“Determination of fluorine in uranium oxyfluoride particles as an indicator of particle age”. Kips R, Pidduck AJ, Houlton MR, Leenaers A, Mace JD, Marie O, Pointurier F, Stefaniak EA, Taylor PDP, van den Berghe S, van Espen P, Van Grieken R, Wellum R, Spectrochimica acta: part B : atomic spectroscopy 64, 199 (2009). http://doi.org/10.1016/J.SAB.2008.12.001
Abstract: As swipe samples from enrichment activities typically contain uranium particles with a detectable amount of fluorine, the question was raised whether the analysis of fluorine in particles could complement the information on the uranium isotope ratios. For this, uranium oxyfluoride particles were prepared from the controlled hydrolysis of uranium hexafluoride (UF6). The relative amount of fluorine was characterized by scanning electron microscopy combined with energy-dispersive X-ray spectrometry (SEM-EDX), as well as ion-microprobe secondary ion mass spectrometry (IM-SIMS). Of particular interest was the assessment of the reduction of the amount of fluorine over time, and after exposure to UV-light and high temperatures. Micro-Raman spectrometry (MRS) was applied to look for differences in molecular structure between these various sample types. Both SEM-EDX and IM-SIMS showed a general reduction of the fluorine-to-uranium ratio after 12 years of storage. The exposure to UV-light and high temperatures was found to have accelerated the loss of fluorine. A distinct peak at 865 cm− 1 Raman shift was detected for the majority of particles analyzed by MRS. For the particles that were heat-treated, the Raman spectra were similar to the spectrum of U3O8. Although often large variations were observed between particles from the same sample, the three particle measurement techniques (IM-SIMS, SEM-EDX and MRS) showed some consistent trends. They therefore appear promising in terms of the ability to place bounds on particle age, as well as shedding light on the complex processes involved in UO2F2 particle ageing.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Chemometrics (Mitac 3)
DOI: 10.1016/J.SAB.2008.12.001
|
|
|
“New insight into UO2F2 particulate structure by micro-Raman spectroscopy”. Stefaniak EA, Darchuk L, Sapundjiev D, Kips R, Aregbe Y, Van Grieken R, Journal of molecular structure 1040, 206 (2013). http://doi.org/10.1016/J.MOLSTRUC.2013.02.012
Abstract: Uranyl fluoride particles produced via hydrolysis of uranium hexafluoride have been deposited on different substrates: polished graphite disks, silver foil, stainless steel and gold-coated silicon wafer, and measured with micro-Raman spectroscopy (MRS). All three metallic substrates enhanced the Raman signal delivered by UO2F2 in comparison to graphite. The fundamental stretching of the UO band appeared at 867 cm−1 in case of the graphite substrate, while in case of the others it was shifted to lower frequencies (down to 839 cm−1). All applied metallic substrates showed the expected effect of Raman signal enhancement; however the gold layer appeared to be most effective. Application of new substrates provides more information on the molecular structure of uranyl fluoride precipitation, which is interesting for nuclear safeguards and nuclear environmental analysis.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.MOLSTRUC.2013.02.012
|
|