Abstract: We introduce a new method to measure structure factors from parallel beam electron diffraction (PBED) patterns. Bloch wave refinement routines were developed which can minimise the difference between simulated and experimental Bragg intensities via variation of structure factors, Debye parameters, specimen thickness and -orientation. Due to plane wave illumination, the PBED refinement is highly efficient not only in computational respect, but also concerning the experimental effort since energy filtering is shown to have no significant effect on the refinement results. The PBED method was applied to simulated GaAs diffraction patterns to derive systematic errors and rules for the identification of plausible refinement results. The evaluation of experimental GaAs PBED patterns yields a 200 X-ray structure factor of -6.33±0.14. Additionally, we obtained -6.35±0.13 from two-dimensional convergent beam electron diffraction refinements. Both results confirm density functional theory calculations published by Rosenauer et al. and indicate the inaccuracy of isolated atom scattering data, which is crucial e.g. for the composition evaluation by lattice fringe analysis.

Abstract: Nano-scale ordering may be revealed in transmission electron microscopy (TEM) by at least three techniques that will be presented in this work: selected area electron diffraction, conventional TEM and high-resolution TEM. Digital image processing is used to extract additional information from the high-resolution micrographs. The described methods are illustrated in a microstructural and compositional study of a 90%Pb(Mg1/3Nb2/3)O-3-10%PbTiO2 ceramic sample. High-resolution images reveal the presence of ordered compositional nano-domains, observable in two specific crystallographic orientations. Antiphase boundaries lying in the (111) planes separate them, while (100) and (111) facets separate the ordered domains from the disordered matrix.

Abstract: The main drawbacks of silicon as the most promising anode material for lithium-ion batteries (theoretical capacity=3572 mAh g−1) are lithiation-induced volume changes and the continuous formation of a solidelectrolyte interphase (SEI) upon cycling. A recent strategy is to focus on the influence of coatings and composite materials. To this end, the evolution of the SEI, as well as an applied carbon coating, on nanosilicon electrodes during the first electrochemical cycles is monitored. Two specific techniques are combined: Transmission Electron Microscopy (TEM) is used to study the surface evolution of the nanoparticles on a very local scale, whereas electrochemical impedance spectroscopy (EIS) provides information on the electrode level. A TEMEELS fingerprint signal of carbonate structures from the SEI is discovered, which can be used to differentiate between the SEI and a graphitic carbon matrix. Furthermore, the shielding effect of the carbon coating and the thickness evolution of the SEI are described.

Abstract: We have revealed thermodynamically stable vortex-antivortex configurations in mesoscopic type I superconducting equilateral triangles. The revealed effect is explained by two factors: (i) vortex confinement in mesoscopic triangles and (ii) appearance of the vortex-antivortex repulsion in mesoscopic type I superconductor triangles in the vicinity of the dual point. The stability of the obtained solutions is examined as a function of material and external parameters – the Ginzburg-Landau parameter K and temperature – as well as a function of a distortion of the sample's shape. The vortex-antivortex. “molecule” turns out to be stable in a wide range of the parameters that makes it possible its experimental visualization.

Abstract: High-resolution transmission electron microscopy was performed on compacted Ni(3)Al nanostructured material prepared by the inert gas condensation technique. From electron diffraction data an incomplete L1(2) ordering of the crystallites is observed in the free particles as well as in the room temperature compacted samples. However, a completely ordered L1(2) structure with much bigger and well-defined crystallites exhibiting several defects is observed in material compacted and annealed at 773 K. Sharp crystallite boundaries as well as amorphous material and voids are observed in between crystallites in all samples, the former being dominant in the annealed material, the latter in the as-prepared one.

Abstract: In this work, the chemical and microstructural stability of YBiO3 buffer layers during the growth of YBa2Cu3O7-δ (YBCO) was studied. The superconducting YBCO films were deposited via both Pulsed Laser Deposition as well as Chemical Solution Deposition. Although excellent superconducting properties are obtained in both cases, self-field critical current densities of 3.6 and 1.2 MA/cm2 respectively, chemical instability of the YBiO3 buffer layer is observed. An elaborate transmission electron microscopy study showed that in the case of vacuum deposited YBCO, the YBiO3 becomes unstable and Bi2O3 sublimates out of the architecture. Due to this structural instability, an intermediate Y2O3 layer is obtained which maintains it microstructural orientation relation with the substrate and acts as growth template for YBCO. For chemical solution deposited YBCO, reaction of YBCO with the YBiO3 buffer layer is observed, leading to large grains of YBa2BiO6 which are pushed towards the surface of the films and strongly reduce the superconducting properties. Upon using high growth temperatures for the superconducting layer, these secondary phases decompose, which subsequently leads to Bi2O3 sublimation and a textured YBCO film which directly nucleated onto the LaAlO3 single crystal substrate. Hence, this electron microscopy study indicates that bismuth-based buffer layers systems are not suitable for implementation in coated conductors.