“Knitting the catalytic pattern of artificial photosynthesis to a hybrid graphene nanotexture”. Quintana M, López AM, Rapino S, Toma FM, Iurlo M, Carraro M, Sartorel A, Maccato C, Ke X, Bittencourt C, Da Ros T, Van Tendeloo G, Marcaccio M, Paolucci F, Prato M, Bonchio M;, ACS nano 7, 811 (2013). http://doi.org/10.1021/nn305313q
Abstract: The artificial leaf project calls for new materials enabling multielectron catalysis with minimal overpotential, high turnover frequency, and long-term stability. Is graphene a better material than carbon nanotubes to enhance water oxidation catalysis for energy applications? Here we show that functionalized graphene with a tailored distribution of polycationic, quaternized, ammonium pendants provides an sp(2) carbon nanoplatform to anchor a totally inorganic tetraruthenate catalyst, mimicking the oxygen evolving center of natural PSII. The resulting hybrid material displays oxygen evolution at overpotential as low as 300 mV at neutral pH with negligible loss of performance after 4 h testing. This multilayer electroactive asset enhances the turnover frequency by 1 order of magnitude with respect to the isolated catalyst, and provides a definite up-grade of the carbon nanotube material, with a similar surface functionalization. Our innovation is based on a noninvasive, synthetic protocol for graphene functionalization that goes beyond the ill-defined oxidation-reduction methods, allowing a definite control of the surface properties.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 69
DOI: 10.1021/nn305313q
|
“KSm(MoO4)2, an incommensurately modulated and partially disordered scheelite-like structure”. Arakcheeva A, Pattison P, Chapuis G, Rossell M, Filaretov A, Morozov V, Van Tendeloo G, Acta crystallographica: section B: structural science 64, 160 (2008). http://doi.org/10.1107/S0108768108001870
Abstract: The incommensurately modulated scheelite-like KSm( MoO4)(2) structure has been refined in the monoclinic superspace group I2/b(alpha beta 0)00 by the Rietveld method on the basis of synchrotron radiation powder diffraction data. The systematic broadening of satellite reflections has been accounted for by applying anisotropic microstrain line-broadening. The microstructure has been studied by transmission electron microscopy (TEM). The partial disorder of the K and Sm cations in the A position is best approximated by a combination of harmonic and complex crenel functions with (0.952Sm + 0.048K) and (0.952K + 0.048Sm) atomic domains. This combination yields a compositional wave distribution from {KMoO4} to {SmMoO4} observed in the ab structure projection along q. The specific features of KSm(MoO4)(2) and degree of the A-cation ordering are discussed in comparison with the previously reported structure of KNd(MoO4)(2).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 23
DOI: 10.1107/S0108768108001870
|
“K₅Eu(MoO₄)₄, red phosphor for solid state lighting applications, prepared by different techniques”. Posokhova SMM, Morozov VA, Deyneko DVV, Redkin BSS, Spassky DAA, Nagirnyi V, Belik AAA, Hadermann J, Pavlova ETT, Lazoryak BII, CrystEngComm 25, 835 (2023). http://doi.org/10.1039/D2CE01107G
Abstract: The influence of preparation techniques on the structure and luminescent properties of K5Eu(MoO4)(4) (KEMO) was investigated. KEMO phosphors were synthesized by three different techniques: solid state and sol-gel (sg) methods as well as the Czochralski (CZ) crystal growth technique. Laboratory powder X-ray diffraction (PXRD) studies revealed that all KEMO samples had a structure analogous to that of other high temperature alpha-K5R(MoO4)(4) palmierite-type phases (space group (SG) R3m). Contrary to laboratory PXRD data, electron diffraction revealed that the KEMO crystal grown by the CZ technique had a (3 + 1)D incommensurately modulated structure (super space group (SSG) C2/m(0 beta 0)00) with the modulation vector q = 0.689b*. A detailed analysis of electron diffraction patterns has shown formation of three twin domains rotated along the c axis of the R-subcell at 60 degrees with respect to each other. Synchrotron XRD patterns showed additional ultra-wide reflexes in addition to reflections of the R-subcell of the palmierite. However, the