“Synthesis and characterization of oxygen-deficient oxides BaCo1-xYxO3-y' x = 0.15, 0.25 and 0.33, with the perovskite structure”. Lomakov MV, Istomin SY, Abakumov AM, Van Tendeloo G, Antipov EV, Solid state ionics 179, 1885 (2008). http://doi.org/10.1016/j.ssi.2008.05.004
Abstract: Oxygen-deficient complex cobalt oxides BaCo1 − xYxO3 − y, = 0.15, 0.25 and 0.33, with a cubic perovskite structure have been synthesized in air at 1100 °C using a citrate route. Cation composition of the compounds was confirmed by energy-dispersed X-ray (EDX) microanalysis while oxygen content was determined by iodometric titration. An electron diffraction (ED) study of the x = 0.25 and 0.33 compositions show the presence of a diffuse intensity, indicating possible short-range ordering of the B cations. It was found that the treatment of BaCo0.75Y0.25O2.55 in a humid atmosphere leads to the absorption of water vapour at the first stage. Oxygen permeation studies of the ceramic membranes of BaCo0.75Y0.25O2.55 and BaCo0.67Y0.33O2.55 with variable thickness showed high oxygen fluxes of 0.170.32 µmol/cm2/s at 950 °C.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.354
Times cited: 9
DOI: 10.1016/j.ssi.2008.05.004
|
“[SrF0.8(OH)0.2]2.526[Mn6O12]: columnar rock-salt fragments inside the todorokite-type tunnel structure”. Abakumov AM, Hadermann J, Van Tendeloo G, Kovba ML, Skolis YY, Mudretsova SN, Antipov EV, Volkova OS, Vasiliev AN, Tristan N, Klingeler R, Büchner B, Chemistry of materials 19, 1181 (2007). http://doi.org/10.1021/cm062508s
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 9
DOI: 10.1021/cm062508s
|
“Coupled anion and cation ordering in Sr3RFe4O10.5 (R=Y, Ho, Dy) anion-deficientperovskites”. Abakumov AM, d' Hondt H, Rossell MD, Tsirlin AA, Gutnikova O, Filimonov DS, Schnelle W, Rosner H, Hadermann J, Van Tendeloo G, Antipov EV, Journal of solid state chemistry 183, 2845 (2010). http://doi.org/10.1016/j.jssc.2010.09.039
Abstract: The Sr3RFe4O10.5 (R=Y, Ho, Dy) anion-deficient perovskites were prepared using a solid-state reaction in evacuated sealed silica tubes. Transmission electron microscopy and 57Fe Mössbauer spectroscopy evidenced a complete A-cations and oxygen vacancies ordering. The structure model was further refined by ab initio structure relaxation, based on density functional theory calculations. The compounds crystallize in a tetragonal a≈2√2ap≈11.3 Å, с≈4сp≈16 Å unit cell (ap: parameter of the perovskite subcell) with the P42/mnm space group. Oxygen vacancies reside in the (FeO5/4□3/4) layers, comprising corner-sharing FeO4 tetrahedra and FeO5 tetragonal pyramids, which are sandwiched between the layers of the FeO6 octahedra. Smaller R atoms occupy the 9-fold coordinated position, whereas the 10-fold coordinated positions are occupied by larger Sr atoms. The Fe sublattice is ordered aniferromagnetically up to at least 500 K, while the rare-earth sublattice remains disordered down to 2 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2010.09.039
|
“New perovskite-based manganite Pb2Mn2O5”. Hadermann J, Abakumov AM, Perkisas T, d' Hondt H, Tan H, Verbeeck J, Filonenko VP, Antipov EV, Van Tendeloo G, Journal of solid state chemistry 183, 2190 (2010). http://doi.org/10.1016/j.jssc.2010.07.032
