“3D FIB/SEM study of Ni4Ti3 precipitates in Ni-Ti alloys with different thermal-mechanical histories”. Cao S, Nishida M, Somsen C, Eggeler G, Schryvers D, , 02004 (2009). http://doi.org/10.1051/esomat/200902004
Abstract: The three-dimensional size, morphology and distribution of Ni4Ti3 precipitates growing in binary Ni-rich Ni-Ti alloys have been investigated via a slice view procedure in a Dual-Beam FIB/SEM system, in order to better stress-free Ni50.8Ti49.2 alloy with all four variants of precipitates and a compressed Ni51Ti49 alloy with aligned precipitates in one family were studied. The Ni4Ti3 precipitates reach a volume fraction of 9.6% in the reconstructed region of the stress-free alloy and 4.3% in the compressed one. In both cases, the mean volume, specific surface area, sphericity and aspect ratio of the precipitates are calculated and the Pair Distribution Functions of the precipitates are obtained. It is shown that most precipitates in the stress-free sample grow larger and have a more lenticular shape, while those in the compressed sample are more cylindrical. Deviations from these ideal shapes reveal internal steps in the stress-free sample and lamellae formation in the compressed one.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/esomat/200902004
|
|
“Cavity nucleation and growth in Cu-Zn-Al irradiated with Cu+ ions at different temperatures”. Zelaya E, Schryvers D, Tolley A, Fitchner PFP, Intermetallics 18, 493 (2010). http://doi.org/10.1016/j.intermet.2009.09.010
Abstract: The effects of high dose ion irradiation in β CuZnAl were investigated between room temperature and 150 °C. Single crystal samples with surface normal close to [001]β were irradiated with 300 keV Cu+ ions. Microstructural changes were characterized using transmission electron microscopy. Irradiation induced cavities located on the surface exposed to the irradiation were observed. The morphology, size and density distribution of these cavities were analyzed as a function of different irradiation conditions. The shape and location of the cavities with respect to the irradiation surface were not affected by irradiation temperature or irradiation dose. Instead, the cavity size distribution showed a bi-modal shape for a dose of 15 dpa, regardless of irradiation temperature. For a dose of 30 dpa the bi-modal distribution was only observed after room temperature irradiation. The diffusion effects of vacancies produced by irradiation are analyzed in shape memory CuZnAl alloys, which main characteristic is the diffusionless martensitic transformation. Particularly, the cavity size distributions were analyzed in terms of nucleation, growth and coalescence.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 1
DOI: 10.1016/j.intermet.2009.09.010
|
|
“Compositional characterization of nickel silicides by HAADF-STEM imaging”. Verleysen E, Bender H, Richard O, Schryvers D, Vandervorst W, Journal of materials science 46, 2001 (2011). http://doi.org/10.1007/s10853-010-5191-z
Abstract: A methodology for the quantitative compositional characterization of nickel silicides by high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) imaging is presented. HAADF-STEM images of a set of nickel silicide reference samples Ni3Si, Ni31Si12, Ni2Si, NiSi and NiSi2 are taken at identical experimental conditions. The correlation between sample thickness and HAADF-STEM intensity is discussed. In order to quantify the relationship between the experimental Z-contrast intensities and the composition of the analysed layers, the ratio of the HAADF-STEM intensity to the sample thickness or to the intensity of the silicon substrate is determined for each nickel silicide reference sample. Diffraction contrast is still detected on the HAADF-STEM images, even though the detector is set at the largest possible detection angle. The influence on the quantification results of intensity fluctuations caused by diffraction contrast and channelling is examined. The methodology is applied to FUSI gate devices and to horizontal TFET devices with different nickel silicides formed on source, gate and drain. It is shown that, if the elements which are present are known, this methodology allows a fast quantitative 2-dimensional compositional analysis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 1
DOI: 10.1007/s10853-010-5191-z
|
|