insufficient number of reflections, their low intensity and large width in the synchrotron X-ray diffraction patterns made it impossible to refine the structure as incommensurately modulated C2/m(0 beta 0)00. An average structure was refined in the C2/m space group with random distribution of K1 and Eu1 in [M1A(2)O(8)]-layers of the palmierite-type structure. The dependence of luminescent properties on utilized synthesis techniques was studied. The emission spectra of all samples exhibit intense red emission originating from the D-5(0) -> F-7(2) Eu3+ transition. The integrated intensity of the emission from the Eu3+ 5D0 term was found to be the highest in the crystal grown by the CZ technique. The quantum yield measured for KEMO crystals demonstrates a very high value of 66.5%. This fact confirms that KEMO crystals are exceptionally attractive for applications as a near-UV converting red phosphor for LEDs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1039/D2CE01107G
|
“La microscopie électronique à, transmission (MET) et son utilisation dans l'étude d'inclusions nano-cristallines dans le verre”. Fredrickx P, Schryvers D, L'archéométrie au service des monuments et des oeuvres d'art 10, 131 (2002)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
“LaFeO3 nanofibers for high detection of sulfur-containing gases”. Queralto A, Graf D, Frohnhoven R, Fischer T, Vanrompay H, Bals S, Bartasyte A, Mathur S, ACS Sustainable Chemistry and Engineering 7, 6023 (2019). http://doi.org/10.1021/ACSSUSCHEMENG.8B06132
Abstract: Lanthanum ferrite nanofibers were electrospun from a chemical sol and calcined at 600 degrees C to obtain singlephase LaFeO3 (LFO) perovskite. High-resolution transmission electron microscopy in conjunction with 3D tomographic analysis confirmed an interwoven network of hollow and porous (surface) LFO nanofibers. Owing to their high surface area and p-type behavior, the nanofiber meshes showed high chemoselectivity toward reducing toxic gases (SO2, H2S) that could be reproducibly detected at very low concentrations (<1 ppm), well below the threshold values for occupational safety and health. An increased sensitivity was observed in the temperature range of 150-300 degrees C with maximum sensor response at 250 degrees C. The surface reaction at the heterogeneous solid (LFO)/gas (SO2) interface that confirmed the formation of La-2(SO4)(3) was investigated by X-ray photoelectron spectroscopy. Moreover, the LFO fibers showed a high selectivity in the detection of oxidizing and reducing gases. Whereas superior detection of NH3 and H2S was measured, little response was observed for CO and NO2. Finally, the integration of nanowire meshes in commercial sensor platforms was successfully demonstrated.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.951
Times cited: 41
DOI: 10.1021/ACSSUSCHEMENG.8B06132
|
“Landscape roughness at an atomic scale”. Van Tendeloo G, De Meulenaere P, Schryvers D, Physica: D : nonlinear phenomena 107, 401 (1997). http://doi.org/10.1016/S0167-2789(97)00108-5
Abstract: A large number of materials have a highly degenerate ground state and therefore a complex microstructure. Because of this degenerate state, phase transitions between the different phases play an important role. High resolution techniques in electron microscopy and nano-scale chemical analysis allow to study not only the microstructure but also the interfaces down to an atomic scale. We focus particularly on the ambiguity of alloys oil approaching the phase transition. The short range order (SRO) in ''1 1/20'' type alloys and the microstructure of ''tweed'' and needle formation in martensite like alloys with composition Ni5Al3 are considered in more detail.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.514
Times cited: 2
DOI: 10.1016/S0167-2789(97)00108-5
|
“Lanthanum-strontium cuprate as a promising cathodic matreila for solid oxide fuel cells”. Mazo GN, Savvin SN, Abakumov AM, Hadermann J, Dobrovol'skii YA, Leonova LS, Russian journal of electrochemistry 43, 436 (2007). http://doi.org/10.1134/S1023193507040106
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.828
Times cited: 8
DOI: 10.1134/S1023193507040106
|