Abstract: A new perovskite based compound Pb2Mn2O5 has been synthesized using a high pressure high temperature technique. The structure model of Pb2Mn2O5 is proposed based on electron diffraction, high angle annular dark field scanning transmission electron microscopy and high resolution transmission electron microscopy. The compound crystallizes in an orthorhombic unit cell with parameters a=5.736(1)Å≈√2a p p p (a p the parameter of the perovskite subcell) and space group Pnma. The Pb2Mn2O5 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110] p (1̄01) p crystallographic shear planes. The blocks are connected to each other by chains of edge-sharing MnO5 distorted tetragonal pyramids. The chains of MnO5 pyramids and the MnO6 octahedra of the perovskite blocks delimit six-sided tunnels accommodating double chains of Pb atoms. The tunnels and pyramidal chains adopt two mirror-related configurations (left L and right R) and layers consisting of chains and tunnels of the same configuration alternate in the structure according to an -LRLR-sequence. The sequence is sometimes locally violated by the appearance of -LL- or -RR-fragments. A scheme is proposed with a JahnTeller distortion of the MnO6 octahedra with two long and two short bonds lying in the ac plane, along two perpendicular orientations within this plane, forming a d-type pattern.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2010.07.032
|
“Structural study of the new complex oxides Ba5-ySryR2-xAl2Zr1+xO13+x/2 (R=Gd-Lu, Y, Sc)”. Shpanchenko RV, Abakumov AM, Antipov EV, Nistor L, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 118, 180 (1995). http://doi.org/10.1006/jssc.1995.1329
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 8
DOI: 10.1006/jssc.1995.1329
|
“Structural transformations in the fluorinated T* phase”. Hadermann J, Abakumov AM, Lebedev OI, Van Tendeloo G, Rozova MG, Shpanchenko RV, Pavljuk BP, Kopnin EM, Antipov EV, Journal of solid state chemistry 147, 647 (1999). http://doi.org/10.1006/jssc.1999.8438
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.1999.8438
|
“Suppression of modulations in fluorinated Bi-2201 phases”. Hadermann J, Khasanova NR, Van Tendeloo G, Abakumov AM, Rozova MG, Alekseeva AM, Antipov EV, Journal of solid state chemistry 156, 445 (2001). http://doi.org/10.1006/jssc.2000.9020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.2000.9020
|
“Synthesis and crystal structure of a new complex oxyfluoride La0.813Sr0.187Cu(o,F)3-\delta”. Abakumov AM, Hadermann J, Rozova MG, Pavljuk BP, Antipov EV, Lebedev OI, Van Tendeloo G, Journal of solid state cemistry 149, 189 (2000). http://doi.org/10.1006/jssc.1999.8521
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.1999.8521
|
“Synthesis and crystal structure of novel CaRMnSnO6(R = La, Pr, Nd, Sm-Dy) double perovskites”. Abakumov AM, Rossell MD, Seryakov SA, Rozova MG, Markina MM, Van Tendeloo G, Antipov EV, Journal of materials chemistry 15, 4899 (2005). http://doi.org/10.1039/b510242a
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 8
DOI: 10.1039/b510242a
|
“Synthesis and structural investigations on the new Sr1.32Mn0.83Cu0.17O3 compound”. Abakumov AM, Mironov AV, Govorov VA, Lobanov MV, Rozova MG, Antipov EV, Lebedev OI, Van Tendeloo G, Solid state sciences 5, 1117 (2003). http://doi.org/10.1016/S1293-2558(03)00141-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 8
DOI: 10.1016/S1293-2558(03)00141-9
|
“Synthesis and structure of Ln4Re6-xO19 (Ln=Ce, Pr, Nd) complex oxides”. Bramnik KG, Abakumov AM, Shpanchenko RV, Antipov EV, Van Tendeloo G, Journal of alloys and compounds 278, 98 (1998). http://doi.org/10.1016/S0925-8388(98)00252-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 8
DOI: 10.1016/S0925-8388(98)00252-7
|
“HREM study of fluorinated Nd2CuO4”. Hadermann J, Van Tendeloo G, Abakumov AM, Rozova MG, Antipov EV, Journal of solid state chemistry 157, 56 (2001). http://doi.org/10.1006/jssc.2000.9038
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 7
DOI: 10.1006/jssc.2000.9038
|