“Defect structures in CuZr martensite, studies by CTEM and HRTEM”. Seo JW, Schryvers D, Journal de physique: 4 C5, 149 (1997). http://doi.org/10.1051/jp4:1997523
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/jp4:1997523
|
|
“Electron microscopy study of twin sequences and branching in Ni66Al34 3r martensite”. Schryvers D, van Landuyt JT, Proceedings Of The International Conference On Martensitic Transformations (icomat-92) , 263 (1993)
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 1
|
|
“EM characterization of precipitates in as-cast and annealed Ni45.5Ti45.5Nb9 shape memory alloys”. Shi H, Frenzel J, Schryvers D, Materials science forum 738/739, 113 (2013). http://doi.org/10.4028/www.scientific.net/MSF.738-739.113
Abstract: Nb-rich precipitates in the matrix of as-cast and annealed Ni45.5Ti45.5Nb9 alloys are investigated by scanning and scanning transmission electron microscopy, including slice-and-view and geometric phase analysis (GPA). The Nb-rich bcc nano-precipitates in the as-cast alloy have a 10% lattice parameter difference with the B2 matrix and reveal compensating interface dislocations. The 3D reconstruction of the configuration of small Nb-rich precipitates in the annealed alloy reveals a wall-like distribution of precipitates, which may increase the thermal hysteresis of the material.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.4028/www.scientific.net/MSF.738-739.113
|
|
“Experimental studies on precursor phenomena in displacive phase transformations”. Schryvers D, Properties Of Complex Inorganic Solids , 321 (1997)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
|
|
“Internal calibration technique for HREM studies of nanoscale particles”. Schryvers D, Goessens C, Safran G, Toth L, Microscopy research and technique
T2 –, JOINT MEETING OF DUTCH SOC FOR ELECTRON MICROSCOPY / BELGIAN SOC FOR, ELECTRON MICROSCOPY / BELGIAN SOC FOR CELL BIOLOGY, DEC 10-11, 1992, ANTWERP, BELGIUM 25, 185 (1993). http://doi.org/10.1002/jemt.1070250216
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.154
Times cited: 1
DOI: 10.1002/jemt.1070250216
|
|
“Nanoscale inhomogeneities in melt-spun Ni-Al”. Potapov P, Ochin P, Pons J, Schryvers D, Journal de physique: 4 11, 439 (2001). http://doi.org/10.1051/jp4:2001873
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/jp4:2001873
|
|
“New method to determine the parity of the number of twin planes in tabular silver halide microcrystals from top views”. Goessens C, Schryvers D, van Landuyt J, de Keyzer R, The journal of imaging science and technology 41, 301 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.348
Times cited: 1
|
|
“On the phase-like nature of the 7m structure in ni-al”. Schryvers D, Tanner LE, , 849 (1994)
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 1
|
|
“On the phase-like nature of the 7M structure in Ni-Al”. Schryvers D, Tanner LE, MRS Japan: shape memory materials 18, 849 (1993)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
|
|
“Some examples of electron microscopy studies of microstructures and phase transitions in solids”. Schryvers D, Van Tendeloo G, van Landuyt J, Amelinckx S, Meccanica 30, 433 (1995). http://doi.org/10.1007/BF01557075
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.949
Times cited: 1
DOI: 10.1007/BF01557075
|
|
“Structural characterisation of melt-spun Ti-Ni-Cu-ribbons”. Schryvers D, Potapov P, Ledda A, Shelyakov A, Journal de physique: 4 11, 363 (2001). http://doi.org/10.1051/jp4:2001861
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/jp4:2001861
|
|
“TEM study of B2 + L12 decomposition in a nanoscale Ni-rich Ni-Al film”. Schryvers D, Yandouzi M, Toth L, Thin solid films : an international journal on the science and technology of thin and thick films 326, 126 (1998). http://doi.org/10.1016/S0040-6090(98)00545-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 1
DOI: 10.1016/S0040-6090(98)00545-8
|
|
“TEM study of the mechanism of Ni ion release from Nitinol wires with original oxides”. Tian H, Schryvers D, Shabalovskaya S, van Humbeeck J, , 05027 (2009). http://doi.org/10.1051/esomat/200905027