“Large pinning forces and matching effects in YBa2Cu3O7-&delta, thin films with Ba2Y(Nb/Ta)O6 nano-precipitates”. Opherden L, Sieger M, Pahlke P, Hühne R, Schultz L, Meledin A, Van Tendeloo G, Nast R, Holzapfel B, Bianchetti M, MacManus-Driscoll JL, Hänisch J, Scientific reports 6, 21188 (2016). http://doi.org/10.1038/srep21188
Abstract: The addition of mixed double perovskite Ba2Y(Nb/Ta)O6 (BYNTO) to YBa2Cu3O7−δ (YBCO) thin films leads to a large improvement of the in-field current carrying capability. For low deposition rates, BYNTO grows as well-oriented, densely distributed nanocolumns. We achieved a pinning force density of 25 GN/m3 at 77 K at a matching field of 2.3 T, which is among the highest values reported for YBCO. The anisotropy of the critical current density shows a complex behavior whereby additional maxima are developed at field dependent angles. This is caused by a matching effect of the magnetic fields c-axis component. The exponent N of the current-voltage characteristics (inversely proportional to the creep rate S) allows the depinning mechanism to be determined. It changes from a double-kink excitation below the matching field to pinning-potential-determined creep above it.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
Times cited: 39
DOI: 10.1038/srep21188
|
“Large scale synthesis of carbon nanotubes and their composite materials”. Nagy JB, Fonseca A, Pierard N, Willems I, Bister G, Pirlot C, Demortier A, Delhalle J, Mekhalif Z, Niesz K, Bossuot C, Pirard J-P, Biró, LP, Konya Z, Colomer J-F, Van Tendeloo G, Kiricsi I, (2001)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
“Large-scale synthesis of single-wall carbon nanotubes by catalytic chemical vapor deposition (CCVD) method”. Colomer JF, Stephan C, Lefrant S, Van Tendeloo G, Willems I, Konya Z, Fonseca A, Laurent C, Nagy JB, Chemical physics letters 317, 83 (2000). http://doi.org/10.1016/S0009-2614(99)01338-X
Abstract: The large-scale production of single-wall carbon nanotubes (SWNTs) is reported. Large quantities of SWNTs can be synthesised by catalytic decomposition of methane over well-dispersed metal particles supported on MgO at 1000 degrees C. The thus produced SWNTs can be separated easily from the support by a simple acidic treatment to obtain a product with high yields (70-80%) of SWNTs. Because the typical synthesis time is 10 min, 1 g of SWNTs can be synthesised per day by this method. The SWNTs are characterized by high-resolution transmission electron microscopy and by Raman spectroscopy, showing the quality and the quantity of products. (C) 2000 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 344
DOI: 10.1016/S0009-2614(99)01338-X
|
“Laser induced phase transition in iron thin films”. Teodorescu VS, Mihailescu IN, Dinescu M, Chitica N, Nistor LC, van Landuyt J, Barborica A, Journal de physique: 3: applied physics, materials science, fluids, plasma and instrumentation 4, 127 (1994). http://doi.org/10.1051/jp4:1994427
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1051/jp4:1994427
|
“Laser synthesis of hard carbon for anodes in Na-ion battery”. Zhang B, Deschamps M, Ammar M-R, Raymundo-Pinero E, Hennet L, Batuk D, Tarascon J-M, Advanced Materials Technologies 2, 1600227 (2017). http://doi.org/10.1002/ADMT.201600227
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 10
DOI: 10.1002/ADMT.201600227
|
“Laser thermotreatment of the SnO2layers”. Rembeza SI, Loginov VA, Svistova TV, Podkopaeva OI, Rembeza ES, van Landuyt J, Eurosensors XII, vols 1 and 2 , 481 (1998)
Abstract: The optical and electrical properties and pi ase composition of magnetron sputtered antimony-doped SnOx thin films are investigated before and after laser thermotreatment The temperature dependencies on mobility and concentration of free charges are measured by Van der Pauw method. The gas sensitivity of SnOx has been measured before and after laser thermotreatment.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
“Laser-induced periodic annular surface structures on fused silica surface”. Liu Y, Brelet Y, He Z, Yu L, Forestier B, Deng Y, Jiang H, Houard A, Applied physics letters 102, 251103 (2013). http://doi.org/10.1063/1.4812354