“The phase transition and crystal structures of Ba3RM2O7.5 complex oxides (R=rare-earth elements, M = Al,Ga)”. Abakumov AM, Shpanchenko RV, Lebedev OI, Van Tendeloo G, Amelinckx S, Antipov EV, Acta crystallographica: section A: foundations of crystallography 55, 828 (1999). http://doi.org/10.1107/S0108767399002068
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.725
Times cited: 7
DOI: 10.1107/S0108767399002068
|
“Pb2.85Ba2.15Fe4SnO13 : a new member of the AnBnO3n-2 anion-deficient perovskite-based homologous series”. Korneychik OE, Batuk M, Abakumov AM, Hadermann J, Rozova MG, Sheptyakov DV, Pokholok KV, Filimonov DS, Antipov EV, Journal of solid state chemistry 184, 3150 (2011). http://doi.org/10.1016/j.jssc.2011.09.029
Abstract: Pb2.85Ba2.15Fe4SnO13, a new n=5 member of the anion-deficient perovskite based AnBnO3n−2 (A=Pb, Ba, B=Fe, Sn) homologous series, was synthesized by the solid state method. The crystal structure of Pb2.85Ba2.15Fe4SnO13 was investigated using a combination of neutron powder diffraction, electron diffraction, high angle annular dark field scanning transmission electron microscopy and Mössbauer spectroscopy. It crystallizes in the Ammm space group with unit cell parameters a=5.7990(1) Å, b=4.04293(7) Å and c=26.9561(5) Å. The Pb2.85Ba2.15Fe4SnO13 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110](1̄01)p crystallographic shear (CS) planes. The corner-sharing FeO6 octahedra at the CS planes are transformed into edge-sharing FeO5 distorted tetragonal pyramids. The octahedral positions in the perovskite blocks between the CS planes are jointly taken up by Fe and Sn, with a preference of Sn towards the position at the center of the perovskite block. The chains of FeO5 pyramids and (Fe,Sn)O6 octahedra of the perovskite blocks delimit six-sided tunnels at the CS planes occupied by double chains of Pb atoms. The compound is antiferromagnetically ordered below TN=368±15 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 7
DOI: 10.1016/j.jssc.2011.09.029
|
“Evaluation of Ce-doped Pr2CuO4for potential application as a cathode material for solid oxide fuel cells”. Kolchina L M, Lyskov NV, Kuznetsov AN, Kazakov SM, Galin MZ, Meledin A, Abakumov AM, Bredikhin SI, Mazo GN, Antipov EV, RSC advances 6, 101029 (2016). http://doi.org/10.1039/C6RA21970E
Abstract: Pr2−xCexCuO4 (x = 0.05; 0.1; 0.15) samples were synthesized and systematically characterized towards application as a cathode material for solid oxide fuel cells (SOFCs). High-temperature electrical conductivity, thermal expansion, and electrocatalytic activity in the oxygen reduction reaction (ORR) were examined. The electrical conductivity of Pr2−xCexCuO4 oxides demonstrates semiconducting behavior up to 900 °C. Small Ce-doping (2.5 at%) allows an increase in electrical conductivity from 100 to 130 S cm−1 in air at 500–800 °C. DFT calculations revealed that the density of states directly below the Fermi level, comprised mainly of Cu 3d and O 2p states, is significantly affected by atoms in rare earth positions, which might give an indication of a correlation between calculated electronic structures and measured conducting properties. Ce-doping in Pr2−xCexCuO4 slightly increases TEC from 11.9 × 10−6 K−1 for x = 0 to 14.2 × 10−6 K−1 for x = 0.15. Substitution of 2.5% of Pr atoms in Pr2CuO4 by Ce is effective to enhance the electrochemical performance of the material as a SOFC cathode in the ORR (ASR of Pr1.95Ce0.05CuO4 electrode applied on Ce0.9Gd0.1O1.95 electrolyte is 0.39 Ω cm2 at 750 °C in air). The peak power density achieved for the electrolyte-supported fuel cell with the Pr1.95Ce0.05CuO4 cathode is 150 mW cm−2 at 800 °C
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 7
DOI: 10.1039/C6RA21970E
|
