“Expanding the Ruddlesden-Popper manganite family : the n=3 La3.2Ba0.8Mn3O10 Member”. Hadermann J, Abakumov AM, Tsirlin AA, Rozova MG, Sarakinou E, Antipov EV, Inorganic chemistry 51, 11487 (2012). http://doi.org/10.1021/ic301332e
Abstract: La3.2Ba0.8Mn3O10, a representative of the rare n = 3 members of the Ruddlesden-Popper manganites A(n+1)Mn(n)O(3n+1), was synthesized in an evacuated sealed silica tube. Its crystal structure was refined from a combination of powder X-ray diffraction (PXD) and precession electron diffraction (PED) data, with the rotations of the MnO6 octahedra described within the symmetry-adapted mode approach (space group Cccm, a = 29.068(1) angstrom, b = 5.5504(5) angstrom, c = 5.5412(5) angstrom; PXD RF = 0.053, RP = 0.026; PED RF = 0.248). The perovskite block in La3.2Ba0.8Mn3O10 features an octahedral tilting distortion with out-of-phase rotations of the Mn06 octahedra according to the (Phi,Phi,0)(Phi,Phi,0) mode, observed for the first time in the n = 3 Ruddlesden-Popper structures. The Mn06 octahedra demonstrate a noticeable deformation with the elongation of two apical Mn-O bonds due to the Jahn-Teller effect in the Mn3+ cations. The relationships between the octahedral tilting distortion, the ionic radii of the cations at the A- and B-positions, and the mismatch between the perovslcite and rock-salt blocks of the Ruddlesden-Popper structure are discussed. At low temperatures, La3.2Ba0.8Mn3O10 reveals a sizable remnant magnetization of about 1.3 mu(B)/Mn at 2K, and shows signatures of spin freezing below 150 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 2
DOI: 10.1021/ic301332e
|
|
|
“New anion-conducting solid solutions Bi1-xTex(O,F)2+\delta (x >, 0.5) and glassceramic material on their base”. Prituzhalov VA, Ardashnikova EI, Vinogradov AA, Dolgikh VA, Videau J-J, Fargin E, Abakumov AM, Tarakina NV, Van Tendeloo G, Journal of fluorine chemistry 132, 1110 (2011). http://doi.org/10.1016/j.jfluchem.2011.06.042
Abstract: The anion-excess fluorite-like solid solutions with general composition Bi1−xTex(O,F)2+δ (x > 0.5) have been synthesized by a solid state reaction of TeO2, BiF3 and Bi2O3 at 873 K with following quenching. The homogeneity areas and polymorphism of the I ↔ IV Bi1−xTex(O,F)2+δ phases were investigated. The crystal structure of the low temperature IV-Bi1−xTex(O,F)2+δ phase has been solved using electron diffraction and X-ray powder diffraction (a = 11.53051(9) Å, S.G. Ia-3, RI = 0.046, RP = 0.041). Glass formation area in the Bi2O3BiF3TeO2 (10% TiO2) system was investigated. IVBi1−xTex(O,F)2+δ phase starts to crystallize at short-time (0.53 h) annealing of oxyfluoride glasses at temperatures above Tg (600615 K). The ionic conductivity of the crystalline Bi1−xTex(O,F)2+δ phase and corresponding glass-ceramics was investigated. Activation energy of conductivity Ea = 0.41(2) eV for the IV-Bi1−xTex(O,F)2+δ crystalline samples and Ea = 0.73 eV for the glass-ceramic samples were obtained. Investigation of the oxyfluoride samples with a constant cation ratio demonstrates essential influence of excess fluorine anions on the ionic conductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.101
Times cited: 2
DOI: 10.1016/j.jfluchem.2011.06.042
|
|
|
“A new structure type of the ternary sulfide Eu1.3Nb1.9S5”. Khasanova NR, Van Tendeloo G, Lebedev OI, Amelinckx S, Grippa AY, Abakumov AM, Istomin SY, D'yachenko OG, Antipov EV, Journal of solid state chemistry 164, 345 (2002). http://doi.org/10.1006/jssc.2001.9501
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1006/jssc.2001.9501
|
|
|
“Structure and magnetic properties of a new anion-deficient perovskite Pb2Ba2BiFe4ScO13 with crystallographic shear structure”. Batuk M, Tyablikov OA, Tsirlin AA, Kazakov SM, Rozova MG, Pokholok KV, Filimonov DS, Antipov EV, Abakumov AM, Hadermann J, Materials research bulletin 48, 3459 (2013). http://doi.org/10.1016/j.materresbull.2013.05.028
Abstract: Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 2
DOI: 10.1016/j.materresbull.2013.05.028
|
|
|
“Synthesis and characterization of new phases: Sr3.75K1.75Bi3O12 and Sr3.1Na2.9Bi3O12”. Pshirkov JS, Kazakov SM, Abakumov AM, Putilin SN, Antipov EV, Bougerol-Chaillout C, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 152, 492 (2000). http://doi.org/10.1006/jssc.2000.8718
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1006/jssc.2000.8718
|
|
|
“Effect of cation vacancies on the crystal structure and luminescent properties of Ca(0.85-1.5x)Gd(x)Eu(0.1)_(0.05+0.5x)WO(4) (0<x<0.567) scheelite-based red phosphors”. Batuk D, Batuk M, Morozov VA, Meert KW, Smet PF, Poelman D, Abakumov AM, Hadermann J, Journal of alloys and compounds 706, 358 (2017). http://doi.org/10.1016/j.jallcom.2017.02.154
