“Superconducting YBa2Cu3O7-δNanocomposites Using Preformed ZrO2Nanocrystals: Growth Mechanisms and Vortex Pinning Properties”. De Keukeleere K, Cayado P, Meledin A, Vallès F, De Roo J, Rijckaert H, Pollefeyt G, Bruneel E, Palau A, Coll M, Ricart S, Van Tendeloo G, Puig T, Obradors X, Van Driessche I, Advanced Electronic Materials 2, 1600161 (2016). http://doi.org/10.1002/aelm.201600161
Abstract: Although high temperature superconductors are promising for power applications, the production of low-cost coated conductors with high current densities—at high magnetic fields—remains challenging. A superior superconducting YBa2Cu3O7–δ nanocomposite is fabricated via chemical solution deposition (CSD) using preformed nanocrystals (NCs). Preformed, colloidally stable ZrO2 NCs are added to the trifluoroacetic acid based precursor solution and the NCs' stability is confirmed up to 50 mol% for at least 2.5 months. These NCs tend to disrupt the epitaxial growth of YBa2Cu3O7–δ, unless a thin seed layer is applied. A 10 mol% ZrO2 NC addition proved to be optimal, yielding a critical current density JC of 5 MA cm−2 at 77 K in self-field. Importantly, this new approach results in a smaller magnetic field decay of JC(H//c) for the nanocomposite compared to a pristine film. Furthermore, microstructural analysis of the YBa2Cu3O7–δ nanocomposite films reveals that different strain generation mechanisms may occur compared to the spontaneous segregation approach. Yet, the generated nanostrain in the YBa2Cu3O7–δ nanocomposite results in an improvement of the superconducting properties similar to the spontaneous segregation approach. This new approach, using preformed NCs in CSD coatings, can be of great potential for high magnetic field applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 26
DOI: 10.1002/aelm.201600161
|
|
|
“Deactivation study of Fe2O3-CeO2 during redox cycles for CO production from CO2”. Dharanipragada NVRA, Meledina M, Galvita VV, Poelman H, Turner S, Van Tendeloo G, Detavernier C, Marin GB, Industrial and engineering chemistry research 55, 5911 (2016). http://doi.org/10.1021/acs.iecr.6b00963
Abstract: Deactivation was investigated in Fe2O3-CeO2 oxygen storage materials during repeated H-2-reduction and CO2-reoxidation. In situ XRD, XAS, and TEM were used to identify phases, crystallite sizes, and morphological changes upon cycling operation. The effect of redox cycling was investigated both in Fe-rich (80 wt % Fe2O3-CeO2) and Ce-rich (10 wt %Fe2O3-CeO2) materials. The former consisted of 100 nm Fe2O3 particles decorated with 5-10 nm Ce1-xFexO2-x. The latter presented CeO2 with incorporated Fe, i.e. a solid solution of Ce1-xFexO2-x, as the main oxygen carrier. By modeling the EXAFS Ce-K signal for as-prepared 10 wt %Fe2O3-CeO2, the amount of Fe in CeO2 was determined as 21 mol %, corresponding to 86% of the total iron content. Sintering and solid solid transformations, the latter including both new phase formation and element segregation, were identified as deactivation pathways upon redox cycling. In Ce-rich material, perovskite (CeFeO3) was identified by XRD. This phase remained inert during reduction and reoxidation, resulting in an overall lower oxygen storage capacity. Further, Fe segregated from the solid solution, thereby decreasing its reducibility. In addition, an increase in crystallite size occurred for all phases. In Fe-rich material, sintering is the main deactivation pathway, although Fe segregation from the solid solution and perovskite formation cannot be excluded.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 26
DOI: 10.1021/acs.iecr.6b00963
|
|
|
“PDMS membranes containing ZIF-coated mesoporous silica spheres for efficient ethanol recovery via pervaporation”. Naik PV, Wee LH, Meledina M, Turner S, Li Y, Van Tendeloo G, Martens JA, Vankelecom IFJ, Journal of materials chemistry A : materials for energy and sustainability 4, 12790 (2016). http://doi.org/10.1039/C6TA04700A
Abstract: The design of functional micro- and mesostructured composite materials is significantly important for separation processes. Mesoporous silica is an attractive material for fast diffusion, while microporous zeolitic imidazolate frameworks (ZIFs) are beneficial for selective adsorption and diffusion. In this work, ZIF-71 and ZIF-8 nanocrystals were grown on the surface of mesoporous silica spheres (MSS) via the seeding and regrowth approach in order to obtain monodispersed MSS-ZIF-71 and MSS-ZIF-8 spheres with a particle size of 2-3 mm. These MSS-ZIF spheres were uniformly dispersed into a polydimethylsiloxane (PDMS) matrix to prepare mixed matrix membranes (MMMs). These MMMs were evaluated for the separation of ethanol from water via pervaporation. The pervaporation results reveal that the MSS-ZIF filled MMMs substantially improve the ethanol recovery in both aspects viz. flux and separation factor. These MMMs outperforms the unfilled PDMS membranes and the conventional carbon and zeolite filled MMMs. As expected, the mesoporous silica core allows very fast flow of the permeating compound, while the hydrophobic ZIF coating enhances the ethanol selectivity through its specific pore structure, hydrophobicity and surface chemistry. It can be seen that ZIF-8 mainly has a positive impact on the selectivity, while ZIF-71 enhances fluxes more significantly.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 26