“Crystal structure and properties of the new vanadyl(IV)phosphates Na2MVO(PO4)2 M=Ca and Sr”. Chernaya VV, Tsirlin AA, Shpanchenko RV, Antipov EV, Gippius AA, Morozova EN, Dyakov V, Hadermann J, Kaul EE, Geibel C, Journal of solid state chemistry 177, 2875 (2004). http://doi.org/10.1016/j.jssc.2004.04.035
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/j.jssc.2004.04.035
|
“Homologous series of layered perovskites An+1BnO3n-1Cl : crystal and magnetic structure of a new oxychloride Pb4BiFe4O11Cl”. Batuk M, Batuk D, Tsirlin AA, Rozova MG, Antipov EV, Hadermann J, Van Tendeloo G, Inorganic chemistry 52, 2208 (2013). http://doi.org/10.1021/ic302667a
Abstract: The nuclear and magnetic structure of a novel oxychloride Pb4BiFe4O11Cl has been studied over the temperature range 1.5700 K using a combination of transmission electron microscopy and synchrotron and neutron powder diffraction [space group P4/mbm, a = 5.5311(1) Å, c = 19.586(1) Å, T = 300 K]. Pb4BiFe4O11Cl is built of truncated (Pb,Bi)3Fe4O11 quadruple perovskite blocks separated by CsCl-type (Pb,Bi)2Cl slabs. The perovskite blocks consist of two layers of FeO6 octahedra located between two layers of FeO5 tetragonal pyramids. The FeO6 octahedra rotate about the c axis, resulting in a √2ap × √2ap × c superstructure. Below TN = 595(17) K, Pb4BiFe4O11Cl adopts a G-type antiferromagnetic structure with the iron magnetic moments confined to the ab plane. The ordered magnetic moments at 1.5 K are 3.93(3) and 3.62(4) μB on the octahedral and square-pyramidal iron sites, respectively. Pb4BiFe4O11Cl can be considered a member of the perovskite-based An+1BnO3n1Cl homologous series (A = Pb/Bi; B = Fe) with n = 4. The formation of a subsequent member of the series with n = 5 is also demonstrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 6
DOI: 10.1021/ic302667a
|
“New germanates RCrGeO5 (R=NdEr, Y): synthesis, structure, and properties”. Shpanchenko RV, Tsirlin AA, Kondakova ES, Antipov EV, Bougerol C, Hadermann J, Van Tendeloo G, Sakurai H, Takayama-Muromachi E, Journal of solid state chemistry 181, 2433 (2008). http://doi.org/10.1016/j.jssc.2008.05.043
Abstract: The new complex germanates RCrGeO5 (R=NdEr, Y) have been synthesized and investigated by means of X-ray powder diffraction, electron microscopy, magnetic susceptibility and specific heat measurements. All the compounds are isostructural and crystallize in the orthorhombic symmetry, space group Pbam, and Z=4. The crystal structure of RCrGeO5, as refined using X-ray powder diffraction data, includes infinite chains built by edge-sharing Cr+3O6 octahedra with two alternating Cr−Cr distances. The chains are combined into a three-dimensional framework by Ge2O8 groups consisting of two edge-linked square pyramids oriented in opposite directions. The resulting framework contains pentagonal channels where rare-earth elements are located. Thus, RCrGeO5 germanates present new examples of RMn2O5-type compounds and show ordering of Cr+3 and Ge+4 cations. Electron diffraction as well as high-resolution electron microscopy confirm the structure solution. Magnetic susceptibility data for R=Nd, Sm, and Eu are qualitatively consistent with the presence of isolated 3d (antiferromagnetically coupled Cr+3 cations) and 4f (R+3) spin subsystems in the RCrGeO5 compounds. NdCrGeO5 undergoes long-range magnetic ordering at 2.6 K, while SmCrGeO5 and EuCrGeO5 do not show any phase transitions down to 2 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/j.jssc.2008.05.043
|
“Transmission electron microscopy study of polymorphism in barium gallate BaGa2O4”. Lemmens H, Amelinckx S, Van Tendeloo G, Abakumov AM, Rozova MG, Antipov EV, Phase transitions 76, 653 (2003). http://doi.org/10.1080/0141159021000051055