Abstract: The Ca0.85-1.5xGdxEu0.1_0.05-0.5xWO4 (0 < x < 0.567) series of cation-deficient scheelites is investigated to unveil the influence of the cation vacancies on the crystal structure and luminescent properties. The concentration of the vacancies is varied by the heterovalent substitution of Gd3+ for Ca2+, keeping the concentration of the Eu3+ luminescent centers constant in all compounds of the series. The crystal structure of the materials is studied using a combination of transmission electron microscopy and synchrotron X-ray powder diffraction. At low vacancy concentration (x = 0.1, 0.2), cations and cation vacancies are randomly distributed in the structure, and the materials preserve the I41/a symmetry of the parent scheelite structure [x = 0.1: a = 5.25151(1) Å, c = 11.39479(2) Å; x = 0.2: a = 5.25042(1) Å, c = 11.41335(2) Å]. At higher concentration, the cation-vacancy ordering gives rise to incommensurately modulated structures. The x = 0.3 structure has a (3 + 2)D tetragonal symmetry [superspace group I41/a(a,b,0)00(-b,a,0)00, a = 5.24700(1) Å, c = 11.45514(3) Å, q1 = 0.51637(14)a* + 0.80761(13)b*, q2 = -0.80761a* + 0.51637b*]. At x = 0.4, the scheelite basic cell undergoes a monoclinic distortion with the formation of the (3 + 1)D structure [superspace group I2/b(a,b,0)00, a = 5.23757(1) Å, b = 5.25035(1) Å, c = 11.45750(2) Å, g = 90.5120(2) o, q = 0.54206(8)a* + 0.79330(8)b*]. In both structures, the antiphase Ca and (Gd,Eu) occupancy modulations indicate that the ordering between the A cations and vacancies also induces partial Ca/(Gd,Eu) cation ordering. Further increase of the Gd3þ content up to x = 0.567 leads to the formation of a monoclinic phase (space group C2/c) with the Eu2/3WO4-type structure. Despite the difference in the cation-vacancy ordering patterns, all materials in the series demonstrate very similar quantum efficiency and luminescence decay lifetimes. However, the difference in the local coordination environment of the A cation species noticeably affects the line width and the multiplet splitting of the 4f6-4f6 transitions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 2
DOI: 10.1016/j.jallcom.2017.02.154
|
|
|
“Chemical activity of the peroxide/oxide redox couple : case study of Ba5Ru2O11 in aqueous and organic solvents”. Grimaud A, Iadecola A, Batuk D, Saubanere M, Abakumov AM, Freeland JW, Cabana J, Li H, Doublet M-L, Rousse G, Tarascon J-M, Chemistry of materials 30, 3882 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B01372
Abstract: The finding that triggering the redox activity of oxygen ions within the lattice of transition metal oxides can boost the performances of materials used in energy storage and conversion devices such as Li-ion batteries or oxygen evolution electrocatalysts has recently spurred intensive and innovative research in the field of energy. While experimental and theoretical efforts have been critical in understanding the role of oxygen nonbonding states in the redox activity of oxygen ions, a clear picture of the redox chemistry of the oxygen species formed upon this oxidation process is still missing. This can be, in part, explained by the complexity in stabilizing and studying these species once electrochemically formed. In this work, we alleviate this difficulty by studying the phase Ba5Ru2O11, which contains peroxide O-2(2-) groups, as oxygen evolution reaction electrocatalyst and Li-ion battery material. Combining physical characterization and electrochemical measurements, we demonstrate that peroxide groups can easily be oxidized at relatively low potential, leading to the formation of gaseous dioxygen and to the instability of the oxide. Furthermore, we demonstrate that, owing to the stabilization at high energy of peroxide, the high-lying energy of the empty sigma* antibonding O-O states limits the reversibility of the electrochemical reactions when the O-2(2-)/O2- redox couple is used as redox center for Li-ion battery materials or as OER redox active sites. Overall, this work suggests that the formation of true peroxide O-2(2-) states are detrimental for transition metal oxides used as OER catalysts and Li-ion battery materials. Rather, oxygen species with O-O bond order lower than 1 would be preferred for these applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 2
DOI: 10.1021/ACS.CHEMMATER.8B01372
|
|
|
“Incommensurately modulated structures and luminescence properties of the AgxSm(2-x)/3WO4 (x=0.286, 0.2) scheelites as thermographic phosphors”. Morozov V, Deyneko D, Basoyich O, Khaikina EG, Spassky D, Morozov A, Chernyshev V, Abakumov A, Hadermann J, Chemistry of materials 30, 4788 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B02029