DOI: 10.1039/C6TA04700A
|
|
|
“Air- and water-resistant noble metal coated ferromagnetic cobalt nanorods”. Lentijo-Mozo S, Tan RP, Garcia-Marcelot C, Altantzis T, Fazzini PF, Hungria T, Cormary B, Gallagher JR, Miller JT, Martinez H, Schrittwieser S, Schotter J, Respaud M, Bals S, Van Tendeloo G, Gatel C, Soulantica K, ACS nano 9, 2792 (2015). http://doi.org/10.1021/nn506709k
Abstract: Cobalt nanorods possess ideal magnetic properties for applications requiring magnetically hard nanoparticles. However, their exploitation is undermined by their sensitivity toward oxygen and water, which deteriorates their magnetic properties. The development of a continuous metal shell inert to oxidation could render them stable, opening perspectives not only for already identified applications but also for uses in which contact with air and/or aqueous media is inevitable. However, the direct growth of a conformal noble metal shell on magnetic metals is a challenge. Here, we show that prior treatment of Co nanorods with a tin coordination compound is the crucial step that enables the subsequent growth of a continuous noble metal shell on their surface, rendering them air- and water-resistant, while conserving the monocrystallity, metallicity and the magnetic properties of the Co core. Thus, the as-synthesized coreshell ferromagnetic nanorods combine high magnetization and strong uniaxial magnetic anisotropy, even after exposure to air and water, and hold promise for successful implementation in in vitro biodiagnostics requiring probes of high magnetization and anisotropic shape.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 25
DOI: 10.1021/nn506709k
|
|
|
“Effect of heat-treatment on luminescence and structure of Ag nanoclusters doped oxyfluoride glasses and implication for fiber drawing”. Kuznetsov AS, Cuong NT, Tikhomirov VK, Jivanescu M, Stesmans A, Chibotaru LF, Velázquez JJ, Rodríguez VD, Kirilenko D, Van Tendeloo G, Moshchalkov VV, Optical materials 34, 616 (2012). http://doi.org/10.1016/j.optmat.2011.09.007
Abstract: The effect of heat treatment on the structure and luminescence of Ag nanoclusters doped oxyfluoride glasses was studied and the implication for drawing the corresponding fibers doped with luminescent Ag nanoclusters has been proposed. The heat treatment results, first, in condensation of the Ag nanoclusters into larger Ag nanoparticles and loss of Ag luminescence, and further heat treatment results in precipitation of a luminescent-loss nano- and microcrystalline Ag phases onto the surface of the glass. Thus, the oxyfluoride fiber doped with luminescent Ag nanoclusters was pulled from the viscous glass melt and its attenuation loss was 0.19 dB/cm in the red part of the spectrum; i.e. near to the maximum of Ag nanoclusters luminescence band. The nucleation centers for the Ag nanoclusters in oxyfluoride glasses have been suggested to be the fluorine vacancies and their nanoclusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.238
Times cited: 25
DOI: 10.1016/j.optmat.2011.09.007
|
|
|
“Effect of oxygen rf-plasma on electronic properties of CNTs”. Felten A, Ghijsen J, Pireaux J-J, Johnson RL, Whelan CM, Liang D, Van Tendeloo G, Journal of physics: D: applied physics 40, 7379 (2007). http://doi.org/10.1088/0022-3727/40/23/019
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.588
Times cited: 25
DOI: 10.1088/0022-3727/40/23/019
|
|
|
“Electronic reconstruction at n-type SrTiO3/LaAlO3 interfaces”. Verbeeck J, Bals S, Lamoen D, Luysberg M, Huijben M, Rijnders G, Brinkman A, Hilgenkamp H, Blank DHA, Van Tendeloo G, Physical review : B : condensed matter and materials physics 81, 085113 (2010). http://doi.org/10.1103/PhysRevB.81.085113
Abstract: Electron-energy-loss spectroscopy (EELS) is used to investigate single layers of LaAlO3 grown on SrTiO3 having an n-type interface as well as multilayers of LaAlO3 and SrTiO3 in which both n- and p-type interfaces occur. Only minor changes in Ti valence at the n-type interface are observed. This finding seems to contradict earlier experiments for other SrTiO3/LaAlO3 systems where large deviations in Ti valency were assumed to be responsible for the conductivity of these interfaces. Ab initio calculations have been carried out in order to interpret our EELS results. Using the concept of Bader charges, it is demonstrated that the so-called polar discontinuity is mainly resolved by lattice distortions and to a far lesser extent by changes in valency for both single layer and multilayer geometries.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 25