Abstract: We report on the formation of laser-induced periodic annular surface structures on fused silica irradiated with multiple femtosecond laser pulses. This surface morphology emerges after the disappearance of the conventional laser induced periodic surface structures, under successive laser pulse irradiation. It is independent of the laser polarization and universally observed for different focusing geometries. We interpret its formation in terms of the interference between the reflected laser field on the surface of the damage crater and the incident laser pulse. (C) 2013 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 19
DOI: 10.1063/1.4812354
|
“Lattice deformations at martensite-martensite interfaces in Ni-Al”. Schryvers D, Boullay P, Kohn R, Ball J, Journal de physique: 4 11, 23 (2001). http://doi.org/10.1051/jp4:2001804
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 9
DOI: 10.1051/jp4:2001804
|
“Lattice deformations in quasi-dynamic strain glass visualised and quantified by aberration corrected electron microscopy”. Lu J, Martinez GT, Van Aert S, Schryvers D, Physica status solidi: B: basic research 251, 2034 (2014). http://doi.org/10.1002/pssb.201350351
Abstract: Advanced transmission electron microscopy and statistical parameter estimated quantification procedures were applied to study the room temperature quasi-dynamical strain glass state in NiTi alloys. Nanosized strain pockets are visualised and the displacements of the atom columns are quantified. A comparison is made with conventional high-resolution transmission electron microscopy images of point defect induced strains in NiAl alloys.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.674
Times cited: 2
DOI: 10.1002/pssb.201350351
|
“Layer-by-layer delithiation during lattice collapse as the origin of planar gliding and microcracking in Ni-rich cathodes”. Yu R, Zeng W, Zhou L, Van Tendeloo G, Mai L, Yao Z, Wu J, Cell reports physical science 4, 101480 (2023). http://doi.org/10.1016/J.XCRP.2023.101480
Abstract: High-energy-density nickel (Ni)-rich cathode materials are used in commercial lithium (Li)-ion batteries for electric vehicles, but they suffer from severe structural degradation upon cycling. Planar gliding and microcracking are seeds for fatal mechanical fracture, but their origin remains unclear. Herein, we show that “layer-by -layer delithiation”is activated at high voltages during the charge process when the “lattice collapse”(a characteristic high-voltage lattice evolution in Ni-rich cathodes) occurs. Layer-by-layer deli-thiation is evidenced by direct observation of the consecutive lattice collapse using in situ scanning transmission electron micro-scopy (STEM). The collapsing of the lattice initiates in the expanded planes and consecutively extends to the whole crystal. Localized strain will be induced at lattice-collapsing interface where planar gliding and intragranular microcracks are generated to release this strain. Our study reveals that layer-by-layer delithia-tion during lattice collapse is the fundamental origin of the mechanical instability in single-crystalline Ni-rich cathodes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.XCRP.2023.101480
|
“Layered CeSO and LiCeSO oxide chalcogenides obtained via topotactic oxidative and reductive transformations”. Cassidy SJ, Pitcher MJ, Lim JJK, Hadermann J, Allen JP, Watson GW, Britto S, Chong EJ, Free DG, Grey CP, Clarke SJ, Inorganic chemistry 58, 3838 (2019). http://doi.org/10.1021/ACS.INORGCHEM.8B03485
Abstract: The chemical accessibility of the Celv oxidation state enables redox chemistry to be performed on the naturally coinagemetal -deficient phases CeM1-xSO (M = Cu, Ag). A metastable black compound with the PbFC1 structure type (space group P4/nmm: a = 3.8396(1) angstrom, c = 6.607(4) angstrom, V = 97.40(6) angstrom(3)) and a composition approaching CeSO is obtained by deintercalation of Ag from CeAg0.8SO. High-resolution transmission electron microscopy reveals the presence of large defect-free regions in CeSO, but stacking faults are also evident which can be incorporated into a quantitative model to account for the severe peak anisotropy evident in all the highresolution X-ray and neutron diffractograms of bulk CeSO samples; these suggest that a few percent of residual Ag remains. A strawcolored