Abstract: Ag+ for Sm3+ substitution in the scheelite-type AgxSm(2-x)/3 square(1-2x)/3WO4 tungstates has been investigated for its influence on the cation-vacancy ordering and luminescence properties. A solid state method was used to synthesize the x = 0.286 and x = 0.2 compounds, which exhibited (3 + 1)D incommensurately modulated structures in the transmission electron microscopy study. Their structures were refined using high resolution synchrotron powder X-ray diffraction data. Under near-ultraviolet light, both compounds show the characteristic emission lines for (4)G(5/2) -> H-6(J) (J = 5/2, 7/2, 9/2, and 11/2) transitions of the Sm3+ ions in the range 550-720 nm, with the J = 9/2 transition at the similar to 648 nm region being dominant for all photoluminescence spectra. The intensities of the (4)G(5/2) -> H-6(9/2) and (4)G(5/2) -> H-6(7/2) bands have different temperature dependencies. The emission intensity ratios (R) for these bands vary reproducibly with temperature, allowing the use of these materials as thermographic phosphors.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 2
DOI: 10.1021/ACS.CHEMMATER.8B02029
|
|
|
“Structure solution and refinement of metal-ion battery cathode materials using electron diffraction tomography”. Hadermann J, Abakumov AM, And Materials 75, 485 (2019). http://doi.org/10.1107/S2052520619008291
Abstract: The applicability of electron diffraction tomography to the structure solution and refinement of charged, discharged or cycled metal-ion battery positive electrode (cathode) materials is discussed in detail. As these materials are often only available in very small amounts as powders, the possibility of obtaining single-crystal data using electron diffraction tomography (EDT) provides unique access to crucial information complementary to X-ray diffraction, neutron diffraction and high-resolution transmission electron microscopy techniques. Using several examples, the ability of EDT to be used to detect lithium and refine its atomic position and occupancy, to solve the structure of materials ex situ at different states of charge and to obtain in situ data on structural changes occurring upon electrochemical cycling in liquid electrolyte is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1107/S2052520619008291
|
|
|
“{110}-Layered B-cation ordering in the anion-deficient perovskite Pb2.4Ba2.6Fe2Sc2TiO13 with the crystallographic shear structure”. Tyablikov OA, Batuk D, Tsirlin AA, Batuk M, Verchenko VY, Filimonov DS, Pokholok KV, Sheptyakov DV, Rozova MG, Hadermann J, Antipov EV, Abakumov AM;, Journal of the Chemical Society : Dalton transactions 44, 10753 (2015). http://doi.org/10.1039/c4dt03867c
Abstract: A novel anion-deficient perovskite-based compound, Pb2.4Ba2.6Fe2Sc2TiO13, was synthesized via the citrate-based route. This compound is an n = 5 member of the A(n)B(n)O(3n-2) homologous series with unit-cell parameters related to the perovskite subcell a(p) approximate to 4.0 angstrom as a(p)root 2 x a(p) x 5a(p)root 2. The crystal structure of Pb2.4Ba2.6Fe2Sc2TiO13 consists of quasi-2D perovskite blocks with a thickness of three octahedral layers separated by the 1/2[110]((1) over bar 01)(p) crystallographic shear (CS) planes, which are parallel to the {110} plane of the perovskite subcell. The CS planes transform the corner-sharing octahedra into chains of edge-sharing distorted tetragonal pyramids. Using a combination of neutron powder diffraction, Fe-57 Mossbauer spectroscopy and atomic resolution electron energy-loss spectroscopy we demonstrate that the B-cations in Pb2.4Ba2.6Fe2Sc2TiO13 are ordered along the {110} perovskite layers with Fe3+ in distorted tetragonal pyramids along the CS planes, Ti4+ preferentially in the central octahedra of the perovskite blocks and Sc3+ in the outer octahedra of the perovskite blocks. Magnetic susceptibility and Mossbauer spectroscopy indicate a broadened magnetic transition around T-N similar to 45 K and the onset of local magnetic fields at low temperatures. The magnetic order is probably reminiscent of that in other A(n)B(n)O(3n-2) homologues, where G-type AFM order within the perovskite blocks has been observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 1
DOI: 10.1039/c4dt03867c
|
|
|
“Reply to Comment on “Frustrated octahedral tilting distortion in the incommensurately modulated Li3xNd2/3-xTiO3 perovskites””. Abakumov AM, Erni R, Tsirlin AA, Chemistry of materials 26, 1288 (2014). http://doi.org/10.1021/cm500005d
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 1
DOI: 10.1021/cm500005d
|
|
|
“Synthesis and crystal structure of the new complex oxide Ca7Mn2.14Ga5.86O17.93”. Kalyuzhnaya AS, Abakumov AM, Rozova MG, d' Hondt H, Hadermann J, Antipov EV, Russian chemical bulletin 59, 706 (2010). http://doi.org/10.1007/s11172-010-0150-z