DOI: 10.1103/PhysRevB.81.085113
|
|
|
“Particle layering in the ceramic-metal thin film Pt-Al2O3”. Gibaud A, Hazra S, Sella C, Laffez P, Désert A, Naudon A, Van Tendeloo G, Physical review : B : condensed matter and materials physics 63, 193407 (2001). http://doi.org/10.1103/PhysRevB.63.193407
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 25
DOI: 10.1103/PhysRevB.63.193407
|
|
|
“Phase selection enabled formation of abrupt axial heterojunctions in branched oxide nanowires”. Gao J, Lebedev OI, Turner S, Li YF, Lu YH, Feng YP, Boullay P, Prellier W, Van Tendeloo G, Wu T, Nano letters 12, 275 (2012). http://doi.org/10.1021/nl2035089
Abstract: Rational synthesis of nanowires via the vaporliquidsolid (VLS) mechanism with compositional and structural controls is vitally important for fabricating functional nanodevices from bottom up. Here, we show that branched indium tin oxide nanowires can be in situ seeded in vapor transport growth using tailored AuCu alloys as catalyst. Furthermore, we demonstrate that VLS synthesis gives unprecedented freedom to navigate the ternary InSnO phase diagram, and a rare and bulk-unstable cubic phase can be selectively stabilized in nanowires. The stabilized cubic fluorite phase possesses an unusual almost equimolar concentration of In and Sn, forming a defect-free epitaxial interface with the conventional bixbyite phase of tin-doped indium oxide that is the most employed transparent conducting oxide. This rational methodology of selecting phases and making abrupt axial heterojunctions in nanowires presents advantages over the conventional synthesis routes, promising novel composition-modulated nanomaterials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 25
DOI: 10.1021/nl2035089
|
|
|
“Point defect clusters and dislocations in FIB irradiated nanocrystalline aluminum films : an electron tomography and aberration-corrected high-resolution ADF-STEM study”. Idrissi H, Turner S, Mitsuhara M, Wang B, Hata S, Coulombier M, Raskin J-P, Pardoen T, Van Tendeloo G, Schryvers D, Microscopy and microanalysis 17, 983 (2011). http://doi.org/10.1017/S143192761101213X
Abstract: Focused ion beam (FIB) induced damage in nanocrystalline Al thin films has been characterized using advanced transmission electron microscopy techniques. Electron tomography was used to analyze the three-dimensional distribution of point defect clusters induced by FIB milling, as well as their interaction with preexisting dislocations generated by internal stresses in the Al films. The atomic structure of interstitial Frank loops induced by irradiation, as well as the core structure of Frank dislocations, has been resolved with aberration-corrected high-resolution annular dark-field scanning TEM. The combination of both techniques constitutes a powerful tool for the study of the intrinsic structural properties of point defect clusters as well as the interaction of these defects with preexisting or deformation dislocations in irradiated bulk or nanostructured materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 25
DOI: 10.1017/S143192761101213X
|
|
|
“Structural phase transition at low temperature, corresponding to charge ordering in the CMR perovskites LN0.5A0.5MNO3”. Laffez P, Van Tendeloo G, Millange F, Caignaert V, Hervieu M, Raveau B, Materials research bulletin 31, 905 (1996). http://doi.org/10.1016/S0025-5408(96)00090-6
Abstract: The magneto resistive perovskites Nd0.5Sr0.5MnO3 and Pr0.5Sr0.41Ca0.09MnO3 undergo a transition from anti ferromagnetic insulator to ferromagnetic metal as function of temperature. The room temperature phase is orthorhombic with the space group Imma and the cell parameters a approximate to root 2a(p), b approximate to 2a(p), and c approximate to root 2a(p). A structural phase transition related to charge ordering accompanying the transition from ferromagnetic state to antiferromagnetic state has been evidenced by low temperature electron diffraction. This transition is reversible and a new superstructure, with a P-type orthorhombic cell. and lattice parameters parameters a approximate to 2 root 2a(p), b approximate to 2a(p), and c approximate to root 2a(p), is formed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 25
DOI: 10.1016/S0025-5408(96)00090-6
|
|
|
“Synthesis and characterization of the reduced single-layer manganite Sr2MnO3.5+x”. Gillie LJ, Wright AJ, Hadermann J, Van Tendeloo G, Greaves C, Journal of solid state chemistry 167, 145 (2002). http://doi.org/10.1006/jssc.2002.9636
