, and some of his contemporaries frequently made use of the pigment chrome yellow that is known to show a tendency toward darkening. This pigment may correspond to various chemical compounds such as PbCrO4 and PbCr1-xSxO4, that may each be present in various crystallographic forms with different tendencies toward degradation. Investigations by X-ray diffraction (XRD), mid-Fourier Transform infrared (FTIR), and Raman instruments (benchtop and portable) and synchrotron radiation-based micro-XRD and X-ray absorption near edge structure spectroscopy performed on oil-paint models, prepared with in-house synthesized PbCrO4 and PbCr1-xSxO4, permitted us to characterize the spectroscopic features of the various forms. On the basis of these results, an extended study has been carried out on historic paint tubes and on embedded paint microsamples taken from yellow-orange/pale yellow areas of 12 Van Gogh paintings, demonstrating that Van Gogh effectively made use of different chrome yellow types. This conclusion was also confirmed by in situ mid-FTIR investigations on Van Goghs Portrait of Gauguin (Van Gogh Museum, Amsterdam).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 79
DOI: 10.1021/ac302158b
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of spectromicroscopic methods : 4 : artificial aging of model samples of co-precipitates of lead chromate and lead sulfate”. Monico L, Janssens K, Miliani C, van der Snickt G, Brunetti BG, Guidi MC, Radepont M, Cotte M, Analytical chemistry 85, 860 (2013). http://doi.org/10.1021/AC3021592
Abstract: Previous investigations about the darkening of chrome yellow pigments revealed that this form of alteration is attributable to a reduction of the original Cr(VI) to Cr(III), and that the presence of sulfur-containing compounds, most often sulfates, plays a key role during this process. We recently demonstrated that different crystal forms of chrome yellow pigments (PbCrO4 and PbCr1xSxO4) are present in paintings by Vincent van Gogh. In the present work, we show how both the chemical composition and the crystalline structure of lead chromate-based pigments influence their stability. For this purpose, oil model samples made with in-house synthesized powders of PbCrO4 and PbCr1xSxO4 were artificially aged and characterized. We observed a profound darkening only for those paint models made with PbCr1xSxO4, rich in SO42 (x ≥ 0.4), and orthorhombic phases (>30 wt %). Cr and S K-edge micro X-ray absorption near edge structure investigations revealed in an unequivocal manner the formation of up to about 60% of Cr(III)-species in the outer layer of the most altered samples; conversely, independent of the paint models chemical composition, no change in the S-oxidation state was observed. Analyses employing UVvisible diffuse reflectance and Fourier transform infrared spectroscopy were performed on unaged and aged model samples in order to obtain additional information on the physicochemical changes induced by the aging treatment.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 49
DOI: 10.1021/AC3021592
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of spectromicroscopic methods : part 5 : effects of nonoriginal surface coatings into the nature and distribution of chromium and sulfur species in chrome yellow paints”. Monico L, Janssens K, Vanmeert F, Cotte M, Brunetti BG, van der Snickt G, Leeuwestein M, Plisson JS, Menu M, Miliani C, Analytical chemistry 86, 10804 (2014). http://doi.org/10.1021/AC502841G
Abstract: The darkening of lead chromate yellow pigments, caused by a reduction of the chromate ions to Cr(III) compounds, is known to affect the appearance of several paintings by Vincent van Gogh. In previous papers of this series, we demonstrated that the darkening is activated by light and depends on the chemical composition and crystalline structure of the pigments. In this work, the results of Part 2 are extended and complemented with a new study aimed at deepening the knowledge of the nature and distribution of Cr and S species at the interface between the chrome yellow paint and the nonoriginal coating layer. For this purpose, three microsamples from two varnished paintings by Van Gogh and a waxed low relief by Gauguin (all originally uncoated) have been examined. Because nonoriginal coatings are often present in artwork by Van Gogh and contemporaries, the understanding of whether or not their application has influenced the morphological and/or physicochemical properties of the chrome yellow paint underneath is relevant in view of the conservation of these masterpieces. In all the samples studied, microscopic X-ray fluorescence (mu-XRF) and