compound with the filled PbFCI (i.e., ZrSiCuAs- or HfCuSi2type) structure (space group P4/nmm: a = 3.98171(1) angstrom, c = 8.70913(5) angstrom, V = 138.075(1) angstrom 3) and a composition close to LiCeSO, but with small amounts of residual Ag, is obtained by direct reductive lithiation of CeAga8S0 or by insertion of Li into CeSO using chemical or electrochemical means. Computation of the band structure of pure, stoichiometric CeSO predicts it to be a Ce' compound with the 4f-states lying approximately 1 eV above the sulfide-dominated valence band maximum. Accordingly, the effective magnetic moment per Ce ion measured in the CeSO samples is much reduced from the value found for the Ce3+-containing LiCeSO, and the residual paramagnetism corresponds to the Ce3+ ions remaining due to the presence of residual Ag, which presumably reflects the difficulty of stabilizing Ce' in the presence of sulfide (S2-). Comparison of the behavior of CeCu0.8SO with that of CeCu0.8SO reveals much slower reaction kinetics associated with the Cu,_xS layers, and this enables intermediate CeCui LixSO phases to be isolated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
DOI: 10.1021/ACS.INORGCHEM.8B03485
|
“Layered ordering of vacancies of lead iron phosphate Pb3Fe2(PO4)4”. Malakho AP, Morozov VA, Pokholok KV, Lazoryak BI, Van Tendeloo G, Solid state sciences 7, 397 (2005). http://doi.org/10.1016/j.solidstatesciences.2005.01.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 7
DOI: 10.1016/j.solidstatesciences.2005.01.007
|
“Layered oxychlorides [PbBiO2]An+1BnO3n-1Cl2(A = Pb/Bi, B = Fe/Ti) : intergrowth of the hematophanite and sillen phases”. Batuk M, Batuk D, Tsirlin AA, Filimonov DS, Sheptyakov DV, Frontzek M, Hadermann J, Abakumov AM, Chemistry of materials 27, 2946 (2015). http://doi.org/10.1021/acs.chemmater.5b00233
Abstract: New layered structures corresponding to the general formula [PbBiO2]A(n+1)B(n)O(3n-1)Cl(2) Were prepared. Pb5BiFe3O10Cl2 (n = 3) and Pb5Bi2Fe4O13Cl2 (n = 4) are built as a stacking of truncated A(n+1)B(n)O(3n-1) perovskite blocks and alpha-PbO-type [A(2)O(2)](2+) (A = Pb, Bi) blocks combined with chlorine sheets. The alternation of these structural blocks can be represented as an intergrowth between the hematophanite and Sullen-type structural blocks. The crystal and-Magnetic structures of Pb5BiFe3O10Cl2 and Pb5Bi2Fe4O13Cl2 were investigated in the temperature range of 1.5-700 K using X-ray and neutron powder diffraction, transmission electron microscopy and Fe-57 Mossbauer spectroscopy. Both compounds crystallize in the I4/mmm space group with the unit cell parameters a approximate to a(p) approximate to 3.92 angstrom (a unit-cell parameter of the perovskite-structure), c approximate to 43.0 angstrom for the n = 3 member and c approximate to 53.5 angstrom for the n = 4 member. Despite the large separation between the slabs containing the Fe3+ ions (nearly 14 angstrom), long-range antiferromagnetic order sets in below similar to 600 K with the G-type arrangement of the Fe magnetic moments aligned along the c-axis. The possibility of mixing d(0) and d(n) cations at the B sublattice of these structures was also demonstrated by preparing the Ti-substituted n = 4 member Pb6BiFe3TiO13Cl2.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 11
DOI: 10.1021/acs.chemmater.5b00233
|
“Layered oxygen vacancy ordering in Nb-doped SrCo1-xFexO3-\delta perovskite”. Van Rompaey S, Dachraoui W, Turner S, Podyacheva OY, Tan H, Verbeeck J, Abakumov A, Hadermann J, Zeitschrift für Kristallographie 228, 28 (2013). http://doi.org/10.1524/zkri.2013.1556
Abstract: The crystal structure of SrCo0.7Fe0.2Nb0.1O2.72 was determined using a combination of precession electron diffraction (PED), high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM) and spatially resolved electron energy loss spectroscopy (STEM-EELS). The structure has a tetragonal P4/mmm symmetry with cell parameters a = b = a(p), c = 2a(p) (a(p) being the cell parameter of the perovskite parent structure). Octahedral BO2 layers alternate with the anion-deficient BO1.4 layers, the different B cations are randomly distributed over both layers. The specific feature of the SrCo0.7Fe0.2NB0.1O2.72 microstructure is a presence of extensive nanoscale twinning resulting in domains with alignment of the tetragonal c-axis along all three cubic direction of the perovskite subcell.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.179