Abstract: The surface of commercial Nitinol wires with original oxides and a thickness in the 30-190 nm range was investigated by different state of art TEM techniques. The oxide surface layer was identified as a combination of TiO and TiO2 depending on the processing of the wire. Between the core of the wires and the oxidized surface, an interfacial Ni3Ti nanolayer was observed while Ni nanoparticles are found inside the original oxide. The particle sizes, their distribution in the surface and the Ti-O stoichiometry were deduced from the analysis of the obtained data. Molecular dynamics calculations performed for evaluation of the stability of Ni particles relative to the atomic state revealed that a pure Ni particle has a lower energy than free Ni atoms inside the TiO2 lattice. The obtained results are discussed with respect to surface stability and Ni release in the human body.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/esomat/200905027
|
|
“Tomographic spectroscopic imaging, an experimental proof of concept”. van den Broek W, Verbeeck J, Schryvers D, de Backer S, Scheunders P, Ultramicroscopy 109, 296 (2009). http://doi.org/10.1016/j.ultramic.2008.11.022
Abstract: Recording the electron energy loss spectroscopy data cube with a series of energy filtered images is a dose inefficient process because the energy slit blocks most of the electrons. When recording the data cube by scanning an electron probe over the sample, perfect dose efficiency is attained; but due to the low current in nanoprobes, this often is slower, with a smaller field of view. In W. Van den Broek et al. [Ultramicroscopy, 106 (2006) 269], we proposed a new method to record the data cube, which is more dose efficient than an energy filtered series. It produces a set of projections of the data cube and then tomographically reconstructs it. In this article, we demonstrate these projections in practice, we present a simple geometrical model that allows for quantification of the projection angles and we present the first successful experimental reconstruction, all on a standard post-column instrument.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2008.11.022
|
|
“Optimization of Automated Crystal Orientation and Phase Mapping in TEM Applied to Ni-Ti All Round Shape Memory Alloy”. Yao X, Li Y, Cao S, Ma X, Zhang X-ping, Schryvers D, MATEC web of conferences
T2 –, Proceedings of ESOMAT 2015 10th European Symposium on Martensitic Transformations, September 14-18, 2015, Antwerp, Belgium 33, 03022 (2015). http://doi.org/10.1051/matecconf/20153303022
Abstract: A new application which focuses on an artificial sphincter fabricated by Ni-Ti SMAs for human implantation is under investigation by applying the all-round shape memory effect with precise control of the phase transformation temperatures. In this study, a Ni51at.%-Ti alloy was fabricated by arc melting with fast solidification, followed by a proper strained aging which induces the two way shape memory effect needed for this particular application. Differential scanning calorimetry was used to investigate the thermal behavior and transmission electron microscopy was used for studying the microstructure of the alloys. With the latter the novel technique of automated crystal orientation microscopy is used and optimized to obtain phase and orientation mapping of the various structures.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/matecconf/20153303022
|
|
“Quantification by aberration corrected (S)TEM of boundaries formed by symmetry breaking phase transformations”. Schryvers D, Salje EKH, Nishida M, De Backer A, Idrissi H, Van Aert S, Ultramicroscopy 176, 194 (2017). http://doi.org/10.1016/j.ultramic.2016.12.022
Abstract: The present contribution gives a review of recent quantification work of atom displacements, atom site occupations and level of crystallinity in various systems and based on aberration corrected HR(S)TEM images. Depending on the case studied, picometer range precisions for individual distances can be obtained, boundary widths at the unit cell level determined or statistical evolutions of fractions of the ordered areas calculated. In all of these cases, these quantitative measures imply new routes for the applications of the respective materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2016.12.022
|
|
“Tailoring the Ti-C nanoprecipitate population and microstructure of titanium stabilized austenitic steels”. Cautaerts N, Delville R, Stergar E, Schryvers D, Verwerft M, Journal of nuclear materials 507, 177 (2018). http://doi.org/10.1016/J.JNUCMAT.2018.04.041