Abstract: The complex oxide Ca7Mn2.14Ga5.86O17.93 was synthesized by the solid-state reaction in a sealed evacuated quartz tube at 1000 °C. Its crystal structure was determined by electron diffraction and X-ray powder diffraction. The structure can be represented as a tetrahedral framework, viz., the polyanion [(Mn0.285Ga0.715)15O29.86]19- stabilized by the incorporated cation [Ca14GaO6]19+. The polycation consists of the GaO6 octahedra surrounded by the Ca atoms, which are arranged to form a cube capped at all places. The tetrahedral framework is partially disordered due to the presence of tetrahedra with two possible orientations in the positions (0, 0, 0) and (x, x, x) with x ≈ 0.15 and 0.17. The relationship between the Ca7Mn2.14Ga5.86O17.93 structures and related ordered phases with the symmetry F23, as well as the influence of the oxygen content on the ordering in the tetrahedral framework, are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 1
DOI: 10.1007/s11172-010-0150-z
|
|
|
“The synthesis and thermodynamic properties of strontium fluoromanganite Sr2.5Mn6O12.5-\deltaF2”. Kovba ML, Skolis YY, Abakumov AM, Hadermann J, Sukhushina IS, Russian journal of physical chemistry A 84, 2033 (2010). http://doi.org/10.1134/S0036024410120046
Abstract: The existence of the [SrF(0.8)O(0.1)](2.5)[Mn(6)O(12)] = Sr(2.5)Mn(6)O(12.5 – delta)F(2) compound was established in the SrO-Mn(2)O(3)-SrF(2) system at 900A degrees C and p(O(2)) = 1 atm. The crystal structure of strontium fluoromanganite was determined from the X-ray powder diffraction data, electron diffraction, and high-resolution electron microscopy. It can be described in the monoclynic system with four Miller hklm indices: hklm: H = h a* + k b* + l c (1) (*) + m q (1), q (1), q (1) = c (2) (*) = gamma c (1) (*) , gamma a parts per thousand 0.632, a a parts per thousand a a parts per thousand 9.72 , b a parts per thousand 9.55 , c (1) a parts per thousand 2.84 , c (2) a parts per thousand 4.49 , monoclinic angle gamma a parts per thousand 95.6A degrees. The electromotive force method with a solid fluorine ion electrolyte was used to refine the composition of fluoromanganite and determine the thermodynamic functions of its formation from phases neighboring in the phase diagram (SrMn(3)O(6), Mn(2)O(3), SrF(2), and oxygen), Delta GA degrees, kJ/mol = -(111.7 +/- 1.9) + (89.5 +/- 1.5) x 10(-3) T.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.581
Times cited: 1
DOI: 10.1134/S0036024410120046
|
|
|
“Synthesis, structure and electrochemical properties of LiNaCo0.5Fe0.5PO4F fluoride-phosphate”. Fedotov SS, Kuzovchikov SM, Khasanova NR, Drozhzhin OA, Filimonov DS, Karakulina OM, Hadermann J, Abakumov AM, Antipov EV, Journal of solid state chemistry 242, 70 (2016). http://doi.org/10.1016/j.jssc.2016.02.042
Abstract: LiNaCo 0.5 Fe 0.5 PO 4 F fluoride-phosphate was synthesized via conventional solid-state and novel freeze-drying routes. The crystal structure was refined based on neutron powder diffraction (NPD) data and validated by electron diffraction (ED) and high-resolution transmission electron microscopy (HRTEM). The alkali ions are ordered in LiNaCo 0.5 Fe 0.5 PO 4 F and the transition metals jointly occupy the same crystallographic sites. The oxidation state and oxygen coordination environment of the Fe atoms were verified by 57 Fe Mössbauer spectroscopy. Electrochemical tests of the LiNaCo 0.5 Fe 0.5 PO 4 F cathode material demonstrated a reversible activity of the Fe 3+ /Fe 2+ redox couple at the electrode potential near 3.4 V and minor activity of the Co 3+ /Co 2+ redox couple over 5 V vs Li/Li + . The material exhibits a good capacity retention in the 2.4÷4.6 V vs Li/Li + potential range with the delivered discharge capacity of more than 82% (theo.) regarding Fe 3+ /Fe 2+ .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 1
DOI: 10.1016/j.jssc.2016.02.042
|
|
|
“Doping of Bi4Fe5O13F with pentagonal Cairo lattice with Cr and Mn: Synthesis, structure and magnetic properties”. Rozova MG, Grigoriev VV, Tyablikov OA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Abakumov AM, Materials research bulletin 87, 54 (2017). http://doi.org/10.1016/J.MATERRESBULL.2016.11.018
Abstract: The substitution of Cr3+ and Mn3+ for Fe3+ in the Bi4Fe6O13F oxyfluoride featuring the magnetically frustrated pentagonal Cairo lattice is reported. Bi4Fe4.1Cr0.9O13F and BiFe4.2Mn0.8O13F have been prepared using a solid state reaction in inert atmosphere. Their crystal structures were studied with transmission electron microscopy, powder X-ray diffraction and Fe-57 Mossbauer spectroscopy (S.G. P4(2)/mbc, a = 8.27836(2)angstrom, c = 18.00330(9) angstrom, R-F = 0.031 (Bi4Fe4.1Cr0.9O13F)), a= 8.29535(3)angstrom, c= 18.0060(1)angstrom, R-F = 0.027 (Bi4Fe4.1Cr0.9O13F)). The structures are formed by infinite rutile-like chains of the edge sharing BO6 octahedra (B transition metal cations) linked by the Fe2O7 groups of two corner-sharing tetrahedra. The"voids in thus formed framework are occupied by the Bi4F tetrahedra. The Fe-57 Mossbauer spectroscopy reveals that Cr3+ and Mn3+ replace Fe3+. exclusively at the octahedral positions. The Mn- and Cr-doped compounds demonstrate antiferromagnetic ordering below T-N =165 K and 120 K, respectively. (C) 2016 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 1