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.06
Times cited: 6
DOI: 10.1080/0141159021000051055
|
“Crystal structure and properties of the Na1-xRu2O4 phase”. Panin RV, Khasanova NR, Abakumov AM, Schnelle W, Hadermann J, Antipov EV, Russian chemical bulletin 55, 1717 (2006). http://doi.org/10.1007/s11172-006-0478-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 5
DOI: 10.1007/s11172-006-0478-6
|
“Original close-packed structure and magnetic properties of the Pb4Mn9O20 manganite”. Abakumov AM, Hadermann J, Tsirlin AA, Tan H, Verbeeck J, Zhang H, Dikarev EV, Shpanchenko RV, Antipov EV, Journal of solid state chemistry 182, 2231 (2009). http://doi.org/10.1016/j.jssc.2009.06.003
Abstract: The crystal structure of the Pb4Mn9O20 compound (previously known as Pb0.43MnO2.18) was solved from powder X-ray diffraction, electron diffraction, and high resolution electron microscopy data (S.G. Pnma, a=13.8888(2) Å, b=11.2665(2) Å, c=9.9867(1) Å, RI=0.016, RP=0.047). The structure is based on a 6H (cch)2 close packing of pure oxygen h-type (O16) layers alternating with mixed c-type (Pb4O12) layers. The Mn atoms occupy octahedral interstices formed by the oxygen atoms of the close-packed layers. The MnO6 octahedra share edges within the layers, whereas the octahedra in neighboring layers are linked through corner sharing. The relationship with the closely related Pb3Mn7O15 structure is discussed. Magnetization measurements reveal a peculiar magnetic behavior with a phase transition at 52 K, a small net magnetization below the transition temperature, and a tendency towards spin freezing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2009.06.003
|
“Spatial separation of covalent, ionic, and metallic interactions in Mg11Rh18B8 and Mg3Rh5B3”. Alekseeva AM, Abakumov AM, Leither-Jasper A, Schnelle W, Prots Y, Van Tendeloo G, Antipov EV, Grin Y, Chemistry: a European journal 19, 17860 (2013). http://doi.org/10.1002/chem.201301512
Abstract: The crystal structures of Mg11Rh18B8 and Mg3Rh5B3 have been investigated by using single-crystal X-ray diffraction. Mg11Rh18B8: space group P4/mbm; a=17.9949(7), c=2.9271(1)angstrom; Z=2. Mg3Rh5B3: space group Pmma; a=8.450(2), b=2.8644(6), c=11.602(2)angstrom; Z=2. Both crystal structures are characterized by trigonal prismatic coordination of the boron atoms by rhodium atoms. The [BRh6] trigonal prisms form arrangements with different connectivity patterns. Analysis of the chemical bonding by means of the electron-localizability/electron-density approach reveals covalent BRh interactions in these arrangements and the formation of BRh polyanions. The magnesium atoms that are located inside the polyanions interact ionically with their environment, whereas, in the structure parts, which are mainly formed by Mg and Rh atoms, multicenter (metallic) interactions are observed. Diamagnetic behavior and metallic electron transport of the Mg11Rh18B8 and Mg3Rh5B3 phases are in agreement with the bonding picture and the band structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 5
DOI: 10.1002/chem.201301512
|
“Structure and high-temperature properties of the (Sr,Ca,Y)(Co,Mn)O3-y perovskites –, perspective cathode materials for IT-SOFC”. Napolsky PS, Drozhzhin OA, Istomin SY, Kazakov SM, Antipov EV, Galeeva AV, Gippius AA, Svensson G, Abakumov AM, Van Tendeloo G, Journal of solid state chemistry 192, 186 (2012). http://doi.org/10.1016/j.jssc.2012.03.056
