Abstract: We studied the morphology of ramps in REBa2CU3O7 (REBCO) epitaxial films on SrTiO3 substrates, fabricated by RF magnetron sputter deposition and pulsed laser deposition (PLD), by scanning probe microscopy (SPM) and high resolution electron microscopy (HREM). The ramps were fabricated by Ar ion beam etching using masks of standard photoresist and TIN. AFM-studies on ramps in sputter deposited films show a strong dependence, i.e. formation of facets and ridges, on the angle of incidence of the ion beam with respect to the substrate surface as well as the rotation angle with respect to the crystal axes of the substrate. Ramps in pulsed laser deposited films did not show this dependence, Furthermore, we studied the effect of an anneal step prior to the deposition of barrier layers (i.e. PrBa2CU3O7, SrTiO3, CeO2) on the ramp. First results show a recrystallization of the ramp surface, resulting in terraces and a non-homogeneous growth of the barrier material on top of it. The thickness variations, for thin layers of barrier material, con even become much larger than expected from the amount of deposited material and are dependent on the deposition and anneal conditions. HREM studies show a well defined interface between barrier layer and electrodes. The angle of the ramp depends on the etch rate of the mask and REBCO, and on the angle of incidence of the ion beam. TiN has a much lower etch rate compared to photoresist, resulting in an angle of the ramp comparable to the angle of incidence, resulting in a low etching rate on the ramp. These results will lead to improved electrical characteristics of ramp-type junctions.

Abstract: Nanocrystalline diamond films have generated much interested due to their diamond-like properties and low surface roughness. Several techniques have been used to obtain a high re-nucleation rate, such as hydrogen poor or high methane concentration plasmas. In this work, the properties of nano-diamond films grown on silicon substrates using a continuous DC bias voltage during the complete duration of growth are studied. Subsequently, the layers were characterised by several morphological, structural and optical techniques. Besides a thorough investigation of the surface structure, using SEM and AFM, special attention was paid to the bulk structure of the films. The application of FTIR, XRD, multi wavelength Raman spectroscopy, TEM and EELS yielded a detailed insight in important properties such as the amount of crystallinity, the hydrogen content and grain size. Although these films are smooth, they are under a considerable compressive stress. FTIR spectroscopy points to a high hydrogen content in the films, while Raman and EELS indicate a high concentration of sp2 carbon. TEM and EELS show that these films consist of diamond nano-grains mixed with an amorphous sp2 bonded carbon, these results are consistent with the XRD and UV Raman spectroscopy data.

Abstract: The superstructure of the RE(2)(Sr0.85-xBaxNd0.15)(2)GaCU2O9 compound is found to change significantly with increasing substitution of Ba for Sr. Most of the changes take place in the (Sr0.85-xBaxNd0.15)O-GaO-(Sr0.85-xBaxNd0.15)O lamella, the rest of the basic structure being hardly affected. The structural changes for O less than or equal to x less than or equal to 0.65 are studied by electron diffraction. The arrangement of the chains of GaO4 tetrahedra in the Ba-free compound becomes disordered at x > 0.25. At x similar to 0.65 a rearrangement of the chains in the GaO layers takes place; they form a meandering arrangement, which can be described on a 4a(p) x 2a(p) x c(p) superlattice. This rearrangement is accompanied by ordering of Ba and Sr atoms in the adjacent (ST0.85-xBaxNd0.15)O layers. A simple scheme is proposed to explain the influence of the substitution of Ba for Sr on the linking of the GaO4 tetrahedra and on the geometry of the ''chains'' in the GaO layer.

Abstract: The atomic structure of single-wall carbon nanotube bundles produced by three different techniques has been characterized by electron diffraction and microscopy. Small bundles produced by Catalytical Chemical Vapor Deposition (CCVD) exhibit only one or two tube chiralities within a single bundle while bundles produced by arc-discharge or laser-ablation exhibit more chiralities. A detailed analysis of the central line of diffraction is also presented. The CCVD nanotubes present more intense spots around 1.7 Angstrom(-1) < k < 2Angstrom(-1) (k is the momentum transfer) compared to what is observed for nanotubes produced by other methods. Amongst the possible explanation for such an anomaly, we put forward that in this range of momentum transfer, the relative tube orientations and translations are important for what concerns the interpretation of the diffraction peaks intensities.

Abstract: Results of dielectric and resonance frequency (f(r)) measurements below room temperature are presented for Pb(ZrxTi1-x)O-3, x = 0.515 and 0.520. It is shown that the temperature coefficient of f(r) changes sign from negative to positive around 210 and 265 K for x = 0.520 and 200 and 260 K for x = 0.515. Anomalies in the real part of the dielectric constant (epsilon') are observed around the same temperatures at which the temperature coefficient of f(r) changes sign because of the electrostrictive coupling between the elastic and dielectric responses. Low-temperature powder x-ray-diffraction (XRD) data, however, reveal only one transition from the tetragonal to monoclinic phase similar to that reported by Noheda et al. [Phys. Rev. B, 61, 8687 (2000)]. Electron-diffraction data, on the other hand, reveal yet another structural transition at lower temperatures corresponding to the second anomaly in the epsilon' vs T and f(r) vs T curves. This second transition is shown to be a cell-doubling transition not observed by Noheda et al. in their XRD studies. The observation of superlattice reflections raises doubts about the correctness of the Cm space group proposed by Noheda et al. for the monoclinic phase of Pb(ZrxTi(1-x))O-3 below the second transition temperature.