Abstract: The present work reports on the microstructural evolution of a new heat of 24% cold worked austenitic DIN 1.4970 (15-15Ti) nuclear cladding steel subjected to ageing heat treatments of varying duration between 500 and 800 degrees C (by steps of 100 degrees C). The primary aim was studying the finely dispersed Ti-C nanoprecipitate population, which are thought to be beneficial for creep and swelling resistance during service. Their size distribution and number density were estimated through dark field imaging and bright field Moire imaging techniques in the transmission electron microscope. Nanoprecipitates formed at and above 600 degrees C, which is a lower temperature than previously reported. The observed nucleation, growth and coarsening behavior of the nanoprecipitates were consistent with simple diffusion arguments. The formation of nanoprecipitates coincided with significant dissociation of dislocations as evidenced by weak beam dark field imaging. Possible mechanisms, including Silcock's stacking fault growth model and Suzuki segregation, are discussed. Recrystallization observed after extended ageing at 800 degrees C caused the redissolution of nanoprecipitates. Large primary Ti(C,N) and (Ti,Mo)C precipitates that occur in the as-received material, and M23C6 precipitates that nucleate on grain boundaries at low temperatures were also characterized by a selective dissolution procedure involving filtration, X-ray diffraction and quantitative Rietveld refinement. The partitioning of key elements between the different phases was derived by combining these findings and was consistent with thermodynamic considerations and the processing history of the steel. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.048
Times cited: 1
DOI: 10.1016/J.JNUCMAT.2018.04.041
|
|
“Study of the Q&prime, (Q)-phase precipitation in Al–Mg–Si–Cu alloys by quantification of atomic-resolution transmission electron microscopy images and atom probe tomography”. Ding L, Orekhov A, Weng Y, Jia Z, Idrissi H, Schryvers D, Muraishi S, Hao L, Liu Q, Journal of materials science 54, 7943 (2019). http://doi.org/10.1007/s10853-019-03427-6
Abstract: The precipitation mechanism of the Q phase in Al-Mg-Si-Cu alloys has long been the subject of ambiguity and debate since its metastable phase (Q 0) has the same crystal structure and similar lattice parameters as its equilibrium counterparts. In the present work, the evolution of the Q 0 (Q) phase during aging is studied by combination of quantitative atomic-resolution scanning transmission electron microscopy and atom probe tomography. It was found that the transformation from the Q 0 to the Q phase involves changes of the occupancy of Al atoms in atomic columns of the Q 0 (Q) phase. The Al atoms incorporated in the Cu, Si and Mg columns are gradually released into the Al matrix, while mixing between Cu and Si atoms occurs in the Si columns. This transformation process is mainly attributed to the low lattice misfit of the equilibrium Q phase. Besides, the formation of various compositions of the Q phase is due to the different occupancy in the atomic columns of the Q phase. The occupancy changes in the columns of the Q phase are kinetically controlled and are strongly influenced by the alloy composition and aging temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 1
DOI: 10.1007/s10853-019-03427-6
|
|
“Dislocation structures and the role of grain boundaries in cyclically deformed Ni micropillars”. Samaee V, Sandfeld S, Idrissi H, Groten J, Pardoen T, Schwaiger R, Schryvers D, Materials Science And Engineering A-Structural Materials Properties Microstructure And Processing 769, 138295 (2020). http://doi.org/10.1016/j.msea.2019.138295
Abstract: Transmission electron microscopy and finite element-based dislocation simulations were combined to study the development of dislocation microstructures after cyclic deformation of single crystal and bicrystal Ni micropillars oriented for multi-slip. A direct correlation between large accumulation of plastic strain and the presence of dislocation cell walls in the single crystal micropillars was observed, while the presence of the grain boundary hampered the formation of wall-like structures in agreement with a smaller accumulated plastic strain. Automated crystallographic orientation and nanostrain mapping using transmission electron microscopy revealed the presence of lattice heterogeneities associated to the cell walls including long range elastic strain fields. By combining the nanostrain mapping with an inverse modelling approach, information about dislocation density, line orientation and Burgers vector direction was derived, which is not accessible otherwise in such dense dislocation structures. Simulations showed that the image forces associated with the grain boundary in this specific bicrystal configuration have only a minor influence on dislocation behavior. Thus, the reduced occurrence of “mature” cell walls in the bicrystal can be attributed to the available volume, which is too small to accommodate cell structures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.4