DOI: 10.1016/J.MATERRESBULL.2016.11.018
|
|
|
“Composition-dependent charge transfer and phase separation in the V1-xRexO2 solid solution”. Mikhailova D, Kuratieva NN, Utsumi Y, Tsirlin AA, Abakumov AM, Schmidt M, Oswald S, Fuess H, Ehrenberg H, Journal of the Chemical Society : Dalton transactions 46, 1606 (2017). http://doi.org/10.1039/C6DT04389E
Abstract: The substitution of vanadium in vanadium dioxide VO2 influences the critical temperatures of structural and metal-to-insulator transitions in different ways depending on the valence of the dopant. Rhenium adopts valence states between + 4 and + 7 in an octahedral oxygen surrounding and is particularly interesting in this context. Structural investigation of V1-xRexO2 solid solutions (0.01 <= x <= 0.30) between 80 and 1200 K using synchrotron X-ray powder diffraction revealed only two polymorphs that resemble VO2: the low-temperature monoclinic MoO2-type form (space group P2(1)/c), and the tetragonal rutile-like form (space group P4(2)/mnm). However, for compositions with 0.03 < x <= 0.15 a phase separation in the solid solution was observed below 1000 K upon cooling down from 1200 K, giving rise to two isostructural phases with slightly different lattice parameters. This is reflected in the appearance of two metal-toinsulator transition temperatures detected by magnetization and specific heat measurements. Comprehensive X-ray photoelectron spectroscopy studies showed that an increased amount of Re leads to a change in the Re valence state from solely Re6+ at a low doping level (<= 3 at% Re) via mixed-valence states Re4+/Re6+ for at least 0.03 < x <= 0.10, up to nearly pure Re4+ in V0.70Re0.30O2. Thus, compositions V1-xRexO2 with only one valence state of Re in the material (Re6+ or Re4+) can be obtained as a single phase, while intermediate compositions are subjected to a phase separation, presumably due to different valence states of Re.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 1
DOI: 10.1039/C6DT04389E
|
|
|
“Synthesis and structural characterization of a novel Sillén &ndash, Aurivillius bismuth oxyhalide, PbBi3VO7.5Cl, and its derivatives”. Charkin DO, Plokhikh IV, Kazakov SM, Kalmykov SN, Akinfiev VS, Gorbachev AV, Batuk M, Abakumov AM, Teterin YA, Maslakov KI, Teterin AY, Ivanov KE, Solid state sciences 75, 27 (2018). http://doi.org/10.1016/j.solidstatesciences.2017.11.006
Abstract: A new Sillen – Aurivillius family of layered bismuth oxyhalides has been designed and successfully constructed on the basis of PbBiO2X(X = halogen) synthetic perites and g-form of Bi2VO5.5 solid elec- trolyte. This demonstrates, for the first time, the ability of the latter to serve as a building block in construction of mixed-layer structures. The parent compound PbBi3VO7.5-dCl (d = 0.05) has been investigated by powder XRD, TEM, XPS methods and magnetic susceptibility measurements. An unexpected but important condition for the formation of the mixed-layer structure is partial (ca. 5%) reduction of VV into VIV which probably suppresses competitive formation of apatite-like Pb – Bi vanadates. This reduction also stabilizes the g polymorphic form of Bi2VO5.5 not only in the intergrowth structure, but in Bi2V1-xMxO5.5-y (M – Nb, Sb) solid solutions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 1
DOI: 10.1016/j.solidstatesciences.2017.11.006
|
|
|
“Light-activated sub-ppm NO2 detection by hybrid ZnO/QD nanomaterials vs. charge localization in core-shell QD”. Chizhov A, Vasiliev R, Rumyantseva M, Krylov I, Drozdov K, Batuk M, Hadermann J, Abakumov A, Gaskov A, Frontiers in materials 6 (2019). http://doi.org/10.3389/FMATS.2019.00231
Abstract: New hybrid materials-photosensitized nanocomposites containing nanocrystal heterostructures with spatial charge separation, show high response for practically important sub-ppm level NO2 detection at room temperature. Nanocomposites ZnO/CdSe, ZnO/(CdS@CdSe), and ZnO/(ZnSe@CdS) were obtained by the immobilization of nanocrystals-colloidal quantum dots (QDs), on the matrix of nanocrystalline ZnO. The formation of crystalline core-shell structure of QDs was confirmed by HAADF-STEM coupled with EELS mapping. Optical properties of photosensitizers have been investigated by optical absorption and luminescence spectroscopy combined with spectral dependences of photoconductivity, which proved different charge localization regimes. Photoelectrical and gas sensor properties of nanocomposites have been studied at room temperature under green light (max = 535 nm) illumination in the presence of 0.12-2 ppm NO2 in air. It has been demonstrated that sensitization with type II heterostructure ZnSe@CdS with staggered gap provides the rapid growth of effective photoresponse with the increase in the NO2 concentration in air and the highest sensor sensitivity toward NO2. We believe that the use of core-shell QDs with spatial charge separation opens new possibilities in the development of light-activated gas sensors working without thermal heating.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.3389/FMATS.2019.00231