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 25
DOI: 10.1006/jssc.2002.9636
|
|
|
“Fe2O3-TiO2 nanosystems by a hybrid PE-CVD/ALD approach : controllable synthesis, growth mechanism, and photocatalytic properties”. Barreca D, Carraro G, Warwick MEA, Kaunisto K, Gasparotto A, Gombac V, Sada C, Turner S, Van Tendeloo G, Maccato C, Fornasiero P;, CrystEngComm 17, 6219 (2015). http://doi.org/10.1039/c5ce00883b
Abstract: Supported Fe2O3–TiO2 nanocomposites are fabricated by an original vapor phase synthetic strategy, consisting of the initial growth of Fe2O3 nanosystems on fluorine-doped tin oxide substrates by plasma enhanced-chemical vapor deposition, followed by atomic layer deposition of TiO2 overlayers with variable thickness, and final thermal treatment in air. A thorough characterization of the target systems is carried out by X-ray diffraction, atomic force microscopy, field emission-scanning electron microscopy, energy dispersive X-ray spectroscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy. High purity nanomaterials characterized by the co-presence of Fe2O3 (hematite) and TiO2 (anatase), with an intimate Fe2O3–TiO2 contact, are successfully obtained. In addition, photocatalytic tests demonstrate that, whereas both single-phase oxides do not show appreciable activity, the composite systems are able to degrade methyl orange aqueous solutions under simulated solar light, and even visible light, with an efficiency directly dependent on TiO2 overlayer thickness. This finding opens attractive perspectives for eventual applications in wastewater treatment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.474
Times cited: 25
DOI: 10.1039/c5ce00883b
|
|
|
“Transport, magnetic, and structural properties of La0.7Ce0.3MnO3 thin films: evidence for hole-doping”. Werner R, Raisch C, Leca V, Ion V, Bals S, Van Tendeloo G, Chasse T, Kleiner R, Koelle D, Physical review : B : solid state 79, 054416 (2009). http://doi.org/10.1103/PhysRevB.79.054416
Abstract: Cerium-doped manganite thin films were grown epitaxially by pulsed laser deposition at 720 °C and oxygen pressure pO2=125 Pa and were subjected to different annealing steps. According to x-ray diffraction (XRD) data, the formation of CeO2 as a secondary phase could be avoided for pO28 Pa. However, transmission electron microscopy shows the presence of CeO2 nanoclusters even in those films which appear to be single phase in XRD. With O2 annealing, the metal-to-insulator transition temperature increases, while the saturation magnetization decreases and stays well below the theoretical value for electron-doped La0.7Ce0.3MnO3 with mixed Mn3+/Mn2+ valences. The same trend is observed with decreasing film thickness from 100 to 20 nm, indicating a higher oxygen content for thinner films. Hall measurements on a film which shows a metal-to-insulator transition clearly reveal holes as dominating charge carriers. Combining data from x-ray photoemission spectroscopy, for determination of the oxygen content, and x-ray absorption spectroscopy (XAS), for determination of the hole concentration and cation valences, we find that with increasing oxygen content the hole concentration increases and Mn valences are shifted from 2+ to 4+. The dominating Mn valences in the films are Mn3+ and Mn4+, and only a small amount of Mn2+ ions can be observed by XAS. Mn2+ and Ce4+ XAS signals obtained in surface-sensitive total electron yield mode are strongly reduced in the bulk-sensitive fluorescence mode, which indicates hole-doping in the bulk for those films which do show a metal-to-insulator transition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 25
DOI: 10.1103/PhysRevB.79.054416
|
|
|
“Controlled growth of hexagonal gold nanostructures during thermally induced self-assembling on Ge(001) surface”. Jany BR, Gauquelin N, Willhammar T, Nikiel M, van den Bos KHW, Janas A, Szajna K, Verbeeck J, Van Aert S, Van Tendeloo G, Krok F, Scientific reports 7, 42420 (2017). http://doi.org/10.1038/srep42420
Abstract: Nano-sized gold has become an important material in various fields of science and technology, where control over the size and crystallography is desired to tailor the functionality. Gold crystallizes in the face-centered cubic (fcc) phase, and its hexagonal closed packed (hcp) structure is a very unusual and rare phase. Stable Au hcp phase has been reported to form in nanoparticles at the tips of some Ge nanowires. It has also recently been synthesized in the form of thin graphene-supported sheets which are unstable under electron beam irradiation. Here, we show that stable hcp Au 3D nanostructures with well-defined crystallographic orientation and size can be systematically created in a process of thermally induced self-assembly of thin Au layer on Ge(001) monocrystal. The Au hcp crystallite is present in each Au nanostructure and has been characterized by different electron microscopy techniques. We report that a careful heat treatment above the eutectic melting temperature and a controlled cooling is required to form the hcp phase of Au on a Ge single crystal. This new method gives scientific prospects to obtain stable Au hcp phase for future applications in a rather simple manner as well as redefine the phase diagram of Gold with Germanium.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
