Abstract: An extension to model-based electron energy loss spectroscopy (EELS) quantification is reported to improve the possibility of modelling fine structure changes in electron energy loss spectra. An equalisation function is used in the energy loss near edge structure (ELNES) region to model the differences between a single atom differential cross section and the cross section for an atom in a crystal. The equalisation function can be shown to approximate the relative density of unoccupied states for the given excitation edge. On a set of 200 experimental h-BN spectra, this technique leads to statistically acceptable models resulting into unbiased estimates of relative concentrations and making the estimated precisions come very close to the Cramer-Rao lower bound (CRLB). The method greatly expands the useability of model-based EELS quantification to spectra with pronounced fine structure. Another benefit of this model is that one also gets an estimate of the unoccupied density of states for a given excitation edge, without having to do background removal and deconvolution, making the outcome intrinsically more reliable and less noisy. (c) 2006 Elsevier B.V. All rights reserved.

Abstract: We consider magnetic flux moving in superconductors with periodic pinning arrays. We show that sample heating by moving vortices produces negative differential resistivity (NDR) of both N and S type (i.e., N- and S-shaped) in the voltage-current characteristic (VI curve). The uniform flux flow state is unstable in the NDR region of the VI curve. Domain structures appear during the NDR part of the VI curve of an N type, while a filamentary instability is observed for the NDR of an S type. The simultaneous existence of the NDR of both types gives rise to the appearance of striking self-organized (both stationary and nonstationary) two-dimensional dynamical structures.

Abstract: A hot dip aluminizing process to simulate the continuous galvanizing line (CGL) was carried out in three successive steps by a hot dip simulator: the pre-treatment for removing scales on the 200 x 250 mm(2) and 1mm in thickness cold rolled steel sheet, the dipping in 660 degrees C Al-Si melt for 3s and the cooling. In a pre-treatment, the steel specimen was partly coated by Au to confirm the mechanism of intermetallic compound (IMC) formation. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), and transmission electron microscopy (TEM) analyses were followed to observe the cross-section and the distribution of the elements. The specimen was analyzed in the boundary of the dipped-undipped part to see the formation mechanism of the aluminized steel. An intermetallic compound (IMC) is rapidly developed and grown in the steel-liquid interface. It has been usually reported that the IMC was formed by the dissolution of iron in the steel substrate toward the melt and the diffusion of aluminum in an opposite direction. The specimen is covered with aluminum-10 wt.% silicon, forms the IMC in the part that was not Au coated. However, IMC is not formed in the Au-coated part. The interface of the dipped-undipped is also analyzed by EDX. At the interface of the steel-IMC, it is clearly shown that the IMC is only formed in the dipped part and exists in the steel substrate as well, and contributes by iron, aluminum and silicon. The result clearly shows that only aluminum diffuses into the steel substrate without the dissolution of iron and forms the IMC between the steel substrate and the melt. Au coating and the short dipping time prevent the iron from dissolving into the aluminum melt. By TEM combined with focused ion beam (FIB) sample preparation, the IMC is confirmed as Fe2SiAl8, a hexagonal structure with space group P6(3)/mmc.

Abstract: Platinum metal was dispersed on microporous, mesoporous, and nonporous support materials including the zeolites Na-Y, Ba-Y, Ferrierite, ZSM-22, ETS-10, and AlPO-11, alumina, and titania. The oxidation of carbon black loosely mixed with catalyst powder was monitored gravimetrically in a gas stream containing nitric oxide, oxygen, and water. The carbon oxidation activity of the catalysts was found to be uniquely related to the Pt dispersion and little influenced by support type. The optimum dispersion is around 3-4% corresponding to relatively large Pt particle sizes of 2040 nm. The carbon oxidation activity reflects the NO oxidation activity of the platinum catalyst, which reaches an optimum in the 20-40 nm Pt particle size range. The lowest carbon oxidation temperatures were achieved with platinum loaded ZSM-22 and AlPO-11 zeolite crystallites bearing platinum of optimum dispersion on their external surfaces.

Abstract: We present an efficient method for the quantification of crystalline versus amorphous phase content in mesoporous materials, making use of electron energy loss spectroscopy. The method is based on fitting a superposition of core-loss edges using the maximum likelihood method with measured reference spectra. We apply the method to mesoporous TiO2 samples. We show that the absolute amount of the crystalline phase can be determined with an accuracy below 5%. This method takes also the amorphous phase into account, where standard X-ray diffraction is only quantitative for crystalline phases and not for amorphous phase. (c) 2006 Elsevier B.V.. All rights reserved.