|
|
|
“Anion ordering in fluorinated La2CuO4”. Hadermann J, Abakumov AM, Van Tendeloo G, Shpanchenko RV, Oleinikov PN, Antipov EV s.l., page 133 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“The local structure of YBCO based materials by TEM”. Van Tendeloo G, Lebedev OI, Verbist K, Abakumov AM, Shpanchenko RV, Antipov EV, Blank DHA Kluwer Academic, Dordrecht, page 11 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Pd nanoparticles on SnO2(Sb) whiskers : aggregation and reactivity in CO detection”. Zhukova AA, Rumyantseva MN, Zaytsev VB, Zaytseva AV, Abakumov AM, Gaskov AM, Journal of alloys and compounds 565, 6 (2013). http://doi.org/10.1016/j.jallcom.2013.02.184
Abstract: Single crystal antimony-doped SnO2 whiskers have been synthesized by in situ doping process in horizontal flow reactor. The produced whiskers were modified with 0.1, 0.2, 0.5, 1 or 2 wt.% Pd. The processes of Pd particles growth and aggregation are described on the base of AFM and STEM data. Depending on the content of introduced Pd precursor, the various mechanisms (Volmer-Weber or Stranski-Krastanov) of Pd nanoparticles growth realize. The dependence of sensor signal to CO on Pd concentration has non-monotonous character determined by the size of Pd nanoparticles and their aggregation degree. The best sensor signal toward CO was observed for whiskers decorated with 0.1 wt.% Pd. This concentration corresponds to the presence of individual 3-5 nm Pd nanoparticles on the surface of the whiskers. (C) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
DOI: 10.1016/j.jallcom.2013.02.184
|
|
|
“Sr21Bi8Cu2(CO3)(2)O-41, a Bi5+ Oxycarbonate with an Original 10L Structure”. Malo S, Abakumov AM, Daturi M, Pelloquin D, Van Tendeloo G, Guesdon A, Hervieu M, Inorganic chemistry 53, 10266 (2014). http://doi.org/10.1021/ic501322w
Abstract: The layered structure of Sr21Bi8Cu2(CO3)(2)O-41 (Z = 2) was determined by transmission electron microscopy, infrared spectroscopy, and powder X-ray diffraction refinement in space group P6(3)/mcm (No. 194), with a = 10.0966(3)angstrom and c = 26.3762(5)angstrom. This original 10L-type structure is built from two structural blocks, namely, [Sr15Bi6Cu2(CO3)O-29] and [Sr6Bi2(CO3)O-12]. The Bi5+ cations form [Bi2O10] dimers, whereas the Cu2+ and C atoms occupy infinite tunnels running along (c) over right arrow. The nature of the different blocks and layers is discussed with regard to the existing hexagonal layered compounds. Sr21Bi8Cu2(CO3)(2)O-41 is insulating and paramagnetic.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
DOI: 10.1021/ic501322w
|
|
|
“Structure of Y123 and Y247 fluorinated phases by HREM”. Lebedev OI, Van Tendeloo G, Abakumov AM, Shpanchenko RV, Rozova MG, Antipov EV, Electron microscopy: vol. 3 , 297 (1998)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Synthesis and structure of fluorinated RBa2Cu2O6+. (R=Dy, Ho and Tm) phases”. Oleynikov PN, Shpanchenko RV, Rozova MG, Abakumov AM, Antipov EV, Hadermann J, Lebedev OI, Van Tendeloo G, Russian journal of inorganic chemistry 46, 153 (2001)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.787
|
|
|
“Synthesis, structure and magnetic ordering of the mullite-type Bi2Fe4-xCrxO9 solid solutions with a frustrated pentagonal Cairo lattice”. Rozova MG, Grigoriev VV, Bobrikov IA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Tsirlin AA, Abakumov AM, Journal of the Chemical Society : Dalton transactions 45, 1192 (2016). http://doi.org/10.1039/c5dt04296h