Times cited: 25
DOI: 10.1038/srep42420
|
|
|
“Nano-single crystal coalesced PtCu nanospheres as robust bifunctional catalyst for hydrogen evolution and oxygen reduction reactions”. Li W, Hu Z-Y, Zhang Z, Wei P, Zhang J, Pu Z, Zhu J, He D, Mu S, Van Tendeloo G, Journal of catalysis 375, 164 (2019). http://doi.org/10.1016/J.JCAT.2019.05.031
Abstract: Because of high electrocatalytic activity, Pt based metal nanospheres (NSs) have attracted a lot of attention. Hence, multi-particle nano-single crystal coalesced PtCu NSs are designed and successfully synthesized by a cost-effective aqueous solution method. The formed PtCu NS catalyst exhibits a superior hydrogen evolution reaction (HER) electrocatalytic activity with an ultralow onset potential of 18 mV at the current density of 2 mA/cm(2) and high mass activity of 1.08 A/mg(pt) (7.2 times higher than that of commercial Pt/C catalysts). Also, it shows an enhancement of 3.2 and 2.7 times in the mass and specific activities toward oxygen reduction reaction (ORR) compared to that of Pt/C. Moreover, it possesses an excellent catalytic durability for both ORR and HER. Even after 10,000 cycles, its ORR mass activity retains 87% of its initial value. The density functional theory (DFT) calculations demonstrate that by introducing Cu atoms into the Pt lattice, a downshift of the D-band center and favorable hydrogen adsorption free energy of approaching to zero (Delta G) occur, indicating the increased electrocatalytic activity of Pt electrocatalysts. (C) 2019 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 25
DOI: 10.1016/J.JCAT.2019.05.031
|
|
|
“Ag nanoparticles on mixed Al2O3-Ga2O3 supports as catalysts for the N-alkylation of amines with alcohols”. Geukens I, Vermoortele F, Meledina M, Turner S, Van Tendeloo G, De Vos DE, Applied catalysis : A : general 469, 373 (2014). http://doi.org/10.1016/j.apcata.2013.09.044
Abstract: The combination of AgNO3 with NaH results in Ag nanoparticles that can selectively perform alcohol aminations under mild reaction conditions (110 °C). NaH not only serves as a reducing agent for the Ag salt, but also activates the alcohol for dehydrogenation to the corresponding ketone/aldehyde. The stability of the particles can be improved by immobilizing them onto mixed Al2O3Ga2O3 supports; the combination of Ga and Al provides materials with stronger Lewis acidic sites compared to pure alumina or gallium oxide supports. This leads to catalysts with enhanced activities, without the necessity of adding external Lewis acids. Detailed TEM characterization also reveals a close interaction between the Ag NPs and the gallium oxide phase. The obtained catalysts are recyclable and show activity for the alcohol amination using a variety of aliphatic and aromatic amines under mild conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 24
DOI: 10.1016/j.apcata.2013.09.044
|
|
|
“Aqueous CSD approach for the growth of novel, lattice-tuned LaxCe1-xO\delta epitaxial layers”. Narayanan V, Lommens P, De Buysser K, Vanpoucke DEP, Huehne R, Molina L, Van Tendeloo G, van der Voort P, Van Driessche I, Journal of materials chemistry 22, 8476 (2012). http://doi.org/10.1039/c2jm15752g
Abstract: Lanthanumcerium oxide (LCO) films were deposited on Ni-5%W substrates by chemical solution deposition (CSD) from water-based precursors. LCO films containing different ratios of lanthanum and cerium ions (from CeO2 to La2Ce2O7) were prepared. The composition of the layers was optimized towards the formation of LCO buffer layers, lattice-matched with the superconducting YBa2Cu3Oy layer, useful for the development of coated conductors. Single, crack-free LCO layers with a thickness of up to 140 nm could be obtained in a single deposition step. The crystallinity and microstructure of these lattice-matched LCO layers were studied by X-ray diffraction techniques, RHEED and SEM. We find that only layers with thickness below 100 nm show a crystalline top surface although both thick and thin layers show good biaxial texture in XRD. On the most promising layers, AFM and (S)TEM were performed to further evaluate their morphology. The overall surface roughness varies between 3.9 and 7.5 nm, while the layers appear much more dense than the frequently used La2Zr2O7 (LZO) systems, showing much smaller nanovoids (12 nm) than the latter system. Their effective buffer layer action was studied using XPS. The thin LCO layers supported the growth of superconducting YBCO deposited using PLD methods.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 24