Times cited: 9
DOI: 10.1524/zkri.2013.1556
|
“Layered perovskite-like Pb2Fe2O5 structure as a parent matrix for the nucleation and growth of crystallographic shear planes”. Batuk D, Hadermann J, Abakumov A, Vranken T, Hardy A, van Bael M, Van Tendeloo G, Inorganic chemistry 50, 4978 (2011). http://doi.org/10.1021/ic200211x
Abstract: The Pb2Fe2O5 compound with a layered intergrowth structure has been prepared by a solid-state reaction at 700 °C. The incommensurate compound crystallizes in a tetragonal system with a = 3.9037(2) Å, c = 3.9996(4) Å, and q = 0.1186(4)c*, or when treated as a commensurate approximant, a = 3.9047(2) Å, c = 36.000(3) Å, space group I4/mmm. The crystal structure of Pb2Fe2O5 was resolved from transmission electron microscopy data. Atomic coordinates and occupancies of the cation positions were estimated from high-angle annular dark-field scanning transmission electron microscopy data. Direct visualization of the positions of the oxygen atoms was possible using annular bright-field scanning transmission electron microscopy. The structure can be represented as an intergrowth of perovskite blocks and partially disordered blocks with a structure similar to that of the Bi2O2 blocks in Aurivillius-type phases. The A-cation positions at the border of the perovskite block and the cation positions in the Aurivillius-type blocks are jointly occupied by Pb2+ and Fe3+ cations, resulting in a layer sequence along the c axis: PbOFeO2PbOFeO2Pb7/8Fe1/8O1xFe5/8Pb3/8O2Fe5/8Pb3/8. Upon heating, the layered Pb2Fe2O5 structure transforms into an anion-deficient perovskite modulated by periodically spaced crystallographic shear (CS) planes. Considering the layered Pb2Fe2O5 structure as a parent matrix for the nucleation and growth of CS planes allows an explanation of the specific microstructure observed for the CS structures in the PbFeO system.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 16
DOI: 10.1021/ic200211x
|
“Layered Silicate Clays as Templates for Anisotropic Gold Nanoparticle Growth”. Hill EH, Claes N, Bals S, Liz-Marzán LM, Chemistry of materials 28, 5131 (2016). http://doi.org/10.1021/acs.chemmater.6b02186
Abstract: Clay minerals are abundant natural materials arising in the presence of water and are composed of small particles of different sizes and shapes. The interlamellar space between layered silicate clays can also be used to host a variety of different organic and inorganic guest molecules or particles. Recent studies of clay−metal hybrids formed by impregnation of nanoparticles into the interlayer spaces of the clays have not demonstrated the ability for templated growth following the shape of the particles. Following this line of interest, a method for the synthesis of gold nanoparticles on the synthetic layered silicate clay laponite was developed. This approach can be used to make metal−clay nanoparticles with a variety of morphologies while retaining the molecular adsorption properties of the clay. The surface enhanced Raman scattering enhancement of these particles was also found to be greater than that obtained from other metal nanoparticles of a similar morphology, likely due to increased dye adsorption by the presence of the clay. The hybrid particles presented herein will contribute to further study of plasmonic
sensing, catalysis, dye aggregation, and novel composite materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 13
DOI: 10.1021/acs.chemmater.6b02186
|
“Layered structures accomodating stoichiometry in M2X2O7 systems, as seen by diffraction and HREM”. Nihoul G, Leroux C, Cesari C, Van Tendeloo G, Electron microscopy: vol. 2 , 295 (1998)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
“Layered-to-Tunnel Structure Transformation and Oxygen Redox Chemistry in LiRhO2upon Li Extraction and Insertion”. Mikhailova D, Karakulina OM, Batuk D, Hadermann J, Abakumov AM, Herklotz M, Tsirlin AA, Oswald S, Giebeler L, Schmidt M, Eckert J, Knapp M, Ehrenberg H, Inorganic chemistry 55, 7079 (2016). http://doi.org/10.1021/acs.inorgchem.6b01008