Abstract: Highly homogeneous mullite-type solid solutions Bi2Fe4-xCrxO9 (x = 0.5, 1, 1.2) were synthesized using a soft chemistry technique followed by a solid-state reaction in Ar. The crystal structure of Bi2Fe3CrO9 was investigated using X-ray and neutron powder diffraction, transmission electron microscopy and Fe-57 Mossbauer spectroscopy (S.G. Pbam, a = 7.95579(9) angstrom , b = 8.39145(9) angstrom, c = 5.98242(7) angstrom, R-F(X-ray) = 0.022, R-F(neutron) = 0.057). The ab planes in the structure are tessellated with distorted pentagonal loops built up by three tetrahedrally coordinated Fe sites and two octahedrally coordinated Fe/Cr sites, linked together in the ab plane by corner-sharing forming a pentagonal Cairo lattice. Magnetic susceptibility measurements and powder neutron diffraction show that the compounds order antiferromagnetically (AFM) with the Neel temperatures decreasing upon increasing the Cr content from T-N similar to 250 K for x = 0 to T-N similar to 155 K for x = 1.2. The magnetic structure of Bi2Fe3CrO9 at T = 30 K is characterized by a propagation vector k = (1/2,1/2,1/2). The tetrahedrally coordinated Fe cations form singlet pairs within dimers of corner-sharing tetrahedra, but spins on the neighboring dimers are nearly orthogonal. The octahedrally coordinated (Fe, Cr) cations form antiferromagnetic up-up-down-down chains along c, while the spin arrangement in the ab plane is nearly orthogonal between nearest neighbors and collinear between second neighbors. The resulting magnetic structure is remarkably different from the one in pure Bi2Fe4O9 and features several types of spin correlations even on crystallographically equivalent exchange that may be caused by the simultaneous presence of Fe and Cr on the octahedral site.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/c5dt04296h
|
|
|
“Evidence for anionic redox activity in a tridimensional-ordered Li-rich positive electrode β-Li2IrO3”. Pearce PE, Perez AJ, Rousse G, Saubanère M, Batuk D, Foix D, McCalla E, Abakumov AM, Van Tendeloo G, Doublet M-L, Tarascon J-M, Nature materials 16, 580 (2017). http://doi.org/10.1038/nmat4864
Abstract: Lithium-ion battery cathode materials have relied on cationic redox reactions until the recent discovery of anionic redox activity in Li-rich layered compounds which enables capacities as high as 300 mAh g(-1). In the quest for new high-capacity electrodes with anionic redox, a still unanswered question was remaining regarding the importance of the structural dimensionality. The present manuscript provides an answer. We herein report on a beta-Li2IrO3 phase which, in spite of having the Ir arranged in a tridimensional (3D) framework instead of the typical two-dimensional (2D) layers seen in other Li-rich oxides, can reversibly exchange 2.5 e(-) per Ir, the highest value ever reported for any insertion reaction involving d-metals. We show that such a large activity results from joint reversible cationic (Mn+) and anionic (O-2)(n-) redox processes, the latter being visualized via complementary transmission electron microscopy and neutron diffraction experiments, and confirmed by density functional theory calculations. Moreover, beta-Li2IrO3 presents a good cycling behaviour while showing neither cationic migration nor shearing of atomic layers as seen in 2D-layered Li-rich materials. Remarkably, the anionic redox process occurs jointly with the oxidation of Ir4+ at potentials as low as 3.4 V versus Li+/Li-0, as equivalently observed in the layered alpha-Li2IrO3 polymorph. Theoretical calculations elucidate the electrochemical similarities and differences of the 3D versus 2D polymorphs in terms of structural, electronic and mechanical descriptors. Our findings free the structural dimensionality constraint and broaden the possibilities in designing high-energy-density electrodes for the next generation of Li-ion batteries.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
DOI: 10.1038/nmat4864
|
|
|
“Nanoscale Characterization of Growth of Secondary Phases in Off-Stoichiometric CZTS Thin Films”. Vishwakarma M, Karakulina OM, Abakumov AM, Hadermann J, Mehta BR, Journal of nanoscience and nanotechnology 18, 1688 (2018). http://doi.org/10.1166/jnn.2018.14261
Abstract: The presence of secondary phases is one of the main issues that hinder the growth of pure kesterite Cu2ZnSnS4 (CZTS) based thin films with suitable electronic and junction properties for efficient solar cell devices. In this work, CZTS thin films with varied Zn and Sn content have been prepared by RF-power controlled co-sputtering deposition using Cu, ZnS and SnS targets and a subsequent sulphurization step. Detailed TEM investigations show that the film shows a layered structure with the majority of the top layer being the kesterite phase. Depending on the initial thin film composition, either about ~1 μm Cu-rich and Zn-poor kesterite or stoichiometric CZTS is formed as top layer. X-ray diffraction, Raman spectroscopy and transmission electron microscopy reveal the presence of Cu2−x S, ZnS and SnO2 minor secondary phases in the form of nanoinclusions or nanoparticles or intermediate layers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.483
DOI: 10.1166/jnn.2018.14261
|
|
|
“Revealing pH-Dependent Activities and Surface Instabilities for Ni-Based Electrocatalysts during the Oxygen Evolution Reaction”. Yang C, Batuk M, Jacquet Q, Rousse G, Yin W, Zhang L, Hadermann J, Abakumov AM, Cibin G, Chadwick A, Tarascon J-M, Grimaud A, ACS energy letters , 2884 (2018). http://doi.org/10.1021/acsenergylett.8b01818