DOI: 10.1039/c2jm15752g
|
|
|
“Design of Ru-zeolites for hydrogen-free production of conjugated linoleic acid”. Philippaerts A, Goossens S, Vermandel W, Tromp M, Turner S, Geboers J, Van Tendeloo G, Jacobs PA, Sels BF, Chemsuschem 4, 757 (2011). http://doi.org/10.1002/cssc.201100015
Abstract: While conjugated vegetable oils are currently used as additives in the drying agents of oils and paints, they are also attractive molecules for making bio-plastics. Moreover, conjugated oils will soon be accepted as nutritional additives for functional food products. While current manufacture of conjugated vegetable oils or conjugated linoleic acids (CLAs) uses a homogeneous base as isomerisation catalyst, a heterogeneous alternative is not available today. This contribution presents the direct production of CLAs over Ru supported on different zeolites, varying in topology (ZSM-5, BETA, Y), Si/Al ratio and countercation (H+, Na+, Cs+). Ru/Cs-USY, with a Si/Al ratio of 40, was identified as the most active and selective catalyst for isomerisation of methyl linoleate (cis-9,cis-12 (C18:2)) to CLA at 165 °C. Interestingly, no hydrogen pre-treatment of the catalyst or addition of hydrogen donors is required to achieve industrially relevant isomerisation productivities, namely, 0.7 g of CLA per litre of solvent per minute. Moreover, the biologically most active CLA isomers, namely, cis-9,trans-11, trans-10,cis-12 and trans-9,trans-11, were the main products, especially at low catalyst concentrations. Ex situ physicochemical characterisation with CO chemisorption, extended X-ray absorption fine structure measurements, transmission electron microscopy analysis, and temperature-programmed oxidation reveals the presence of highly dispersed RuO2 species in Ru/Cs-USY(40).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.226
Times cited: 24
DOI: 10.1002/cssc.201100015
|
|
|
“Evidence of oxygen-dependent modulation in LuFe2O4”. Bourgeois J, Hervieu M, Poienar M, Abakumov AM, Elkaïm E, Sougrati MT, Porcher F, Damay F, Rouquette J, Van Tendeloo G, Maignan A, Haines J, Martin C;, Physical review : B : condensed matter and materials physics 85, 064102 (2012). http://doi.org/10.1103/PhysRevB.85.064102
Abstract: A polycrystalline sample of LuFe2O4 has been investigated by means of powder synchrotron x-ray and neutron diffraction and transmission electron microscopy (TEM), along with Mössbauer spectroscopy and transport and magnetic properties. A monoclinic distortion is unambiguously evidenced, and the crystal structure is refined in the monoclinic C2/m space group [aM = 5.9563(1) Å, bM = 3.4372(1) Å, cM = 8.6431(1) Å, β = 103.24(1)°]. Along with the previously reported modulations distinctive of the charge-ordering (CO) of the iron species, a new type of incommensurate order is observed, characterized by a vector q⃗1 = α1a⃗M* + γ1c⃗M* (with α1 ≅ 0.55, γ1 ≅ 0.13). In situ heating TEM observations from 300 to 773 K confirm that the satellites associated with q⃗1 vanish completely, only at a temperature significantly higher than the CO temperature. This incommensurate modulation has a displacive character and corresponds primarily to a transverse displacive modulation wave of the Lu cations position, as revealed by the high resolution, high angle annular dark field scanning TEM images and in agreement with synchrotron data refinements. Analyses of vacuum-annealed samples converge toward the hypothesis of a new ordering mechanism, associated with a tiny oxygen deviation from the O4 stoichiometry.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 24
DOI: 10.1103/PhysRevB.85.064102
|
|
|
“Functionalization of MWCNTs with atomic nitrogen”. Ruelle B, Felten A, Ghijsen J, Drube W, Johnson RL, Liang D, Erni R, Van Tendeloo G, Sophie P, Dubois P, Godfroid T, Hecq M, Bittencourt C;, Micron 40, 85 (2009). http://doi.org/10.1016/j.micron.2008.01.003
Abstract: In this study of the changes induced by exposing MWCNTs to a nitrogen plasma, it was found by HRTEM that the atomic nitrogen exposure does not significantly etch the surface of the carbon nanotube (CNT). Nevertheless, the atomic nitrogen generated by a microwave plasma effectively grafts amine, nitrile, amide, and oxime groups onto the CNT surface, as observed by XPS, altering the density of valence electronic states, as seen in UPS. (C) 2008 Elsevier Ltd. All fights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.98
Times cited: 24