X-ray absorption near edge structure (mu-XANES) investigations showed that Cr(III)-based alteration products are present in the form of grains inside the coating (generally enriched of S species) and also homogeneously widespread at the paint surface. The distribution of Cr(III) species may be explained by the mechanical friction caused by the coating application by brush that picked up and redistributed the superficial Cr compounds, likely already present in the reduced state as result of the photodegradation process. The analysis of the XANES profiles allowed us to obtain new insights into the nature of the Cr(III) alteration products, that were identified as sulfate-, oxide-, organo-metal-, and chloride-based compounds. Building upon the knowledge acquired through the examination of original paint samples and from the investigation of aged model paints in the last Part 4 paper, in this study we aim to characterize a possible relation between the chemical composition of the coating and the chrome yellow degradation pathways by studying photochemically aged model samples covered with a dammar varnish contaminated with sulfide and sulfate salts. Cr speciation results did not show any evidence of the active role of the varnish and added S species on the reduction process of chrome yellows.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 25
DOI: 10.1021/AC502841G
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of synchrotron X-ray spectromicroscopy and related methods : 1 : artificially aged model samples”. Monico L, van der Snickt G, Janssens K, de Nolf W, Miliani C, Verbeeck J, Tian H, Tan H, Dik J, Radepont M, Cotte M, Analytical chemistry 83, 1214 (2011). http://doi.org/10.1021/ac102424h
Abstract: On several paintings by artists of the end of the 19th century and the beginning of the 20th Century a darkening of the original yellow areas, painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is observed. The most famous of these are the various Sunflowers paintings Vincent van Gogh made during his career. In the first part of this work, we attempt to elucidate the degradation process of chrome yellow by studying artificially aged model samples. In view of the very thin (1−3 μm) alteration layers that are formed, high lateral resolution spectroscopic methods such as microscopic X-ray absorption near edge (μ-XANES), X-ray fluorescence spectrometry (μ-XRF), and electron energy loss spectrometry (EELS) were employed. Some of these use synchrotron radiation (SR). Additionally, microscopic SR X-ray diffraction (SR μ-XRD), μ-Raman, and mid-FTIR spectroscopy were employed to completely characterize the samples. The formation of Cr(III) compounds at the surface of the chrome yellow paint layers is particularly observed in one aged model sample taken from a historic paint tube (ca. 1914). About two-thirds of the chromium that is present at the surface has reduced from the hexavalent to the trivalent state. The EELS and μ-XANES spectra are consistent with the presence of Cr2O3·2H2O (viridian). Moreover, as demonstrated by μ-XANES, the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide], is likely.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 113
DOI: 10.1021/ac102424h
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of synchrotron X-ray spectromicroscopy and related methods : 2 : original paint layer samples”. Monico L, van der Snickt G, Janssens K, de Nolf W, Miliani C, Dik J, Radepont M, Hendriks E, Geldof M, Cotte M, Analytical chemistry 83, 1224 (2011). http://doi.org/10.1021/AC1025122
Abstract: The darkening of the original yellow areas painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is a phenomenon widely observed on several paintings by Vincent van Gogh, such as the famous different versions of Sunflowers. During our previous investigations on artificially aged model samples of lead chromate, we established for the first time that darkening of chrome yellow is caused by reduction of PbCrO4 to Cr2O3·2H2O (viridian green), likely accompanied by the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide]. In the second part of this work, in order to demonstrate that this reduction phenomenon effectively takes place in real paintings, we study original paint samples from two paintings of V. van Gogh. As with the model samples, in view of the thin superficial alteration layers that are present, high lateral resolution spectroscopic methods that make use of synchrotron radiation (SR), such as microscopic X-ray absorption near edge (μ-XANES) and X-ray fluorescence spectrometry (μ-XRF) were employed. Additionally, μ-Raman and mid-FTIR analyses were carried out to completely characterize the samples. On both paint microsamples, the local presence of reduced Cr was demonstrated by means of μ-XANES point measurements. The presence of Cr(III) was revealed in specific areas, in some cases correlated to the presence of Ba(sulfate) and/or to that of aluminum silicate compounds.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 84