Abstract: Multiple electrochemical processes are involved at the catalyst/ electrolyte interface during the oxygen evolution reaction (OER). With the purpose of elucidating the complexity of surface dynamics upon OER, we systematically studied two Ni-based crystalline oxides (LaNiO3−δ and La2Li0.5Ni0.5O4) and compared them with the state-of-the-art Ni−Fe (oxy)- hydroxide amorphous catalyst. Electrochemical measurements such as rotating ring disk electrode (RRDE) and electrochemical quartz microbalance microscopy (EQCM) coupled with a series of physical characterizations including transmission electron microscopy (TEM) and X-ray absorption spectroscopy (XAS) were conducted to unravel the exact pH effect on both the OER activity and the catalyst stability. We demonstrate that for Ni-based crystalline catalysts the rate for surface degradation depends on the pH and is greater than the rate for surface reconstruction. This behavior is unlike that for the amorphous Ni oxyhydroxide catalyst, which is found to be more stable and pH-independent.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1021/acsenergylett.8b01818
|
|
|
“Toward unlocking the Mn3+/Mn2+ redox pair in alluaudite-type Na2+2zMn2-z(SO4)3-x(SeO4)x cathodes for sodium-ion batteries”. Kirsanova MA, De Sloovere D, Karakulina OM, Hadermann J, Van Bael MK, Hardy A, Abakumov AM, Journal of solid state chemistry 277, 804 (2019). http://doi.org/10.1016/J.JSSC.2019.07.032
Abstract: In polyanion cathodes, the inductive effect alters the potential of a M(n+1)+/Mn+ redox couple (M – transition metal) according to the electronegativity of the X cation in the polyanion groups (XO4m+). To manipulate the operating potential, we synthesized a series of mixed sulfate-selenate alluaudites, with structure formulas Na2+2zMn2-z(SO4)(3-x)(SeO4)(x) and Na2.81Ni1.60(SO4)(1.43)(SeO4)(1.57). Their crystal structure was determined from powder X-ray diffraction data, revealing that the Mn-based alluaudites form solid solutions with the same crystal structure for x = 0.75; 1.125 and 1.5. Na2.81Ni1.60(SO4)(1.43)(SeO4)(1.57) is isostructural to the Mn-based alluaudites. Although the Na2+2zMn2-z(SO4)(3-x)(SeO4)(x) compound with the highest selenium content demonstrates a reversible discharge capacity of 60 mAh g(-1), only a small part of this electrochemical activity can be ascribed to the Mn3+/Mn2+ redox couple. The redox potential of the Mn3+/Mn2+ pair in Na2+2zMn2-z(SO4)(3-)x(SeO4)(x) decreases with increasing values of x, in agreement with the lower electronegativity of Se compared to that of S.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/J.JSSC.2019.07.032
|
|
|
“Tuning the crystal structure of A2CoPO4F(A=Li,Na) fluoride-phosphates : a new layered polymorph of LiNaCoPO4F”. Fedotov SS, Aksyonov DA, Samarin AS, Karakulina OM, Hadermann J, Stevenson KJ, Khasanova NR, Abakumov AM, Antipov E V, European journal of inorganic chemistry 2019, 4365 (2019). http://doi.org/10.1002/EJIC.201900660
Abstract: Co-containing fluoride-phosphates are of interest in sense of delivering high electrode potentials and attractive specific energy values as positive electrode materials for rechargeable batteries. In this paper we report on a new Co-based fluoride-phosphate, LiNaCoPO4F, with a layered structure (2D), which was Rietveld-refined based on X-ray powder diffraction data [P2(1)/c, a = 6.83881(4) angstrom, b = 11.23323(5) angstrom, c = 5.07654(2) angstrom, beta = 90.3517(5) degrees, V = 389.982(3) angstrom(3)] and validated by electron diffraction and high-resolution scanning transmission electron microscopy. The differential scanning calorimetry measurements revealed that 2D-LiNaCoPO4F forms in a narrow temperature range of 520-530 degrees C and irreversibly converts to the known 3D-LiNaCoPO4F modification (Pnma) above 530 degrees C. The non-carbon-coated 2D-LiNaCoPO4F shows reversible electrochemical activity in Li-ion cell in the potential range of 3.0-4.9 V vs. Li/Li+ with an average potential of approximate to 4.5 V and in Na-ion cell in the range of 3.0-4.5 V vs. Na/Na+ exhibiting a plateau profile centered around 4.2 V, in agreement with the calculated potentials by density functional theory. The energy barriers for both Li+ and Na+ migration in 2D-LiNaCoPO4F amount to 0.15 eV along the [001] direction rendering 2D-LiNaCoPO4F as a viable electrode material for high-power Li- and Na-ion rechargeable batteries. The discovery and stabilization of the 2D-LiNaCoPO4F polymorph indicates that temperature influence on the synthesis of A(2)MPO(4)F fluoride-phosphates needs more careful examination with perspective to unveil new structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
DOI: 10.1002/EJIC.201900660
|
|