DOI: 10.1016/j.micron.2008.01.003
|
|
|
“High resolution electron tomography”. Bals S, Van Aert S, Van Tendeloo G, Current opinion in solid state and materials science 17, 107 (2013). http://doi.org/10.1016/j.cossms.2013.03.001
Abstract: Reaching atomic resolution in 3D has been the ultimate goal in the field of electron tomography for many years. Significant progress, both on the theoretical as well as the experimental side has recently resulted in several exciting examples demonstrating the ability to visualise atoms in 3D. In this paper, we will review the different steps that have pushed the resolution in 3D to the atomic level. A broad range of methodologies and practical examples together with their impact on materials science will be discussed. Finally, we will provide an outlook and will describe future challenges in the field of high resolution electron tomography.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.938
Times cited: 24
DOI: 10.1016/j.cossms.2013.03.001
|
|
|
“Light-assisted nucleation of silver nanowires during polyol synthesis”. Lin H, Ohta T, Paul A, Hutchison JA, Kirilenko D, Lebedev O, Van Tendeloo G, Hofkens J, Uji-i H, Journal of photochemistry and photobiology: A: chemistry 221, 220 (2011). http://doi.org/10.1016/j.jphotochem.2011.04.015
Abstract: This report describes the effect of light irradiation on the synthesis of silver nanowires by the well-known polyol method. High quality nanowires are produced in high yields when the reaction suspension is irradiated with 400500 nm light during the nucleation stage. These studies suggest that light accelerates the formation of the nanoparticle seeds most appropriate for nanowire growth.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.625
Times cited: 24
DOI: 10.1016/j.jphotochem.2011.04.015
|
|
|
“Modified chitosan coated mesoporous strontium hydroxyapatite nanorods as drug carriers”. Filippousi M, Siafaka PI, Amanatiadou EP, Nanaki SG, Nerantzaki M, Bikiaris DN, Vizirianakis IS, Van Tendeloo G, Journal of materials chemistry B : materials for biology and medicine 3, 5991 (2015). http://doi.org/10.1039/c5tb00827a
Abstract: Mesoporous strontium hydroxyapatite (SrHAp) nanorods (NRs) have been successfully synthesized using a simple and efficient chemical route, i.e. the hydrothermal method. Structural and morphological characterization of the as-synthesized SrHAp NRs have been performed by transmission electron microscopy (TEM) and high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). TEM and HAADF-STEM measurements of the NRs reveal the coexistence of longer and shorter particles with the length ranging from 50 nm to 400 nm and a diameter of about 20-40 nm. Electron tomography measurements of the NRs allow us to better visualize the mesopores and their facets. Two model drugs, hydrophobic risperidone and hydrophilic pramipexole, were loaded into the SrHAp NRs. These nanorods were coated using a modified chitosan (CS) with poly(2-hydroxyethyl methacrylate) (PHEMA), in order to encapsulate the drug-loaded SrHAp nanoparticles and reduce the cytotoxicity of the loaded materials. The drug release from neat and encapsulated SrHAp NRs mainly depends on the drug hydrophilicity. Importantly, although neat SrHAp nanorods exhibit some cytotoxicity against Caco-2 cells, the Cs-g-PHEMA-SrHAp drug-loaded nanorods show an acceptable cytocompatibility.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.543
Times cited: 24
DOI: 10.1039/c5tb00827a
|
|
|
“Modulated formation of MOF-5 nanoparticles : a SANS analysis”. Nayuk R, Zacher D, Schweins R, Wiktor C, Fischer RA, Van Tendeloo G, Huber K, The journal of physical chemistry: C : nanomaterials and interfaces 116, 6127 (2012). http://doi.org/10.1021/jp3003728
Abstract: MOF-5 nanoparticles were prepared by mixing a solution of [Zn4O(C6H5COO)(6)] with a solution of benzene-1,4-dicarboxylic acid in DMF at ambient conditions. The former species mimics as a secondary building unit (SBU), and the latter acts as linker. Mixing of the two solutions induced the formation of MOF-5 nanoparticles in dilute suspension. The applied conditions were identified as suitable for a closer investigation of the particle formation process by combined light and small angle neutron scattering (SANS). Scattering analysis revealed a significant impact of the molar ratio of the two components in the reaction mixture. Excessive use of the building unit slowed down the process. A similar effect was observed upon addition of 4n-decylbenzoic acid, which is supposed to act as a modulator. The formation mechanism leads to initial intermediates, which turn into cubelike nanoparticles with a diameter of about 60-80 nm. This initial stage is followed by an extended formation period, where nucleation proceeds over hours, leading to an increasing number of nanoparticles with the same final size of 60-80 nm.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 24
