Abstract: The structure and defect structure of Bi2-xPbxSr3.5Cu2 (CO3)O8-delta compounds with 0 less-than-or-equal-to x less-than-or-equal-to 0.75 are carefully investigated by electron diffraction and high-resolution electron microscopy. All compounds have an orthorhombic structure with a almost-equal-to b almost-equal-to 5.4 angstrom and c almost-equal-to 39.5 angstrom. The length of the b-axis decreases monotonically with increasing x. The space group for the basic structure is Abm2. The structure can be considered as an intergrowth of Bi2Sr2CuO6 lamellae with Sr2CuO2 (CO3) lamellae along the c-axis. CO3 groups behave as bridges connecting the CuO6 octahedra. In the x = 0 compound the carbon atoms are shifted away from their symmetry positions; the orientational ordering of the CO3 groups (or the carbon shift) in successive CO planes alternates along +b and -b. Typical Bi-type and Pb-type modulations are found along the b-axis up to a Pb content x = 0.5. Electron beam irradiation destroys the ordering of the CO3 groups and alters the modulated structure. (C) 1994 Academic press, inc.

Abstract: A model for superstructure ordering in the <<chain>> layers of Ga (Co) substituted YBCO intergrowths with general formula (REO2)NSr2MCu2O5 (M = Co, Ga; n = 1, 2, ...) is proposed. By Ga or Co substitution for Cu, the structure of the <<chain>> layer changes : instead of the CuO4 planar squares, the chains consist of MO4 tetrahedra (M = Ga, Co) running along the [110] perovskite direction. The existing model for the Ga substituted <<123>> implies that all the chains are the same. Our new model is based on the results of Electron diffraction and High-resolution electron microscopy investigations. The model reveals the occurrence of two types of chains as a consequence of <<opposite>> ordering between neighbouring tetrahedra. The comer linked tetrahedra in each chain appear as alternatingly rotated in opposite sense, and a chain itself, as being displaced with respect to the underlying structure in one of two senses ; either forth (right) or back (left) along the chain direction. The regular alternation of chains of opposite type doubles the periodicity within a layer and induces the possibility for intrinsic disorder in the chain layer stacking sequence. The planar superstructure and a staggered stacking of the tetrahedral chain layers is found irrespective of the rest of the intergrowth structure. Superstructure ordering in the case of Co substitution is more perfect than for the Ga substitution.