Times cited: 1
DOI: 10.1016/j.msea.2019.138295
|
|
“Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses”. Penders A, Konstantinovic MJ, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology , 1 (2020). http://doi.org/10.1080/1478422X.2020.1785651
Abstract: Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.8
Times cited: 1
DOI: 10.1080/1478422X.2020.1785651
|
|
“DSC cycling effects on phase transformation temperatures of micron and submicron grain Ni50.8Ti49.2 microwires”. Pourbabak S, Verlinden B, Van Humbeeck J, Schryvers D, Shape memory and superelasticity , 1 (2020). http://doi.org/10.1007/S40830-020-00278-Y
Abstract: The effect of thermal cycling parameters on the phase transformation temperatures of micron and submicron grain size recrystallized Ni-Ti microwires was investigated. The suppression of martensitic transformation by thermal cycling was found to enhance when combined with room temperature aging between the cycles and enhances even more when aged at elevated temperature of 100 degrees C. While aging at room temperature alone has no clear effect on the martensitic transformation, elevated temperature aging at 100 degrees C alone suppresses the martensitic transformation. All aforementioned effects were found to be stronger in large grain samples than in small grain samples. Martensitic transformation suppression in all cases was in line with the formation of Ni4Ti3 precursors in the form of < 111 & rang;(B2) Ni clusters as concluded from the observed diffuse intensity in the electron diffraction patterns revealing short-range ordering enhancement. Performing thermal cycling in some different temperature ranges to separate the effect of martensitic transformation and high temperature range of DSC cycling revealed that both high temperature- and martensitic transformation-included cycles enhance the short-range ordering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1007/S40830-020-00278-Y
|
|
“3D reconstruction of Ni4Ti3 precipitates in a Ni51Ti49 alloy in a FIB/SEM dual-beam system”. Cao S, Tirry W, van den Broek W, Schryvers D, Materials science forum 583, 277 (2008). http://doi.org/10.4028/www.scientific.net/MSF.583.277
Abstract: Ni4Ti3 precipitates play an important role in the shape memory and superelastic behaviour of thermo-mechanically treated Ni-Ti material. The 3D morphology and distribution of such precipitates with lenticular shape and rhombohedral atomic structure in the austenitic B2 matrix of a binary Ni-rich Ni-Ti alloy has been elucidated via a slice view procedure in a Dual-Beam FIB/SEM system. With the sequence of cross-section SE images obtained from the SEM, a 3D reconstruction has been achieved after proper alignment and image processing, from which both qualitative and quantitative analysis can be performed. Careful imaging is needed to ensure that all variants of the precipitates are observed with equal probability, regardless sample orientation. Moreover, due to the weak contrast of the precipitates, proper imaging conditions need to be selected to allow for semi-automated image treatment. Finally, a volume ratio of 10.2% for the Ni4Ti3 precipitates could be calculated, summed over all variants, which yields a net composition of Ni50.36Ti49.64 for the matrix, leading to an increase of 113 degrees for the martensitic start temperature Ms. Also, the expected relative orientation of the different variants of the precipitates could be confirmed. In the near future, other quantitative measures on the distribution of the precipitates can be expected.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
DOI: 10.4028/www.scientific.net/MSF.583.277
|
|
“3D strain fields surrounding Ni4Ti3: direct measurement and correlation with the R-phase”. Tirry W, Schryvers D, , 02032 (2009). http://doi.org/10.1051/esomat/200902032