Abstract: Oxygen deficient perovskites Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75, were prepared by using the citrate route at 1373-1573 K for 48 h. The cubic Pm-3m perovskite structure for x=0.5 was confirmed by electron diffraction study and refined using neutron powder diffraction (NPD) data. For x=0.75, the superstructure corresponding to a=root 2 x a(per), b=2 x a(per), c=root 2 x a(per) (a(0)b(-)b(-) tilt system, space group Imma) was revealed by electron diffraction. The solid solution Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= x <= 0.6 and compound Ca0.75Y0.25Mn0.85Co0.15O2.92 were prepared in air at 1573 K for 48 h. The crystal structure of Ca0.75Y0.25Mn0.85Co0.15O2.92 was refined using NPD data (S.G. Pnma, a=5.36595(4), b=7.5091(6), c=5.2992(4) angstrom, R-p=0.057, R-wp=0.056, chi(2)=4.26). High-temperature thermal expansion properties of the prepared compounds were studied in air using both dilatometry and high-temperature X-ray powder diffraction data (HTXRPD). They expanding non-linearly at 298-1073 K due to the loss of oxygen at high temperatures. Calculated average thermal expansion coefficients (TECs) for Sr0.75Y0.25Co1-xMnxO3-y, x=0.5, 0.75 and Ca0.75Y0.25Mn0.85Co0.15O2.92(1) are 15.5, 15.1, and 13.8 ppm K-1, respectively. Anisotropy of the thermal expansion along different unit cell axes was observed for Sr0.15Ca0.6Y0.25Co0.25Mn0.75O3-y, and Ca0.75Y0.25Mn0.85Co0.15O2.92. Conductivity of Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75 increases with the temperature reaching 110 S/cm for x=0.5 and 44 S/cm for x=0.75 at 1173 K. Samples of Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= y <= 0.6 were found to be n-type conductors at room temperature with the similar temperature dependence of the conductivity and demonstrated the increase of the sigma value from similar to 1 to similar to 50 S/cm as the temperature increases from 300 to 1173 K. Their conductivity is described in terms of the small polaron charge transport with the activation energy (E-p) increasing from 340 to 430 meV with an increase of the calcium content from x=0 to x=0.6. (C) 2012 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2012.03.056
|
“Synthesis and structural study of Pb2Re2O7-x pyrochlores”. Abakumov AM, Shpanchenko RV, Antipov EV, Kopnin EM, Capponi JJ, Marezio M, Lebedev OI, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 138, 220 (1998). http://doi.org/10.1006/jssc.1998.7778
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1006/jssc.1998.7778
|
“Synthesis, structure and magnetic properties of the new mixed-valence vanadate Na2SrV3O9”. Shpanchenko RV, Chernaya VV, Antipov EV, Hadermann J, Kaul EE, Geibel C, Journal of solid state chemistry 173, 244 (2003). http://doi.org/10.1016/S0022-4596(03)00039-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/S0022-4596(03)00039-2
|
“Ca6.3Mn3Ga4.4Al1.3O18: a novel complex oxide with 3D tetrahedral framework”. Abakumov AM, Hadermann J, Kalyuzhnaya AS, Rozova MG, Mikheev MG, Van Tendeloo G, Antipov EV, Journal of solid state chemistry 178, 3137 (2005). http://doi.org/10.1016/j.jssc.2005.07.028
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2005.07.028
|
“High-temperature properties of (La,Ca)(Fe,Mg,Mo)O3-\delta perovskites as prospective electrode materials for symmetrical SOFC”. Istomin SY, Morozov AV, Abdullayev MM, Batuk M, Hadermann J, Kazakov SM, Sobolev AV, Presniakov IA, Antipov EV, Journal of solid state chemistry 258, 1 (2018). http://doi.org/10.1016/J.JSSC.2017.10.005