DOI: 10.1021/AC1025122
|
“Dehazing redox homeostasis to foster purple bacteria biotechnology”. Alloul A, Blansaer N, Cabecas Segura P, Wattiez R, Vlaeminck SE, Leroy B, Trends in biotechnology : regular edition 41, 106 (2023). http://doi.org/10.1016/J.TIBTECH.2022.06.010
Abstract: Purple non-sulfur bacteria (PNSB) show great potential for environmental and industrial biotechnology, producing microbial protein, biohydrogen, polyhydroxyalkanoates (PHAs), pigments, etc. When grown photoheterotrophically, the carbon source is typically more reduced than the PNSB biomass, which leads to a redox imbalance. To mitigate the excess of electrons, PNSB can exhibit several ‘electron sinking’ strategies, such as CO2 fixation, N2 fixation, and H2 and PHA production. The lack of a comprehensive (over)view of these redox strategies is hindering the implementation of PNSB for biotechnology applications. This review aims to present the state of the art of redox homeostasis in phototrophically grown PNSB, presenting known and theoretically expected strategies, and discussing them from stoichiometric, thermodynamic, metabolic, and economic points of view.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 17.3
DOI: 10.1016/J.TIBTECH.2022.06.010
|
“Demonstration of a 2 × 2 programmable phase plate for electrons”. Verbeeck J, Béché, A, Müller-Caspary K, Guzzinati G, Luong MA, Den Hertog M, Ultramicroscopy 190, 58 (2018). http://doi.org/10.1016/j.ultramic.2018.03.017
Abstract: First results on the experimental realisation of a 2 × 2 programmable phase plate for electrons are presented. The design consists of an array of electrostatic elements that influence the phase of electron waves passing through 4 separately controllable aperture holes. This functionality is demonstrated in a conventional transmission electron microscope operating at 300 kV and results are in very close agreement with theoretical predictions. The dynamic creation of a set of electron probes with different phase symmetry is demonstrated, thereby bringing adaptive optics in TEM one step closer to reality. The limitations of the current design and how to overcome these in the future are discussed. Simulations show how further evolved versions of the current proof of concept might open new and exciting application prospects for beam shaping and aberration correction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 73
DOI: 10.1016/j.ultramic.2018.03.017
|
“Demonstration of lanthanum in liver cells by energy-dispersive X-ray spectroscopy, electron energy loss spectroscopy and high-resolution transmission electron microscopy”. Yang Z, Schryvers D, Roels F, d' Haese PC, de Broe ME, Journal of microscopy 223, 133 (2006). http://doi.org/10.1111/j.1365-2818.2006.01601.x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Pathophysiology
Impact Factor: 1.692
Times cited: 29
DOI: 10.1111/j.1365-2818.2006.01601.x
|
“Densification of thin a-C: H films grown from low-kinetic energy hydrocarbon radicals under the influence of H and C particle fluxes: a molecular dynamics study”. Neyts E, Bogaerts A, van de Sanden MCM, Journal of physics: D: applied physics 39, 1948 (2006). http://doi.org/10.1088/0022-3727/39/9/034
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.588
Times cited: 3
DOI: 10.1088/0022-3727/39/9/034
|
“Density dependence of the rectification of vortex motion in a circular asymmetric channel”. Lin NS, Misko VR, Heitmann TW, Yu K, Plourde BLT, Physica: C : superconductivity 479, 137 (2012). http://doi.org/10.1016/j.physc.2011.12.028
Abstract: We study the rectification of vortex motion in an asymmetric ring channel in a Corbino setup. With an applied ac current, the motion of vortices in the channel is rectified by the asymmetric potential and induces a dc net flow. The net flow in such a system strongly depends on vortex density, and we distinguish “single-vortex'' rectification regime (for low density, when each vortex is rectified individually) determined by the potential-energy landscape inside each cell of the channel and ”multi-vortex'', or "collective'', rectification (high density case) when the interaction between vortices becomes important. (C) 2012 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.404
DOI: 10.1016/j.physc.2011.12.028
|