Abstract: Strain fields introduced by coherent Ni4Ti3 precipitates in austenitic Ni-Ti are believed to be a possible origin of why the R-phase transformation is introduced as an extra step before transforming to the B19'. The presence of this strain field was already confirmed in the past by conventional transmission electron microscopy (TEM) techniques and measured quantitatively by high resolution TEM (HRTEM). This time the geometrical phase method is applied on HRTEM micrographs to measure the full 3D strain tensor of the strain fields. Since each atomic resolution micrograph only results in a 2D measurement of the strain, observations in two different zone orientations are combined to retrieve the 3 x 3 strain tensor. In this work observations in a [1-1 1](B2) and [1 0-1](B2) zone orientation are used and this in case of precipitates with a diameter of around 50nm. In a next step the measured strain tensor is compared to the calculated eigenstrain of the R-phase in reference to the B2 matrix. This comparison shows that the introduced strain is very similar to the eigenstrain of one R-phase variant. Since for both structures, Ni4Ti3 and R-phase, four orientation variants are possible, each variant of the R-phase is thus able to accommodate the strain field of one of the Ni4Ti3 variants.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
DOI: 10.1051/esomat/200902032
|
|
“Advanced electron microscopy characterisation of important precipitation and ordering phenomena in shape memory systems”. Schryvers D, Shape memory and superelasticity 1, 78 (2015). http://doi.org/10.1007/s40830-015-0006-3
Abstract: The present paper discusses some important aspects of precipitation and ordering in alloy systems that show a martensitic transformation and can or are used as shape memory or superelastic metallic systems. The precipitates are investigated by a variety of conventional and advanced electron microscopy techniques, including atomic resolution, 3D slice-and-view, energy loss spectroscopy etc. Depending on the system, such secondary phases can decrease the probability of a displacive transformation by changing the phase stability in the system, such as in the case of NiAl or NiTiPd, or can mechanically hinder the passage of the transformation interface, as in NiTiNb. On the other hand, properly controlling the nucleation and growth of some precipitates can strongly improve the properties of some types of materials, as is the case for the well-known Ni4Ti3 precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1007/s40830-015-0006-3
|
|
“Advanced TEM and SEM methods applied to 3D nano- and microstructural investigations of Ni4Ti3 precipitates in Ni-Ti (SMA)”. Schryvers D, Tirry W, Cao S, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 229 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.229
Abstract: Two different kinds of experimental approaches yielding three-dimensional structural information on metastable semi-coherent precipitates are demonstrated. By combining high-resolution images from two independent viewing directions a full description of the strain field surrounding a nano-sized Ni4Ti3 precipitate in Ni-Ti can be obtained. The principal axes and strains correlate well with the transformation strain of the observed R-phase transformation close to the precipitate. Using a slice-and-view procedure in a FIB/SEM dual-beam instrument, a three-dimensional voxel dataset is produced from which morphological and distributional information on the same precipitates can be obtained yielding new insight into the particular transformation paths of these alloys, relevant for their functional behaviour.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.4028/www.scientific.net/SSP.172-174.229
|
|
“Advanced TEM investigations on Ni-Ti shape memory material: strain and concentration gradients surrounding Ni4Ti3 precipitates”. Schryvers D, Tirry W, Yang Z, , 329 (2005)
Abstract: Lattice deformations and concentration gradients surrounding Ni4Ti3 precipitates grown by appropriate annealing in a Ni51Ti49 B2 austenite matrix are determined by a combination of TEM techniques. Quantitative Fourier analysis of HRTEM images reveals a deformed nanoscale region with lattice deformations up to 2% while EELS and EDX indicate a Ni depleted zone up to 150 nm away from the matrix-precipitate interface.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
“Advanced TEM studies of martensite and related phase transformations”. Schryvers D s.l., page 947 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|