Abstract: La1-yCayFe0.5+x(Mg,Mo)(0.5-x)O3-delta oxides with the orthorhombic GdFeO3-type perovskite structure have been synthesized at 1573 K. Transmission electron microscopy study for selected samples shows the coexistence of domains of perovskite phases with ordered and disordered B-cations. Mossbauer spectroscopy studies performed at 300 K and 573 K show that while compositions with low Ca-content (La0.55Ca0.45Fe0.5Mg0.2625Mo0.2375O3-delta and La0.5Ca0.5Fe0.6Mg0.175Mo0.225O3-delta) are nearly oxygen stoichiometric, La0.2Ca0.8Fe0.5Mg0.2625Mo0.2375O3-delta is oxygen deficient with delta approximate to 0.15. Oxides are stable in reducing atmosphere (Ar/H-2, 8%) at 1173 K for 12 h. No additional phases have been observed at XRPD patterns of all studied perovskites and Ce1-xGdxO2-x/2 electrolyte mixtures treated at 1173-1373K, while Fe-rich compositions (x >= 0.1) react with Zr1-xYxO2-x/2 electrolyte above 1273 K. Dilatometry studies reveal that all samples show rather low thermal expansion coefficients (TECs) in air of 11.4-12.7 ppm K-1. In reducing atmosphere their TECs were found to increase up to 12.1-15.4 ppm K-1 due to chemical expansion effect. High-temperature electrical conductivity measurements in air and Ar/H-2 atmosphere show that the highest conductivity is observed for Fe- and Ca-rich compositions. Moderate values of electrical conductivity and TEC together with stability towards chemical interaction with typical SOFC electrolytes make novel Fe-containing perovskites promising electrode materials for symmetrical solid oxide fuel cell.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/J.JSSC.2017.10.005
|
“Crystal structure and magnetic properties of novel reduced V(IV)-based oxide Pb2V5O12”. Shpanchenko RV, Chyornaya VV, Abakumov AM, Antipov EV, Hadermann J, Van Tendeloo G, Kaul E, Geibel C, Sheptyakov D, Balagurov AM, Zeitschrift für anorganische und allgemeine Chemie 627, 2143 (2001). http://doi.org/10.1002/1521-3749(200109)627:9<2143::AID-ZAAC2143>3.0.CO;2-R
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.144
Times cited: 4
DOI: 10.1002/1521-3749(200109)627:9<2143::AID-ZAAC2143>3.0.CO;2-R
|
“High resolution electron microscopic study of Ba7Sc6Al2O19 and related phases”. Shpanchenko RV, Nistor L, Van Tendeloo G, Amelinckx S, Antipov EV, Kovba LM, Journal of solid state chemistry 113, 193 (1994). http://doi.org/10.1006/jssc.1994.1359
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 3
DOI: 10.1006/jssc.1994.1359
|
“Microstructural aspects of the degradation behavior of SnO2-based anodes for aluminum electrolysis”. Vassiliev SY, Laurinavichute VK, Abakumov AM, Govorov VA, Bendovskii EB, Turner S, Filatov AY, Tarasovskii VP, Borzenko AG, Alekseeva AM, Antipov EV, Journal of the electrochemical society 157, C178 (2010). http://doi.org/10.1149/1.3327903
Abstract: The performance of SnO2 ceramic anodes doped with copper and antimony oxides was examined in cryolite alumina melts under anodic polarization at different cryolite ratios, temperatures, times, and current densities. The corroded part consists of a narrow strong corrosion zone at the anode surface with damage of the intergrain contacts and a large increase in porosity, a wider moderate corrosion zone with a smaller porosity increase, and a Cu depletion zone, where the ceramic retains its initial microstructure and a slight porosity increase occurs due to the removal of the Cu-rich inclusions. Mechanical destruction of the anode was never observed in the 10100 h tests. A microstructural model of the ceramic was suggested, consisting of grains with an Sb-doped SnO2 grain core surrounded by an ~200 to 500 nm grain shell where SnO2 was simultaneously doped with Sb and Mn+ (M=Cu2+,Fe3+,Al3+). The grains were separated by a few nanometers thick Cu-enriched grain boundaries. Different secondary charge carrier (holes) concentrations and electric conductivities in the grain core and grain shell result in a higher current density at the intergrain regions that leads to their profound degradation, especially in the low temperature acidic melt.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 3
DOI: 10.1149/1.3327903
|