Abstract: Layered Li(M,Li)O2 (where M is a transition metal) ordered rock-salt-type structures are used in advanced metal-ion batteries as one of the best hosts for the reversible intercalation of Li ions. Besides the conventional redox reaction involving oxidation/reduction of the M cation upon Li extraction/insertion, creating oxygen-located holes because of the partial oxygen oxidation increases capacity while maintaining the oxidized oxygen species in the lattice through high covalency of the M–O bonding. Typical degradation mechanism of the Li(M,Li)O2 electrodes involves partially irreversible M cation migration toward the Li positions, resulting in gradual capacity/voltage fade. Here, using LiRhO2 as a model system (isostructural and isoelectronic to LiCoO2), for the first time, we demonstrate an intimate coupling between the oxygen redox and M cation migration. A formation of the oxidized oxygen species upon electrochemical Li extraction coincides with transformation of the layered Li1–xRhO2 structure into the γ-MnO2-type rutile–ramsdellite intergrowth LiyRh3O6 structure with rutile-like [1 × 1] channels along with bigger ramsdellite-like [2 × 1] tunnels through massive and concerted Rh migration toward the empty positions in the Li layers. The oxidized oxygen dimers with the O–O distances as short as 2.26 Å are stabilized in this structure via the local Rh–O configuration reminiscent to that in the μ-peroxo-μ-hydroxo Rh complexes. The LiyRh3O6 structure is remarkably stable upon electrochemical cycling illustrating that proper structural implementation of the oxidized oxygen species can open a pathway toward deliberate employment of the anion redox chemistry in high-capacity/high-voltage positive electrodes for metal-ion batteries. Upon chemical or electrochemical oxidation, layered LiRhO2 shows a unique structural transformation that involves both cation migration and oxidation of oxygen resulting in a stable tunnel-like rutile−ramsdellite intergrowth LiyRh3O6 structure. This structure demonstrates excellent performance with the steady and reversible capacity of ∼200 mAh/g. The stability of LiyRh3O6 is rooted in the accommodation of partially oxidized oxygen species through the formation of short O−O distances that are compatible with the connectivity of RhO6 octahedra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 12
DOI: 10.1021/acs.inorgchem.6b01008
|
“La1.5Sr0.5NiMn0.5Ru0.5O6 double perovskite with enhanced ORR/OER bifunctional catalytic activity”. Retuerto M, Calle-Vallejo F, Pascual L, Lumbeeck G, Fernandez-Diaz MT, Croft M, Gopalakrishnan J, Pena MA, Hadermann J, Greenblatt M, Rojas S, ACS applied materials and interfaces 11, 21454 (2019). http://doi.org/10.1021/ACSAMI.9B02077
Abstract: Perovskites (ABO(3)) with transition metals in active B sites are considered alternative catalysts for the water oxidation to oxygen through the oxygen evolution reaction (OER) and for the oxygen reduction through the oxygen reduction reaction (ORR) back to water. We have synthesized a double perovskite (A(2)BB'O-6) with different cations in A, B, and B' sites, namely, ((La15Sr0.5)-Sr-.)(A)(Ni0.5Mn0.5)(B)(Ni0.5Ru0.5)(B)O-6 (LSNMR), which displays an outstanding OER/ORR bifunctional performance. The composition and structure of the oxide has been determined by powder X-ray diffraction, powder neutron diffraction, and transmission electron microscopy to be monoclinic with the space group P2(1)/n and with cationic ordering between the ions in the B and B' sites. X-ray absorption near-edge spectroscopy suggests that LSNMR presents a configuration of similar to Ni2+, similar to Mn4+, and similar to Ru5+. This bifunctional catalyst is endowed with high ORR and OER activities in alkaline media, with a remarkable bifunctional index value of similar to 0.83 V (the difference between the potentials measured at -1 mA cm(-2) for the ORR and +10 mA cm(-2) for the OER). The ORR onset potential (E-onset) of 0.94 V is among the best reported to date in alkaline media for ORR-active perovskites. The ORR mass activity of LSNMR is 1.1 A g(-1) at 0.9 V and 7.3 A g(-1) at 0.8 V. Furthermore, LSNMR is stable in a wide potential window down to 0.05 V. The OER potential to achieve a current density of 10 mA cm(-2) is 1.66 V. Density functional theory calculations demonstrate that the high ORR/OER activity of LSNMR is related to the presence of active Mn sites for the ORR- and Ru-active sites for the OER by virtue of the high symmetry of the respective reaction steps on those sites. In addition, the material is stable to ORR cycling and also considerably stable to OER cycling.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