DOI: 10.1021/jp3003728
|
|
|
“Multi-step loading of titania on mesoporous silica: influence of the morphology and the porosity on the catalytic degradation of aqueous pollutants and VOC's”. de Witte K, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Sepúlveda-Escribano A, Rodríguez-Reinoso F, Vansant EF, Cool P, Applied catalysis : B : environmental 84, 125 (2008). http://doi.org/10.1016/j.apcatb.2008.03.015
Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 9.446
Times cited: 24
DOI: 10.1016/j.apcatb.2008.03.015
|
|
|
“Room temperature and low-temperature structure of Nd1-xCaxMnO3 (0.3*x*0.5)”. Richard O, Schuddinck W, Van Tendeloo G, Millange F, Hervieu M, Caignaert C, Raveau B, Acta crystallographica: section A: foundations of crystallography 55, 704 (1999). http://doi.org/10.1107/S0108767398012215
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.725
Times cited: 24
DOI: 10.1107/S0108767398012215
|
|
|
“Selectivity in sorption and hydrogenation of methyl oleate and elaidate on MFI zeolites”. Philippaerts A, Paulussen S, Turner S, Lebedev OI, Van Tendeloo G, Poelman H, Bulut M, de Clippel F, Smeets P, Sels B, Jacobs P, Journal of catalysis 270, 172 (2010). http://doi.org/10.1016/j.jcat.2009.12.022
Abstract: Different zeolites were tested for selective removal of methyl elaidate (trans isomer) from an equimolar mixture with methyl oleate (cis isomer). Sorption experiments of the geometric isomers show that only ZSM-5 samples with reduced Al content in the framework are able to discriminate among the bent cis and the linear trans fatty acid methyl esters. Hydrogenation experiments of equimolar methyl oleate and elaidate mixtures at low temperature (65 °C) and high hydrogen pressure (6.0 MPa), using Pt catalysts, confirm this result. Only with a Pt/NaZSM-5 catalyst outspoken selectivity for the hydrogenation of the trans isomer is obtained. In order to prepare a selective Pt/ZSM-5 catalyst, the influence of Pt addition (impregnation, ion-exchange and competitive ion-exchange) and Pt activation (different calcination and reduction temperatures) on the Pt-distribution and Pt particle size was investigated using SEM, bright-field and HR TEM, EDX, electron tomography, CO-chemisorption, XPS, XRD, and UVvis measurements. The best result in terms of hydrogenation activity and selectivity is obtained with a Pt/ZSM-5 catalyst, which is prepared via competitive ion-exchange, followed by slow calcination up to 350 °C under high O2 flow and a reduction up to 500 °C under H2. This preparation method leads to a Pt/ZSM-5 catalyst with the best Pt distribution and the smallest Pt clusters occluded in the zeolite structure. Finally, the influence of zeolite crystal size, morphology, and elemental composition of ZSM-5 on hydrogenation activity and selectivity was investigated in detail.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 24
DOI: 10.1016/j.jcat.2009.12.022
|
|
|
“Structural and magnetotransport transitions in the electron-doped Pr1-xSrxMnO3(0.85\leq x\leq1) manganites”. Hervieu M, Martin C, Maignan A, Van Tendeloo G, Jirak Z, Hejtmanek J, Barnabe A, Thopart D, Raveau B, Chemistry and materials 12, 1456 (2000). http://doi.org/10.1021/cm000016o
Abstract: The exploration of the Mn4+-rich side of the Pr1-xSrxMnO3 system has allowed the extension of the domain of the cubic perovskite, by using a two-step process, combining synthesis under Ar flow at high temperature and O-2 pressure annealing at lower temperature. We show that these Pr-doped cubic perovskites exhibit a coupled structural (cubic-tetragonal) and magnetic (para-antiferro) transition connected with a resistivity jump at the same temperature. The strong interplay between lattice, charges, and spins for these oxides results from the appearance at low temperature of the distorted C-type antiferromagnetic structure. The Pr1-xSrxMnO3 magnetic phase diagram shows, for 0.9 less than or equal to x less than or equal to 1 (i.e., on the Mn4+-rich side), the existence at low temperature of C- and G-type antiferromagnetism. The absence of ferromagnetic-antiferromagnetic competition explains that magnetoresistante properties are not observed in this system, in contrast to Mn4+-rich Ln(1-x)Ca(x)MnO(3) systems.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 24
DOI: 10.1021/cm000016o
|
|
|
“Synthesis and crystal structure of the palladium oxides NaPd3O4, Na2PdO3 and K3Pd2O4”. Panin RV, Khasanova NR, Abakumov AM, Antipov EV, Van Tendeloo G, Schnelle W, Journal of solid state chemistry 180, 1566 (2007). http://doi.org/10.1016/j.jssc.2007.03.005
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 24
DOI: 10.1016/j.jssc.2007.03.005
|
|