Times cited: 12
DOI: 10.1021/ACSAMI.9B02077
|
“La2MnVO6 double perovskite: a structural, magnetic and X-ray absorption investigation”. Mandal TK, Croft M, Hadermann J, Van Tendeloo G, Stephens PW, Greenblatt M, Journal of materials chemistry 19, 4382 (2009). http://doi.org/10.1039/b823513a
Abstract: The synthesis, electron diffraction (ED), synchrotron X-ray and neutron structure, X-ray absorption spectroscopy (XAS) and magnetic property studies of La2MnVO6 double perovskite are described. Analysis of the synchrotron powder X-ray diffraction data for La2MnVO6 indicates a disordered arrangement of Mn and V at the B-site of the perovskite structure. Absence of super-lattice reflections in the ED patterns for La2MnVO6 supports the disordered cation arrangement. Room temperature time-of-flight (TOF) neutron powder diffraction (NPD) data show no evidence of cation ordering, in corroboration with the ED and synchrotron studies (orthorhombic Pnma, a = 5.6097(3), b = 7.8837(5) and c = 5.5668(3) ; 295 K, NPD). A comparison of XAS analyses of La2TVO6 with T = Ni and Co shows T2+ formal oxidation state while the T = Mn material evidences a Mn3+ admixture into a dominantly Mn2+ ground state. V-K edge measurements manifest a mirror image behavior with a V4+ state for T = Ni and Co with a V3+ admixture arising in the T = Mn material. The magnetic susceptibility data for La2MnVO6 show ferromagnetic correlations; the observed effective moment, µeff (5.72 µB) is much smaller than the calculated moment (6.16 µB) based on the spin-only formula for Mn2+ (d5, HS) /V4+ (d1), supportive of the partly oxidized Mn and reduced V scenario (Mn3+/V3+).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 10
DOI: 10.1039/b823513a
|
“Leached natural saponite as the silicate source in the synthesis of aluminosilicate hexagonal mesoporous materials”. Linssen T, Cool P, Baroudi M, Cassiers K, Vansant EF, Lebedev O, van Landuyt J, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 106, 4470 (2002). http://doi.org/10.1021/jp015578p
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.177
Times cited: 23
DOI: 10.1021/jp015578p
|
“Lead-mercury based superconductors: the 1212 cuprate Pb0.7Hg0.3Sr2+xCa0.7Nd0.3-xCu2O7-\delta and the new oxycarbonate Pb0.7Hg0.3Sr4Cu2CO3O7”. Martin C, Hervieu M, Huvé, M, Michel C, Maignan A, Van Tendeloo G, Raveau B, Physica C-Superconductivity And Its Applications 222, 19 (1994)
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 0.942
Times cited: 49
|
“Lead-mercury-based superconductors –, the 1212-cuprate Pb0.7Hg0.3Sr2+xCa0.7Nd0.3-xCu2O7-\delta and the new oxycarbonate Pb0.7Hg0.3Sr4Cu2CO3O7”. Martin C, Hervieu M, Huvé, M, Michel C, Maignan A, Van Tendeloo G, Raveau B, Physica: C : superconductivity 222, 19 (1994). http://doi.org/10.1016/0921-4534(94)90109-0
Abstract: A new superconducting mercury oxycarbonate, Pb0.7Hg0.3Sr4Cu2CO3O7, has been synthesized. This tetragonal phase (a = 3.824 angstrom, c= 16.468 angstrom) consists of an intergrowth of two nonsuperconducting compounds, Sr2CuO2CO3 and Pb0.7Hg0.3Sr2CuO5. It exhibits after optimization a critical temperature of 70 K, with a sharp transition and a superconducting volume fraction of 50%. Its behavior can be compared to that of thallium oxycarbonates previously isolated. This study is completed by a reinvestigation of the 1212 cuprate of the system Hg-Pb-Sr-Ca-Nd-Cu. A superconducting phase with the 1212 structure, similar to that previously obtained but with a significantly different composition, Pb0.7Hg0.3Sr2+xCa0.7Nd0.3-xCu2O7, has been obtained, with a T(c onset) of 100 K. The behavior of the latter is compared with other lead-based 1212 cuprates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 49
DOI: 10.1016/0921-4534(94)90109-0
|